Sr2Si5N8∶Eu2+荧光粉的制备与发光性能

以α-Si₃N₄,SrCO₃,Eu₂O₃为原料,采用碳热还原氮化法制备了Sr₂Si₅N₈∶Eu²⁺荧光粉。研究了材料的结构与光谱特性,分析了影响材料发光性能的工艺因素。结果表明,石墨粉含量和助熔剂的用量对Sr₂Si₅N₈相的形成和发光性能有重要影响。当n_C/n_Sr=1.5,助熔剂用量为4wt%时,合成样品的主晶相为正交晶系Sr₂Si₅N₈,在400~550 nm可见光激发下,可发射峰值波长位于609 nm荧光。激发带的位置与Eu²⁺离子浓度无关,为400~550 nm之间的宽带激发;但发射强度随Eu²⁺离子浓度的增加而增加,Eu²⁺离子浓度达到5mol%时发射强度达最大值,在Eu²⁺离子浓度为2mol%~5mol%之间,观察到发射峰的红移现象。     

Eu3+离子在Ca2PbO4一维结构基质中的发光研究

A Eu³⁺-doped Ca₂PbO₄ with one-dimensional structure was prepared with a solid-state reaction method and its characteristics were investigated. The XRD results show that the substitution of Ca²⁺ by Eu³⁺ has no influence on the structure of Ca₂PbO₄. Under the excitation of ultraviolet light， the Ca₂PbO₄:Eu³⁺ phosphor exhibits strong red emission at about 618 nm which is assigned to the ⁵D₀- ⁷F₂ electric-dipole transition. The compounds Sr₂CeO₄ and Ca₂SnO₄ have the same crystal symmetry as that of Ca₂PbO₄ and it is found that the emission intensity of Ca₂PbO₄∶Eu³⁺ is higher than that of Sr₂CeO₄∶Eu³⁺ and lower than that of Ca₂SnO₄∶Eu³⁺. The excitation spectrum of Ca₂PbO₄∶Eu³⁺ appears to be a broad band with two peaks at about 289 nm and 340 nm. The former peak is attributed to the Eu³⁺-O₂- charge transfer transition， while the latter one may be related to the absorption of Ca₂PbO₄ host or its crystal defects.     

SrAl2O4：Eu2+，Dy3+的助熔剂法制备及其发光特性

以B₂O₃为助熔剂，在1 350 ℃、还原性气氛下成功制备了SrAl₂O₄单相粉末样品。用同样的方法制备了系列单相Sr_1-x-yAl₂O₄：Eu²⁺_x，Dy³⁺_y·nB₂O₃(0.005≤x≤0.07， 0.01≤y≤0.05，0.05≤n≤0.25)样品并表征了其长余辉发光特性。结果表明，最佳的Eu²⁺含量为0.02。辅助激活离子Dy³⁺在Sr_0.98Al₂O₄：Eu²⁺_0.02中的掺杂在一定范围内可以显著提高亮度和余辉时间，最佳Dy³⁺含量为0.03。研究不同B₂O₃含量对Sr_0.95Al₂O₄：Eu²⁺_0.02，Dy³⁺_0.03发光性能的影响，结果说明最佳的B₂O₃含量为n=0.1，余辉肉眼可见(≥0.32 mcd·m^-2)时间达4 000 min。利用正电子湮灭技术和热释光技术，研究和讨论了B₂O₃对Sr_0.95Al₂O₄：Eu²⁺_0.02，Dy³⁺_0.03的发光和余辉性能的影响，结果表明B₂O₃的添加有助于Dy³⁺在晶格中形成深度合适、有益于余辉的空位缺陷。     

Sr7Zr(PO4)6∶xEu2+蓝色荧光粉的合成及其发光特性

通过高温固相反应合成了新型的蓝色荧光粉Sr₇Zr(PO₄)₆∶xEu²⁺。通过X射线粉末衍射(XRD)、紫外可见(UV-Vis)吸收光谱、荧光光谱研究了Sr₇Zr(PO₄)₆∶xEu²⁺材料的相纯度及荧光性质。结果表明,Eu²⁺掺杂获得的Sr₇Zr(PO₄)₆∶xEu²⁺荧光粉为纯相,且200~400 nm范围内的近紫外(NUV)光均能对其进行有效的激发。在315 nm的激发下,Sr₇Zr(PO₄)₆∶xEu²⁺荧光粉发射出峰值位于415 nm左右的蓝光,且Eu²⁺在Sr₇Zr (PO₄)₆基质中的最佳掺杂浓度为0.05,相应的CIE色度坐标为(0.164,0.021),比商用BaMgAl₁₀O₁₇∶Eu²⁺(BAM)蓝色荧光粉具有更高的色纯度。     

红色发光长余辉材料Ca2SnO4∶Eu3+的性能研究

利用高温固相法合成了Ca₂SnO₄∶Eu³⁺红色发射长余辉发光材料,对样品进行了X射线衍射分析、荧光光谱分析、形貌分析以及发光寿命测量。分析结果表明,在1 350 ℃下烧结3 h的Ca₂SnO₄∶Eu³⁺为单相产物,所得Ca₂SnO₄∶Eu³⁺发光材料具有良好的发光性能,在267 nm紫外线激发下发出最强发射位于617 nm的锐线发射,并且具有明显的长余辉发光性能。     

空气中合成固溶体荧光粉Ba2(Zn, Mg)Si2O7:Ce3+,Eu2+,Eu3+及其发光特性

采用高温固相法在空气中合成了Ba_1.97-yZn_1-xMg_xSi₂O₇:0.03Eu,yCe³⁺系列荧光粉。分别采用X-射线衍射和荧光光谱对所合成荧光粉的物相和发光性质进行了表征。在紫外光330~360 nm激发下,固溶体荧光粉Ba_1.97-yZn_1-xMg_xSi₂O₇:0.03Eu的发射光谱在350~725 nm范围内呈现多谱峰发射,360和500 nm处有强的宽带发射属于Eu²⁺离子的4f⁶5d¹-4f⁷跃迁,590~725 nm红光区窄带谱源于Eu³⁺的⁵D₀-⁷F_J (J=1,2,3,4)跃迁,这表明,在空气气氛中,部分Eu³⁺在Ba_1.97-yZn_1-xMg_xSi₂O₇基质中被还原成了Eu²⁺;当x=0.1时,荧光粉Ba_1.97Zn_0.9Mg_0.1Si₂O₇:0.03Eu的绿色发光最强,表明Eu³⁺被还原成Eu²⁺离子的程度最大。当共掺入Ce³⁺离子后,形成Ba_1.97-yZn_0.9Mg_0.1Si₂O₇:0.03Eu,yCe³⁺荧光粉体系,其发光随着Ce³⁺离子浓度的增大由蓝绿区经白光区到达橙红区;发现名义组成为Ba_1.96Zn_0.9Mg_0.1Si₂O₇:0.01Ce³⁺,0.03Eu的荧光粉的色坐标为(0.323,0.311),接近理想白光,是一种有潜在应用价值的白光荧光粉。讨论了稀土离子在Ba₂Zn_0.9Mg_0.1Si₂O₇基质中的能量传递与发光机理。     

CaSb2O6:Bi3+,Eu3+荧光粉的制备和发光性质

采用共沉淀法及1 200 ℃后续煅烧4 h,成功制备了CaSb₂O₆:Bi³⁺,Eu³⁺荧光粉,并对其结构及发光性能进行了研究。所制备荧光粉颗粒为六边形类圆饼状,平均尺寸在100~600 nm之间。对CaSb₂O₆:Bi³⁺,Eu³⁺发光的机理分析表明,Bi³⁺对Eu³⁺的发光存在高效的敏化与能量传递。当Bi³⁺和Eu³⁺的掺杂浓度分别为0.5%和8%,Eu³⁺位于580 nm(⁵D₀→⁷F₀ )处的荧光发射显著增强,Bi³⁺,Eu³⁺共掺样品的荧光强度是CaSb₂O₆:Eu³⁺的10倍左右。调节Bi³⁺/Eu³⁺离子掺杂比,色坐标呈现了从蓝、白光到红光的变化,表明该荧光粉可分别作为蓝或红色荧光粉使用,甚至可实现从蓝、白光到红光的自由调控,这为白光LED荧光粉的发展提供了参考。     

SrAl2O4∶Eu2+，Dy3+纳米长余辉发光材料的制备与表征

采用溶胶-凝胶法制备了SrAl₂O₄∶Eu²⁺，Dy³⁺ 纳米长余辉发光材料，研究了pH值、反应温度和络合剂等对溶胶-凝胶形成的影响，研究了灼烧温度对SrAl₂O₄∶Eu²⁺，Dy³⁺ 晶相、颗粒尺度和发光性能的影响。利用XRD, SEM，光谱分析等手段对产物进行了结构和性能分析。实验结果表明，在800 ℃时SrAl₂O₄晶相开始形成但没有发光，而在1 100 ℃烧结的样品则具有很好的发光性能。样品平均晶粒尺寸随灼烧温度升高而增加，平均晶粒尺寸为20～40 nm。样品的激发光谱是峰值在240，330，378和425 nm的连续宽带谱，发光光谱是峰值在523nm的宽带谱，与SrAl₂O₄∶Eu²⁺，Dy³⁺ 粗晶材料相比，发光光谱发生了“红移”现象。样品的热释光峰值位于157 ℃，与SrAl₂O₄∶Eu²⁺，Dy³⁺ 粗晶材料相比，峰值向低温移动了13℃。     

Sr3Al2O6∶Eu2+红色发光纳米晶的新型形貌与发光性能的研究

A red luminescent Sr₃Al₂O₆∶Eu²⁺ nanocrystallites with new morphology were synthesized by sol-gel route assisted by microwave irradiation. The phosphor powders were characterized by X-ray diffraction (XRD)， scanning electron microscopy (SEM) and fluorescence spectroscopy. The results reveal that the calcination temperature of the Sr₃Al₂O₆∶Eu²⁺ phosphor crystallites greatly affects its morphology. With temperature increasing， the phosphor crystallites morphology showed primarily from nanorod-like， mixture of nanorod and flower-like to homogeneous flower-like morphology. The effects of new morphology on luminescent properties of phosphors were investigated. Uniformly dispersed flower-like Sr₃Al₂O₆∶Eu²⁺ phosphor powders showed the strongest luminescent intensity and the longest afterglow time.     

La7O6(BO3)(PO4)2:Eu3+/Tb3+荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La₇O₆（BO₃）（PO₄）₂：Eu³⁺材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为⁵D₀→⁷F₂特征能级跃迁,Eu³⁺的最优掺杂浓度为0.08,对应的CIE坐标为（0.610 2,0.382 3）;La₇O₆（BO₃）（PO₄）₂：Tb³⁺材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb³⁺的⁵D₄→⁷F₅能级跃迁,Tb³⁺离子的最优掺杂浓度为0.15,对应的CIE坐标为（0.317 7,0.535 2）。此外,对2种材料的变温光谱分析发现Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂荧光材料均具有良好的热稳定性。     

Li_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3,Na_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3的离子交换研究

研究了在不同温度下的NaNO3和AgNO3水溶液中Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3离子交换行为.实验表明Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3均显示出了高选择性与Na+和Ag+进行离子交换的特征,且对Ag+的选择性高于Na+.升高温度可显著提高Ag/Li和Ag/Na的交换反应速度.     

电感耦合等离子体光谱法(ICP-AES)测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量

针对银精矿样品复杂,难消解的特点,研究了不同酸溶法和碱熔法对样品的消解情况,建立了硝酸,盐酸,氢氟酸,高氯酸消解银精矿的方法。根据元素灵敏度和抗干扰性,选定各元素的测定波长。通过酸溶样和碱熔样测定结果比对,验证了方法准确性。建立了四酸消解-电感耦合等离子体光谱法测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的方法,元素的线性相关系数均在0.9999以上。通过共存元素干扰实验,确定了银精矿中高含量元素(铜、铅、锌、铁、锑、铋等)对测定元素结果没有影响。方法检出限：Cu 0.0063 mg/L, Pb 0.0159 mg/L ,Zn 0.0090 mg/L,As 0.0192 mg/L, Cd 0.0093 mg/L ,Ca 0.0084 mg/L, Mg 0.0075 mg/L, Mn 0.0081 mg/L。测定下限：Cu 0.0105mg/L,Pb 0.0265 mg/L, Zn 0.0150 mg/L, As 0.0320 mg/L, Cd 0.0155 mg/L, Ca 0.0140 mg/L, Mg 0.0125 mg/L,Mn 0.0135 mg/L。3个样品的相对标准偏差在0.87%~3.56%之间,加标回收率在95.00%~103.56%之间。方法流程短,操作简单,快速,灵敏度和再现性高,结果准确可靠,可以满足银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的测定。     

Near infrared study of aqueous rare-earth ethylsulfates

The near infrared spectra of aqueous solutions of the ethylsulfates of La, Nd, Gd, Tb, Er, Yb, Lu, Y, and Na have been determined from about 0.2 mol-dm^–3 to nearly saturation. The extinction coefficients of water have been calculated taking into account the absorption of ethylslfate anions determined in separate experiments. Their values appeared to be nearly the same as that of pure water. The relative contents of free OH groups in 0.5 and 0.7M solutions have been estimated from the absorbances at 1160 nm. They were lower in solutions of the heavy rare-earth ethylsulfates (Tb, Er, Yb, Lu) than in equimolar solutions of the lighter ones (La, Nd), confirming our previous view that secondary hydration of the heavy trivalent rare-earth cations is distinctly stronger than that of the lighter ones. A comparison of the spectra of these aqueous ethylsulfates with those of perchlorates shows that the structure-breaking ability of the C₂H₅SO ₄ ^– ion is much smaller than that of perchlorate anion.     

电感耦合等离子体光谱法测定铜冶炼烟尘中锌

本实验介绍了电感耦合等离子体光谱法测定铜冶炼烟尘中锌含量的分析方法。针对样品碳,硅含量高的特点,有针对性的研究了样品的消解方法,确定采用盐酸、硝酸、氢氟酸、高氯酸对铜冶炼烟尘样品进行消解。同时进行了干扰试验,确定样品中高含量的铜,铅,砷等对样品测定结果没有影响。并对仪器的工作参数进行了优化。方法检出限为为0.011 mg/L,测定下限为0.019 mg/L,3个样品的相对标准偏差在0.54%~0.92%之间,加标回收率在96%~101.14%之间。该方法样品消解完全,流程短,操作简单,快速,测定准确度高,可以满足铜冶炼烟尘中锌含量的测定。     

Syntheses and characterization of two oxoborates, (Pb3O)2(BO3)2MO4 (M=Cr, Mo)

Two oxoborates, (Pb₃O)₂(BO₃)₂MO₄ (M=Cr, Mo), have been prepared by solid-state reactions below 700 °C. Single-crystal XRD analyses showed that the Cr compound crystallizes in the orthorhombic group Pnma with a=6.4160(13) Å, b=11.635(2) Å, c=18.164(4) Å, Z=4 and the Mo analog in the group Cmcm with a=18.446(4) Å, b=6.3557(13) Å, c=11.657(2) Å, Z=4. Both compounds are characterized by one-dimensional chains formed by corner-sharing OPb₄ tetrahedra. BO₃ and CrO₄ (MoO₄) groups are located around the chains to hold them together via Pb–O bonds. The IR spectra further confirmed the presence of BO₃ groups in both structures and UV–vis diffuse reflectance spectra showed band gaps of about 1.8 and 2.9 eV for the Cr and Mo compounds, respectively. Band structure calculations indicated that (Pb₃O)₂(BO₃)₂MoO₄ is a direct semiconductor with the calculated energy gap of about 2.4 eV.     

Decomposition of P2S2N4(Si(CH3)3)4A12C14 as Studied by FT-Raman and Quantum Chemistry Means

The dimeric title compound decomposes upon heating to give the monomer and desulphurized monomer as shown by FT-Raman and quantum chemical means.     

On the crystal chemistry of three copper(II)-arsenates: Cu3(AsO4)2-III,Na4Cu(AsO4)2, and KCu4(AsO4)3

The three copper(II)-arsenates were synthesized under hydrothermal conditions; their crystal structures were determined by single-crystal X-ray diffraction methods:Cu₃(AsO₄)₂-III:a=5.046(2) Å,b=5.417(2) Å,c=6.354(2) Å, =70.61(2)°, =86.52(2)°, =68.43(2)°,Z=1, space group ,R=0.035 for 1674 reflections with sin / 0.90 Å^–1.Na₄Cu(AsO₄)₂:a=4.882(2) Å,b=5.870(2) Å,c=6.958(3) Å, =98.51(2)°, =90.76(2)°, =105.97(2)°,Z=1, space group ,R=0.028 for 2157 reflections with sin / 0.90 Å^–1.KCu₄(AsO₄)₃:a=12.234(5) Å,b=12.438(5) Å,c=7.307(3) Å, =118.17(2)°,Z=4, space group C2/c,R=0.029 for 1896 reflections with sin / 0.80 Å^–1.Within these three compounds the Cu atoms are square planar [4], tetragonal pyramidal [4+1], and tetragonal bipyramidal [4+2] coordinated by O atoms; an exception is the Cu(2)^[4+1] atom in Cu₃(AsO₄)₂-III: the coordination polyhedron is a representative for the transition from a tetragonal pyramid towards a trigonal bipyramid. In KCu₄(AsO₄)₃ the Cu(1)^[4]O₄ square and the As(1)O₄ tetrahedron share a common O—O edge of 2.428(5) Å, resulting in distortions of both the CuO₄ square and the AsO₄ tetrahedron. The two Na atoms in Na₄Cu(AsO₄)₂ are [6] coordinated, the K atom in KCu₄(AsO₄)₃ is [8] coordinated by O atoms.Die drei Kupfer(II)-Arsenate wurden unter Hydrothermalbedingungen gezüchtet und ihre Kristallstrukturen mittels Einkristall-Röntgenbeugungsmethoden ermittelt:Cu₃(AsO₄)₂-III:a = 5.046(2) Å,b = 5.417(2) Å,c = 6.354(2) Å, = 70.61 (2)°, = 86.52(2)°, = 68.43(2)°,Z = 1, Raumgruppe ,R = 0.035 für 1674 Reflexe mit sin / 0.90 Å^–1.Na₄Cu(AsO₄)₂:a = 4.882(2) Å,b = 5.870(2) Å,c = 6.958(3) Å, = 98.51(2)°, = 90.76(2)°, = 105.97(2)°,Z = 1, Raumgruppe ,R = 0.028 für 2157 Reflexe mit sin / 0.90 Å^–1.KCu₄(AsO₄)₃:a = 12.234(5) Å,b = 12.438(5) Å,c = 7.307(3) Å, = 118.17(2)°,Z = 4, Raumgruppe C2/c,R = 0.029 für 1896 Reflexe mit sin / 0.80 Å^–1.Die Cu-Atome in diesen drei Verbindungen sind durch O-Atome quadratisch planar [4], tetragonal pyramidal [4 + 1] und tetragonal dipyramidal [4 + 2]-koordiniert; eine Ausnahme ist das Cu(2)^{[4 + 1]}-Atom in Cu₃(AsO₄)₂-III: Das Koordinationspolyeder stellt einen Vertreter des Übergangs von einer tetragonalen Pyramide zu einer trigonalen Dipyramide dar. In KCu₄(AsO₄)₃ haben das Cu(1)^[4]O₄-Quadrat und das As(1)O₄-Tetraeder eine gemeinsame O—O-Kante von 2.428(5) Å, was eine Verzerrung der beiden Koordinationsfiguren CuO₄-Quadrat und AsO₄-Tetraeder bedingt. Die zwei Na-Atome in Na₄Cu(AsO₄)₃ sind durch O-Atome [6]-koordiniert, das K-Atom in KCu₄(AsO₄)₃ ist [8]-koordiniert.

---

Zur Kristallchemie dreier Kupfer (II)-Arsenate: Cu₃(AsO₄)₂-III, Na₄Cu(AsO₄)₂ und KCu₄(AsO₄)₃

     

Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.     

Near infrared study of aqueous lanthanide perchlorates

The near infrared spectra of water in aqueous solutions of La(ClO₄)₃, Pr(ClO₄)₃, Nd(ClO₄)₃, Gd(ClO₄)₃, Er(ClO₄)₃, Yb(ClO₄)₃, Lu(ClO₄)₃, and NaClO₄ have been measured in the concentration range from 0.3 to 2.5 mol-dm^–3, at 25°C. The relative contents of free OH groups in the 1.0, 1.6, and 2.2M solutions have been calculated from extinction coefficients for water at 1160 nm. They increase with increasing salt concentration and are greater in solutions of the lighter lanthanide perchlorates at any fixed molarity. The results are discussed in terms of the stoichiometry and structure of hydrated cations of trivalent lanthanides.     

PbCu3(OH)(NO3)(SeO3)3·1/2H2O und Pb2Cu3O2(NO3)2(SeO3)2: Synthese und Kristallstrukturuntersuchung

Crystals of PbCu₃(OH)(NO₃)(SeO₃)₃·1/2H₂O [a=7.761(3)Å,b=9.478(4)Å,c=9.514(4)Å, =66.94(2)°, =69.83(2)°, =81.83(2)°, space group P ,Z=2] and Pb₂Cu₃O₂(NO₃)₂(SeO₃)₂ [a=5.884(2)Å,b=12.186(3)Å,c=19.371(4)Å, space group Cmc2₁,Z=4] were synthesized under hydrothermal conditions. Their crystal structures were refined with three-dimensional X-ray data toR _w=0.033 resp. 0.055. In PbCu₃(OH)(NO₃)(SeO₃)₃·1/2H₂O the Cu atoms are [4+1] and [4+2] coordinated and via SeO₃ groups a three-dimensional atomic arrangement is built up. In Pb₂Cu₃O₂(NO₃)₂(SeO₃)₂ there are sheets, which are connected only via Pb-O bonds ranging from 2.98 Å to 3.16 Å.