中空介孔SiO2纳米球的制备、改性及其对Al3+荧光识别研究

中空介孔SiO2由于中空多孔的结构而常用作功能材料的基底.将中空介孔SiO2进行官能团修饰,并应用为荧光传感材料是中空介孔SiO2一个重要的研究领域.本论文采用聚丙烯酸(PAA)为中空模板,聚醚F127为造孔剂,正硅酸乙酯(TEOS)为硅源,氨水为催化剂在乙醇体系中制备了中空介孔SiO2纳米球.系统研究了搅拌速度和聚醚F127引入量对中空介孔SiO2纳米球形貌及比表面积的影响.通过透射电镜、N2-等温吸附脱附曲线等表征说明该合成方法具有很好的普适性,通过调节F127的引入可以实现对比表面积的有效控制.通过氨基化、席夫碱反应进行荧光修饰,进一步研究表明荧光修饰后的中空介孔SiO2纳米球在水溶液中能够实现对Al3+的有效检测,检测限为1.19×10 -7M.     

四方体MgO的制备及对有机染料的吸附

以六水氯化镁和六次甲基四胺为原料,采用水热法合成四方体MgO,考察其对有机染料甲基橙和亚甲基蓝的吸附行为.通过TGA-DTA、SEM、XRD、N2-sorption和FT-IR等手段表征样品.结果表明,原料浓度、温度和表面活性剂对四方体MgO结构的形成影响较小,而反应时间的延长有助于有序结构的组装.温度170℃、时间24h、MgCl2·6H2O与C6H12N4浓度比为1∶2和表面活性剂PVP是制备四方体MgO的最佳条件.在溶液浓度10mg · L-1的单一吸附实验过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为91.3;和22.3;,吸附过程均为单层吸附且符合Langmuir等温吸附模型和伪二级吸附动力学方程.在溶液浓度40 mg·L-1、甲基橙和亚甲基蓝浓度比3∶1的混合溶液吸附过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为80.1;和97.9;.     

减压扩散高阻密栅技术应用研究

本文对减压扩散机理及高阻密栅技术作了详细的分析,并就设备及工艺方面的关键技术进行了阐述,最后对减压扩散高方阻工艺及密栅匹配技术电池效率进行了对比分析,有以下结论:(1)减压扩散在工艺优化后,方阻均匀性得到大幅改善,达到3;以内.(2)减压扩散电池效率完全可达到常规产线的水平,且在高阻密栅方面更有优势,可有效提升太阳电池效率.     

纳米CeO2吸附剂的制备及对六价铬的吸附性能

吸附法是去除水中重金属离子的重要方法,开发新型吸附剂一直是研究热点.利用浸渍法和水热法制备了片状和无定形的纳米CeO2吸附剂,探讨其对六价铬的吸附性能,分析pH、吸附时间、六价铬初始浓度等因素对其吸附性能的影响,并通过循环吸附实验考察纳米CeO2吸附剂的再生能力.结果表明:厚度30 nm、直径大小约为400 nm的片状CeO2吸附剂具有更强的吸附能力和更快的吸附速率,80 min时基本达到吸附平衡;两种吸附剂的最佳吸附pH为3;吸附动力学均符合伪二级动力学方程,Langmuir模型和Freundlich模型均能很好地拟合等温吸附过程,表明纳米CeO2对六价铬的吸附以单层吸附为主.片状CeO2四次吸附-解吸实验之后吸附率稍有下降,表明片状CeO2吸附剂有较好的再生能力,因而,该片状CeO2吸附剂适用于与酸性Cr(Ⅵ)废水的处理.     

烧结温度对煤系高岭土制备堇青石陶瓷的影响

我国的煤系高岭土具有明显的资源优势,应对其进行充分地研究和合理地应用,以缓和优质高岭土资源枯竭的燃眉之急.以鄂尔多斯煤系高岭土、鄂尔多斯滑石、工业氧化铝为原料,通过反应烧结一步合成堇青石,探讨了堇青石合成温度范围,以拓宽该煤系高岭土的应用范围.通过高温显微镜观察堇青石试样的合成温度范围为1400～1420℃.经1420℃合成的堇青石试样的吸水率为16.11;,显气孔率为28.44;,体积密度为1.77 g/cm3,径向烧成收缩为1.77;,厚度烧成收缩为4.80;,抗折强度为43.56 MPa.镁铝尖晶石是合成堇青石的重要中间产物,适当提高烧结温度可以促进镁铝尖晶石相向堇青石相转变,有利于堇青石晶粒的生长与发育.烧结温度的变化是堇青石晶粒发生变化的原因,同时导致液相量的变化,最终影响堇青石试样显微结构和烧结性能.     

A post curing strategy toward the feasible covalent adaptable networks in polyacrylate latex films

The implementation of covalent adaptable networks (CANs) in general resin system is becoming attractive. In this work, we propose a simple post-curing strategy based on the core-shell structured acrylate latex for the achievement on both the improved general performance and the CANs characteristics in latex films. The building to the CANs was relied on the introduction of 4,4′-diaminophenyl disulfide as the curing agent, which cured the acetoacetoxy decorated shell polymer through the ketoamine reaction. The metathesis reaction of aromatic disulfides in the crosslinking segments enabled the thermally induced dynamic behavior of the network as revealed in the stress relaxation tests by comparison with other diamine crosslinking agents without the incorporation of disulfide. The synergism of the dynamic crosslinking of the shell polymer and static crosslinking in the core polymer contributed to the improved mechanical strength (15 MPa, strain% = 250%) and the suppressed water adsorption (~1% in 24 h of soaking) of the latex film, which exhibited above 90% of recovery in both strength and strain from a cut-off film damage within 1 h at 80°C. Moreover, the cured latex film could be recycled, and 75% of the mechanical performance was regained after three fragmentation-hot-pressing cycles. These, in addition with the feasible and environmental friendly characteristics, suggest a sustainable paradigm toward the smart thermosetting latex polymers.     

红外动态场景生成装置空间分辨率的测试

建立了一套基于刀口灰度图红外探测的实验装置,对红外场景生成器的空间分辨率进行了测试。首先通过被测红外场景生成器产生带有刀口标志的红外图像,然后利用红外热像仪采集红外场景生成器所成的红外图像,通过对采集到的红外热图的数据处理,实现了对红外场景生成器空间分辨率的测量。测得的红外场景生成器的空间分辨率为5lp/mm,标准误差为0.04。     

离子对反相高效液相色谱法同时测定尿液中复方α-酮酸片的5种有效成分

建立了同时测定尿液中复方α-酮酸片5种有效成分(消旋羟蛋氨酸钙(HMACa)、酮缬氨酸钙(KVCa)、消旋酮异亮氨酸钙(KILCa)、酮亮氨酸钙(KLCa)和酮苯丙氨酸钙(KPACa))的离子对反相高效液相色谱法。分别考察了离子对试剂浓度、缓冲盐浓度和流动相pH值等参数对分离情况的影响。最终采用Waters Symmetry C18色谱柱(250 mm×4.6 mm,5μm);以乙腈和含15 mmol/L四丁基氢氧化铵的20 mmol/L磷酸盐缓冲液(pH 7.0)为流动相进行梯度洗脱,流速为1.0 mL/min;柱温为35℃;检测波长为210 nm。在上述条件下,5种有效成分得到很好的分离,并且不受尿液中内源性基质的干扰,在20~200 mg/L范围内线性关系良好(r≥0.999 0);HMACa、KVCa、KILCa、KLCa和KPACa的检出限(S/N=3)分别为3.0、5.0、3.6、5.7和2.5 mg/L;定量限(S/N=10)分别为9.6、16.7、12.0、19.0和8.3 mg/L;日间、日内精密度均小于7%;平均回收率在86.79%~112.00%之间,RSD小于9%(n=5)。该方法准确,灵敏度高,重现性好,适用于尿液中这5种有效成分的检测。     

Cu2O/TiO2-Bi2WO6三元复合催化剂的制备及光催化性能研究

采用水热法制备花状Bi2 WO6,并利用超声分散法制备了Cu2 O/TiO2-Bi2 WO6复合光催化剂,通过FESEM、XRD、XPS、FI-IR、UV-vis DRS和PL对光催化剂进行了分析和表征.表征结果证明:花状Bi2 WO6表面负载着碎片状的TiO2和立方体Cu2 O形成Cu2 O/TiO2-Bi2 WO6复合光催化剂;以短链脂肪酸(SCFAs)为牺牲剂,考察复合光催化剂的光催化产生氢气和烷烃的性能.实验结果表明:Cu2 O/TiO2-Bi2 WO6复合光催化剂以乙酸为牺牲剂,主要产氢气和甲烷,降解率高达91.82;;以丙酸为牺牲剂,产物主要是乙烷和丁烷,降解率高达90.70;;以丁酸为牺牲剂,除了氢气,甲烷,乙烷,丙烷,丁烷外,气体产物还含有一定量的戊烷,其降解率高达91.50;.结合反应液中间产物的成分进行检测,由此推断出光催化反应的可能机理.