臭氧催化氧化脱除低浓度甲醛的新方法（英文）

甲醛作为一种典型的室内挥发性有机污染物,对人体健康危害很大.目前,在可用于室内甲醛脱除的诸多方法之中,臭氧催化氧化法因可于室温下使用廉价的金属氧化物催化剂实现对甲醛的高效脱除,从而受到了科研工作者的广泛关注.然而,考虑到室内甲醛的浓度极低,且存在着长期缓慢释放的特点,传统的臭氧催化氧化法应用于实际的室内甲醛脱除不仅会造成能量的浪费,而且还易因未完全分解臭氧的连续释放带来二次污染问题.为了提高臭氧催化氧化脱除甲醛过程的臭氧利用率,降低能耗,并有效缓解未分解臭氧引起的二次污染,本文将一种循环的甲醛存储-臭氧催化氧化新方法应用于室内低浓度甲醛的脱除.该新方法包含甲醛存储与臭氧催化氧化两个过程,在存储阶段低浓度甲醛吸附存储于催化剂表面,而在臭氧催化氧化阶段臭氧将存储的甲醛氧化为CO_2与H_2O,并重新释放催化剂表面的吸附位.因负载型氧化锰具有优良的臭氧分解能力,本研究以Al_2O_3负载的MnO_x为催化剂,通过研究前驱体及担载量对甲醛脱除反应的影响,筛选出了最优的MnO_x/Al_2O_3催化剂,并对相对湿度的影响规律进行了考察,最后通过低浓度甲醛存储-臭氧催化氧化循环实验验证了该甲醛臭氧催化氧化新过程的可靠性.我们采用传统的等体积浸渍法,基于不同的前驱体制备MnO_x/Al_2O_3催化剂.XRD表征结果表明,乙酸锰为前驱体制得的MA/Al_2O_3催化剂中MnO_x相主要为Mn3O4(粒径约为6.0 nm);而硝酸锰前驱体所得MN/Al_2O_3催化剂中则含有MnO2与Mn_2O_3相,且其MnO_x颗粒粒径较大,约为9.5 nm.XPS测试结果表明,MA/Al_2O_3催化剂含有Mn~(2+),Mn~(3+)及Mn~(4+),其中Mn~(3+)与Mn~(4+)的含量分别为75%与12%;而MN/Al_2O_3催化剂则仅含有Mn~(3+)与Mn~(4+),含量分别为35%与65%.上述XRD与XPS结果相一致,说明以乙酸锰为前驱体所得催化剂的分散度较高且易形成低氧化态的Mn.甲醛存储-臭氧催化氧化实验结果表明,与Al_2O_3及MN/Al_2O_3相比,MA/Al_2O_3催化剂具有更高的甲醛存储与催化氧化脱除性能.基于MA/Al_2O_3催化剂,不同Mn负载量下的甲醛存储与臭氧催化氧化实验结果表明,Mn负载量为10 wt%时MA/Al_2O_3的性能最佳.因而,进一步的实验中我们均选用最优的10 wt%MA/Al_2O_3为催化剂,其在50%相对湿度下的甲醛存储量为26.9μmol/mL,臭氧催化氧化阶段碳平衡为92%,CO_2选择性为100%.相对湿度的影响结果(23°C)则表明,由于水分子与甲醛分子间存在着竞争吸附作用,甲醛存储容量随相对湿度的增加而降低;但因相对湿度增加可建立利于甲醛氧化的新途径,故臭氧催化氧化性能随相对湿度增加而增强.综合考虑,10 wt%MA/Al_2O_3上甲醛存储-臭氧催化氧化的最优相对湿度为50%.为验证所提出新方法的实用性,我们基于10 wt%MA/Al_2O_3开展了甲醛存储-臭氧催化氧化的4次循环实验.4次循环实验中的甲醛存储以及臭氧催化氧化处理的规律可基本保持一致.50%相对湿度下,低浓度甲醛(15×10-6)在空速为27000 h-1时的穿透时间为110 min,而在臭氧催化氧化阶段(150×10-6臭氧,空速15000 h-1)仅需约50 min即可实现对存储甲醛的氧化脱除(碳平衡大于92%,CO_2选择性100%),表明该新方法较传统的臭氧催化氧化方法臭氧用量可节省60%.     

室温MnO_x上O_3氧化脱除空气中甲醛

采用氧化还原法制备了MnOx催化剂,X射线衍射结果表明其主要为无定形结构.在甲醛和臭氧浓度分别为137和642mg/m3,相对湿度为56%(25oC),GHSV为2×105h-1条件下,MnOx催化剂上O3可将甲醛全部氧化为CO2,反应150min内甲醛转化率和CO2选择性一直保持在～100%.另外,当臭氧与甲醛的摩尔比约为2:3,即显著低于化学计量比时,CO2选择性仍可达～100%.采用傅里叶变换红外光谱仪在线分析了甲醛氧化反应产物,未检测到任何副产物,从而确认了MnOx催化剂上O3对甲醛的完全氧化.     

SrO对Al2O3载体的改性及MnOx/SrO-Al2O3催化剂的甲烷燃烧活性

以Mn(CH3COO)2为前驱体，制备了MnOx/Al2O3,MnOx/SrO-Al2O3系列催化剂，考察了SrO对Al2O3热稳定性的影响及MnOx/SrO-Al2O3催化甲烷燃烧的活性，并用X－射线衍射（XRD），程序升温还原（TPR）对其进行了表征，结果表明，随SrO加入量的增加复合载体SrO-Al2O3的比表面发生明显变化，高温焙烧过程中生成SrAl2O4,SrO.6Al2O3,SrO的加入抑制了Al2O3的α相变，SrO-Al2O3(1000℃焙烧）负载的MnOx催化剂，其还原性能有较大提高，对甲烷燃烧的催化活性明显增强。     

MnOx/g-C3N4光热协同催化净化NO的性能增强和反应机理

许多研究表明, MnOx和g-C3N4均有催化氧化NO的活性, 并且探索了它们各自的转化机理. 然而, MnOx/g-C3N4复合材料的光热催化机理仍然是一个未解决的问题. 我们通过室温沉淀法直接合成不同摩尔比的MnOx/g-C3N4, 并发现其表现出良好的光热协同催化氧化NO的性能. MnOx/g-C3N4催化剂在g-C3N4表面含有不同价态的MnOx. 通过原位红外光谱在60 ℃下研究了紫外-可见光诱导的MnOx热催化NO的机理以及MnOx/g-C3N4光热协同催化NO的机理. 结果表明, 光照对MnOx热催化NO的过程几乎没有影响, 但对MnOx/g-C3N4光热协同催化NO产生积极作用并且形成重要的催化循环机制. 具体过程是光生电子(e-)转移到MnOx上参与光热协同的还原循环(Mn4+→Mn3+→Mn2+), 且低价Mn离子易给出电子(e-)与光生空穴(h+)相结合而诱导逆向的循环(Mn2+→Mn3+→Mn4+), 使活性氧空位再生. 通过MnOx(Mn4+/Mn3+/Mn2+)变价而产生的活性氧(O-)可将中间产物(NOH和N2O2-)氧化为终产物(NO2-和NO3-). 这将为开发更好的净化NOx的催化剂提供重要的指导意义. XRD表征结果表明, MnOx/g-C3N4复合催化剂的结晶度较低. TEM和XPS表征结果表明, g-C3N4表面含有多种低结晶度的MnOx, 主要含有MnO, MnO2和Mn2O3. 此外, 通过对比MnOx和1:5 MnOx/g-C3N4催化净化NO的XPS结果, 发现反应后的MnOx含有大量Mn-Nitrate且Mn3+和Mn4+大幅度减少; 同时, 反应前后1:5 MnOx/g-C3N4的Mn2+, Mn3+和Mn4+的含量变化微弱. BET-BJH测试结果显示, MnOx/g-C3N4复合催化剂的比表面积和孔容均高于纯g-C3N4. UV-Vis DRS测试结果显示, MnOx/g-C3N4复合催化剂显示了良好的可见光吸收能力. 紫外-可见光催化去除NO的测试结果表明, 1:5 MnOx/g-C3N4(44%)的光催化活性明显高于MnOx(28%)和g-C3N4(36%). ESR测试结果表明, 参与反应的主要活性物种为·O2-自由基. EPR测试结果表明, 1:5 MnOx/g-C3N4的氧空位明显多于MnOx, 丰富的活性氧空位更有利于电子的迁移且促进Mnn+(n = 2, 3和4)的变价而诱导O2分子形成活性氧(O-). 以上结果清晰地表明1:5 MnOx/g-C3N4表现出不同的理化特性.可见光催化氧化NO的原位红外光谱表明, 光照前后MnOx催化氧化NO的过程没有明显的变化, 表明其属于典型的热催化过程, 综合上述表征结果发现MnOx的氧缺陷是Mnn+(n = 3和4)变价的活性位点, 可诱导O2产生活性氧催化氧化NO为硝酸盐吸附在MnOx上; 光照前后1:5 MnOx/g-C3N4催化氧化NO的过程有明显不同, 光照前主要表现为g-C3N4表面MnOx的热催化过程, 而光照后1:5 MnOx/g-C3N4为光热协同催化NO的过程. 具体过程是g-C3N4的光生电子(e-)转移到MnOx上参与光热协同的还原循环(Mn4+→Mn3+→Mn2+), 且低价Mn离子易给出电子(e-)与光生空穴(h+)相结合而诱导逆向的循环(Mn2+→Mn3+→Mn4+)使活性氧空位再生. 通过MnOx(Mn4+/Mn3+/Mn2+)变价而产生的活性氧(O-)可将中间产物(NOH和N2O2-)氧化为终产物(NO2-和NO3-).     

尿素水解法制备降解地表臭氧的Pd-Mnox/Al2O3催化剂

采用尿素水解法制备了Pd-MnOx/Al2O3催化剂,运用低温N2吸附-脱附和X射线衍射对其进行了表征,并评价了其催化降解地表O3反应活性,考察了Pd,MnOx焙烧时间和MnOx含量刘催化剂活性的影响.结果表明,在高空速(660000h-1)、高相对湿度(85%～90%)条件下,MnOx焙烧时间为6h且.MnOx含量为...     

TiO_2晶相对MnO_x/TiO_2催化剂催化NO氧化性能的影响（英文）

以浸渍在不同晶相TiO2(金红石型(R)、锐钛矿型(A)和P25型(P))上的锰基催化剂为对象,研究了TiO2晶相对MnOx/TiO2催化剂催化NO氧化活性的影响.结果表明,MnOx/TiO2(P)催化剂活性最高,NO转化率在300°C及GHSV=20000 h–1条件下可达83%.各催化剂活性顺序为MnOx/TiO2(P)MnOx/TiO2(A)MnOx/TiO2(R).采用X射线粉末衍射、场发射扫描电子显微镜、X射线光电子能谱、H2程序升温还原和O2程序升温脱附等手段研究了TiO2晶相影响MnOx/TiO2催化剂催化活性的作用机理.结果表明,相比于A和R型TiO2,P型TiO2能够增加MnOx在其表面的分散度并抑制催化剂颗粒的团聚和粘连,且更有利于Mn2O3的生成,而后者催化NO氧化活性比其它MnOx更高;此外,P型TiO2可以增加MnOx尤其是Mn2O3的还原性,并可促进O2–从M3+–O键的脱附.     

富氧条件下Ag/Al2O3和Cu/Al2O3组合催化剂催化C3H6选择性还原Nox的性能

 在全自动催化剂活性评价装置上,考察了富氧条件下Ag/Al2O3和Cu/Al2O3两种催化剂上催化丙烯还原NOx的活性. 在实验温度范围(200～650 ℃)内,Ag/Al2O3具有 优异的催化丙烯选择性还原NOx的活性,但同时有大量副产物CO形成. Cu/Al2O3选择性催化丙烯还原NOx的活性不高,却能有效促进CO的氧化. 在无水条件,Ag/Al2O3-Cu/Al2O3组合体系具有与Ag/Al2O3相似的脱除NOx活性,同时使CO在300 ℃以后几乎完全转化. 在10%水蒸气存在的情况下,Ag/Al2O3-Cu/Al2O3组合催化剂脱除NOx的活性下降,但水蒸气对CO转化率的影响不大.     

不同载体稳定的纳米金催化剂室温催化氧化甲醛研究

甲醛是一种常见的室内空气污染物,人们针对其消除已经做了大量的研究工作.催化氧化法是脱除挥发性有机物的一种重要方法,能在较低温度下通过催化剂作用将甲醛完全氧化为无毒的CO2和H2O.所用催化剂主要为负载型贵金属催
　　化剂和非贵金属催化剂,但只有担载贵金属Pt或Pd的催化剂可在室温下将甲醛完全氧化,而非贵金属一般则需要较高的温度. Au催化剂是近年来催化领域的一个研究热点,但是关于纳米Au催化剂室温消除甲醛的研究较少.本课题组前期研究发现,以可还原性氧化物(CeO2, FeOx)为载体负载的Au催化剂具有优异的室温氧化甲醛活性;并且突破以可还原性载体负载金的传统思路,首次发现“惰性载体”γ-Al2O3,负载的金催化剂在室温、有水条件下具有优异的甲醛氧化活性.本文对比了还原性氧化物(CeO2, FeOx)和非还原性氧化物(Al2O3, SiO2和HSZM-5)载体负载金催化剂,研究了载体氧化还原性质对负载金催化剂在高空速(600000 ml/(g·s))条件下室温催化氧化甲醛的活性和稳定性影响.结果表明,在室温、高空速且相对湿度为50%的条件下, Au/Al2O3催化剂的初活性最高,且较为稳定. Au/SiO2和Au/HZSM-5催化剂的初活性虽然较高,但很快失活.而还原性氧化物载体(CeO2, FeOx)负载的金催化剂初活性较低,但是稳定性较好.通过电镜对负载金催化剂表面Au粒子大小的表征,并将粒子尺寸与负载金催化剂室温氧化甲醛初活性相关联,它与催化氧化甲醛反应速率成线性关系. Au粒子尺寸较小的催化剂(Au/Al2O3和Au/SiO2),在高空速条件下具有更高的氧化甲醛活性,而Au粒子尺寸较大的Au/FeOx催化剂活性较差.载体的氧化还原性质虽然不直接影响Au催化剂初活性,但直接影响催化剂稳定性.由于Au与SiO2或HZSM-5载体的相互作用较弱,导致反应过程中Au粒子聚集长大,使其失活较快;而Au/Al2O3催化剂表面则富含羟基物种,能够与Au形成配体或产生锚定作用,因此反应过程中金粒子没有明显长大.而表面中间物种的沉积并覆盖活性位是负载金催化剂缓慢失活的主要原因.     

常温下 MnO2/Al2O3催化剂催化臭氧氧化甲苯反应

采用浸渍法制备了Al2O3负载的5种过渡金属氧化物催化剂,考察了它们在常温下催化臭氧氧化甲苯的性能,并运用程序升温还原、程序升温氧化、N2吸附-脱附和X射线光电子能谱对催化剂进行了表征.结果表明,NiO/Al2O3,CoO/Al2O3和MnO2/Al2O3催化剂上活性氧中心数量较少,臭氧与甲苯转化率较高;而Fe2O3/...     

MnOx／Al2O、MnOx／BaO—Al2O3催化剂的制备、表征及其对甲烷低温燃烧的催化活性

改变锰的负载最及前驱体,制备了MnOx/Al2O、MnOx/BaO-Al2O3系列催化剂;采用X-射线衍射（XRD）、程序升温还原（TPR）对催化剂进行表征,并考察了BaO的加入对CH4低温燃烧催化活性的影响。结果表明,用醋酸锰作前驱体与用硝酸锰制备的催化剂相比,其活性组分分散性好、氧中心活性高,催化CH4低温燃烧的活性高。在Al2O3载体中掺入BaO,催化剂的氧中心数目的没有明显变化,但氧中心活性有所下降,因而降低了对CH4低湿燃烧的催化活性。     

Structure and oxidation state of silica-supported manganese oxide catalysts and reactivity for acetone oxidation with ozone

Silica-supported manganese oxide catalysts with loadings of 3, 10, 15, and 20 wt % (as MnO2) were characterized with use of X-ray absorption spectroscopy and X-ray diffraction (XRD). The edge positions in the X-ray absorption spectra indicated that the oxidation state for the manganese decreased with increasing metal oxide loading from a value close to that of Mn2O3 (+3) to a value close to that of Mn3O4 (+2(2)/3). The XRD was consistent with these results as the diffractograms for the supported catalysts of higher manganese oxide loading matched those of a Mn3O4 reference. The reactivity of the silica-supported manganese oxide catalysts in acetone oxidation with ozone as an oxidant was studied over the temperature range of 300 to 600 K. Both oxygen and ozone produced mainly CO2 as the product of oxidation, but in the case of ozone the reaction temperature and activation energy were significantly reduced. The effect of metal oxide loading was investigated, and the activity for acetone oxidation was greater for a 10 wt % MnOx/SiO2 catalyst sample compared to a 3 wt % MnOx/SiO2 sample.     

锰氧八面体分子筛室温同时去除甲醛和臭氧的性能研究

通过回流法、无溶剂法及水热法合成了3种锰氧八面体分子筛催化剂（OMS-2）,并对其室温同时去除甲醛和臭氧的反应活性进行了研究.结果表明无溶剂法制备的锰氧八面体分子筛（OMS-2-S）具有最高的甲醛转化率,且水气的加入对3种OMS-2催化剂的二氧化碳产率均具有明显的促进作用.并通过XRD、SEM和XPS等技术对催化剂进行表征,考察了催化剂物理化学性质对其催化活性的影响.从表征结果可得,较强的吸附能力、丰富的氧空位及较强的氧物种移动性是OMS-2-S催化剂活性较高的原因.     

Zr-Ni/Al2O3催化剂上苯由H2O2氧化直接氨基化制苯胺

用浸渍法制备了Ni／Al2O3和Zr-Ni／Al2O3催化剂，用于以过氧化氢为氧化剂的苯直接氧化胺化制苯胺反应，并对催化剂进行了程序升温还原、室温氧吸附和氢吸附及XRD表征，结果表明，我们所制的Ni基催化剂对苯胺的生成都有活性，加入Zr后，催化剂中Ni物种更分散，低温可还原物种增加，室温吸氧和吸氢能力都增强，反应活性和对目标产物的选择性增大，Zr一方面使Ni物种进一步分散，增大催化剂的吸氢量和表面可还原Ni物种，有利于C-H键的活化；同时Zr与Ni的相互作用，促进了低温可还原物种的生成，使催化剂室温吸氧量增大，有利于苯的氧化，这种Zr和Ni的协同作用提高了催化剂的活性和选择性，催化剂的制备方法影响Zr与Ni的协同作用，使含Zr的两个催化剂的活性和选择性显示出差异。     

Mn/Ba/Al2O3催化剂的NOx氧化-储存和耐硫性能

采用分步等体积浸渍法制备了Mn/Ba/Al2O3催化剂, 并用XRD和TPD等方法进行表征. 考察了催化剂在不同温度下NOx氧化-储存特性和NOx脱附行为. 结果表明, Mn/Ba/Al2O3催化剂具有较高的催化NO氧化活性和较大的NOx储存容量. BaMnO3是主要的活性组分；Mn能够催化NO的氧化反应, 且具有一定的NOx储存能力; Ba是主要的储存组分, 将NOx以硝酸盐的形式储存; 硝酸盐在300～600 ℃分解, 释放出NOx. Mn/Ba/Al2O3催化剂在800 ℃老化6 h后, NO氧化活性和NOx储存能力稍有下降. 低含量的SO2对催化剂的NO氧化活性和NOx储存能力没有明显影响; 高含量的SO2使催化剂的NO氧化活性降低, NOx储存量减小, 最终导致催化剂失活.     

Selective catalytic oxidation of NO with O2 over Ce-doped MnOx/TiO2 catalysts

A series of Ce-doped MnOx/TiO2 catalysts were prepared by impregnation method and used for catalytic oxidation of NO in the presence of excess O2. The sample with the Ce doping concentration of Ce/Mn=1/3 and calcined at 300°C shows a superior activity for NO oxidation to NO2. On Ce(1)Mn(3)Ti catalyst, 58% NO conversion was obtained at 200°C and 85% NO conversion at 250°C with a GHSV of 41000 h-1, which was much higher than that over MnOx/TiO2 catalyst (48% at 250°C). Characterization results implied that the higher activity of Ce(1)Mn(3)Ti could be attributed to the enrichment of well-dispersed MnOx on the surface and the abundance of Mn3+ and Ti3+ species. The addition of Ce into MnOx/TiO2 could improve oxygen storage capacity and facilitate oxygen mobility of the catalyst as shown by PL and ESR, so that its activity for NO oxidation could be enhanced. The effect of H2O and SO2 on the catalyst activity was also investigated.     

The effect of hydrogen reduction of α-MnO2 on formaldehyde oxidation: The roles of oxygen vacancies

A series of α-MnO₂ catalysts with various Mn valence states were treated by hydrogen reduction for different periods of time. Their catalytic capacity for formaldehyde (HCHO) oxidation was evaluated. The results indicated that hydrogen reduction dramatically improves the catalytic performance of α-MnO₂ in HCHO oxidation. The α-MnO₂ sample reduced by hydrogen for 2 h possessed superior activity and could completely oxidize 150 ppm HCHO to CO₂ and H₂O at 70 °C. Multiple characterization results illustrated that hydrogen reduction contributed to the production of more oxygen vacancies. The oxygen vacancies on the catalyst surface enhanced the adsorption, activation and mobility of O₂ molecules, and thereby enhanced HCHO catalytic oxidation. This study provides novel insight into the design of outstanding MnO_x catalysts for HCHO oxidation at low temperature.     

球形氧化铝负载锰基双金属氧化物催化剂催化臭氧深度氧化NO

在工业锅炉烟气处理领域,由于锅炉容量低,烟气温度往往无法满足传统选择性催化还原(SCR)所需温度窗口.工业锅炉烟气成分的复杂性也给氮氧化物治理带来了严峻考验.臭氧深度氧化NO结合湿法洗涤同时脱硫脱硝技术具有独特的应用优势.传统臭氧氧化技术中,NO被臭氧氧化为NO2,进而在脱硫塔中实现一体化脱硫脱硝.但由于NO2溶解度相对较低,需要在脱硫浆液中加入添加剂提高脱硝效率,造成运行成本增加.NO经臭氧深度氧化后,NO2进一步转化为溶解度高的N2O5,传统脱硫石膏浆液即可实现高效吸收N2O5,从而有效提高氮氧化物吸收效率.但由于N2O5生成反应速率低,深度氧化存在臭氧投入量大、反应时间长及臭氧残留多的缺点.臭氧耦合催化剂深度氧化NO可有效解决以上问题.首先,本文采用溶胶-凝胶法合成一系列单金属氧化物(Mn,Co,Ce,Fe,Cu,Cr)作为臭氧深度氧化NO的催化剂.结果发现锰氧化物表现出最高的催化活性,在70oC下,O3/NO摩尔比为2.0时经过0.12 s的反应时间催化剂即可实现80%以上的转化效率.但根据N2O5生成的总包反应(2NO+3O3=N2O5+3O2)可以看出,O3/NO摩尔比为1.5时即可实现N2O5的完全转化.由于催化臭氧氧化反应温度较低,中间产物在催化剂表面聚集,占据大量活性位,进而导致无法实现1.5摩尔比的高效转化.通过采用球形氧化铝作为载体,避免粉末状催化剂紧凑型布置,增加换热面积,可有效降低催化剂表面中间产物聚集;同时延长了气体与催化剂的接触时间,提高反应效率.在球形氧化铝载体上负载锰基双金属氧化物(Ce-Mn,Fe-M,Cr-Mn,Cu-Mn和Co-Mn),在初始NO浓度为410 mg/m3,反应温度100oC,O3/NO摩尔比1.5,催化反应时间0.12 s的工况下,催化剂最终实现95%(Fe-Mn)和88%(Ce-Mn)的转化效率,剩余NO和NO2的浓度分别低于20 mg/m3(Fe-Mn)和50 mg/m3(Ce-Mn),臭氧残留浓度低于25 mg/m3.同负载单一锰氧化物(83%转化率)相比,双金属氧化物进一步提高了N2O5生成效率.因此,臭氧耦合催化剂深度氧化NO结合湿法吸收在工业锅炉超低排放(NOx<50 mg/m3)领域具有广泛应用前景.通过XRD、氮气吸附、H2-TPR和XPS等手段研究了催化剂的晶体结构、孔结构参数、氧化还原性能和表面原子价态.催化臭氧深度氧化NO主要与催化剂对臭氧的分解性能和对NO的氧化性能有关.较大的比表面积和孔容有利于催化剂的吸附.氧空位有利于臭氧的吸附和分解.Mn4+和Mn3+的均衡分布既有利于NO的吸附氧化又有利于臭氧的吸附分解,最终提高了N2O5生成效率.     

MnOx/Al2O3/Ce0.45Zr0.45M0.10Oy （M = Mn, Y, La） catalysts used for ethanol catalytic combustion

MnOx/Al2O3/Ce0.45Zr0.45M0.10Oy (M = Mn,Y,La) catalysts were prepared by impregnation method and characterized by BET,TPR and XRD analyses.The catalytic activities toward ethanol combustion were investigated in a microreactor.The results demonstrated that the catalytic activity of MnOx/Al2O3/Ce0.50Zr0.50O2 monolithic catalyst could be improved by doping Mn,Y and La into Ce0.50Zr0.50O2.When doping Y into Ce0.50Zr0.50O2,the catalyst MnOx/Al2O3/Ce0.45Zr0.45Y0.10O1.95 showed the highest activity.The 100% conversion temperature of ethanol was 230 ℃.Furthermore,once the conversion of ethanol started,the complete conversion was quickly achieved.The doping of Mn,Y and La led to better activity for ethanol combustion and lower temperature reduction peaks in TPR profiles.The doping of Mn resulted in enhanced oxygen storage capacity (OSC),larger area of the reduction peaks,and excellent reactivity,and the doping of Y resulted in the lowest reduction temperature and the best activity.