水热法合成K0.5Bi0.5TiO3纳米陶瓷粉体

K_0.5Bi_0.5TiO₃(KBT)nanocrystalline particles were hydrothermally synthesized from Bi(NO₃)₃·5H₂O, TiO₂ and KOH. The crystal phase, chemical composition and microstructure were characterized by XRD, XRF, Raman scattering spectroscopy and TEM. The results indicated that the products were pure perovskite structured K_0.5Bi_0.5TiO₃ with chemical stoichiometry and perovskite structure. The TEM observation revealed that the particles possessed a feature of cubic shape and a nano-scale of about 40 nm. The KBT ceramics sintered at 1 040 ℃ from hydrothermal powders show higher density and better electric properties than that prepared by a solid-state reaction method.     

N,N-双(α-萘基-苯基)-4,4''''-联苯二胺纳米管的制备及其光谱行为

利用多孔氧化铝作模板采用熔融法成功制备了一种定向有序排列的有机小分子(NPB)纳米管,并用场发射扫描电镜(FESEM)、 X射线能量损失谱(EDX)、透射电子显微镜(TEM)和荧光显微镜对其进行了表征.发现该纳米管具有整齐的形貌和规整的尺寸.进一步的研究表明,多孔氧化铝模板的亲油亲水处理对能否成功地大量获得纳米管起到非常重要的作用.值得注意的是,在对不同尺寸纳米管材荧光光谱的测定中,可明确观察到材料光学性质的尺寸依赖性.     

一种新型钛体系（Ⅳ）──α－酮酸钛酸酯与锂试剂的还原反应

一种新型钛体系（Ⅳ）──α－酮酸钛酸酯与锂试剂的还原反应段新方，尹承烈（北京师范大学化学系，北京，１００８７５）关键词加成，还原，钛酸酯，交换反应由于钛的优良调整作用，使得锂试剂ＲＬｉ不仅可以和α－酮酸钛酸酯ＡｒＣＯＣＯＯＴｉ（ＯＲ１）３中的酮发生加...     

具有超大通道结构的介孔氧化硅柱层状钛酸的合成和催化应用初探

A mesoporous (d=2.3mm) silica-pillared layered tetratitanate with a super gallery (d₀₀₁=1.84mm)was prepared by first preswelling layered tetratitanate with n-dodecyl amine, then reacting with 20wt% NH₂(CH₂)₃Si(OC₂H₅)₃ aqueous solution, and finally calcinating the resultant solid product in air at 550℃. All the reaction was carried out hydrothermally in an autoclave at 130℃. The obtained material has a relatively high BET surface area of 204m²·g^-1 and a thermal stability beyond 600℃. The catalytic application of the material was also investigated by using the dehydration of isopropanol and the reform of n-hexane as two probing reactions.     

POPOP诱导环糊精形成纳米管的研究

用紫外吸收光谱、稳态荧光、荧光各向异性和动态光散射等方法研究了2,2′-p-亚苯基-双(5-苯基噁唑) (POPOP)分子与环糊精(CD)的相互作用. 结果表明, POPOP分子在浓度较低时与β-CD形成1:2的包合物, 在浓度较高时可以进一步诱导β-CD形成纳米管结构. 同时发现, POPOP分子也可以诱导γ-CD形成纳米管结构. 对比于β-CD, POPOP分子在γ-CD水溶液中的荧光发射峰, 不仅有明显的红移而且也缺失了精细结构, 呈现较宽的大包峰. 这是由于POPOP分子成对进入γ-CD空腔形成了激基缔合物的缘故. pH和温度效应实验进一步表明, POPOP诱导β-CD形成的纳米管在pH大于12和温度高于331 K的环境下不能稳定存在.     

乙醇在碳修饰的二氧化钛纳米管负载的钯电催化剂上的催化氧化

 通过有机物分解碳化处理TiO2 纳米管制得了TiO2C, 并以其为载体制备了Pd/TiO2C电催化剂,考察了该催化剂对碱性介质中乙醇电催化氧化的活性. 结果表明,碳化导电处理的TiO2C纳米管载体能有效改善催化剂中贵金属的分散度和电极结构,从而提高催化剂的电催化活性. 对催化剂活性组分的优化实验表明, Pd/TiO2C质量比为1/1时催化剂的活性最高. 在1 mol/L KOH溶液中Pd载量均为0.3 mg/cm2的条件下, Pd/TiO2C催化剂对乙醇氧化的催化活性是Pd/C催化剂的3.8倍.     

纳米晶PbTiO3负载CuO催化NO分解

A large specific surface area perovskite-type mixed oxide PbTiO₃ supported cupric oxide was synthesized as a catalyst for NO decomposition and characterized by techniques such as XPS, XRD, H₂-TPR before and after NO decomposition reactions. The catalytic properties were tested with a fix-bed micro-reactor. The results showed that the PbTiO₃ was inactive for the reactions, but 1wt % Cu/PbTiO₃ catalyst gave fairly good activities for NO decomposition at temperature as low as 473 K. Copper species were found well-dispersed but weakly interacted with the support before NO decomposition, and the NO decomposition caused significant change in the environment of the copper species, which became Cu(Ⅰ) and most probably incorporated into surface crystal lattice of the nano-sized PbTiO₃. In NO reaction, a large amount of oxygen atoms from the decomposition of NO penetrated into the nano-sized PbTiO₃ support and caused small expansion of crystal lattice. The transport of oxygen between the copper species and the catalyst support may be helpful to speed up the kinetic regeneration of active metal sites from oxygen occupancy and resulted in good catalytic performance.     

一种制备大量氧化锌纳米管的简单方法(英)

ZnO nanotubes were synthesized in large scale by thermal decomposition of the precursors obtained via chemical reaction between Zn(CH₃COO)₂·2H₂O and NaHCO₃ in the presence of surfactant sodium dodecyl sulfate (SDS). The inner diameters of the tubes were in the range of 80～100 nm, and outer diameters in the range of 160～260 nm with lengths up to a few micrometers. The products were characterized with XRD, TEM, and SEM.     

N-TiO2/ZnO复合纳米管阵列的掺杂机理及其光催化活性

以ZnO纳米柱阵列为模板, 采用溶胶-凝胶法制备出TiO2/ZnO和N掺杂TiO2/ZnO的复合纳米管阵列. 扫描电镜(SEM)、X射线光电子能谱(XPS)和紫外-可见漫反射吸收光谱(UV-Vis)的结果表明: 两种阵列的纳米管均为六角形结构, 直径约为100 nm, 壁厚约为20 nm; 在N-TiO2/ZnO复合纳米管阵列中, 掺入的N离子主要是以N-Ox、N-C和N-N的形式化学吸附在纳米管表面, 仅有少量的N离子以取代式掺杂的方式占据TiO2晶格O的位置; 表面N物种形成的表面态能级和取代式掺杂导致带隙的窄化, 增强了纳米管阵列的光吸收效率, 促进了光生载流子的分离. 光催化实验结果表明, N离子的掺杂有利于N-TiO2/ZnO复合纳米管阵列光催化活性的提高.     

N-TiO2/ZnO复合纳米管阵列的掺杂机理及其光催化活性

以ZnO纳米柱阵列为模板, 采用溶胶-凝胶法制备出TiO2/ZnO和N掺杂TiO2/ZnO的复合纳米管阵列. 扫描电镜(SEM)、X射线光电子能谱(XPS)和紫外-可见漫反射吸收光谱(UV-Vis)的结果表明: 两种阵列的纳米管均为六角形结构, 直径约为100 nm, 壁厚约为20 nm; 在N-TiO2/ZnO复合纳米管阵列中, 掺入的N离子主要是以N-Ox、N-C和N-N的形式化学吸附在纳米管表面, 仅有少量的N离子以取代式掺杂的方式占据TiO2晶格O的位置; 表面N物种形成的表面态能级和取代式掺杂导致带隙的窄化, 增强了纳米管阵列的光吸收效率, 促进了光生载流子的分离. 光催化实验结果表明, N离子的掺杂有利于N-TiO2/ZnO复合纳米管阵列光催化活性的提高.