银纳米线的制备及电催化还原氧性能研究

分别以聚乙烯基吡咯烷酮(PVP),乙二醇作为软模板和还原剂,采用不同晶种(AgCl、Ag)快速合成了银纳米线.通过SEM和TEM表征,证明合成银纳米线材料形貌均一,颗粒含量很少.并且发现以AgCl为晶种合成的银纳米线长径比为200左右(SNWH),而以Ag为晶种合成的长径比为30左右(SNWL).以银纳米线作为电催化氧...     

溶剂热法制备银纳米晶

以聚乙烯吡咯烷酮(PVP)作为表面活性剂,利用乙二醇溶剂热法成功制备了银纳米颗粒;利用场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)、X射线衍射(XRD)分析了样品的形貌和晶体结构,并考察了溶剂组成等因素对银纳米颗粒形貌的影响.研究结果表明所得银纳米晶粒径均一,直径约为90nm;增大PVP的加入量会降低产物的粒径,溶剂中水的引入会影响银纳米晶的形貌.     

银纳米晶体的制备与表征

在聚乙烯吡咯烷酮存在的条件下,用水合肼还原硝酸银,通过控制反应条件成功制备出了粒径均一、有良好分散性的银纳米微粒,并以此为种子,利用种子诱导生长,在十六烷基三甲基溴化铵的棒状胶束环境中制备出了银纳米棒和纳米线.并用X射线衍射、透射电子显微镜、傅立叶红外光谱和紫外-可见光谱等手段对产品的形貌、结构进行了表征.     

多羟基化合物法制备五次孪晶银纳米线的生长机理

运用多羟基化合物方法, 在添加表面活性剂聚乙烯吡咯烷酮(PVP) K30的溶液中合成了多次孪晶银纳米颗粒和纳米线. 运用透射电子显微术(TEM)和光吸收谱, 对不同的摩尔比n(PVP):n(AgNO3)和不同的搅拌条件下制备的纳米线进行了对比研究. 结果表明, 这种方法的制备过程中不仅存在由五个{111}面包裹成的锥形生长, 而且还同时存在垂直于生长方向的{110}层状生长, 并且两者之间还存在着竞争; 另外对纳米线的弯折处进行的高分辨电子显微学研究表明, 纳米线制备过程中遭受的塑性变形在纳米线中产生了大量的层错和位错; 纳米线折断产生的新鲜断口容易成为新的晶粒形核位置.     

液相合成方形PbS纳米晶的光学特性

采用一种简单、温和的液相合成方法制备了PbS纳米晶，利用透射电镜和高分辨透射电镜对PbS纳米晶的形貌与晶型结构进行了表征．研究了PbS纳米晶的光学吸收和光致发光特性，并比较分析了包覆剂聚乙烯吡咯烷酮(PVP)和回流时间对产物光学特性的影响．结果表明：PVP分子链中的O原子与纳米晶表面吸附的游离态Pb原子形成Pb-O配位键，使产物的激子吸收大为减弱，同时引起了表面浅束缚态能量的升高，最终导致了荧光淬灭现象．     

电子显微镜技术表征聚乙二醇包覆的银纳米线的显微结构特征

以缓慢的水热合成法制备聚乙二醇(PEG)包覆的银纳米线,并用电子显微镜对其微观形貌和结构进行了表征。PEG是一种对银表面呈弱亲和性的水溶性聚合物,它在银纳米线合成中既作为Ag+的还原剂,又作为银线的包覆剂。扫描电镜和透射电镜表征显示,这种银纳米线的直径为80～300 nm,长度大于100μm;并且其中一部分银纳米线首尾相接形成了闭合纳米线圈,是首例以化学法制取的金属闭合纳米线圈。闭合环状纳米线的形成进一步支持了金属纳米线的融合生长机制。透射电镜和选区电子衍射以及银纳米线横截面切片的透射电镜表征显示,这种PEG包覆的银纳米线具有轴对称的五重挛晶结构。银纳米线经过长时间的水热孵化而保持其五重挛晶结构,这一点与某些文献报道的情况有所不同,说明银纳米线结构及其演化具有一定的复杂性。     

聚乙烯吡咯烷酮修饰的CdS纳米晶：多元醇合成、表征和可见光活性

采用溶剂热法合成了具有不同晶粒尺寸的聚乙烯吡咯烷酮（PVP）修饰的CdS纳米晶,并运用XRD,N₂物理吸附,TEM,IR,UV-Vis等手段进行表征。结果表明,所制得的样品均为聚乙烯吡咯烷酮(PVP)修饰的CdS纳米晶;添加四甲基氢氧化铵(TMAH)有利于获得晶粒尺寸较小的CdS纳米晶;受纳米晶粒尺寸的影响,CdS纳米晶的吸收边发生蓝移且可见光催化活性明显提高。     

PVP-SDS软模板引导常温水相一锅法合成银纳米棒

以银氨络离子为前躯体, 葡萄糖为还原剂, 在聚乙烯吡咯烷酮(PVP)和十二烷基硫酸钠(SDS)组成的软模板中反应, 首先得到形貌均一、粒径为(50±5) nm的纳米银颗粒, 随后自发生长成银纳米棒. 测试结果表明纳米银颗粒的等离子共振吸收峰在441 nm处, XRD表明其为面心立方体, 在(111)晶面有最强吸收|高分辨透射电镜(HRTEM)观察到的晶格条纹和孪晶面证实其为多重孪晶(MTP), 选区电子衍射(SAED)进一步证实了其具有五重孪晶结构. 由于孪晶结构具有很高的生长活性, 故推断上述孪晶纳米银颗粒经PVP-SDS软模板诱导, 在常温、水相且无需多元醇辅助的条件下, 仅通过受约束Ostwald熟化生长, 便可一锅法合成出各向异性的银纳米棒. 用该法替代高温有机相并加入晶种的多元醇方法, 提高了湿化学方法的实用性并可以显著降低制备一维银纳米材料的成本.     

边长为微米级的银纳米片的简易合成与形成机理

用低温(60 ℃)溶剂热法, 以N,N-二甲基甲酰胺(DMF)为主还原剂和溶剂, 以聚乙烯吡咯烷酮(PVP)为辅助还原剂和晶面生长控制剂, 以硝酸银为前驱物, 大量制备了高纯度的、边长为微米级、宽厚比≥10的单晶银纳米片. 采用粉末X射线衍射(PXRD)、场发射扫描电镜(FE-SEM)、透射电子显微镜(TEM)等表征和分析了合成产物的成分、形貌和结构. 结果表明, 合成的银纳米片为面心立方单晶, 边长为1-4 μm, 厚度为50-100 nm. 考察了不同溶剂对银纳米结构的影响, 并提出了大尺寸的银纳米片的形成机理. 本文为调控单晶银纳米片的边长和宽厚比提供了一种新的可靠的动力学方法, 制备的长边长、大宽厚比的单晶银纳米片在聚合物基导电复合材料和电磁屏蔽材料方面有潜在的重要应用.     

用双还原法制备三角形银纳米片及其光学性能

在硼氢化钠和柠檬酸三钠共存的体系中还原硝酸银, 以聚乙烯吡咯烷酮(PVP)为表面活性剂和保护剂, 水浴加热制备得到三角形银纳米片, 用X射线衍射(XRD)、透射电子显微镜(TEM)、紫外-可见(UV-Vis)吸收光谱、表面增强拉曼散射(SERS)光谱对其进行了表征. 结果表明: 三角形银纳米片产物为立方相金属银, 边长为(100±40) nm, 厚度为(10±5) nm; 产物表现出与球形银纳米粒子完全不同的吸收光谱; 柠檬酸根在银晶核不同晶面的选择吸附、PVP的包覆作用及Ag(111)晶面的层错对产物的形成起决定作用; 与球形纳米颗粒相比, 三角形银纳米片膜对吡啶(Py)分子有显著的SERS活性.     

银元素的循环实验

设计并完成了由5步构成的银元素的循环实验,从银粉出发,经过银在硝酸中溶解,银离子与氯离子反应生成氯化银沉淀,氯化银溶解于氨水,银氨络离子与乙炔反应生成乙炔银,水合肼将乙炔银还原为单质银等化学反应,完成了银的循环实验。     

Idiosyncratic Ag7Pt2O7: An Electron Imprecise yet Diamagnetic Small Band Gap Oxide

The seminal qualitative concepts of chemical bonding, as presented by Walter Kossel and Gilbert Newton Lewis back in 1916, have lasting general validity. These basic rules of chemical valence still serve as a touchstone for validating the plausibility of composition and constitution of a given chemical compound. We report on Ag₇Pt₂O₇, with a composition that violates the basic rules of chemical valence and an exotic crystal structure. The first coordination sphere of platinum is characteristic of tetravalent platinum. Thus, the electron count corresponds to Ag₇Pt₂O₇*e⁻, where excess electrons are associated with the silver substructure. Such conditions given, it is commonly assumed that the excess electrons are either itinerant or localized in Ag−Ag bonds. However, the material does not show metallic conductivity, nor does the structure feature Ag-Ag pairs. Instead, the excess electrons organize themselves in 2e−4c bonds within the silver substructure. This subvalent silver oxide reveals a new general facet pertinent to silver chemistry.     

Influence of Temperature and Time on the Stability of Silver in Silica Sol-Gel Glasses

The darkening of silica sol-gel glasses doped with 0.05 mol% silver was studied. Six sols were prepared from TEOS and silver nitrate. Different additives were used, to influence the chemical and physical states of silver: oxidizing or reducing agents (H₂O₂, As₂O₅), colloid stabilizer (sodium citrate) and network modifiers (Li₂O, CaO). Sols were gelified at 60°C and densified at 600°C. The samples without additives and those prepared with H₂O₂ at room temperature even if they were protected from light. With increased temperature, the darkening became samples were heated above, 400°C, reversible bleaching took place. This darkening-bleaching is of thermal nature (“thermochromic effect”) and seems to be determined by a reversible aggregation-disaggregation of tiny silver particles. The presence of sodium citrate, as an additive delayed the darkening effect and the presence of CaO delayed it even further. Lithium oxide inhibited it totally.     

In-Situ Formation of AgCl Nanocrystallites in Films Prepared by the Sol-Gel and Silver Nanoparticles in Silica Glass Films

We are reporting on a novel preparation of silver chloride in sol-gel silica films as a precursor for nanoparticles of silver. The precipitation of silver chloride particles in-situ was achieved by the reaction of silver nitrate with trichloroacetic acid. The reaction leads to a slow release of chloride leading to a controlled precipitation of AgCl. The existence of an isotropic crystalline AgCl phase in the glass films was demonstrated by X-rays Diffraction Analysis (XRD) and Scanning Electron Microscope and Energy Dispersive Analysis of X-rays (SEM-EDAX). The resulting films are of good optical quality and exhibit a strong coloration upon irradiation with sunlight or heating to 600°C, due to the reduction of AgCl to silver nanoparticles. The absorption spectra of the films before and after irradiation are shown.     

银/聚合物纳米复合材料

银/聚合物纳米复合材料是一种典型的聚合物基复合材料, 其结构和性能依赖于合成方法,因此开发材料的优异性能必须以深入研究纳米材料的先进合成技术为前提。本文综述了纳米银粒子及其与聚合物形成的纳米复合材料的最新合成进展, 重点介绍了基于液相化学还原方法合成纳米银粒子的新方法, 如溶胶-凝胶法、沉淀法、微乳液法和离子液体法, 以及纳米银粒子的分散技术和原位法合成银/聚合物纳米复合材料的新技术, 并介绍了纳米银复合材料的电绝缘性、表面增强拉曼散射性能、抗菌性及其在生物医学等领域中的应用。     

单分散性银纳米粒子的可控制备

以卤化银或氧化银作为前驱体,室温下以水为溶剂,在较高溶液浓度下,利用化学还原法制备了单分散性银纳米粒子,并通过改变前驱体的种类,实现了粒径可控制备。采取扫描电子显微镜（SEM）、紫外-可见光谱仪（UV-Vis）、X射线-粉末衍射仪（XRD）、X射线-光电子能谱仪（XPS）等对所制备的银纳米粒子的形貌及成分进行了表征。结果显示,所制备的银纳米粒子具有较高的单分散性,粒径在40~150 nm之间,具有面心立方多晶结构。该方法制备的银纳米粒子可用于喷墨打印RFID天线。     

Resonance Light Scattering Spectra of Silver Thiocyanate System and its Application in Analysis

A novel determination method of Ag^＋ was established. In acetic acid-sodium acetate buffer （pH 5.0） medium, Ag^＋ reacts with SCN^- to form AgSCN in the presence of TritonX-100,which results in an increase of resonance light scattering （RLS）and giving a new RLS spectrum.The maximum RLS peak was at 585 nm,The enhancement of resonance light scattering at 585 nm was proportional to the concentration of Ag^＋ ranging from 0.0045-4.00μg mL^-1 （r=9991）,and the detection limit was 1.37 ng mL^-1 with the recovery of 97.70%- 104.80%。     

Fabrication of a Simple and Cheap Screen-printed Silver/Silver Chloride (Ag/AgCl) Quasi-reference Electrode

In this work, a silver/silver chloride ink is fabricated using two steps. First the silver ink is prepare using silver, nail polish and acetone. Then the silver ink is painted in a paper substrate and a silver chloride layer is deposited using a bleach solution. The result is the silver/silver chloride conductive ink. The silver ink is cheap ($2.49/g), well-dispersive and very easy to fabricate. The materials were characterized by SEM and XRD. The Ag ink showed the formation of a continuous network throughout the silver ink film with fewer agglomeration. The effective chlorination process was also observed in the Ag/AgCl characterization. Since the Ag/AgCl substrate will be used as a quasi-reference electrode, it is important to investigate the electrical properties. The Ag ink showed an average ohmic resistance of 2.27 Ω. The addition of the AgCl layer decreases the conductivity, as expected. In summary, the Ag/Ag/Cl ink developed is simple, well-dispersed, cheap and with good conductivity. Therefore, it can be used as a conductive ink in the fabrication of quasi-reference electrodes.     

银纳米微球和银纳米棒自组装膜的制备及SERS研究

采用硼氢化钠还原硝酸银,用振荡器在不同转速下振荡得到单分散的银纳米微球和银纳米棒,再将银纳米微球及银纳米棒自组装于被3-氨丙基-三甲氧基硅烷(APTMS)修饰的玻璃基片上,制得了具有表面增强拉曼(SERS)活性的基底,分别以罗丹明6G(R6G)和罗丹明B(RB)为探针分子对这两种基底进行SERS活性检测,结果发现这两种基底均为较理想的SERS衬底。     

A study of the silver form of a natural zeolitic material of the clinoptilolite type

The silver forms of a natural zeolitic material (from the East Slovakian deposit) on the clinoptilolite type has been prepared. The silver forms of the natural zeolitic material were investigated by X-ray powder diffractometry, IR spectroscopy, ESCA measurements, scanning electron microscopy and conductivity measurements. Depending on the preparation conditions, the content of silver ions in the zeolitic products was found to be in the range from 16 to 24%. In the sample with a silver loading of 18.6%, the silver uptake is due to an ion exchange process, mostly involving Na(I), Ca(II) and Mg(II) ions.