Study on the Superhydrophilicity of the SiO2-TiO2 Thin Films Prepared by Sol-Gel Method at Room Temperature

Nanoscale SiO₂-TiO₂ composite thin films with the thickness of about 100 nm were prepared by sol-gel method at room temperature in air. The chemical states of the elements on the surface and near the surface were measured by XPS. The results showed that the Ti on/near the surface of the thin films existed not only as TiO₂ but also as Ti₂O₃. Part of the TiO₂ was changed to Ti₂O₃ after UV irradiation. The crystalline structure of the TiO₂ in the SiO₂-TiO₂ thin films was anatase with the crystallite size of 14–20 nm. It was found that the thin film prepared at room temperature in air has good superhydrophilic property and has strong adherence to the substrate.     

Relationship between the dynamic softening transition and wet sliding friction of elastomer compounds

For properly chosen elastomer compounds, thermorheological characterization is combined with an examination of the variation of the wet sliding friction with temperature. A conceptual argument leads to the assumption that the wet sliding friction should maximize at the energy dissipation peak associated with the dynamic softening transition at a characteristic frequency determined by the sliding speed and the effective smallest surface asperity scale. The dynamic softening transition is characterized with the peak in tan δ/G′ⁿ, where tan δ is the loss tangent, G′ is the elastic modulus, and n is a constant between 0 and 1. The William–Landel–Ferry transform is uncritically applied for extrapolating the position of the peak in tan δ/G′ⁿ at high frequencies. Even based on the criterion of tan δ, the results obtained on a concrete surface indicate that the effective smallest asperity scale is of order of 100 μm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2467–2478, 2004     

高压增氧T′相R_2CuO_(4+δ)(R=Nd～Tm)低温磁性研究

T′相R2CuO4稀土铜氧化合物由于尺度效应而产生弱铁磁性行为已经被人们关注,报导了通过高温高氧压(6GPa,1000℃)合成稀土T′相R2CuO4(R=Nd,Sm,Eu,Gd,Tb,Dy,Ho,Er和Tm)化合物的结构和磁学性能。磁化率曲线显示,在低温下所有的高压增氧R2CuO4样品都出现新的低温弱铁磁性反常行为,转变温度在28K附近。新的低温弱铁磁性行为是由于CuO2面上微量氧空穴的掺入,使处于反铁磁有序CuO2面形成局域化的铁磁性团簇造成。实验证明新发现的低温弱铁磁性行为与尺度效应产生弱铁磁性行为属于完全不同的物理机制。结果还预示T′相R2CuO4稀土铜氧化合物很难通过空穴掺杂而实现超导。     

离子束增强沉积VO2多晶薄膜的温度系数

用改进的离子束增强沉积方法和恰当的退火从V2O5粉末直接制备了VO2多晶薄膜.实验测试表明，薄膜的取向单一、相变特性显著、结构致密、界面结合牢固、工艺性能良好，薄膜的电阻温度系数（TCR）最高可达4.23%/K.从成膜机理出发，较详细地讨论了离子束增强沉积 VO2多晶薄膜的TCR高于VOx薄膜的TCR的原因.分析认为，单一取向的VO2结构使薄膜晶粒具有较高的电导激活能，致密的薄膜结构减少了氧空位和晶界宽度，使离子束增强沉积 VO2多晶薄膜结构比其他方法制备的VOx薄膜更接近于单晶VO2是其具有高TCR的原 关键词： VO2多晶薄膜 离子束增强沉积 热电阻温度系数     

双阳极磁控注入枪束流特性的研究

 介绍了用于34GHz基波回旋速调管的双阳极磁控注入枪的结构特点，为了准确分析磁控注入枪的束流特性，建立了阴极表面理论模型，用新编制的程序模拟了电子轨迹。模拟和测量结果显示磁场对磁控注入枪的束流有影响，磁控注入枪的束流也与阴极温度和空间电荷效应有关系。     

Prediction of critical temperature of n-alkanes and n-alkenes from surface tension vs. temperature data

 The surface tension versus temperature data of homologous series of n-alkanes and n-alkenes is analyzed. Critical temperatures are shown to be predicted from these data, with a very high precision, after some corrections are made. The corrections are shown to arise from the effect of the critical pressure on the extrapolated data to surface tension approaching zero. Received: 29 October 1996 Accepted: 13 December 1996     

一种漂移室定位子性能反常现象的研究

研究了一种漂移室定位子性能的反常现象,它关系到定位子的使用寿命．着重测量了暗电流和随机噪声与时间、高压及温度的关系.     

折射率温敏式光纤温度传感器的理论模型

提出了折射率温敏式光纤温度传感器的理论模型，包括子午光线和偏射光线的影响，讨论了多模光纤的弯曲损耗，理论的分析和结果与实验相当一致。     

N_2和O_2纯转动拉曼光谱(PRRS)的温度特性

计算了N2 和O2 的PRRS ,讨论了其温度特性。提出通过测量N2 和O2 的PRRS计算大气温度的方法。     

线状锗等离子体X射线线谱的时间分辨测量

用自行研制的X射线条纹晶体谱仪首次测量了线状锗等离子体的X射线时间分辨谱。给出了类Ne-锗L线共振线的时间演化过程,并用类Ne-锗L线共振线与其双电子俘获伴线的相对强度比粗估了锗等离子体的电子温度及其随时间的变化,实验给出了X光激光增益区介质的电子温度为400～760eV,同时给出了电子温度保持相对恒定的时间不小于90ps(电子温度变化小于2％)。