Mo-Ni2P/SBA-15催化剂的制备、表征及加氢脱硫催化性能

以介孔分子筛SBA-15 为载体, 通过分步浸渍硝酸镍、磷酸氢二铵、钼酸铵, 然后在H₂气流下程序升温还原(H₂-TPR), 制备了一系列不同Mo 含量的Mo-Ni₂P/SBA-15 催化剂. 采用X 射线衍射(XRD)、氮气吸脱附(BET)、透射电子显微镜(TEM)和X射线光电子能谱(XPS)对催化剂的结构进行了表征, 评价了催化剂对二苯并噻吩(DBT)的加氢脱硫(HDS)活性. 结果表明, Mo-Ni₂P/SBA-15 催化剂仍然保留有介孔结构, 催化剂的物相主要是Ni₂P. 催化剂表面的Ni 以Ni^δ+和Ni²⁺形式存在; P以P^δ-和P⁵⁺形式存在; Mo以Mo^δ+和Mo⁶⁺形式存在. Mo能促进催化性能的提高, 其中Mo含量为1% (w, 质量分数)的Mo-Ni₂P/SBA-15 催化剂具有最好的二苯并噻吩加氢脱硫催化活性, 在反应温度为380 ℃, 反应压力为3.0 MPa的条件下, 二苯并噻吩的转化率可达99.03%, 所有考察的Mo-Ni₂P/SBA-15都以直接加氢脱硫(DDS)途径为主.     

Mo助剂含量对Mo-Ni2P/SBA-15/堇青石整体式催化剂加氢脱硫性能的影响

 采用共浸渍法制备了 P/Ni 摩尔比为 2 的 Ni2P/SBA-15, 再通过二次浸渍引入助剂 Mo 制得 Mo-Ni2P/SBA-15, 将它调制成活性胶后均匀涂敷于预处理后的载体表面, 干燥焙烧后在氢气流中采用程序升温还原法, 制备了一系列 Mo-Ni2P/SBA-15/堇青石整体式催化剂. 采用 X 射线衍射、N2 吸附-脱附和 X 射线光电子能谱对催化剂结构进行了表征, 以二苯并噻吩为模型含硫化合物, 考察了催化剂的加氢脱硫性能. 结果表明, Mo 的加入增大了催化剂的比表面积, 在催化剂表面形成了 MoNiP2, 且 Ni2P 为主要活性物相. Mo 在催化剂表面主要以 Mo6+和 Moδ+形式存在; 当 w(Mo) = 4.2% 时, n(Mo)/n(Ni+Mo) = 0.18 的整体式催化剂上二苯并噻吩的转化率最高, 且在较低反应温度时以直接脱硫机理为主, 而较高反应温度时以加氢脱硫机理为主.     

镧助剂对模拟生物沼气重整制备合成气中Ni/SBA-15催化剂结构和性能的影响

以介孔分子筛SBA-15为载体, 采用浸渍法制备了镍质量分数(w)为12.5%, 并且分别添加质量分数(w)为2.5%的镧、铈、镁、钙、锶等助剂的系列Ni基催化剂. 以CH4/CO2体积比为2:1的模拟生物沼气和适量氧气作为原料气, 在常压固定床反应器上评价了催化剂对模拟生物沼气重整制合成气的反应性能. 采用X射线粉末衍射(XRD)、N2吸附/脱附、透射电子显微镜(TEM)、X射线光电子能谱(XPS)及H2程序升温还原(H2-TPR)等对催化剂的结构进行了表征. 催化活性评价显示, 添加镧助剂的2.5%La/12.5%Ni/SBA-15催化剂比添加铈、镁、钙、锶等助剂的催化剂具有更高的催化活性, 并且具有很好的稳定性. 因此, 文中着重研究了镧助剂对催化剂结构和模拟生物沼气重整制合成气的反应性能的影响. 结果表明, 镧能明显提高Ni/SBA-15催化剂的表面镍含量, 同时还具有很好的抗积炭作用, 在850 ℃的温度下反应820 h没有发现积炭生成, 这些可能是提高催化剂性能和稳定性的重要因素.     

不同助剂对CuO-ZnO/SBA-15催化CO_2加氢制甲醇性能影响的研究

以硅质骨架结构介孔分子筛SBA-15为载体,采用浸渍法合成CuO-ZnO/SBA-15(CZ/SBA-15)、CuO-ZnO-MnO_2/SBA-15(CZM/SBA-15)、CuO-ZnO-ZrO_2/SBA-15(CZZ/SBA-15)三组多孔催化剂,在固定床反应器上评价了各组催化剂催化CO_2加氢合成甲醇的性能,同时结合N_2吸附-脱附(BET)、X射线衍射(XRD)、H_2程序升温还原(H_2-TPR)、程序升温脱附(H_2-TPD、CO_2-TPD)、N_2O滴定、X射线光电子能谱(XPS)、透射电子显微镜(TEM)等表征研究了不同助剂对CO_2催化加氢制甲醇的影响。结果表明,催化剂中的金属氧化物改变了SBA-15分子筛载体的孔径大小和比表面积;催化剂CuO-ZnO-MnO_2/SBA-15、CuO-Zn O-ZrO_2/SBA-15中铜的分散度(D_(Cu))和比表面积(A_(Cu))更大,表面CuO粒径更小,更易被还原;相比Mn-O簇,Zr-O簇为增强了碱性位点,提高了甲醇选择性。此外,CuO-ZnO-ZrO_2/SBA-15具有更高的氧空位浓度,催化活性更好,其甲醇选择性为25.02%,与CuO-ZnO/SBA-15、CuO-ZnO-Mn O_2/SBA-15相比分别提高了28%和136.9%,催化效果最好。     

钾调变Mo/SBA-15催化剂用于乙烷选择氧化制乙醛(英文)

采用两步浸渍法制备钾改性的Mo/SBA-15催化剂.采用N2吸附,X射线衍射(XRD),透射电镜(TEM),紫外-可见(UV-Vis)吸收光谱,拉曼(Raman)光谱,NH3程序升温脱附(NH3-TPD),CO2程序升温脱附(CO2-TPD),H2程序升温还原(H2-TPR)等手段表征催化剂的物理化学性质.研究结果表明,在Mo0.75/SBA-15中添加K之后,有新物种钾钼酸盐生成,并且当K/Mo的摩尔比不同时,钼物种的存在状态也不同.添加钾之后,催化剂的活性和总醛(甲醛、乙醛、丙烯醛)的选择性均有所提高,并且受钾的添加量影响.在575°C时,在K0.25-Mo0.75/SBA-15催化剂上醛的收率可高达8.5%(摩尔分数).     

Cu-Zn-Zr/SBA-15介孔催化剂的制备及CO2加氢合成甲醇的催化性能

以具有骨架结构的SBA-15介孔分子筛为载体,采用浸渍法合成了具有高比表面积、不同金属氧化物含量的Cu-Zn-Zr介孔催化剂CZZx/SBA-15(x=0.3,0.4,0.5,0.6).采用N2吸附-脱附(BET)、X射线衍射(XRD)、H2程序升温还原(H2-TPR)、CO2吸附(CO2-TPD)和透射电子显微镜(TEM)等手段对样品进行了表征.在固定床反应器上评价了其CO2加氢合成甲醇的催化性能.实验结果表明,CZZx/SBA-15催化剂具有介孔结构,负载的Cu O,Zn O和Zr O2能够很好地分散在表面,并且负载氧化物晶粒尺寸不同.催化剂的铜比表面积SCu与甲醇催化活性呈近似线性关系,其中CZZ0.4/SBA-15催化剂表现出最大甲醇选择性(54.32%),与CZZ相比,甲醇选择性增加24.85%.随着金属氧化物负载量的增大,催化剂比表面积和SCu明显减小,甲醇选择性与收率也相应减小,负载型CZZx/SBA-15催化剂表面结构对CO2加氢合成甲醇反应活性起关键作用.     

高稳定性Ni/SBA-15催化剂的结构特征及其对二氧化碳重整甲烷反应的催化性能

 采用浸渍法制备了Ni含量为2.5%～20%的系列Ni/SBA-15催化剂,在常压连续流动固定床反应器上考察了催化剂对二氧化碳重整甲烷制合成气的催化性能,并用X射线衍射和N2吸附法研究了Ni/SBA-15催化剂的结构特征. 结果表明, Ni/SBA-15催化剂具有很高的CH4和CO2转化率, 12.5%Ni/SBA-15催化剂在800 ℃反应600 h后活性没有明显下降,但反应710 h后CH4的转化率下降了约50%, CO2的转化率下降了约25%. 其活性下降的主要原因是催化剂积炭. 在高温条件下反应时, SBA-15的介孔结构也没有遭到破坏,分子筛的孔壁能有效阻止活性组分Ni的团聚. SBA-15孔中组装一定量的Ni活性组分后,除了SBA-15的介孔外,还会形成另外一种较小的孔,但这不影响SBA-15的有序介孔结构,只是其孔径、孔容和BET比表面积降低.     

Cu-Co/SBA-15催化剂的结构特征及其催化甲苯燃烧性能

 以介孔 SBA-15 分子筛为载体, 用等体积共浸渍法制备了不同 Cu/Co 比和不同 Cu-Co 含量的 Cu-Co/SBA-15 催化剂, 采用 N2 吸附-脱附、高分辨透射电镜、X 射线衍射、X 射线光电子能谱和程序升温还原等手段对催化剂进行了表征, 并在微型固定床反应器上评价了催化剂催化甲苯燃烧性能. 结果表明, 所有催化剂仍具有 SBA-15 分子筛的介孔结构, Cu 含量较低时催化剂中存在 Cu-Co-O 固溶体, Cu 含量较高时会形成 CuO. 催化剂表面的 Co 对甲苯催化燃烧有重要的作用, 催化剂中的 Cu 可以降低 Co 的还原温度, 从而有利于催化剂活性的提高. 40%(Cu0.25Co0.75)/SBA-15 催化剂具有最高的活性, 在 285 oC 时可完全催化燃烧消除甲苯.     

介孔Ni-β-Mo2C/SBA-16催化剂在CH4/CO2重整制合成气反应中的催化性能

采用等体积浸渍将双金属活性组分负载到介孔分子筛SBA-16上,通过热分解制备了负载型催化剂Ni--Mo2C/SBA-16.N2吸附-脱附、X射线粉末衍射和透射电镜等结果表明,引入活性组分后,样品依然保持原有的有序介孔结构,活性组分高度分散于载体上,没有团聚.在CH4/CO2重整制合成气反应中,Ni--Mo2C/SBA-16催化剂具有较高的CH4和CO2转化率,以及CO和H2选择性,有明显的抗积炭作用.     

Ni2P/SBA-15催化剂的结构及加氢脱硫性能

以硝酸镍为镍源,磷酸氢二铵为磷源,介孔分子筛SBA-15为载体,用共浸渍法制备了含磷化镍前驱体的样品,然后在氢气流中采用程序升温还原法,制备了Ni2P质量分数为5%-40%的Ni2P/SBA-15催化剂.用X射线衍射(XRD)、N2吸附脱附、透射电子显微镜(TEM)、傅立叶变换红外光谱(FTIR)等分析测试技术对催化剂的结构进行了表征,以噻吩和二苯并噻吩(DBT)为模型化合物,在微型同定床反应器上对催化剂的加氧脱硫(HDS)性能进行了评价.结果表明,Ni2P/SBA-15催化剂中SBA-15的介孔结构依然存在,活性组分Ni2P具有良好的分散性,但随Ni2P含量的增加,催化剂的比表面积、孔容和孔径均有明显减小.当反应温度为320℃时,Ni2P含量为15%-25%(w)的催化剂就具有很好的加氢脱硫催化性能;反应温度在360℃以上时,所有催化剂都具有优异的深度脱硫催化性能.Ni2P/SBA-15催化剂对二苯并噻吩的加氢脱硫(HDS)主要以直接脱硫机理(DDS)进行.     

Effect of Ni Loading and CexZr1-xO2 Promoter on Ni-Based SBA-15 Catalysts for Steam Reforming of Methane

A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt?xZn-xO2/SBA-15 (z=0, 0.5, 1) were prepared. The structures of the catalysts were characterized using XRD, TPR, TEM and BET techniques. The catalytic activities of the catalysts for steam reforming of methane were evaluated in a continuous flow microreactor. The results indicated that both the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts had good catalytic activities at atmospheric pressure. The 10wt%Ni/SBA-15 catalyst exhibited excellent stability at 800癈 for time on stream of 740 h. After the reaction, carbon deposits were not formed on the surface of the catalyst. There existed a regular hexagonal mesoporous structure in the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts. The nickel species and the CexZr1-xO2 component were all confined in the SBA-15 mesopores. The CexZr1-xO2 could promote dispersion of the nickel species in the Ni/CexZr1-xO2/SBA-15 catalysts.     

Preparation,characterization and hydrodesulfurization performances of Co-Ni_2P/SBA-15 catalysts

A series of Co-Ni2P/SBA-15 catalysts with various Co contents, Ni2P contents and P/Ni molar ratios were prepared by impregnating nickel nitrate, diammonium hydrogen phosphate, and then cobalt nitrate into SBA-15 support followed by temperature-programmed reduction in a H2 flow. The catalyst structure was characterized by X-ray diffraction(XRD), high resolution-transmission electron microscopy(HR-TEM)and N2adsorption-desorption techniques and their catalytic performance of the hydrodesulfurization(HDS) of dibenzothiophene(DBT) was evaluated. The effects of Co contents, Ni2 P contents and P/Ni molar ratios on the catalyst structure and HDS of DBT over the Co-Ni2P/SBA-15 catalyst were investigated. The results indicated that the mesoporous structure was mainly maintained and the nickel phosphides were well dispersed in all of the characterized catalysts. The 4Co-25Ni2P/SBA-15(P/Ni = 0.8) catalyst with the Co and Ni2 P contents of 4 wt% and25 wt%, respectively, and the P/Ni molar ratio of 0.8 showed the highest catalytic performance for HDS of DBT. Under the reaction conditions of 380?C and 3.0 MPa, the DBT conversion can reach 99.62%. The HDS of DBT proceeded mainly via the direct desulfurization(DDS)pathway with biphenyl(BP) as the dominant product on all of the catalysts and the BP selectivity was slightly enhanced after the introduction of Co promoters.     

B助剂对Ni2P/SBA-15催化剂结构及其加氢脱硫性能的影响

以介孔分子筛SBA-15为载体, 磷酸氢二铵为磷源, 硝酸镍为镍源, 硼酸为硼源, 采用共浸渍法制备了B-Ni₂P/SBA-15催化剂前驱体, 然后采用程序升温氢气还原法, 制备了n_P/n_Ni=0.8, B含量为0.35%-2.10%(w)的一系列B-Ni₂P/SBA-15催化剂. 用X射线衍射(XRD)、N₂吸附脱附、透射电子显微镜(TEM)和氨气程序升温脱附(NH₃-TPD)等表征技术对催化剂的结构进行了研究, 以1%(w)二苯并噻吩(DBT)/十氢萘溶液为模型化合物, 在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价. 结果表明, B-Ni₂P/SBA-15催化剂仍具有介孔结构, Ni₂P为主要的活性物相. 适量B助剂的加入可促使Ni₂P晶粒减小, 催化剂比表面积增加. 此外, 随着B含量的增加, B-Ni₂P/SBA-15催化剂的总酸量也增加. 当反应压力为3.0 MPa, 反应温度由300 ℃升高至360 ℃时, B含量对Ni₂P/SBA-15催化剂活性有明显的影响, B含量为1.40%(w)的B-Ni₂P/SBA-15催化剂加氢脱硫活性最高. B-Ni₂P/SBA-15催化剂上二苯并噻吩的加氢脱硫的反应机理以直接脱硫为主.     

Ni2P/SBA-15催化剂的结构及加氢脱硫性能

以硝酸镍为镍源, 磷酸氢二铵为磷源, 介孔分子筛SBA-15为载体, 用共浸渍法制备了含磷化镍前驱体的样品, 然后在氢气流中采用程序升温还原法, 制备了Ni2P质量分数为5%-40%的Ni2P/SBA-15催化剂. 用X射线衍射(XRD)、N2吸附脱附、透射电子显微镜(TEM)、傅立叶变换红外光谱(FTIR)等分析测试技术对催化剂的结构进行了表征, 以噻吩和二苯并噻吩(DBT)为模型化合物, 在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价. 结果表明, Ni2P/SBA-15催化剂中SBA-15 的介孔结构依然存在, 活性组分Ni2P具有良好的分散性, 但随Ni2P含量的增加, 催化剂的比表面积、孔容和孔径均有明显减小. 当反应温度为320 ℃时, Ni2P含量为15%-25%(w)的催化剂就具有很好的加氢脱硫催化性能; 反应温度在360 ℃以上时, 所有催化剂都具有优异的深度脱硫催化性能. Ni2P/SBA-15催化剂对二苯并噻吩的加氢脱硫(HDS)主要以直接脱硫机理(DDS)进行.     

Carbon dioxide reforming of methane over Ni/Mo/SBA-15-La2O3 catalyst: Its characterization and catalytic performance

The Ni/Mo/SBA-15 catalyst was modified by La2O3 in order to improve its thermal stability and carbon deposition resistance during the CO2 reforming of methane to syngas. The catalytic performance, thermal stability, structure, dispersion of nickel and carbon deposition of the modified and unmodified catalysts were comparatively investigated by many characterization techniques such as N2 adsorption, H2-TPR, CO2-TPD, XRD, FT-IR and SEM. It was found that the major role of La2O3 additive was to improve the pore structure and inhibit carbon deposition on the catalyst surface. The La2O3 modified Ni/Mo/SBA-15 catalyst possessed a mesoporous structure and high surface area. The high surface area of the La2O3 modified catalysts resulted in strong interaction between Ni and Mo-La, which improved the dispersion of Ni, and retarded the sintering of Ni during the CO2 reforming process. The reaction evaluation results also showed that the La2O3 modified Ni/Mo/SBA-15 catalysts exhibited high stability.     

氮化SBA-16负载镍基催化剂的制备及其对甲烷二氧化碳重整反应的催化性能

通过软模板法合成了SBA-16分子筛,采用高温氨气氮化的方法使有序介孔硅材料中的氧原子部分被氮原子取代,得到氮化的SBA-16载体(SBA-16-N)。采用满孔浸渍法制备了镍基催化剂,并将制得的Ni/SBA-16和Ni/SBA-16-N催化剂用于甲烷二氧化碳重整反应。通过透射电镜、氮气物理吸附、X射线衍射、X射线光电子能谱和二氧化碳程序升温脱附等手段研究了载体和催化剂的结构,并利用热重分析对反应之后回收催化剂进行了表征。结果表明,高温氮化后的分子筛中掺入了氮元素,增加了载体的碱性,改善了载体对反应气体的吸附活化能力,增强了载体与金属之间的相互作用,从而提高了催化剂的活性和抗积炭性能。     

Co-Ni2P/SBA-15/Cordierite整体式催化剂的制备及其二苯并噻吩加氢脱硫性能

用共浸渍法制备了Co-Ni2P/SBA-15前躯体,将其调制成活性胶后均匀涂覆到预处理后的堇青石载体上,程序升温还原后制备了一系列Co-Ni2P/SBA-15/堇青石整体式催化剂。采用XRD、N2吸脱附和XPS等对催化剂进行了表征,以1 wt%二苯并噻吩(DBT)/十氢萘溶液为模型化合物,在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价。结果表明,不同Co含量的Co-Ni2P/SBA-15/堇青石整体式催化剂中都形成了Ni2P相。Co的加入提高Ni2P/SBA-15/堇青石催化剂的比表面积和孔体积。Co含量为0.55wt%的Co-Ni2P/SBA-15/堇青石整体式催化剂有最好的二苯并噻吩加氢脱硫活性,在380℃,二苯并噻吩转化率能够达到98.8%。Co的加入能够提高二苯并噻吩直接加氢脱硫产物联苯的选择性。