微波合成a＆b取向的T型分子筛膜及其在渗透汽化耦合酯化反应中的应用

利用微波辅助水热合成法制备了高性能的a&b取向的T型分子筛膜. 并用于乙酸与正丁醇的渗透汽化耦合反应,结果表明, T型分子筛膜可以有效地从反应混合物中脱出产物水,其它反应物与产物仍留在反应体系中,反应转化率可以达到100%.     

Ba,Fe掺杂La-Co-O系列混合导电型透氧膜研究

采用改进的Ｐｅｃｈｉｎｉ法合成了Ｌａ（Ｂａ）Ｃｏ（Ｆｅ）Ｏ３－δ系列透氧膜材料,考察了Ｂａ和Ｆｅ掺和量对材料的结构、氧脱附性能及透氧性能等的影响的提高;Ｆｅ的引入使材料在较高Ｂａ掺杂量时也能保持稳定的钙钛矿结构,同时使材料的密封性能较好,稳定操作时间加长,氧在低温区的脱附量增大。     

MCM-22型分子筛的合成及其用于生产异丙苯的催化性能

MCM-22 molecular sieve was first reported by Rubin et al[1] in Mobil Company.Similar to ZSM-5 zeolite, MCM-22 belongs to the category of medium pore zeolites.However, it possesses unique structural features[2] that have not been demonstrated before. The structure of MCM-22 was resolved by Mobil scientists using high resolution microscopy and X-ray diffraction analysis. It is found that MCM-22 consists of two independent and non-interconnecting channel systems, each accessible through 10-ring apertures. One of these pore systems is composed of uniform circular 10-ring pores about 0.6 nm. The other is composed of 12-ring egg-shaped supercages with inner free diameter of 0.71 nm and inner height of 1.82 nm. Usually the zeolite crystallizes as thin sheets or plates of stocked layers. Therefore, MCM-22 has been actively studied and this peculiar zeolite may have potential applications in the petrochemical and petroleum industries in the near future, including reactions such as disproportionation[3], catalytic cracking of hydrocarbons[4], aromatic/ethylene alkylation[5], isoalkane/olefins[6] and methanol/olefins alkylation[7] etc.     

担载型钼催化剂上的丙烷芳构化

与新鲜Ｍｏ／ＨＺＳＭ－５（Ｆ）催化剂相比,于９７３Ｋ以甲烷活化后的Ｍｏ／ＨＺＳＭ－５（Ａ）对丙烷芳构化的活性和芳烃选择性都得到显著提高,芳烃的收率从３．３５％提高到１３．８２％,根据催化剂（Ｆ）用于甲烷芳构化时存在活性诱导期,结合本实验的丙烷芳构化结果及ＸＲＤ结果,提出担载于分子筛表面的ＭｏＯ３经甲烷活化后转化为α－Ｍｏ２Ｃ后才对烷烃芳构化有较高活性。碳化钼是活性相,它的作用不在于活化烷烃,而是为     

甲烷芳构化的内标分析法与放大回收实验

将内标 分析法 用于 Ｍｏ／ Ｈ Ｚ Ｓ Ｍ５ 催化的 甲烷非 氧芳 构化 反应 的 产物 分 析,较 准确 地 得出了甲烷 转化率 及各产物 和积炭的 选择性 ． 采用 单管放大 实验和 烧炭实验 验证了 内标分析 法的可靠性． 在催化剂 成型过 程中对载 体表面 的适当改 性可抑制 由粘结 剂引起的 严重积 炭．     

澄清溶液中NaA型分子筛膜的合成及气体渗透性能

The use of zeolite membranes in separation or combined reaction and separation processes is very attractive. Advantages of using such a type of membranes include their ability to discriminate molecules based on the molecular size and their stability[1]. In the past ten years, most efforts were involved in the synthesis and permeation studies of MFI zeolite membrane[2, 3]. Recently, NaA zeolite membrane has attracted much attention because of its high potential in the dehydration of organic liquids[4]. However, few gas permeation results were reported[5]. Furthermore, most of the NaA zeolite membrane was synthesized from gel[4]. In this letter, the synthesis of NaA zeolite membrane from clear solution and its gas permeation properties are reported.     

烃类转化多金属催化剂的研究——铂、铱、金重整催化剂的研究

本文研究在氧化铝表面上,高分散度多金属值化剂金属相互作用和反应性能的关系。以正庚烷和甲基环戊烷为原料,模拟重整的芳构化和加氢裂解反应。发现在铂值化剂中加入金时甲基环戊烷氢解活性下降,芳构化选择性提高。在铱催化剂中加入金时,则氢解括性明显地提高,脱氢环化选择性下降。而铂、铱、金三元催化剂在芳构化选择性和稳定性方面都优于双组份或单组份催化剂。上述结果表明,各种金属的相互影响所产生的复杂效果对多金属催化剂选择性和稳定性的改变起重要作用。     

有机-无机杂化L-Rh／SiO2氢甲酰化催化剂的研究I．PPh3-Rh／SiO2的催化性能及表征

利用有机-无机杂化的概念，以三苯基膦直接修饰Rh／SiO2制备了PPh3-Rh／SiO2多相催化剂．在浆态床烯烃氢甲酰化反应中，该催化剂在1．0MPa，373K温和条件下的活性和选择性远高于Rh／SiO2的活性和选择性，与相应的均相催化剂HRhCO(PPh3)3的性能相当，且具有易分离的优点．^31P MAS NMR和XPS技术表征结果表明，催化剂中的配体PPh3与高度分散的Rh之间存在配位作用，形成了兼具多相和均相催化性能的有机一无机杂化催化剂．该催化剂对不同碳数烯烃的氢甲酰化反应都具有较好的催化性能．     

乙苯在Pt、Re、Sn/Al_2O_3系催化剂上的程序升温表面反应

本文通过乙苯在氢气流和氦气流中的程序升温表面反应,考察了Pt系、Re系及Pt-Re系催化剂中金属K和Sn的作用,结果认为K可降低催化剂的脱甲基性能和裂解性能,而Sn却极大地抑制了催化剂的脱甲基性能和裂解性能,同时认为Re-K/Al_2O_3催化剂比Pt-K/Al_2O_3的脱甲基能力大得多,且在Re-K/Al_2O_3中加入Pt后脱甲基能力和脱乙基能力都更进一步提高,而若在Pt-Re-K/Al_2O_3中加入Sn则能抑制Pt的裂解活性而不影响其脱氢活性,从而改善了乙苯脱氢的选择性。