焙烧温度对ZnO粉体结晶及其光学性能的影响

以草酸铵和醋酸锌为原料,采用直接沉淀法制备ZnO粉体,考察了焙烧温度对粉体结晶和光学性能的影响。采用热重分析(TGA-DTA)、X射线衍射、紫外-可见漫反射(UV-Vis)、荧光分光光度计(FS)和扫描电子显微镜(SEM)等方法对样品进行了分析。结果表明,制备的前驱物为C2O4Zn·2H2O,最低焙烧温度400℃,随着焙烧温度的提高,粉体结晶度提高,一次粒径增大;600℃焙烧后有较强紫外发光峰,粉体由200 nm的粒子排列成层叠状;900℃焙烧后有较强可见发光峰,粉体粒子大于500 nm,团聚严重;粉体有较强的紫外吸收,吸收峰有蓝移。     

V_2O_5/CeO_2催化剂固相反应的Raman光谱研究

采用浸渍法制备了不同V2O5负载量(分别为5%和15%)的V2O5/CeO2催化剂.利用不同激发波长(514和325nm)的Raman光谱,结合X射线衍射(XRD)、紫外-可见漫反射(UV-VisDRS)和N2物理吸附技术,考察了V2O5/CeO2催化剂中V2O5和载体CeO2之间的固相反应.结果表明:催化剂在300℃焙烧时,V2O5与CeO2反应生成CeVO4,升高温度有利于固相反应的发生.样品对325nm光的吸收明显大于对514nm光的吸收,因此325nm激发波长的Raman光谱对催化剂的表层信息更为敏感.当焙烧温度较低时,由于受到表层CeVO4的阻碍,未反应的V2O5残留在载体CeO2孔道或粒子堆积孔道内部,因此514nm激发波长下能观察到V2O5的Raman峰,而表面灵敏的325nm激发波长下观察不到此现象.     

乳状液膜法制备硫氧化物超细X射线发光粉

采用乳状液膜法制备了颗粒均匀的Gd-Tb草酸盐微粒，将草酸盐粒子放在硫气气氛下焙烧后得到Gd2O2S：Tb超细X射线发光粉。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、红外(IR)光谱、光致发光(PL)光谱和X射线激发发光光谱(XEL)对微晶进行了表征。结果表明，900℃下焙烧后的粒子显示了单一的六角形Gd2O2S晶相，与传统固相法相比，有效降低了焙烧温度。根据谢乐公式，估算一次粒径为29nm，初级粒子尺寸较小，这在一定程度上可以提高成像系统的空间分辨率。从SEM照片来看，粒子显示了一定的团聚性，但团聚尺寸＜5μm，为超细X射线发光粉。同时，在254nm紫外光和X射线激发下，Gd2O2S：Tb发光粉都显示出Tb^3 的特征发射峰，并且通过分析红外光谱对样品发光性能的影响作了详细的讨论。     

MAA修饰ZnO量子点及其发光特性

以ZnAc2·2H2O为原料,在乙醇中通过70℃回流4h,得到ZnO前驱物,与LiOH·H2O反应,制备出ZnO.采用巯基乙酸(mercaptoacetic acid,MAA)对所合成的ZnO进行表面修饰,修饰后的产物经SEM和XRD表征,证明获得了物相单一、近似球状、粒径为4.6nm的ZnO量子点.借助紫外-可见和荧光分析,研究了MAA对该量子点的修饰效果,探讨了设置条件下ZnO的发光机理和性质.发现该实验体系之所以产生荧光表面缺陷发射峰消失和激子发射峰明显增加的光学现象,是因为MAA有效地覆盖了ZnO的表面缺陷,并稳定包裹住ZnO粒子.同时还研究了MAA加量、温度、电解质对修饰产物发光性能的影响,发现经MAA修饰后的ZnO量子点具有较强的荧光发光性能、良好的长期陈放稳定性,以及一定的抗电解质影响能力.研究结果对ZnO量子点应用于生物分析具有重要参考价值.     

若干物理处理方法对稀土荧光粉Y2O3:Eu3+发光性能的影响

采用物理法对商品化稀土荧光粉Y2O3：Eu^3＋进行改性，考察了真空干燥温度、焙烧温度对其发光性能的影响。SEM和TEM观测结果表明，经过200℃真空干燥后，随着焙烧温度的增加，荧光粉的分散性得到改善，且以纳米颗粒为主（5～85nm）。XRD测量结果表明，随着焙烧温度的增加，Y203：Eu^3＋的结晶度逐渐增加。发射光谱测试结果表明，真空干燥温度为200℃，焙烧温度为1200℃时得到的样品的发光性能较好。     

共沉淀-喷雾干燥法制备Sm2O3掺杂CeO2纳米粉体

以Sm（NO3）3.6H2O和Ce（NO3）3.6H2O为原料,用共沉淀-喷雾干燥法制备了Sm2O3掺杂CeO2（SDC）粉体。通过沉降实验、TG-DSC、XRD、BET、SEM和粒度分布对前驱体的分散性、稳定性及制得的SDC粉体性能进行表征,研究了洗涤方法、分散剂对前驱体及SDC粉体的影响。结果表明：无机陶瓷膜洗涤后前驱体分散性好,经500℃以上温度焙烧后的粉体为立方萤石型结构。加入分散剂后前驱体的分散性明显提高,制得的SDC粉体比表面积显著增加,最终获得了晶粒平均粒径为12.51 nm、团聚态颗粒为球形的SDC纳米粉体。     

绿色银纳米粒子的共振散射光谱研究

以柠檬酸钠作光还原剂,采用紫外光-可见光二步光化学法制备了绿色银纳米离子,在399.4nm和691.5nm处有二个紫外-可见吸收峰;在340nm,470nm和520nm处有三个共振散射峰,从超分子和纳米粒子这一整体出发,探讨了共振散射光谱产生的原因及银超分子光反应机理。     

绿色银纳米粒子的共振散射光谱研究

以柠檬酸钠作光还原剂,采用紫外光-可见光二步光化学法制备了绿色银纳米离子,在399.4nm和691.5nm处有二个紫外-可见吸收峰;在340nm,470nm和520nm处有三个共振散射峰,从超分子和纳米粒子这一整体出发,探讨了共振散射光谱产生的原因及银超分子光反应机理。     

偏硼酸锶系列发光材料的制备及其发光性能研究

利用液相共沉淀法制备了SrB2O4 4H2O和SrB2O4 4H2O∶Eu3+,利用高温焙烧前驱体法制备了SrB2O4和SrB2O4∶Eu3+发光材料,通过X射线粉晶衍射(XRD)、X射线能谱分析(EDS)和扫描电子显微镜(SEM)等手段对产物进行了表征.通过荧光光谱研究了其发光性质,并考察了反应时间及Eu3+掺杂浓度对发光强度的影响.结果表明,基质SrB2O4 4H2O和SrB2O4在紫外区具有较强的发光性能,SrB2O4 4H2O∶Eu3+和SrB2O4∶Eu3+均在613 nm有最强发射峰.通过调整反应时间和提高掺杂量,可以克服结构水的猝灭作用的影响,大大提高SrB2O4 4H2O∶Eu3+发光性能,且具有更高的红橙比,是一种良好的新型发光基质.     

维生素E绿色还原法制备银纳米粒子的研究

采用一种绿色还原法制备银纳米粒子,以维生素E为还原剂,淀粉为稳定剂,在液相中还原硫酸银,通过改变溶液的pH值和反应时间,得到不同粒径的黄色银纳米粒子,并分别采用透射电镜、红外光谱、紫外-可见吸收光谱、扫描电镜和电化学方法对银纳米粒子进行表征。结果表明:维生素E在溶液中被氧化生成苯醌,反应得到的银纳米粒子为球形,粒径为8~25 nm;在较强碱性条件下,得到的银纳米粒子尺寸较小,分布较均匀,其平均粒径约为10 nm;不同条件下生成的银溶胶分别在417、411、409、408 nm处出现紫外吸收峰,这些吸收峰均为银纳米粒子的表面共振吸收;生成的银纳米粒子具有很好的电化学性质,并对L-半胱氨酸的电化学反应显示了良好的催化活性。     

纳米ZnO室温选择氧化H2S特性的研究

碱式碳酸锌在不同焙烧温度下制得的纳米ZnO具有六方晶系纤锌矿结构，平均粒径为15.4 nm、19.1 nm、22.9 nm和33 nm，以其为脱硫剂，对H2S室温脱硫性能进行了研究。利用XRD和XPS技术对脱硫反应前后的样品进行了表征。实验结果表明，纳米ZnO的脱硫性能随粒径的增大而降低，常温、常压下，260 ℃焙烧的纳米ZnO对H2S有高的去除率，并且H2S可选择性地被氧化为单质硫。     

γ-Fe2O3纳米粒子的(湿)固相研磨法制备研究

在聚乙二醇(PEG-400)存在下,于室温下研磨适量FeCl3与NaOH的混合物制备了γ-Fe2O3纳米粒子.所得各样品用XRD,Mossbauer谱,TEM,Tg-DTA和FTIR等手段进行了表征.结果表明,研磨后的样品经60℃干燥2h后即可得结晶较差的γ-Fe2O3纳米粉体,经450℃热处理1h后得粒径约为30nm结晶较好的γ-Fe2O3纳米粒子,经500℃热处理1h后得到粒径约为40nm、结晶完好的γ-Fe2O3纳米粒子.     

Effect of synthesis method variables on particle size in the preparation of homogeneous doped nano ZnO material

Homogeneous doped ZnO nanoparticles were synthesised by the Pechini method. A statistical experimental design was used to study the effects of the synthesis method variables on the particle size. The variables were the molar ratios of the reagents and the calcination temperature. The results indicated that the calcination temperature was the only factor that had a significant effect on the particle size. The particle size of ZnO varied between 16 and 76 nm with calcination temperatures of 400–800 °C. The homogeneity was studied by the ICP-MS technique, and the powders were found to be highly homogeneous.     

锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.     

ZIF-8衍生ZnO耦合HZSM-5一步催化合成气制烃醚燃料

通过水热溶剂法合成有机骨架结构材料ZIF-8,以其为前驱体调变焙烧温度制备ZnO纳米粒子。采用XRD、TEM、XPS、Raman等表征研究ZnO的组成结构及晶粒粒径形态变化;将ZnO与HZSM-5耦合形成双功能催化剂,考察其在合成气转化中的催化活性。结果表明,焙烧温度对ZnO的颗粒粒径结构影响较大,温度影响晶粒的形成速率,提高温度会促进ZnO的聚集; ZIF-8衍生ZnO通过调变温度影响ZnO晶粒粒径,起到改变产物分布的作用。当焙烧温度≤450℃时,以碳包覆ZnO纳米粒子结构存在,ZnO晶粒粒径小于20 nm,含碳ZnO耦合HZSM-5催化剂的产物以二甲醚为主;当温度≥500℃,以纯相ZnO存在,ZnO晶粒粒径皆大于20 nm,ZnO耦合HZSM-5催化剂的产物以烃类为主。ZnO与HZSM-5的耦合方式对双功能催化剂的产物选择性有显著影响。     

ZnTiO3-TiO2纳米复合材料的光催化性能

通过溶胶 凝胶（Sol-Gel）法制备了ZnTiO3-TiO2纳米复合光催化剂,利用透射电子显微镜、X射线衍射、紫外-可见吸收光谱和ζ电位等测试技术对其形貌、晶体结构及其光谱响应特性进行了表征。 以亚甲基蓝（MB）溶液的脱色降解为模型反应,考察了光源和焙烧温度对该纳米复合材料光催化性能的影响。 结果表明,所得纳米复合材料的催化性能与材料的尺寸、在介质中的分散性能、表面荷电性质等有关。 600 ℃下焙烧3 h所得的ZnTiO3-TiO2纳米复合材料尺寸小（约60 nm）、分散性能好、表面荷负电荷量最高、催化性能最好,且在太阳光下的活性高于紫外光下的。 如太阳光下7 h可使亚甲基蓝（MB）溶液的脱色降解率达到93%,而在紫外光下只有82%;并且其催化活性高于纯TiO2和ZnO的。 该纳米复合催化剂重复使用4次仍能使亚甲基蓝（MB）溶液的脱色降解率在80%以上。 因此,具有较好的光催化稳定性能。     

Preparation of Ultrafine Ceramic Powder Used for Making PTCR Ceramics by Sol-gel Method

Amorphous gel powder containing Ba, Sr, Ca, Ti, Si, Mn, Li and Y elements has been prepared by a modified sol-gel method, the ultrafine PTCR (Positive Temperature Coefficient of Resistance) powder was obtained through calcination for 2 h at 800℃ in air. According to XRD, DSC, BET and SEM. it can be concluded that it's crystal structure is cubical perovskite phase at room temperature, it's average crystallite size is about 28.4nm (using the Debye-Scherrer formula) or about 40 nm (using BET) or about 50nm(using SEM), it's specific surface area is 24.80 m²/g, and which is two twice as much as that of the sample prepared by old sol-gel method^[l,2], it's particle size displays normal distribution with average particle size of 437.2nm.     

花形ZnO纳米片微球的合成、表征及光催化性能

以ZnCl2和尿素为原料,采用水热法合成了由纳米片组成的花形微球碱式碳酸锌前驱体,然后在300℃下煅烧0.5 h得到了形貌一致的ZnO产物。采用XRD、FTIR、TG、SEM、TEM、XPS对其进行表征,结果表明产物为六方纤维矿结构ZnO;组成3D花型微球的纳米片构筑单元厚度为10 nm,表面呈孔装结构,比表面积为72 m2.g-1。分别以花形ZnO纳米片、单分散ZnO纳米片和商用ZnO纳米颗粒为光催化剂,通过降解罗丹明B(Rh B)进行了光催化活性研究。结果表明,与商用ZnO纳米颗粒相比,水热法制备的花形ZnO纳米片显示了更好的光催化活性,可能是由于花形ZnO纳米片微球有较高的比表面积和3D花形形貌所致。     

ZnO/Eu~(3+)发光材料的高温固相合成及其发光性能

采用高温固相法制备了ZnO/Eu3+红色长余辉发光材料.应用正交试验设计法(每个因素取3个水平,选用L9(34)正交试验表),以初始亮度为指标,研究了煅烧温度、Eu3+质量分数、敏化剂Li+质量分数、煅烧时间等4个因素对发光性能的影响;利用X射线衍射仪对合成的ZnO/Eu3+发光材料进行了物相分析,应用荧光分光光度计测定了样品的激发光谱和发射光谱,应用照射计测定了样品的发光特性.结果表明,当各个因素在水平范围内变化时,所制备的样品均具有ZnO晶格结构;荧光粉的主激发峰位于365 nm和458 nm处,主发射峰位于480 nm、570 nm和600 nm~640 nm,对应于Eu3+的4f和5d间的激发和发射.所确定的最佳合成条件为:煅烧温度850℃,w(Eu3+)=4%,w(Li+)=2.5%,煅烧时间3 h.     

预处理条件对用于CO_2加氢的超细CuO－ZnO－SiO_2催化剂性能的影响

采用ＸＲＤ、ＢＥＴ、ＴＰＲ手段，研究了焙烧和还原温度对超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂的性质及其ＣＯ２加氢反应催化活性的影响．胶体在５７３－７７３Ｋ范围内焙烧生成ＣｕＯ、Ｃｕ２Ｏ、ＺｎＯ晶相，随着焙烧温度继续升高，ＣｕＯ和ＺｎＯ晶粒逐渐变大，但催化剂的比表面积和孔容变化很小．在９７３Ｋ焙烧后出现Ｚｎ２ＳｉＯ４晶相，使催化剂比表积和孔容变小，导致催化剂活性降低．焙烧温度对催化剂活性的影响大于对ＣＯ２加氢产物分布的影响．在５４８－６４８Ｋ范围内，催化剂还原温度对其催化活性影响不大．７０３Ｋ高温还原后，可能由于Ｃｕ０晶粒的出现，使得催化剂的活性下降．ＴＰＲ研究结果进一步表明，焙烧温度影响ＣｕＯ同ＺｎＯ、ＳｉＯ２之间的相互作用和催化剂的还原行为．