Influence of pH values in the preparation of CuO-CeO2 on its catalytic performance for the preferential oxidation of CO in excess hydrogen

CuO-CeO2 catalyst prepared with co-precipitation showed high catalytic performance for the preferential oxidation of CO in excess hydrogen (PROX). Influence of pH values in the preparation of CuO-CeO2 on its catalytic performance was investigated in this work. The CuO-CeO2 catalyst prepared at pH = 13.03 had the smallest particle size (5.4 nm), the largest surface areas (138 m2/g) and the highest activity with CO conversion of 99.6% at 130 ℃. The CuO-CeO2 catalyst was characterized using BET, XRD and TPR techniques. The results showed that when the pH value of the mixed solution containing Cu and Ce species was properly adjusted, both the adsorption layers and diffusion layers of the formed colloidal particles in hydroxide precursor of CuO-CeO2 were modified, resulting in the better catalytic performance for PROX on the final CuO-CeO2 catalyst.     

Kinetics of hydrogen production of methanol reformation using Cu/ZnO/Al2O3 catalyst

The catalytic performance of methanol reformation using Cu/ZnO/Al2O3 was investigated at low temperature. The operation conditions, such as composition of Cu, Zn, and Al, temperature, molar ratio of H2O/CH3OH, weight hourly space velocity, catalyst weight, and kind and flow rate of carrier gas (helium and air), were evaluated to obtain the optimum reaction condition. The catalysts were prepared by oxalic coprecipitation, coprecipitation, and polyol method. The weight composition of Cu, Zn, and Al prepared by oxalic coprecipitation was 15:15:5 by high-throughput screening of combinatorial chemistry method, which was the best Cu/ZnO/Al2O3 catalyst. The prepared catalysts showed high activity and selectivity towards hydrogen formation. The methanol conversion, production rate, and volumetric percentage of hydrogen using this best catalyst were larger than 95%, 0.65 mol/h x g and 59%, respectively, and the CO volumetric percentage was smaller than 0.22% when the reaction temperature was 240 degrees C. The size and dispersity of copper, and the activity and turnover frequency of the catalyst were calculated as well.     

Influence of preparation methods on CuO-CeO2 catalysts in the preferential oxidation of CO in excess hydrogen

Influence of three different preparation methods, i.e. impregnation, coprecipitation, and inverse coprecipitation, on the preferential oxidation of CO in excess hydrogen （PROX） over CuO-CeO2 catalysts has been investigated and CuO-CeO2 catalysts are characterized using BET, XPS, XRD, UV Raman, and TPR techniques. The results show that the catalysts prepared by coprecipitation have smaller particle sizes, well-dispersed CuOx species, more oxygen vacancies, and are more active in the PROX than those prepared by the other methods. However. the inverse coprecipitation depresses the catalytic performance of CuO-CeO2 catalysts and causes the growth of CuO-CeO2 because of different pH value in the precipitation process.     

不同助剂掺杂的铬基催化剂的制备及其对乙烷氧化脱氢的催化性能

以硝酸盐作为前驱体,Al₂O₃为载体,采用等体积浸渍法制备了系列不同助剂（Mn, Co, Ce）及不同助剂含量（1%, 3%, 5%, 7%, 10%）掺杂的铬基催化剂,其结构经X-射线粉末衍射(XRD)、 H₂程序升温还原(H₂-TPR)和CO₂程序升温脱附（CO₂-TPD）表征。并考察了催化剂对乙烷氧化脱氢反应的催化性能。结果表明：添加Co助剂有利于活性组分铬的分散,10Cr₃Co/γ-Al₂O₃催化剂表现出最佳催化性能,在反应温度为650 ℃, V(CO₂) ：V(C₂H₆)=3 ：1,空速(GHSV)为3 600 mL·（g·h）^-1条件下,在该催化剂上乙烯产率为36.5%。     

焙烧及还原温度对 Co-Pt-ZrO2/γ-Al2O3催化剂费托合成反应性能的影响

采用浸渍法制备了Co-Pt-ZrO₂/γ-Al₂O₃催化剂,对其进行了BET、XRD和TPR等表征,并在浆态床反应器上考察了焙烧温度和还原温度对催化剂费托合成反应性能的影响。结果表明,焙烧温度过高,容易造成Co物种和载体间的相互作用增强,使部分氧化钴颗粒聚集或烧结,导致催化剂的F-T合成反应活性和C₅₊烃选择性降低。还原温度较低时,钴物种不能充分还原,CO加氢活性低,甲烷选择性高,重质烃选择性低;还原温度过高,则可能造成活性物种的烧结,反而降低了催化剂的活性和重质烃选择性。在原料气n(H₂)/n(CO)=2.0、483 K、2.4 MPa和空速3.6 L/(gcat·h)的条件下,31.08%Co～0.11%Pt～7.16%ZrO₂/Al₂O₃催化剂在673 K焙烧。纯H₂下653 K还原后,其费托性能最佳;CO转化率为27.0%,C₅₊的选择性为83.0%。     

Influence of rare-earth metal doping on the catalytic performance of CuO-CeO2 for the preferential oxidation of CO in excess hydrogen

Doping of different rare-earth metals （Pr, Nd, Y and La） had an evident influence on the catalytic performance of CuO-CeO2 for the preferential oxidation （PROX） of CO in excess hydrogen. As for Pr, the doping enhanced the catalytic activity of CuO-CeO2 for PROX. For example, the CO conversion over the above catalyst for PROX was higher than 99% at 120 °C. Especially, the doping of Pr widened the temperature window by 20 °C over CuO-CeO2 with 99% CO conversion. For Nd, Y, and La, the doping depressed the catalytic activity of CuO-CeO2 for PROX. However, the doping of transition metals markedly improved the selectivity of CuO-CeO2 for PROX.     

NiO/LaMnO3催化剂用于乙醇水蒸气重整反应

采用柠檬酸络合-浸渍法制备了NiO/LaMnO3钙钛矿型复合氧化物催化剂并将其应用于乙醇水蒸汽重整制氢反应, 考察了NiO含量、焙烧温度对催化剂性能的影响, 采用XRD、TPR和热分析等手段对催化剂进行了表征. 结果表明, 该催化剂具有高活性、高选择性和良好的稳定性. 催化剂中的NiO含量和焙烧温度对催化性能有显著影响. 在原料气体积组成为20%(体积分数, φ) C2H5OH 和水以及80%(φ)N2, 其中水醇摩尔比为3:1, 空速为80000 mL·h-1·g-1 cat, 反应温度为400 ℃时, 15%(质量分数, w)的NiO/LaMnO3上, 乙醇转化率接近100%. 关联催化剂活性和TPR及XRD实验结果, 发现催化剂的高活性源于由催化剂前驱体中进入钙钛矿型复合氧化物晶格中的镍离子被还原所得的金属镍.     

铜基催化剂用于一氧化碳催化消除研究进展

催化消除CO主要包括CO的完全氧化(CO-COOX)和优先氧化(CO-PROX).首先,结合本课题组的相关研究,按照催化剂体系介绍了Cu基催化剂在CO-COOX中的活性物种和组分之间的相互作用.其次,对用于富氢气氛下CO-PROX的Cu基催化剂进行了系统的分类总结,重点阐述了CuO-CeO2催化剂的制备方法、助剂改性、载体调变以及过渡金属离子掺杂(CuO/Ce1-xMxO2)、反相结构(CeO2/CuO)等方面对CO-PROX催化性能的影响.最后,总结了Cu基催化剂在CO-PROX中存在的问题,并展望了未来的研究趋势.     

制备方法对Ni/MgO/Al2O3催化剂在甲烷与二氧化碳重整反应活性的影响

采用浸渍－还原法制备的Ｎｉ／ＭｇＯ／Ａｌ２Ｏ３在ＣＨ４与ＣＯ２重整制合成气反应中显示出良好的催化性能和一定的抗积炭能力;在１０２３Ｋ下流动反应气氛中连续运转１００ｈ,未见活性下降,ＣＨ４及Ｃ弦均为９０％左右,ＣＯ收率高于９０％,实验还发现,ＣＨ４转化率随着原料气中ＣＯ２浓度的增加而升高,当Ｖ（ＣＯ２）／Ｖ（ＣＨ４）＝２时ＣＨ４转化率可达１００％,通过ＢＥＴ比表面积测定及ＸＲＤ,ＴＥＭ等分析手段,比     

Low-temperature CO oxidation over CuO-CeO2/SiO2 catalysts：Effect of CeO2 content and carrier porosity

The effects of CeO2 contents and silica carder porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 catalysts in CO oxidation were investigated. The catalysts were characterized by N2 adsorption/desorption at low temperature, X-ray diffraction (XRD), temperature-programmed reduction by H2 (H2-TPR), oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS). The results suggested that, the ceria content and the porosity of SiO2 carder possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts. When appropriate content of CeO2(Ce content ≤8 wt%) was added, the catalytic activity was greatly enhanced. In the catalyst supported on silica carrier with larger pore diameter, higher dispersion of CuO was observed, better agglomeration-resistant capacity was displayed and more lattice oxygen could be found, thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation.     

焙烧温度对柴油车氧化催化剂Pt-Pd-（x）ZrO2/Ce0.3Zr0.7O2-Al2O3性能的影响

制备了氧化铝、铈锆固溶体复合氧化物负载铂、钯的双金属催化剂Pt-Pd/ Ce0.3Zr0.7O2-Al2O3,并添加3% ZrO2助剂改性,用于柴油车尾气中CO、HC和NO的催化氧化,其中贵金属负载量仅为0.68 wt%。考察了制备过程中焙烧温度对催化剂性能的影响。催化剂活性评价结果表明,与未添加ZrO2的催化剂比较。添加ZrO2明显提高了催化剂的低温氧化活性,而且焙烧温度对催化剂的氧化性能有较大影响。焙烧温度为800 ?C时,CO和C3H6的起燃温度最低,分别为168、189 ?C,焙烧温度为700 ?C时,NO转化为NO2的转化率最高,最大转化率为36%,具有较好的热稳定性。通过XRD、N2吸附-脱附、CO化学吸附、XPS、H2-TPR等表征手段考察了催化剂物理化学性质随焙烧温度的变化情况,并分析了与催化剂活性之间的关系,得到贵金属分散度、表面化学吸附氧含量、催化剂的还原性质对氧化性能有重要影响,发挥协同作用。进而可以通过优化焙烧温度提升柴油车氧化催化剂性能,对提高工业应用柴油车尾气后处理系统的净化效率有重要意义。     

Influence of reduction energy match among CuO species in CuO-CeO2 catalysts on the catalytic performance for CO preferential oxidation in excess hydrogen

In the present study, we have investigated the reducibility of CuO species on CuO-CeO2 catalysts and the influence of CuO species on the catalytic performance for CO preferential oxidation (CO PROX) in excess hydrogen. It is revealed that the smaller the difference of reduction temperature (denoted as ?T) for two adjacent CuO species is, the higher the catalytic activity of CuO-CeO2 for the PROX in excess hydrogen may be obtained. It means that if the reduction energy of Cu0-Cu2+ pairs matched better, the reduction-oxidation recycle of Cu0-Cu2+ pairs would go on more easily, then the transferring energy of Cu0-Cu2+ pairs would be lesser. Therefore, the CuO-CeO2 catalysts will be largely improved in their catalytic performance if the different CuO species on the catalysts have matched the reduction energy, which would allows them to cooperate effectively.     

Low-temperature CO oxidation over CuO-CeO_2/SiO_2 catalysts:Effect of CeO_2 content and carrier porosity

The effects of CeO2 contents and silica carrier porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 cata-lysts in CO oxidation were investigated.The catalysts were characterized by N2 adsorption/desorption at low temperature,X-ray diffraction (XRD),temperature-programmed reduction by H2 (H2-TPR),oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS).The results suggested that,the ceria content and the porosity of SiO2 carrier possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts.When appropriate content of CeO2 (Ce content 8 wt%) was added,the catalytic activity was greatly enhanced.In the catalyst supported on silica carrier with larger pore diameter,higher dispersion of CuO was observed,better agglomeration-resistant capacity was displayed and more lattice oxygen could be found,thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation.     

草酸钠改性共沉淀制备高效Cu/ZrO2催化剂及其 在甲醇部分氧化制氢反应中的应用

采用四种不同沉淀剂并流共沉淀制备系列Cu/ZrO2催化剂, 结果表明经过Na2C2O4和NaOH改性沉淀的催化剂在甲醇部分氧化制氢反应中表现出比NaOH, Na2CO3和Na2C2O4-Na2CO3沉淀的催化剂更优越的催化性能, 在533 K可获得92%的氢气产率而CO含量低于1.5%, 并且在110 h寿命测试中保持良好的稳定性. 采用X射线粉末衍射, N2低温吸附, H2-TPR, N2O滴定和X射线光电子能谱对其进行系统表征, 阐述了该改性共沉淀法所得催化剂高性能的本质原因.     

Ni/ZrO2催化剂上甲烷水蒸气重整反应的研究

研究了Ni/ZrO2催化剂对甲烷水蒸气重整制合成气的反应性能。考察了催化剂的还原温度、载体焙烧温度以及反应温度、原料配比和空速等对催化剂性能的影响。利用XRD、TEM、XPS等手段对催化剂的织构形貌进行了表征。研究表明，Ni/ZrO2催化剂用于甲烷水蒸气重整制合成气不仅具有较高的活性，也具有较好的稳定性。水蒸气比增加，CH4转化率增大、CO选择性下降。CH4转化率及CO选择性均随空速增大而下降。使用10%Ni/ZrO2催化剂，在650 ℃、空速1.984×104 h－1、原料气配比H2O∶CH4∶N2=2∶1∶2.67的条件下，获得CH4转化率85%、CO选择性70%的结果。     

Mn_xCo_(3-x)O_4复合氧化物及改性催化剂催化分解N_2O

用共沉淀法制备了一组不同组成的MnxCo3-xO4尖晶石型复合氧化物,表面负载碱金属助剂制备改性催化剂,用于催化分解N2O.用X射线衍射(XRD)、N2物理吸附(BET)、红外光谱(FTIR)、扫描电镜(SEM)、H2程序升温还原(H2-TPR)、X射线光电子能谱(XPS)等技术表征催化剂结构.考察了复合氧化物组成、碱金属助剂类型、钾前驱物等制备参数对催化剂结构和催化活性的影响.结果表明:添加助剂K、Cs降低了催化剂表面Co、Mn元素的电子结合能,弱化了Co—O和Mn—O键,有利于氧物种的脱除,提高了催化剂活性.优化出了活性较高的催化剂K/Mn0.4Co2.6O4(K2CO3),有氧无水、有氧有水气氛400℃连续反应50 h,N2O转化率分别保持100%和74.2%,催化剂稳定性较高.     

尿素燃烧法制备CuO-ZnO/HZSM-5及其催化CO_2加氢合成二甲醚的性能

以尿素为燃烧剂,先采用燃烧法制备CuO-ZnO催化剂,接着采用研磨法将其与HZSM-5分子筛均匀混合形成CuO-ZnO/HZSM-5双功能催化剂.采用固定床反应器,在反应温度260℃、压力3.0 MPa、空速1 500 h-1条件下,考察了不同Cu/Zn(摩尔比)催化剂在CO_2加氢合成二甲醚反应中的催化性能.通过XRD、N_2等温吸附脱附、H2-TPR、NH3-TPD对催化剂进行表征,研究了不同Cu/Zn对催化剂结构及表面酸性的影响.结果表明:当Cu∶Z n=6∶4时,催化剂对CO_2催化加氢直接合成二甲醚反应的催化活性和选择性最佳,CO_2的转化率、DME的选择性分别为11.95%和28.74%,且在催化剂上具有更多的低温还原Cu和较强的酸中心,从而提高了CO_2加氢活性和二甲醚的选择性.     

La2O3/MgO催化剂上的甲烷氧化偶联

研究了甲烷在La_2O_3/MgO催化剂上的氧化偶联。发现制备过等对催化剂的行为有显著影响。比较了催化剂的反应性能和体相结构,表明在MgO上存在着三种La_2O_3的状态:高分散La_2O_3是最活泼的;La(OH)_3不太活泼;而呈六方晶相的La_2O_3晶粒活性最低。在催化剂中加入Na_2CO_3和K_2CO_3可以改进催化剂的活性和选择性。还考察了反应条件如温度和空速的影响。     

Microcalorimetric Adsorption of Alumina Oxide Catalysts for Combination of Ethylbenzene dehydrogenation and carbon Dioxide Shift-reaction

Styrene (STY) is now produced industrially in fairly large quantities by the dehydrogenation of ethylbenzene (EB) using promoted iron oxide catalyst with superheated steam.In this case, small amount of carbon dioxide formed as a by-product was known to inhibit the catalytic activity of commercial catalyst. Recently, there have been some reports which carbon dioxide showed positive effects to promote catalytic activities on the reaction over several catalysts.In this study, we attempted to combine the dehydrogenation of EB to STY with the carbon dioxide shift-reaction. The combine reaction (EB + CO2 → STY + H2O + CO) can be considered as one of the ways of using CO2 resources and can yield simultaneously STY and Carbon oxide.Alumina oxide catalysts such as Al2O3, Na2O/Al2O3 and K2O/Al2O3 were prepared by the usual impregnation method with an aqueous solution of NaNO3 and KNO3, and then calcined at 650℃ for 5 h in a stream of air. The reaction condition is 600℃, flow of CO2 38ml/mon and space velocity (EB) 1.28h-1.     

钙钛矿型稀土复合氧化物催化剂上一氧化碳的选择氧化

考察了在钙钛矿型稀土复合氧化物催化剂上，氢气中一氧化碳选择氧化的催化性能，发现该催化剂具有优良的催化活性和选择性。LaMnO3中的锰被铜部分取代后可以提高其催化活性，当其中的镧再被锶或钡部分取代后所得的催化剂的催化活性进一步提高。其中以La0.8Sr0.2Mn0.5Cu0.5O3的催化活性为最佳，在该催化剂上，在40 000 mL·g－1·h－1下，155 ℃时CO可被完全转化为CO2，此时的选择性达54%，与铂催化剂的性能相近。反应气中加入CO2时，CO转化率下降，但选择性有所提高；加入水蒸气则使CO的转化率和反应选择性均下降。