带羧基单分散彩色微球的制备

采用两步活性溶胀种子聚合法, 制备了可用于免疫检测的3种不同颜色的表面带有羧基功能基的粒径在400—800 nm之间的彩色单分散微球. 先用无皂乳液聚合法制备出单分散聚苯乙烯种子, 然后用邻苯二甲酸二正丁酯(DBP)作为溶胀剂对微球进行溶胀, 溶涨后的种子模板再用混溶的苯乙烯、二乙烯苯、丙烯酸、双键彩色染料以及引发剂(BPO)溶胀, 升温聚合后得到理想的单分散微球. 考察了DBP和单体用量、各单体配比及染料对微球的形貌和单分散性的影响.     

分散聚合-种子溶胀聚合法制备中空微球的研究

采用分散聚合法制备聚苯乙烯(PSt).以甲苯一正辛醇作致孔溶剂,过氧化苯甲酰为引发剂,PSt为单分散种球,反应单体苯乙烯和交联单体二乙烯基苯(DVB)通过种子溶胀聚合法,在水介质中制备了呈单分散的中空聚合物微球[P(St-DVB),粒径5 μm-8μm],其形态及热力学行为经SEM,DSC和TGA表征.讨论了DVB用量及溶剂组成对P(St-DVB)形态的影响.     

单分散PS/PAA聚合物微球的研制

以苯乙烯为单体,采用分散聚合法制备了单分散性的聚苯乙烯(PS)微球,然后以PS微球作为种子、丙烯酸(AA)进行无皂种子乳液聚合制备了PS／PAA微球。考察了单体、引发剂、分散剂用量,反应介质极性和交链剂等因素对微球粒径大小及其分布的影响,探讨了分散聚合的反应机理。结果表明,通过改变反应工艺条件,能够制备粒径为1．0～3．0μm、单分散性很好的PS微球;通过无皂种子乳液聚合得到的核壳结构的PS／PAA微球粒径为2．50μm,多分散系数(PI)为0．0325,酸值为10．27mgNaOH／g,其表面带有羧基的特性能进一步扩大应用范围。     

苯乙烯和N-乙烯基吡咯烷酮共聚物/Ag复合微球的制备及性能研究

首先用无皂乳液聚合法制备了单分散聚苯乙烯(PSt)乳液,以此为种子乳液,使用N,N-亚甲基双丙烯酰胺(MBA)为交联剂,过硫酸钾(KPS)为引发剂,进行苯乙烯和N-乙烯基吡咯烷酮(NVP)共聚合制备了以PSt为核、St和NVP共聚物为壳的具有核-壳结构的聚合物微球(P(St-NVP)).以此微球为模板通过化学沉积法得到了粒径分布均匀、单分散的P(St-NVP)/Ag复合微球.傅里叶红外光谱、X-射线衍射、扫描电镜、透射电镜、激光粒度仪和紫外-可见光谱对复合微球的结构、形貌、物相及催化性能进行了表征.结果表明,P(St-NVP)/Ag复合微球具有规则的球形结构,粒径在400～700 nm之间,随交联剂浓度或种子乳液浓度的增加,复合微球粒径减小.粒径在十几个纳米左右的银粒子均匀分布在微球表面和内部.载银复合微球在NaBH4还原4-硝基苯酚为4-氨基苯酚的模型反应中表现出较高的催化活性.     

单分散、大粒径聚苯乙烯微球的制备

以聚乙烯基吡咯烷酮为分散剂、偶氮二异丁腈为引发剂、醇／水混合物为分散介质进行了苯乙烯的分散聚合，讨论了初始单体浓度、分散剂用量、引发剂浓度、分散介质组成和反应温度等反应条件对所得聚合物颗粒直径和直径分布的影响．通过大量的试验，筛选出了较为理想的分散聚合的条件及配方，制备出了粒径为４８μｍ的单分散聚苯乙烯微球．然后，以分散聚合所制得的聚合物颗粒为种子，用动力学溶胀法制成了粒径增大近四倍的单分散、大粒径聚苯乙烯微球，并讨论了滴水速度和补加分散剂对溶胀的影响     

分散聚合法制备单分散交联聚苯乙烯微球

以苯乙烯为单体、二乙烯基苯为交联剂,通过优化反应条件,制备了平均粒径为3.28～9.04 μm的单分散聚苯乙烯微球和平均粒径为6.60 μm的单分散交联聚苯乙烯微球.探讨了单体浓度、引发剂含量、分散稳定剂用量对微球粒径和分散性的影响.热稳定性分析表明:交联聚苯乙烯微球耐热性明显优于线性聚苯乙烯.     

种子乳胶粒表面修饰法制备核壳结构PSt/TiO_2复合微球

首先采用无皂乳液聚合法合成了表面带负电荷、粒径为360 nm的单分散聚苯乙烯(PSt)乳液,并利用聚乙烯亚胺(PEI)在25℃下对PSt乳胶粒表面进行修饰,得到了表面带有正电荷的PSt种子乳液;然后以乙醇和水的混合物为反应介质,采用种子乳液加入法,使钛酸正丁酯(TBT)在修饰后的乳胶粒表面进行水解与缩合,制备出了核壳结构PSt/TiO2复合微球,利用电镜对复合微球的结构形态进行了表征.结果表明,PSt乳液改性时体系的zeta电位随着PEI用量的增加而升高,当PEI用量为PSt聚合物重量的15%时,体系的zeta电位从原来的-40.3 mV升高到了38.3 mV,达到对PSt乳胶粒表面改性的最佳值;在制备PSt/TiO2复合微球时,TiO2包覆量随着反应时间的延长而增加,反应7 h时达到90.2%的最大值;随介质中水含量的增加,吸附到复合微球表面上的TiO2纳米颗粒逐渐减少,复合微球表面逐渐变得光滑,当EtOH/H2O质量比为100/6.0时,得到结构均一、壳层厚度为29 nm的核壳结构PSt/TiO2复合微球.     

种子表面改性法制备核壳结构PSt/SiO_2复合微球

首先采用无皂乳液聚合法合成了表面带负电荷、粒径为360nm的单分散聚苯乙烯(PSt)种子乳液,并以EtOH/H2O混合物为分散介质,利用γ-氨丙基三乙氧基硅烷(KH-550)在25℃下对PSt微球表面进行改性,得到了表面硅烷化并带有正电荷的改性PSt种子乳液,然后在碱性条件下加入原硅酸乙酯(TEOS)使其和微球进行共水解与共缩聚,制备出了核壳结构PSt/SiO2复合微球,并利用电镜对复合微球的结构形态进行了表征.研究表明,PSt种子乳液改性时体系的zeta电位随着KH-550用量的增加而升高,当KH-550用量为PSt种子重量的1/3时,体系的zeta电位从原来的-34.5mV升高到了38mV,达到对PSt微球表面改性的最佳值;在制备PSt/SiO2复合微球时,TEOS水解缩聚形成的SiO2包覆到改性微球上的量随着反应时间的延长而增加,反应24h时达到97.9%的最大值;随介质中水含量的增加,吸附到复合微球表面上的SiO2纳米颗粒逐渐减少,复合微球表面逐渐变得光滑,当EtOH/H2O质量比降低到60/28.5时,得到结构均一、壳层厚度为35nm的核壳结构PSt/SiO2复合微球。     

单分散聚苯乙烯胶体颗粒的界面电性质研究

以过硫酸钾(KPS)为引发剂,以水为反应介质,采用无皂乳液聚合工艺,制备出粒径在500nm左右单分散(分散系数<5%)聚苯乙烯微球。所制备的聚苯乙烯微球为光滑的球形颗粒。研究发现:由无皂乳液聚合法制备的胶体颗粒其ζ电势在不同的离子强度下随pH的变化曲线均出现平台pH6～10.5,说明在一定的离子强度和pH条件下,聚苯乙烯胶乳的ζ电势具有良好的稳定性。聚苯乙烯胶乳有望作为具有一定电势值的标准颗粒。     

无皂乳液聚合法合成阴离子PS微球及粒径控制

以苯乙烯(St)和丙烯酸(AA)为单体,过硫酸钾(KPS)为引发剂,采用无皂乳液聚合法合成了单分散阴离子聚苯乙烯(PS)微球,并对微球结构和影响单分散性的因素进行了研究。结果表明,AA单体也已共聚到聚合物链上,AA的加入使PS微球粒径减小,并赋予PS微球表面负电性;聚合反应的活化能为42.95kJ/mol,升高聚合温度提高了反应速率;随着KPS用量的增加,PS微球粒径减小,在用量为0.6%时呈现最好单分散性;随着反应介质中丙酮含量增加,聚合物在介质中溶解度增加,使PS微球粒径有所减小,但微球粒径分布有所变宽。     

Preparation of organic/inorganic hybrid and hollow particles by catalytic deposition of silica onto core/shell heterocoagulates modified with poly[2-(N,N-dimethylamino)ethyl methacrylate

The organic/inorganic hybrid particles PSt/P(St-CPEM)(θ)-g-PDMAEMA/SiO(2) were prepared by catalytic hydrolysis and subsequent polycondensation of tetraethoxysilane in the poly[2-(N,N-dimethylamino)ethyl methacrylate] (PDMAEMA) layers grafted on the PSt/P(St-CPEM)(θ) core/shell heterocoagulates. The micron-sized PSt core and the submicron-sized P(St-CPEM) shell particles bearing ATRP initiating groups were synthesized by dispersion polymerization of styrene (St) and emulsifier-free emulsion polymerization of St with 2-chloropropionyloxyethyl methacrylate (CPEM), respectively. The raspberry-shaped PSt/P(St-CPEM)(θ) heterocoagulates with a controlled surface coverage (θ=0.51, 0.81) were prepared by hydrophobic coagulation between the core and the shell particles in an aqueous NaCl solution near the T(g) of P(St-CPEM). Surface modification of heterocoagulates was carried out by ATRP of DMAEMA from the shell particles adsorbed on the core particles. Silica deposition was performed by simply adding tetraethoxysilane to a water/methanol dispersion of PSt/P(St-CPEM)(θ)-g-PDMAEMA. The SEM and TGA revealed that the resulting PSt/P(St-CPEM)(θ)-g-PDMAEMA/SiO(2) composites maintain a raspberry-like morphology after deposition of silica onto the PDMAEMA layer grafted on heterocoagulates. The micron-sized, raspberry-shaped or the submicron-sized, hole-structured silica hollow particles were obtained selectively by thermal decomposition of the PSt/P(St-CPEM)(θ)-g-PDMAEMA/SiO(2). The oriented particle array was fabricated by dropping anisotropically perforated silica particles onto a glass substrate settled at the bottom of a bottle filled with chloroform.     

Preparation of styrene/acrylic acid copolymer microspheres: polymerization mechanism and carboxyl group distribution

 Poly(styrene-co-acrylic acid) (St/AA) copolymer microspheres were prepared by batch emulsifier-free emulsion copolymerization of St with AA. The monomer conversion, the morphology and the composition of the particles along the polymerization process were monitored by a gravimetric method, transmission electron microscopy observation and Fourier transform IR analysis, respectively. A shift of the polymerization locus from inside the particles to “outside” the particles in the postnucleation stage was proposed. The results of the study of the distribution of carboxyl groups by a combination of elemental and X-ray photoelectron spectroscopy analyses implied a core/shell structure for the St/AA copolymer microspheres. By chemical metal deposition, nickel particles were formed and deposited on the surface of St/AA microspheres, forming polymer/metal composite particles. Received: 16 February 2001 Accepted: 8 August 2001     

Toward designer magnetite/polystyrene colloidal composite microspheres with controllable nanostructures and desirable surface functionalities

An effective method was developed for synthesizing magnetite/polymer colloidal composite microspheres with controllable variations in size and shape of the nanostructures and desirable interfacial chemical functionalities, using surfactant-free seeded emulsion polymerization with magnetite (Fe(3)O(4)) colloidal nanocrystal clusters (CNCs) as the seed, styrene (St) as the monomer, and potassium persulfate (KPS) as the initiator. The sub-micrometer-sized citrate-acid-stabilized Fe(3)O(4) CNCs were first obtained via ethylene glycol (EG)-mediated solvothermal synthesis, followed by 3-(trimethoxysilyl)propyl methacrylate (MPS) modification to immobilize the active vinyl groups onto the surfaces, and then the hydrophobic St monomers were polymerized at the interfaces to form the polymer shells by seeded emulsion radical polymerization. The morphology of the composite microspheres could be controlled from raspberry- and flower-like shapes, to eccentric structures by simply adjusting the feeding weight ratio of the seed to the monomer (Fe(3)O(4)/St) and varying the amount of cross-linker divinyl benzene (DVB). The morphological transition was rationalized by considering the viscosity of monomer-swollen polymer matrix and interfacial tension between the seeds and polymer matrix. Functional groups, such as carboxyl, hydroxyl, and epoxy, can be facilely introduced onto the composite microspheres through copolymerization of St with other functional monomers. The resultant microspheres displayed a high saturation magnetization (46 emu/g), well-defined core-shell nanostructures, and surface chemical functionalities, as well as a sustained colloidal stability, promising for further biomedical applications.     

pH值和前驱体用量对核壳结构PSt/SiO2复合微球结构形态的影响

首先通过无皂乳液聚合法制得表面含羧基、粒径为360 nm的单分散聚苯乙烯(PSt)种子乳液,并在EtOH/H2O混合介质中用γ-氨丙基三乙氧基硅烷(KH-550)对其进行改性,制得表面含有活性硅乙氧基并带有正电荷的改性PSt乳胶粒,然后再加入原硅酸乙酯(TEOS)进行共水解与共缩聚反应,制备出了核壳结构PSt/SiO2...     

Preparation of micron-sized nonspherical polystyrene/poly(styrene-<Emphasis Type="Italic">co</Emphasis>-ethyleneglycol dimethacrylate) particles by seeded soap-free emulsion polymerization

Micron-sized nonspherical polymer particles having different morphologies were synthesized by seeded soap-free emulsion polymerization of styrene(St) and ethyleneglycol dimethacrylate(EGDMA,used as a crosslinker) on spherical, linear polystyrene(PS) seed particles.The morphology of the resulting PS/poly(St-co-EGDMA) particles was dependent on the crosslinker concentration and polymerization temperature.     

DESIGN AND CONTROL OF SOAP-FREE HYDROPHILIC-HYDROPHOBIC CORE-SHELL LATEX PARTICLES WITH HIGH CARBOXYL CONTENT IN THE CORE OF THE PARTICLES

Soap-free hydrophilic-hydrophobic core-shell latex particles with high carboxyl content in the core of the particles were synthesized via the seeded emulsion polymerization using methyl methacrylate(MMA),butyl acrylate(BA), methacrylic acid(MAA),styrene(St)and ethylene glycol dimethacrylate(EGDMA)as monomers,and the influences of MMA content used in the core preparation on polymerization,particle size and morphology were investigated by transmission electron microscopy,dynamic light scattering and conductometric titration.The results showed that the seeded emulsion polymerization could be carried out smoothly using "starved monomer feeding process" when MAA content in the core preparation was equal to or less than 24 wt%,and the encapsulating efficiency of the hydrophilic P(MMA-BA-MAAEGDMA) core with the hydrophobic PSt shell decreased with the increase in MAA content.When an interlayer of P(MMAMAA -St)with moderate polarity was inserted between the P(MMA-BA-MAA-EGDMA)core and the PSt shell,well designed soap-free hydrophilic-hydrophobic core-shell latex particles with 24 wt%MAA content in the core preparation were obtained.     

超声无皂乳液聚合制备BA/St/AM三元共聚物乳胶粒及其聚合机理研究

将超声技术引入到无皂乳液聚合方法中,在不加入任何引发剂和乳化剂的情况下,制备了丙烯酸丁酯(BA)/苯乙烯(St)/丙烯酰胺(AM)三元共聚纳米乳胶粒.研究了不同超声时间对单体转化率、乳胶粒粒径以及乳液粘度的影响.同时还探讨了超声无皂乳液聚合机理,认为AM在聚合过程中起到了引发和稳定的作用.TEM照片表明,乳胶粒直径大约在80nm左右,FTIR及DSC分析表明产物为三元共聚物,而不是共混物.     

Preparation and characterization of core-shell polystyrene/polychloromethylstyrene and hollow polychloromethylstyrene micrometer-sized particles of narrow-size distribution

Polystyrene core microspheres of narrow-size distribution were prepared by dispersion polymerization of styrene in a mixture of ethanol and 2-methoxy ethanol. Polystyrene/polychloromethylstyrene and polystyrene/poly(chloromethylstyrene-divinylbenzene) core-shell microspheres of narrow-size distribution were prepared by seeded emulsion polymerization of chloromethylstyrene or chloromethylstyrene and divinylbenzene in the presence of the polystyrene core microspheres at 71 °C. Core-shell particles with different properties (size, surface morphology, and composition) have been prepared by changing various parameters belonging to the emulsion polymerization process, e.g., volume of the chloromethylstyrene and the volume ratio of chloromethylstyrene to divinylbenzene. Dissolution of the polystyrene core of the polystyrene/poly(chloromethylstyrene-divinylbenzene) core-shell particles resulted in the formation of crosslinked hollow polychloromethylstyrene microspheres, broken crosslinked polychloromethylstyrene shells, or particles containing voids, depending on the composition of the polystyrene/poly(chloromethylstyrene-divinylbenzene) particles.