MoO3/γ-Al2O3, MoO3/TiO2和MoO3/SiO2的还原性质及表面状态研究

本文以XPS为检测手段研究了浸渍法制备的MoO_3/γ-Al_2O_3、MoO_3/TiO_2和MoO_3/SiO_2三个系列样品的还原性质。用XPS测定还原后与还原前强度比的比值, 实验结果表明阈值后的样品还原后强度比急剧增大, 说明晶相MoO_3从内孔向颗粒外表面大幅度迁移。而单层MoO_3的性质却各不相同, TiO_2上的单层MoO_3还原后部分凝聚, SiO_2上单层则部分迁移, 而γ-Al_2O_3上的单层MoO_3既不迁移也不凝聚, 亦即单层MoO_3的稳定性是Mo(Al)>Mo(Ti)>Mo(Si)。这也是MoO_3与这三个载体表面作用力强弱的顺序。用计算机对Mo3d谱峰解叠, 结果表明, 几乎所有样品还原后都只含有四价和五价钼。Mo(Al)和Mo(Si)体系还原后Mo~Ⅳ的百分数随负载量的增大而增大。我们认为反映了两种载体表面区域的不均匀性。Mo(Ti)体系还原后Mo~Ⅳ百分数在阈值附近出现转折点, 阈值前各点还原性质相同, 说明在应用还原为探测手段时, TiO_2表面表现为均匀的。以Mo~(Ⅳ)百分数衡量时, 三个体系的还原性为Mo(Al)相似文献   

MoO3/γ-AI2O3, MoO3/TiO2, MoO3/SiO2的氨溶性质及表面状态的研究

本文用浸渍法制备了不同含量的MoO_3/γ-Al_2O_3、MoO_3/TiO_2、MoO_3/SiO_2系列样品, 用氨溶、水溶, XPS、XRD等实验手段对这三个体系进行了研究。氨溶实验表明MoO_3在γ-Al_2O_3和TiO_2表面呈单层分散, 其分散阈值(即最大分散量)与XPS强度比法, XRD相定量法所测结果基本一致。这二个体系氨溶曲线在阈值前斜率分别为0.71和0.66, 说明分散在γ-Al_2O_3或TiO_2上的单层MoO_3分为氨水可溶和不可溶二种状态, 这二种状态以确定的比例共存于阀值前的整个浓度区间。这一现象也为氮溶前后样品XPS强度比的比值所证实。实验还表明MoO_3/γ-Al_2O_3样品的氨溶残渣经脱水加热可产生大量可溶的MoO_3, 随着烘烤温度的提高, 时间的延长, 新生成的可溶MoO_3分率趋近样品氨溶前的可溶分率。我们认为分散在γ-Al_2O_3或TiO_2上的单层MoO_3分为二种结构状态, 一种是Mo~(6+)处在氧八面体空隙中, 另一种则处在氧四面体空隙中。二种状态相互邻接, 共用O~(2-)离子, 以特定连结方式(类似于γ-氧化铝Mo_4O_(11)形成“单层聚集小片”。这样的小片是热力学稳定态。由于二种结构状态与载体的相互作用强弱不同而造成了氨水可溶或不可溶二种状态。MoO_3/SiO_2体系, 对氨溶而言, 只有一种状态, 分散在SiO_2上的MoO_3几乎全部溶解。由此可见, MoO_3与SiO_2表面的作用比上述二个体系弱得多。     

MoO3/γ-Al2O3和MoO3/SiO2体系的表面酸性研究

通过样品在溶液中对正丁胺的吸附等温线和吸附指示剂法,测定了一系列MoO_3/γ-Al_2O_3和MoO_3/SiO_2样品的表面酸性。两种方法所得结果相符。表明MoO_3/γ-Al_2O_3和MoO_3/SiO_2都具有数量可观的、较强的表面酸位;酸量取决于MoO_3的表面浓度,酸量的极大值与由XPS和XRD所测得的MoO_3在载体上单层分散的阈值相对应;酸位数与表面 MoO_3分子数之比高达0.5—1。与纯MoO_3的表面酸性相比较,可以说明作品的表面酸性正是酸性氧化物在载体表面单层分散的结果。     

MoO3-SnO2相互作用的研究

用沉淀法、浸渍法和机械混合物焙烧法制备了三组MoO_3-SnO_2催化剂。XDR, IR和ESR等研究表明: MoO_3-SnO_2之间存在明显的相互作用, 两组份间发生电子迁移现象, 导致Mo(Ⅵ)→Mo(Ⅴ)的价态变化, 产生pKa≤+3.3的表面酸位和甲醇选择氧化活性位。制备方法对这种相互作用以及样品的催化性能有明显影响。沉淀法所得样品中MoO_3可溶于SnO_2形成固溶体; 浸渍法则可发生钼离子向SnO_2体相的扩散; 机械混合物焙烧法在一定MoO_3含量下, MoO_3可在SnO_2表面形成近似单层分散。红外光谱中950 cm~(-1)的新吸收谱带可归因于表面上Mo(Ⅴ)=0振动。表面Mo(Ⅴ)位可能是催化剂表面酸位和甲醇氧化的活性中心。没有发现催化剂中Sn~(4+)价态有明显变化。     

MoO3在Ga2O3上的分散研究

采用ＸＲＤ,ＬＲＳ,ＦＴ－ＩＲ,ＵＶ－ＤＲＳ和ＴＰＲ研究了ＭｏＯ３在体载体Ｇａ２Ｏ３上的分散情况。结果表明：ＭｏＯ３的分散状态受Ｇａ２Ｏ３表面结构的影响,ＭｏＯ３在Ｇａ２Ｏ３上的分散容量约为８．４μｍｏｌ／ｍ＾２;低于该分散容量时,Ｍｏ＾６＋主要以高分散态存在于Ｇａ２Ｏ３表面,而高于该分散容量时,除在分散态的Ｍｏ－Ｏ物种外,还有残余的ＭｏＯ３晶相出现。ＴＰＲ结果表明：ＭｏＯ３低于分散容量时,体系中     

MoO3 / Al2O3、MoO3 / TiO2与NiO-MoO3 / TiO2催化剂上活性相还原行为的XPS考察

The H_2 reduction behaviours of MoO_3/Al_2O_3, MoO_3/TiO_2 and NiO-MoO_3/TiO_2 samples prepared by impregnation method were studied at various temperatures for different times by XPS technique. The recored XPS spectra of Mo3d from those samples were treated by computer curve fittingprogram to measure the distribution of various molybdenum oxide species with different valence states. The results of computer fitting shows that there areMo(Ⅵ), Mo(Ⅴ)and Mo(Ⅳ) on the all of reduced samples. However, after H_2 reductonin same way, the percentage of low valence species Mo(V) and Mo(IV) on the MoO_3/TiO_2 is much higher than on the MoO_3/Al_2O3 (Fig.2). For example, after H_2 treatment at 500 ℃ for 2 hrs., Mo(IV) species on the surface of MoO_3/TiO_2 sample is about 60% and it is three times higher than what is found on the MoO_3/Al_2O_3 sample. In addition, the reduction of molybdena on TiO_2 support is much easier and faster than on Al_2O_3 support (Fig.3). Addition of NiO further promotes the reduction of molybdena to cause the strting reduction temperature producing Mo(IV) and Mo(V) to be decreased about 100 ℃. and 80% of molyb dena on NiO-MoO_3/TiO_2 support could be reduced to Mo(IV) (Fig.2). A detail discussion about the interaction between molybdena and carries was presented. It was suggested that TiO_2 is certainly involved in the reduction and oxidation process of molybdenum oxide species on the surface of it.     

Thermal stability of In2(MoO4)3 and phase equilibria in the MoO3–In2O3 system

Thermal stability of a compound forming in a binary system MoO₃?CIn₂O₃ was investigated by DTA/TG, XRD and SEM methods in this study. For the first time, the diagram of phase equilibria established in the whole range of concentrations of this system's components has been constructed. The temperature and concentration ranges of the components of MoO₃?CIn₂O₃ system in which the compound In₂(MoO₄)₃ co-exists in solid state with MoO₃ or In₂O₃ or with the liquid were determined. The composition and melting point of the eutectic mixture consisting of In₂(MoO₄)₃ and MoO₃ were found.     

MoO3在Al2O3薄膜表面扩散的研究

氧化物和盐类在高比表面载体上的单层分散现象已被大量实验所证实［１］．ＭｏＯ_３在γ－Ａｌ_２Ｏ_３等高比表面载体上的分散已经研究很多,近来的研究证实ＭｏＯ３等在α－Ａｌ２Ｏ３等小比表面载体上也能自发单层分散［２］,但是分散的过程仍然缺乏直接的观察研究．本工作通过多种表面分析方法首次研究了ＭｏＯ３在平整无定形的Ａｌ２Ｏ３薄膜上的扩散过程以及影响因素．发现除温度升高外、水汽的存在对该扩散过程也有促进作用．１实验部分１．１样品的制备采用ＳＳ－３２００真空磁控溅射镀膜机,通入Ａｒ－Ｏ２作为反应气,直流磁控…     

MoO3/g-Al2O3催化剂单分子层选择性的表征

采用TPR,氧吸附,UV-VIS光谱,XRD和XPS技术研究了MoO_3/γ-Al_2O_3催化剂的单分子层特性。当MoO_3含量低于16wt%时,MoO_3处于高分散状态。低温氧吸附和XPS相对强度比表明:MoO_3在γ-Al_2O_3担体上的饱和单分子层容量分别为5.2和5.5μmol/m~2(BET)。超过单分子层饱和容量,则首先形成Al_2(MoO_4)_3晶粒。随着MoO_3含量增加,孔大小分布也受到很大的影响。由于Mo离子的聚结,当MoO_3含量增高时,小孔对总孔体积的贡献明显地减少。     

Sm对MoO3-Bi2O3催化剂性能的影响

在MoO3-B i2O3催化剂中加入稀土氧化物Sm2O3,在固定床反应器中考查了Sm2O3添加量、反应温度、异丁烯浓度、原料气流量等对异丁烯转化为甲基丙烯醛反应的影响。实验表明,添加Sm2O3可明显提高异丁烯的转化率和甲基丙烯醛的选择性。用XRD技术研究了催化剂的组成,Mo-B i-O催化剂的成分主要是B i2O3和MoO3的混合物,添加Sm后出现了Sm2Mo3O12的衍射峰,且衍射峰的强度随着Sm添加量的增加而增强。     

甲醇选择氧化MoO3—TiO2催化剂的研究

用XRD、LRS、ESR、XPS等方法对机械混合物焙烧法制备的两组MoO_3—TiO_2催化剂进行了表征,同时考察了催化剂的甲醇选择氧化活性和选择性。结果表明:MoO_3与TiO_2机械混合物在450℃焙烧过程中发生TiO_2中锐钛矿转变成金红石的相变,但若将TiO_2在空气中550℃预处理8h后再与MoO_3混合焙烧则未观察到相变的发生。在上述两组催化剂中都发生了MoO_3在TiO_2表面的分散。当MoO_3含量小于10wt％时,MoO_3晶相消失,钼以表面钼氧物种存在。MoO_3与TiO_2之间的强相互作用导致Mo(Ⅴ)的生成和pKa≤+3.3的表面酸位的产生。TiO_2晶型对催化剂表面结构及反应活性有明显影响,锐钛矿转变为金红石使最佳反应温度提高20～40℃,Mo在表面富集程度增大,而Mo(Ⅴ)和表面酸位浓度下降。表面Mo(Ⅴ)和高分散于表面的八面体配位钼氧物种可能是甲醇氧化的活性位。     

MoO3/TiO2-Al2O3催化剂表面结构的LRS研究

负载型Mo和Co-Mo催化剂由于工业上的广泛应用,多年来一直是催化工作者的重要研究课题.工业上应用的Mo和Co-Mo催化剂多以活性Al_2O_3和SiO_2-Al_2O_3为载体,近年来也有用TiO_2,ZrO_2和活性碳作为催化剂载体的研究报导.有关催化剂活性组分与载体之间相互作用对催化剂表面相结构和催化性能的影响方面研究已引起人们的重视。我们多年来在金属-载体相互作用研究基础上,以石油加氢精制催化剂为应用背景,开     

TiO2调变对MoO3／γ—Al2O3和CoO—MoO3／γ—Al2O3催化性能的影响

采用气相流动吸附法制备ＴｉＯ２／γ－Ａｌ２Ｏ３复合载体，用浸渍法其担载一定量的ＭｏＯ３或ＣｏＯ－ＭｏＯ３。用ＸＲＤ、ＬＲＳ和ＴＰＲ等技术，考察了Ｍｏ或Ｃｏ－Ｍｏ催化剂的表面结构和还原性能，并有和中压固定床反应装置测定催化剂的噻吩加氢脱硫和环己烯加氢的活性。     

添加第二组分金属氧化物对MoO3／Al2O3上MoO3还原行为影响的XPS研究

应用XPS技术,对添加了3wt％第二组分金属氧化物M_xO_y(ZnO,La_2O_3,SnO_2,V_2O_5与Re_2O_7)的MoO_3/γ-Al_2O_3催化剂(MoO_3的浓度为12wt％)的氢还原行为进行了考察,样品的氢还原在电子能谱仪的样品预处理室进行,然后不暴露于大气直接进入能谱分析腔进行XPS测定。同时对第二组分金属氧化物的金属氧化价态也作了相应的XPS测定。结果表明,第二组分的引入,可显著地影响MoO_3/γ-Al_2O_3上MoO_3之氢还原行为,而且不同第二组分与MoO_3及担体的相互作用也有明显差别。     

固体超强酸催化剂SO4^2——MoO3—ZrO2中MoO3的作用与催化性能

根据固体超强酸催化剂ＳＯ４＾２－ＭｏＯ３－ＺｒＯ２的特点,结合活性评价结果,用ＢＥＴ、ＤＴＡ／ＴＧ、ＸＲＤ、ＬＲＳ等方法,对其进行了物性表征,考察了催化剂的结构形态、性质随催化剂组成的变化,以及催化剂的物性结构特点与催化活性的关系。研究结果表明,ＭｏＯ３含量对催化剂活性有着显著影响;催化剂的比表面积随ＭｏＯ３的含量变化存在极大值;ＭｏＯ３具有延迟ＺｒＯ２晶化、稳定ＳＯ４＾２－的作用,并提高了ＳＯ４     

MoO3/TiO2-Al2O3对H2S吸附的XPS研究

应用ＸＰＳ对ＭｏＯ３／ＴｉＯ２－Ａｌ２Ｏ３体系的ＭｏＯ３在ＴｉＯ２－Ａｌ２Ｏ３载体上的存在状态及其对Ｈ２Ｓ的吸附和脱附性能进行了表征，结果表明：ＭｏＯ３在ＴｉＯ２－Ａｌ２Ｏ３表面存在分散状态的不同，这导致了对Ｈ２Ｓ吸附性能的不同，在相同的条件下，吸附剂的０．１５ｇＭｏＯ３／ｇＴｉＯ２－Ａｌ２Ｏ３时具有最大载硫量，且随吸附温度的升高载硫量也增加，达饱和对Ｓ／Ｍｏ原子比接近１，较好的氧化脱附温度为１５