锂离子电池用Cr2O3/TiO2复合材料的电化学性能

采用高温固相反应法合成了Cr₂O₃/TiO₂复合材料, 运用X射线衍射(XRD)、扫描电子显微镜(SEM)、充放电测试、循环伏安(CV)、电化学阻抗谱(EIS)等对其结构、形貌和电化学性能进行了表征. 研究结果表明: TiO₂掺杂能够显著改善Cr₂O₃的充放电循环性能, Cr₂O₃/TiO₂复合材料在充放电循环22周后仍有454 mAh·g^-1的可逆循环容量, 容量保持率达到了73.6%, 主要归因于TiO₂掺杂能够显著提高Cr₂O₃的电导率. Cr₂O₃/TiO₂复合材料首次放电过程中由于电极体积膨胀导致的固体电解质相界面(SEI)膜迅速增厚和活性材料电导率的降低可能是其首次充放电过程中存在较大不可逆容量和循环容量衰减的重要原因.     

TiO2/Cu2O/Pt复合空心微球的制备及其光催化性能

以锐钛矿相TiO₂溶胶为基底,采用沉淀法和液相沉积法制备了TiO₂/Cu₂O/Pt复合空心微球,通过改变n_Ti⁴⁺∶ n_Cu²⁺和H₂PtCl₆·6 H₂O溶液的加入量对TiO₂的形貌和结构进行调控,采用不同的方法对不同样品的物相及结构、微观形貌和光学性能进行了对比分析。分析结果表明,复合材料中Pt与Cu₂O的引入产生协同效应,不仅在一定程度上阻止了电子-空穴的复合,还降低了禁带宽度,在可见光区域光吸收明显增强。与TiO₂、Cu₂O和TiO₂/Cu₂O光催化剂相比较,TiO₂/Cu₂O/Pt降解有机污染物的能力显著增强,首次光照120 min可降解93%的甲基橙(MO)溶液,4次循环后降解率为71%,具有良好的光催化稳定性能。     

模板法制备的Fe3+/TiO2中空纳米纤维的光催化性能

以棉花纤维为模板,利用浸渍-热转化两步法制备了Fe³⁺掺杂的二氧化钛(Fe³⁺/TiO₂)中空纳米纤维光催化材料,并利用扫描电镜(SEM)、X射线衍射(XRD)、紫外-可见光谱(UV-Vis)和ζ电位等技术对其形貌、结构、光吸收特性及其表面状态等进行了表征。以亚甲基蓝(methylene blue,MB)溶液的脱色降解为模型反应,考察了煅烧温度与时间对Fe³⁺/TiO₂中空纳米纤维光催化性能的影响。结果表明：利用该法可以制得棉花纤维形貌的Fe³⁺/TiO₂中空纳米结构材料;所得材料的催化性能除与材料的尺寸、相结构有关外,还与表面荷电性质有关,表面荷电量越高、表面结构缺陷越多、表面活性位越多,催化活性越高。500 ℃下煅烧2 h所得材料表面长有大量的粒子(平均尺寸为12 nm),其中TiO₂为锐钛矿结构,表面荷负电荷量最高,催化性能最好,如在太阳光下,2 h可使MB溶液的脱色降解率达93%,6 h完全脱色,而在纯TiO₂中空纤维材料上约为70%;该材料还具有良好的催化稳定性能,重复使用5次仍可使MB溶液的脱色降解率保持在90%以上,且该催化剂材料易于离心分离去除。     

不同浓度Sn4+离子掺杂TiO2的结构、性质和光催化活性

采用溶胶-凝胶法制备出纯TiO₂和不同浓度Sn⁴⁺离子掺杂的TiO₂光催化剂(TiO₂-Snx%, x%代表Sn⁴⁺离子掺杂的TiO₂样品中Sn⁴⁺离子摩尔分数). 利用X 射线衍射(XRD)、X 射线光电子能谱(XPS)和表面光电压谱(SPS)确定了TiO₂-Snx%催化剂的晶相结构和能带结构, 结果表明: 当Sn⁴⁺离子浓度较低时, Sn⁴⁺离子进入TiO₂晶格, 取代并占据Ti⁴⁺离子的位置, 形成取代式掺杂结构(Ti_1-xSn_xO₂), 其掺杂能级在导带下0.38 eV处; 当Sn⁴⁺离子浓度较高时, 掺入的Sn⁴⁺离子在TiO₂表面生成金红石SnO₂, 形成TiO₂和SnO₂复合结构(TiO₂/SnO₂), SnO₂的导带位于TiO₂导带下0.33 eV处. 利用瞬态光电压谱和荧光光谱研究了TiO₂-Snx%催化剂光生载流子的分离和复合的动力学过程, 结果表明, Sn⁴⁺离子掺杂能级和表面SnO₂能带存在促进光生载流子的分离, 有效地抑制了光生电子与空穴的复合; 然而, Sn⁴⁺离子掺杂能级能更有效地增加光生电子的分离寿命, 提高了光生载流子的分离效率, 从而揭示了TiO₂-Snx%催化剂的光催化机理.     

GO/TiO2-g-C3N4纳米复合材料的制备及可见光催化性能

以水热法制备的20% g-C₃N₄/TiO₂（20%为质量分数）为基,将其与不同质量分数的氧化石墨烯（GO）复合制备出可见光催化性能优良的GO/TiO₂-g-C₃N₄三元复合材料。利用X射线衍射（XRD）、扫描电子显微镜（SEM）、X射线光电子能谱（XPS）、紫外-可见漫反射光谱（UV-Vis DRS）、光致荧光光谱（PL）、瞬态光电流响应等分析测试手段对样品的结构、形貌和光电性能进行表征。研究了不同质量分数GO的加入对GO/TiO₂-g-C₃N₄在可见光下降解亚甲基蓝（MB）溶液的影响。结果表明： g-C₃N₄/TiO₂与GO复合后,锐钛矿相TiO₂颗粒形成小团簇附着在g-C₃N₄和GO片层表面,且当GO含量为15%时,TiO₂形成的团簇最小,对可见光的吸收最多且光生电子-空穴对的复合率最低。可见光照射下,15% GO/TiO₂-g-C₃N₄复合材料对MB的降解率在3 h内可达98.4%,且其降解速率常数（0.022 4 min^-1）分别是纯TiO₂（0.001 5 min^-1）和g-C₃N₄/TiO₂（0.002 5 min^-1）的15倍和9倍。     

Gd3+掺杂TiO2纳米复合材料的可见光响应性能

采用溶胶-凝胶技术,在钛酸四丁酯(TBOT)的水解过程中,加入硝酸钆(Gd(NO₃)₃),得到具有可见光响应活性的Gd³⁺/TiO₂复合材料。应用TEM、XRD、TG-DTA和UV-Vis等手段对纳米TiO₂复合材料进行了表征。当Gd³⁺的掺杂量为0.5%时,Gd³⁺/TiO₂复合材料在550 nm附近产生宽强吸收带。Gd³⁺进入TiO₂晶格中,形成了新的掺杂能级(E_g=1.27 eV)。适量Gd³⁺掺杂的纳米TiO₂复合材料的光催化性能优于纯TiO₂粉体材料。     

Ti3+自掺杂的TiO2(A)/TiO2(R)/In2O3纳米异质结的制备与可见光催化性能

以TiCl₃和InCl₃为Ti源和In源,在不使用还原剂的条件下,首先通过液相沉淀反应制备前驱体沉淀,然后采用后续水热处理制备Ti³⁺自掺杂的TiO₂(A)/TiO₂(R)/In₂O₃纳米异质结,考察了水热处理温度对材料结构和性能的影响。利用X射线衍射、透射电子显微镜、X射线光电子能谱和紫外-可见漫反射光谱对样品进行表征。分别以罗丹明B和苯酚溶液为模拟废水评价了样品的可见光催化降解性能。结果表明,与纯的TiO₂、In₂O₃以及Ti³⁺自掺杂的TiO₂相比,Ti³⁺自掺杂的TiO₂(A)/TiO₂(R)/In₂O₃纳米异质结在可见光区有明显的吸收,并具有良好的可见光催化降解性能,200℃下水热处理24 h所得样品光催化降解罗丹明B的反应速率常数(0.0444 min^-1)分别是纯TiO₂和In₂O₃的17.76倍和8.71倍。瞬态光电流时间响应结果表明样品的光催化性能主要来源于TiO₂(A)/TiO₂(R)/In₂O₃纳米异质结导致的提高的光生电子和空穴分离效率。     

水热法制备具有高光催化活性的镧掺杂二氧化钛纳米晶

采用水热法合成钛酸钾(K₂Ti₈O₁₇)纳米棒,并将它作为前驱体水热转晶合成TiO₂纳米晶,同时通过在水热体系中引入稀土元素La³⁺实现对TiO₂的La掺杂.考察了不同条件下钛酸盐向TiO₂的转晶过程,发现水热溶液的pH值、温度以及预处理步骤对转晶过程有很大的影响.利用X射线衍射以及透射电子显微镜对样品的晶相和形貌进行了表征.利用电感耦合等离子体原子发射光谱测量了所合成的La掺杂TiO₂样品中的La含量.通过在紫外光下降解甲基橙(MO,10mg/L)测试了La掺杂TiO₂样品的光催化性能.结果表明La掺杂后TiO₂的光催化活性大大提高.在0.15mol/LLa³⁺浓度下180oC水热合成的La掺杂TiO₂样品显示了最佳的光催化活性.其对MO的光催化降解反应常数高达0.11min^-1,大约是空白TiO₂样品的9.20倍,P25TiO₂的3.69倍.     

TiO2纳米微球的制备及在染料敏化太阳能电池中的应用

以四氯化钛、盐酸为原料,制备出花状TiO₂纳米微球,利用扫描电子显微镜（SEM）、X射线衍射（XRD）等测试方法,对样品的结构和形貌进行了表征。为了提高TiO₂微球电池的光电性能,利用TiO₂微球作为反射层构造了双层结构的薄膜电极,结果表明,双层结构染料敏化太阳能电池在100 mW·cm^-2（1.5 G）光照条件下,短路光电流J_sc为17.64 mA·cm^-2,开路光电压Voc为0.74 V,填充因子FF为0.63和光电转化效率η为8.33%。相比TiO₂微球制备的太阳能电池,双层结构染料敏化太阳能电池光电转化效率提高至5.3倍。最后对电极中染料的吸附量、电极的光散射性能和电池的电化学阻抗做了进一步研究和分析,研究表明,双层结构电池增强光的捕获能力,从而提高光伏性能。     

RE/TiO2光催化剂的谱学特性与气相光催化性能的研究

采用改进的sol-gel法和浸渍法制备了TiO₂掺杂稀土离子La³⁺、Y³⁺、Gd³⁺、Er³⁺、Nd³⁺、Pr³⁺的RE/TiO₂光催化剂,运用FTIR、XRD、TEM、低温氮吸附/脱附、TG/DTA、UV-Vis DRS、表面光电压谱(SPS)等进行表征,以气相光催化降解乙烯、溴代甲烷作为探针反应,阐明了RE/TiO₂光催化剂的谱学特性与气相光催化性能的关系。结果显示,稀土离子掺杂后,TiO₂的锐钛矿含量增加,比表面积增大,粒径变小,吸收边发生蓝移,表面光电压的响应阈值增大,此外,Pr³⁺除外的其它稀土离子掺杂的TiO₂的表面光电压信号增强;光催化降解实验表明,与纯TiO₂相比,La³⁺、Y³⁺、Gd³⁺、Er³⁺、Nd³⁺掺杂TiO₂样品上乙烯、溴代甲烷的光催化活性均有不同程度的增强,而且表现出较强的矿化能力。但是,掺杂Pr³⁺的TiO₂的光催化性能降低恰好对应较弱的表面光电压信号。所以,本文认为提高光生电子-空穴对的分离效率是改善光催化性能的关键因素。     

金@氧缺陷二氧化钛核壳纳米颗粒的制备及光催化产氢

通过水解TiCl_3在金纳米颗粒外表生长TiO_2,然后在Ar/H2气氛中高温煅烧成功地合成了核壳形貌的Au@H-TiO_2缺陷结构。采用XRD、TEM、XPS、UV-Vis测试方法对产物的物相结构、形貌及光吸收能力做了系统的分析。与不存在缺陷态的TiO_2和Au@A-TiO_2相比,Au@H-TiO_2表现出最高的产氢速率,这可以归因于其电荷分离效率的提高和电荷转移阻抗的降低,瞬态光电流测试以及电化学阻抗数据证实了这一结论。这些性能的改进可能与Au@H-TiO_2中的Ti~(3+)自掺杂和Au修饰有关。     

Preparation and properties of amorphous titania-coated zinc oxide nanoparticles

Amorphous TiO₂-coated ZnO nanoparticles were prepared by the solvothermal synthesis of ZnO nanoparticles in ethanol and the followed by sol-gel coating of TiO₂ nanolayer. The analyses of X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that the resultant ZnO nanoparticles were hexagonal with a wurtzite structure and a mean diameter of about 60 nm. Also, after TiO₂ coating, the TEM images clearly indicated the darker ZnO nanoparticles being surrounded by the lighter amorphous TiO₂ layers. The zeta potential analysis revealed the pH dependence of zeta potentials for ZnO nanoparticles shifted completely to that for TiO₂ nanoparticles after TiO₂ coating, confirming the formation of core-shell structure and suggesting the coating of TiO₂ was achieved via the adhesion of the hydrolyzed species Ti-O⁻ to the positively charged surface of ZnO nanoparticles. Furthermore, the analyses of Fourier transform infrared (FTIR) and Raman spectra were also conducted to confirm that amorphous TiO₂ were indeed coated on the surface of ZnO nanoparticles. In addition, the analyses of ultraviolet-visible (UV-VIS) and photoluminescence (PL) spectra revealed that the absorbance of amorphous TiO₂-coated ZnO nanoparticles at 375 nm gradually decreased with an increase in the Ti/Zn molar ratio and the time for TiO₂ coating, and the emission intensity of ZnO cores could be significantly enhanced by the amorphous TiO₂ shell.     

The Preparation and Characterization of La Doped TiO2 Nanotubes and Their Photocatalytic Activity

La-doped TiO₂ nanotubes (La/TiO₂ NTs) were prepared by the combination of sol-gel process with hydrothermal treatment. The prepared samples were characterized by using transmission electron microscopy, x-ray diffraction, x-ray photoelectron spectra, and ultraviolet-visible spectra. The photocatalytic performance of La/TiO₂ NTs was studied by testing the degradation rate of methyl orange under ultraviolet (UV) irradiation. The results indicated La/TiO₂ NTs calcined at 300°C consisted of anatase as the unique phase. The absorption spectra of the La/TiO₂ NTs showed a stronger absorption in the UV range and a slight red shift in the band gap transition than that of pure TiO₂ nanotubes. The photocatalytic performance of TiO₂ NTs could be improved by the doping of lanthanum ions, which is ascribed to several beneficial effects the formation of Ti-O-La bond and charge imbalance, existing of oxygen defects and Ti³⁺ species, stronger absorption in the UV range and a slight red shift in the band gap transition, as well as higher equilibrium dark adsorption of methyl orange. 0.75 wt% La/TiO₂ NTs had the best catalytic activity.     

The preparation and characterization of La doped TiO2 nanoparticles and their photocatalytic activity

In this paper, pure and La doped TiO₂ nanoparticles with different La content were prepared by a sol-gel process using Ti (OC₄H₉)₄ as raw material, and also were characterized by XRD, TG-DTA, TEM, XPS, DRS and Photoluminescence (PL) spectra. We mainly investigated the effects of calcining temperature and La content on the properties and the photocatalytic activity for degrading phenol of as-prepared TiO₂ samples, and also discussed the relationships between PL spectra and photocatalytic activity as well as the mechanisms of La doping on TiO₂ phase transformation. The results showed that La³⁺ did not enter into the crystal lattices of TiO₂ and was uniformly dispersed onto TiO₂ as the form of La₂O₃ particles with small size, which possibly made La dopant have a great inhibition on TiO₂ phase transformation; La dopant did not give rise to a new PL signal, but it could improve the intensity of PL spectra with a appropriate La content, which was possibly attributed to the increase in the content of surface oxygen vacancies and defects after doping La; La doped TiO₂ nanoparticles calcined at 600°C exhibited higher photocatalytic activity, indicating that 600°C was an appropriate calcination temperature. The order of photocatalytic activity of La doped TiO₂ samples with different La content was as following: 1>1.5>3>0.5>5>0 mol%, which was the same as the order of their PL intensity, namely, the stronger the PL intensity, the higher the photocatalytic activity, demonstrating that there were certain relationships between PL spectra and photocatalytic activity. This could be explained by the points that PL spectra mainly resulted from surface oxygen vacancies and defects during the process of PL, while surface oxygen vacancies and defects could be favorable in capturing the photoinduced electrons during the process of photocatalytic reactions.     

Photocatalytic degradation of methylene blue on Fe3+-doped TiO2 nanoparticles under visible light irradiation

Fe³⁺-doped TiO₂ composite nanoparticles with different doping amounts were successfully synthesized using sol-gel method and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and ultravioletvisible spectroscopy (UV-Vis) diffuse reflectance spectra (DRS). The photocatalytic degradation of methylene blue was used as a model reaction to evaluate the photocatalytic activity of Fe³⁺/TiO₂ nanoparticles under visible light irradiation. The influence of doping amount of Fe³⁺ (ω: 0.00%–3.00%) on photocatalytic activities of TiO₂ was investigated. Results show that the size of Fe³⁺/TiO₂ particles decreases with the increase of the amount of Fe³⁺ and their absorption spectra are broaden and absorption intensities are also increased. Doping Fe³⁺ can control the conversion of TiO₂ from anatase to rutile. The doping amount of Fe³⁺ remarkably affects the activity of the catalyst, and the optimum efficiency occurs at about the doping amount of 0.3%. The appropriate doping of Fe³⁺ can markedly increase the catalytic activity of TiO₂ under visible light irradiation. __________ Translated from Journal of Northwest Normal University (Natural Science), 2006, 42(6): 55–56 [译自: 西北师范大学学报(自然科学版)]     

Au改性TiO2纳米复合物对人结肠癌细胞的光催化杀伤作用

提出了通过TiO₂表面修饰纳米Au的方法来提高纳米TiO₂光催化杀伤癌细胞的效率. 采用化学还原法合成了Au改性的TiO₂ (Au/TiO₂)纳米复合物, 并研究了不同掺杂量(1 wt%, 2 wt%, 4 wt%)的Au/TiO₂对人结肠癌LoVo细胞的光催化杀伤效应. 结果显示, Au的掺杂大大地提高了TiO₂纳米粒子光催化杀伤结肠癌LoVo细胞的效率, 而且Au掺杂量的高低影响Au/TiO₂光催化杀伤癌细胞的效率, 掺金量为2%的Au/TiO₂对结肠癌LoVo细胞具有最高的光催化杀伤效率. 在光强为1.8 mW/cm²的紫外灯(λ_max＝365 nm)下光照110 min, 50 μg/mL掺金量为2%的Au/TiO₂能够杀死所有的癌细胞, 而同样浓度的TiO₂只能杀死70%的癌细胞.     

载有C60的TiO2纳米粒子光催化活性

以水溶性C₆₀和TiO₂粒子为前驱体,采用水热法制备了载有C₆₀的锐钛矿型TiO₂纳米粒子。应用X射线衍射、透射电子显微镜、红外光谱、紫外-可见漫反射光谱、荧光光谱对产物进行了表征。以对-硝基苯酚为模型污染物研究了产物的光催化活性,结果表明适量负载C₆₀可以提高TiO₂纳米粒子的光催化活性,C₆₀起着传输电子、促进TiO₂光生载流子分离的作用,且经7次循环使用后对-硝基苯酚的降解效率仍能达到74%。讨论了载有C₆₀的TiO₂纳米粒子光催化降解对-硝基苯酚的机理。     

Photoinduced interactions between colloidal TiO2 nanoparticles and calf thymus-DNA

The interaction of colloidal TiO₂ nanoparticles with calf thymus-DNA was studied by using absorption, FT-IR, steady state and time resolved fluorescence spectroscopic techniques. The apparent association constant has been deduced (K_app = 2.85 × 10³ M⁻¹) from the absorption spectral changes of the DNA-colloidal TiO₂ nanoparticles using the Benesi–Hildebrand equation. Addition of colloidal TiO₂ nanoparticles quenched the fluorescence of EtBr–DNA. The number of binding sites (n = 0.97) and the apparent binding constant (K = 6.68 × 10³ M⁻¹) were calculated from relevant fluorescence quenching data. The quenching, through a static mechanism, was confirmed by time resolved fluorescence spectroscopy.     

TiO2 nanoparticles incorporated with CuInS2 clusters: preparation and photocatalytic activity for degradation of 4-nitrophenol

TiO₂ nanoparticles incorporated with CuInS₂ clusters were prepared in a solvothermal process and characterized with X-ray diffraction (XRD), transmission electron microscopy (TEM), and energy-dispersion X-ray analysis (EDX). Compared with pure TiO₂ nanoparticles, the TiO₂ nanoparticles incorporated with CuInS₂ clusters display higher photocatalytic activity with 99.9% of degradation ratio of 4-nitrophenol after 2 h irradiation. In order to investigate the effect of the CuInS₂ clusters on the photocatalytic activity of TiO₂ nanoparticles, diffuse reflectance UV–Vis spectra (DRS), photoluminescence (PL) spectra, and photocurrent action spectra were measured. The results indicate that the enhanced photocatalytic activity is probably due to the interface between TiO₂ and CuInS₂ as a trap of the photogenerated electrons to decrease the recombination of electrons and holes.