Crystal structure and magnetic properties of Nd（Mn1-xFex）2Si2 compounds

X-ray powder diffraction,resistivity and magnetization studies have been performed on polycrystalline Nd(FexMn1-x)2Si2 (0 ≤ x ≤ 1) compounds which crystallize in a ThCr2Si2-type structure with the space group I4/mmm.The field-cooled temperature dependence of the magnetization curves shows that,at low temperatures,NdFe2Si2 is antiferromagnetic,while the other compounds show ferromagnetic behaviour.The substitution of Fe for Mn leads to a decrease in lattice parameters a,c and unit-cell volume V .The Curie temperature of the compounds first increases,reaches a maximum around x = 0.7,then decreases with Fe content.However,the saturation magnetization decreases monotonically with increasing Fe content.This Fe concentration dependent magnetization of Nd(FexMn1-x)2Si2 compounds can be well explained by taking into account the complex effect on magnetic properties due to the substitution of Mn by Fe.The temperature’s square dependence on electrical resistivity indicates that the curve of Nd(Fe0.6Mn0.4)2Si2 has a quasi-linear character above its Curie temperature,which is typical of simple metals.     

Mn离子取代M型钡铁氧体的研究

本文对Mn离子取代M型钡铁氧体BaFe_12-xMn_xO₁₉作了较系统的研究。主要结论如下:(1)在我们的实验条件下,Mn的取代量x可达4,其中约有0.1—0.3的Mn²⁺存在,其余Mn为三价。(2)Mn离子主要进入12k和2a晶位。(3)BaFe_12-xMn_xO₁₉的各向异性常数K₁₉,居里温度T_c和饱和磁化强度σ_s均随x的增加而下降。(4)Mn引起BaFe_12-xMn_xO₁₉的非共线自旋结构。(5)Mn³⁺在12k和2a晶位中的平均零场劈裂因子D^h比尖晶石中八面体B位上的Mn³⁺之D^c值小近一个数量级。 关键词：     

Tb0.3Dy0.7(Fe0.9T0.1)1.95合金的结构、自旋重取向和穆斯堡尔谱

系统研究了室温下Tb_0.3Dy_0.7(Fe_0.9T_0.1)_1.95(过渡金属元素T=Mn，Fe，Co，B，Al，Ga)合金中ⅢA族金属和过渡金属元素T替代Fe对结构、自旋重取向和穆斯堡尔谱的影响.结果发现，不同金属T替代Fe，Tb_0.3Dy_0.7(Fe_0.9T_0.1)_1.95，合金具有相同的MgCu₂型立方Laves相结构；Al，Ga替代使Tb_0.3Dy_0.7(Fe_0.9T_0.1)_1.95合金的易磁化方向在{110}面逐渐偏离了立方晶体的主对称轴，即自旋重取向，B，Mn，Co替代未使易磁化轴发生明显转动；Al，Ga元素替代使超精细场H_hf略有下降，B，Mn替代对超精细场H_hf的影响不大，而Co元素替代使超精细场H_hf有较大增加；所有元素替代使同质异能移IS有所增加；B，Al，Ga和Mn替代使四极劈裂Q_s增加，而Co替代使四极劈裂Q_s下降. 关键词： 立方Laves相 自旋重取向 穆斯堡尔谱     

Influence of manganese substitution and annealing temperature on the formation,microstructure and magnetic properties of Mn–Zn ferrites

The effects of annealing temperature and manganese substitution on the formation, microstructure and magnetic properties of Mn_xZn_1−xFe₂O₄ (with x varying from 0.3 to 0.9) through a solid-state method have been investigated. The correlation of the microstructure and the grain size with the magnetic properties of Mn–Zn ferrite powders was also reported. X-ray diffraction (XRD), a scanning electron microscope (SEM) and a vibrating sample magnetometer (VSM) were utilized in order to study the effect of variation of manganese substitution and its impact on crystal structure, crystalline size, microstructure and magnetic properties of the ferrite powders formed. The XRD analysis showed that pure single phases of Mn–Zn ferrites were obtained by increasing the annealing temperature to 1200–1300 °C. Increasing the annealing temperature to ?1300 °C led to abnormal grain growth with inter-granular pores and this led to a decrease in the saturation magnetization. Moreover, an increase in the Mn²⁺ ion substitution up to x=0.8 increased the lattice parameter of the formed powders due to the high ionic radii of the Mn²⁺ ion. Mn–Zn ferrites phases were formed and the positions of peaks were shifted by substituting manganese. The average crystalline size was increased by increasing the annealing temperature and decreased by increasing the substitution by manganese up to 0.8. The average crystalline size was in the range 95–137.3 nm. The saturation magnetization of the Mn–Zn-substituted ferrite powders increased continuously with an increase in the Mn concentration up to 0.8 at annealing temperatures of 1200–1300 °C. Further increase of Mn substitution up to 0.9 led to a decrease of saturation magnetization. The saturation magnetization increased from 17.3 emu/g for the Mn_0.3Zn_0.7Fe₂O₄ phase particles produced to 59.08 emu/g for Mn_0.8Mn_0.2Fe₂O₄ particles.     

Micro Raman,Mossbauer and magnetic studies of manganese substituted zinc ferrite nanoparticles: Role of Mn

A series of Mn–Zn Ferrite nanoparticles (<15 nm) with formula Mn_xZn_1−xFe₂O₄ (where x=0.00, 0.35, 0.50, 0.65) were successfully prepared by citrate-gel method at low temperature (400 °C). X-ray diffraction analysis confirmed the formation of single cubic spinel phase in these nanoparticles. The FESEM and TEM micrographs revealed the nanoparticles to be nearly spherical in shape and of fairly uniform size. The fractions of Mn²⁺, Zn²⁺ and Fe³⁺ cations occupying tetrahedral sites along with Fe occupying octahedral sites within the unit cell of different ferrite samples are estimated by room temperature micro-Raman spectroscopy. Low temperature Mossbauer measurement on Mn_0.5Zn_0.5Fe₂O₄ has reconfirmed the mixed spinel phase of these nanoparticles. Room temperature magnetization studies (PPMS) of Mn substituted samples showed superparamagnetic behavior. Manganese substitution for Zn in the ferrite caused the magnetization to increase from 04 to18 emu/g and Lande's g factor (estimated from ferromagnetic resonance measurement) from 2.02 to 2.12 when x was increased up to 0.50. The FMR has shown that higher Mn cationic substitution leads to increase in dipolar interaction and decrease in super exchange interaction. Thermomagnetic (M–T) and magnetization (M–H) measurements have shown that the increase in Mn concentration (up to x=0.50) enhances the spin ordering temperature up to 150 K (blocking temperature). Magnetocrystalline anisotropy in the nanoparticles was established by Mossbauer, ferromagnetic resonance and thermomagnetic measurements. The optimized substitution of manganese for zinc improves the magnetic properties and makes these nanoparticles a potential candidate for their applications in microwave region and biomedical field.     

Tb2AlFe16-xMnx化合物的结构、磁性及正电子湮没谱研究

通过X射线衍射、磁测量及正电子湮没谱等手段研究了Tb₂AlFe_16-xMn_x（x=1—8）化合物的结构和磁性.X射线衍射研究结果表明Tb₂AlFe_16-xMn_x化合物具有六角相的Th₂Ni₁₇型结构.室温下的正电子湮没实验研究表明,Mn对Fe的替代导致化合物中的铁磁相互作用减弱,并且化合物中存在着较强烈的磁弹耦合效应.磁测量研究结果表明,Mn的替代导致Tb₂AlFe_16-xMn_x化合物的居里温度及自发磁化强度急剧下降. 关键词： 2AlFe_16-xMn_x化合物')" href="#">Tb₂AlFe_16-xMn_x化合物 磁弹耦合效应 居里温度     

Enhancement of initial permeability due to Mn substitution in polycrystalline Ni0.50−xMnxZn0.50Fe2O4

The structural and magnetic properties of Mn substituted Ni_0.50−xMn_xZn_0.50Fe₂O₄ (where x=0.00, 0.10 and 0.20) sintered at various temperatures have been investigated thoroughly. The lattice parameter, average grain size and initial permeability increase with Mn substitution. Both bulk density and initial permeability increase with increasing sintering temperature from 1250 to 1300 °C and above 1300 °C they decrease. The Ni_0.30Mn_0.20Zn_0.50Fe₂O₄ sintered at 1300 °C shows the highest relative quality factor and highest initial permeability among the studied samples. The initial permeability strongly depends on average grain size and intragranular porosity. From the magnetization as a function of applied magnetic field, M(H), it is clear that at room temperature all samples are in ferrimagnetic state. The number of Bohr magneton, n(μ_B), and Neel temperature, T_N, decrease with increasing Mn substitution. It is found that Mn substitution in Ni_0.50−xMn_xZn_0.50Fe₂O₄ (where x=0.20) decreases the Neel temperature by 25% but increases the initial permeability by 76%. Possible explanation for the observed characteristics of microstructure, initial permeability, DC magnetization and Neel temperature of the studied samples are discussed.     

Tailoring of structural, electrical and magnetic properties of BaCo2 W-type hexaferrites by doping with Zr-Mn binary mixtures for useful applications

Single-phase W-type hexaferrite, BaCo₂Fe_16−2x(ZrMn)_xO₂₇ (x=0.0-1.0), has been synthesized by the chemical co-precipitation technique. Mössbauer analysis indicates substitution of Zr ions on tetrahedral (4e and 4f_IV) sites and Mn ions on the octahedral ‘4f_VI site’ at low-doped concentration when the concentration is increased Mn ions but show preference for the octahedral ‘2b site’. The highest enhancement in the value of the room temperature resistivity of 2.82×10⁹ Ω cm has been obtained by doping with Zr-Mn content of x=0.6. The dissipation factor increases from 6.49×10³ to 9.97×10³ at 10 kHz with the addition of Zr-Mn dopants. Such materials are potentially suitable for electromagnetic attenuation purposes, for microwave absorption and as radar absorbing material. High values of saturation magnetization (67 emu/g) and remanent magnetization (34.7 emu/g) are obtained for substitution level of x=0.4 making them suitable for data processing devices.     

Superconductivity coexisting with ferromagnetism in mixed-valence Mn doped La1.85−(4/3)xSr0.15+(4/3)xCu1−xMnxO4

The effect of Mn substitution for Cu in mixed-valence Mn doped La_{1.85−(4/3)x}Sr_0.15+(4/3)xCu_1−xMn_xO₄ (x=0.06) has been investigated by electric resistivity, magnetization and electron spin resonance experiments. Coexistence of superconductivity and ferromagnetism was observed.     

镍锰铁氧体纳米线阵列的制备与表征

采用真空负压灌注技术, 结合溶胶-凝胶法在多孔氧化铝模板的纳米孔洞中成功制备了平均直径为80 nm左右的Ni_{1- x}Mn_xFe₂O₄(x=0, 0.25, 0.5, 0.75) 纳米线阵列. XRD结果显示所制备的纳米线阵列为立方尖晶石结构, SEM和TEM的结果表明纳米线是由大量不同晶体取向的亚微晶粒联接组成. 磁测量结果显示, 随着Mn掺杂浓度的增加, 饱和磁化强度先增加而后减小, 这种变化与离子在尖晶石结构中的替代、占位变化有关. 相比于块体材料的NiFe₂O₄, 由于非线性磁结构比例的增加, 导致了线体NiFe₂O₄的饱和磁化强度降低.     

A structural, magnetostrictive and M?ssbauer study of Tb0.3Dy0.7(Fe0.9 T 0.1)1.95 alloys

The effect of IIIA metal and transition metalT substitution for Fe on crystal structure, magnetostriction and spontaneous magnetostriction, anisotropy and spin reorientation of a series of polycrystalline Tb_0.3 Dy_0.7 (Fe_0.9 T _0.1)_1.95 (T=Mn, Fe, Co, B, Al, Ga) alloys at room temperature were investigated systematically. It was found that the primary phase of the Tb_0.3 Dy_0.7 (Fe_0.9 T _0.1)_1.95 alloys is the MgCu₂-type cubic Laves phase structure for different substitution. The magnetostriction λ{ins} decrases greatly for the substitution of IIIA metal, B, Al and Ga, but is saturated more easily for Al and Ga substitution, showing that the Al and Ga substitution is beneficial to a decrease in the magnetocrystalline anisotropy of Tb_0.3 Dy_0.7 (Fe_0.9 T _0.1)_1.95 alloys. However, the substitution of transition metal Mn and Co decreases slightly the magnetostriction λ{ins}. It was also found that the effect of different substitutions on the spontaneous magnetostriction λ{in111} is distinct. The analysis of the M?ssbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry for Al and Ga substitution, namely spin reorientation, but it does not change evidently for B, Mn and Co substitution.     

V替代Mn对La_(0.45)Ca_(0.55)MnO_3电荷有序相及自旋玻璃态的影响

用固相反应法制备了La0.45Ca0.55Mn1-xVxO3(x=0.00,0.10)多晶样品.通过X射线衍射谱、质量磁化强度-温度曲线、电子自旋共振谱,研究了V5+替代Mn3+/Mn4+对La0.45Ca0.55MnO3电荷有序相和自旋玻璃态的影响.实验结果表明,当x=0.10时,不仅母体的电荷有序相基本破坏,而且母体在40K左右出现的自旋玻璃态也被融化.电荷有序相被破坏的主要原因是用V5+替代Mn3+/Mn4+后,增加了Mn3+与Mn4+的比例,使铁磁双交换作用优于反铁磁超交换作用;自旋玻璃态的融化是由于V替代Mn后破坏了反铁磁背景下有少量铁磁成分的自旋玻璃态的形成条件.     

Charge order and spin order in Nd0.5Sr0.5Mn1? x (Ga x , Ti x )O3 system

Magnetic properties of Nd0.5Sr0.5Mn1-x(Gax,Tix)O3 system (0.04≤x≤0.4) were investigated through magnetization and electron spin resonance (ESR) measurements. It was observed that a small amount of Ti substitution for Mn will destroy the charge-ordering (CO) phase completely and induce the cluster-spin-glass phase in the system, which displays a procedure of collapse of CO and of an enhancement of spin ordering (SO) phase. In contrast, the Ga substitution for Mn induces a melting of CO phase in the system. It was observed that with substitution the CO phase is suppressed gradually and the remanent CO phase is retained all the while, and withal, there is a co-existence of AFM CO phase and FM SO at low temperature. In addition, an abrupt rise of magnetization was observed in M-Tcurves. We attributed this abnormal phenomenon to a transition from canted AFM SO to FM SO in CO region.     

Room-temperature ferromagnetism in pure and Mn doped SnO2 powders

We report here observation of ferromagnetism in pure and Mn doped SnO₂ powder with different Mn contents. Magnetic measurements revealed that all samples exhibit room temperature ferromagnetism (RTFM), which is identified as an intrinsic characteristic. The RTFM has been observed in the pure SnO₂ powder, which is believed to be defect induced, with a saturation magnetization of ～0.017 emu/g. The RTFM was enhanced considerably in the Mn doped samples and the magnetic properties strongly depend on doping content. A sample with 1% of Mn is ferromagnetic at room temperature with a saturation magnetization of ～0.98 emu/g, a remanent magnetization of ～27%, and a coercivity of ～270 Oe. The average magnetic moment per Mn atom decreases with increasing Mn content. Our results reveal that the large RTFM observed in Mn doped SnO₂ powder originates from a combination effect of oxygen vacancies and transition metal doping.     

Magnetic behavior of the II-V-diluted magnetic semiconductor Cd1−xMnxSb

Polycrystalline samples of the II-V-diluted magnetic semiconductor Cd_1−xMn_xSb (x=0.05-0.20) were synthesized. Standard high temperature ceramic methods under an inert atmosphere were utilized for sample fabrication. Structural characterization was done using X-ray diffractometry (XRD), which indicated that a simple substitution of Mn for Cd is probably not occurring. Hysteresis, ac susceptibility, dc magnetization, and spontaneous magnetization measurements were performed for Cd_0.90Mn_0.10Sb. The hysteresis data indicated the presence of a ferromagnetic component. Ferromagnetism in the Cd_0.90Mn_0.10Sb system is likely due to two sources: Mn spins in small Mn-rich regions and a small amount of MnSb in a minority phase. Analysis of the spontaneous magnetization as a function of temperature for Cd_0.90Mn_0.10Sb yielded the value 0.172 for the critical exponent β. In MnSb, β was found to have the value 0.379, which is close to the theoretical value for 3D-Heisenberg systems. Thus, in Cd_0.90Mn_0.10Sb, the ferromagnetism is not of the 3D-Heisenberg type; rather, it is closer to 2D Ising behavior, indicating reduced effective dimensionality.     

Structural, magnetic and electronic structure studies of Mn doped TiO2 thin films

We report structural, magnetic and electronic structure study of Mn doped TiO₂ thin films grown using pulsed laser deposition method. The films were characterized using X-ray diffraction (XRD), dc magnetization, X-ray magnetic circular dichroism (XMCD) and near edge X-ray absorption fine structure (NEXAFS) spectroscopy measurements. XRD results indicate that films exhibit single phase nature with rutile structure and exclude the secondary phase related to Mn metal cluster or any oxide phase of Mn. Magnetization studies reveal that both the films (3% and 5% Mn doped TiO₂) exhibit room temperature ferromagnetism and saturation magnetization increases with increase in concentration of Mn doping. The spectral features of XMCD at Mn L_3,2 edge show that Mn²⁺ ions contribute to the ferromagnetism. NEXAFS spectra measured at O K edge show a strong hybridization between Mn, Ti 3d and O 2p orbitals. NEXAFS spectra measured at Mn and Ti L_3,2 edge show that Mn exist in +2 valence state, whereas, Ti is in +4 state in Mn doped TiO₂ films.     

Magnetic response of microbially synthesized transition metal- and lanthanide-substituted nano-sized magnetites

The magnetic susceptibility (κ_RT) and saturation magnetization (M_S) of microbially synthesized magnetites were systematically examined. Transition metal (Cr, Mn, Co, Ni and Zn)- and lanthanide (Nd, Gd, Tb, Ho and Er)-substituted magnetites were microbially synthesized by the incubation of transition metal (TM)- and lanthanide (L)-mixed magnetite precursors with either thermophilic (TOR-39) or psychrotolerant (PV-4) metal-reducing bacteria (MRB). Zinc incorporated congruently into both the precursor and substituted magnetite, while Ni and Er predominantly did not. Microbially synthesized Mn- and Zn-substituted magnetites had higher κ_RT than pure biomagnetite depending on bacterial species and they exhibited a maximum κ_RT at 0.2 cationic mole fraction (CMF). Other TMs’ substitution linearly decreased the κ_RT with increasing substitution amount. Based on the M_S values of TM- and L-substituted magnetite at 0.1 and 0.02 CMF, respectively, Zn (90.7 emu/g for TOR-39 and 93.2 emu/g for PV-4)- and Mn (88.3 emu/g by PV-4)-substituted magnetite exhibited higher M_S than standard chemical magnetite (84.7 emu/g) or pure biomagnetite without metal substitution (76.6 emu/g for TOR-39 and 80.3 emu/g for PV-4). Lanthanides tended to decrease M_S, with Gd- and Ho-substituted magnetites having the highest magnetization. The higher magnetization of microbially synthesized TM-substituted magnetites by the psychrotroph, PV-4 may be explained by the magnetite formation taking place at low temperatures slowing mechanics, which may alter the magnetic properties compared to the thermophile, through suppression of the random distribution of substituted cations.     

Magnetic study of CaMn0.96Mo0.04O3, canting vs. phase separation

CaMn_0.96Mo_0.04O₃ is an example of Mn⁴⁺ rich perovskite manganites, which exhibits a net ferromagnetic component at low temperature, observed by dc magnetization and ac susceptibility. To characterize the magnetic state of this compound, neutron powder diffraction was carried out in the 2-400 K temperature range, showing that it is necessary to use three components (ferromagnetic and G- and A-type antiferromagnetic) to describe it. This particular state is in agreement with the unusual magnetic behaviour observed by macroscopic measurements and is compared to the one observed for manganites with similar Mn valence but obtained by A-site substitution.     

A structural,magnetostrictive and Mössbauer study of Tb<Subscript>0.3</Subscript>Dy<Subscript>0.7</Subscript>(Fe<Subscript>0.9</Subscript><Emphasis Type="Italic">T</Emphasis><Subscript>0.1</Subscript>)<Subscript>1.95</Subscript> alloys

The effect of IIIA metal and transition metalT substitution for Fe on crystal structure, magnetostriction and spontaneous magnetostriction, anisotropy and spin reorientation of a series of polycrystalline Tb_0.3 Dy_0.7 (Fe_0.9 T _0.1)_1.95 (T=Mn, Fe, Co, B, Al, Ga) alloys at room temperature were investigated systematically. It was found that the primary phase of the Tb_0.3 Dy_0.7 (Fe_0.9 T _0.1)_1.95 alloys is the MgCu₂-type cubic Laves phase structure for different substitution. The magnetostrictionλ _s decrases greatly for the substitution of IIIA metal, B, Al and Ga, but is saturated more easily for Al and Ga substitution, showing that the Al and Ga substitution is beneficial to a decrease in the magnetocrystalline anisotropy of Tb_0.3 Dy_0.7 (Fe_0.9 T _0.1)_1.95 alloys. However, the substitution of transition metal Mn and Co decreases slightly the magnetostrictionλ _s . It was also found that the effect of different substitutions on the spontaneous magnetostrictionλ ₁₁₁ is distinct. The analysis of the Mössbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry for Al and Ga substitution, namely spin reorientation, but it does not change evidently for B, Mn and Co substitution.     

Nd2(Fe1-xMnx)14B的低温内禀矫顽力

当x<0.5时,Nd₂(Fe_1-xMn_x)₁₄B可形成四方晶体结构,空间群为P4₂/mnm。在低温下,该赝三元化合物的大块铸态样品具有高矫顽力。此矫顽力不依赖于热处理等工艺过程,因此具有内禀性质。内禀矫顽力 _iH_c与样品的成分有关。Nd₂(Fe_1-xMn_x)₁₄B的起始磁化曲线具有传播场H_p,并且H_p的数值与 _iH_c接近。这表明内禀矫顽力是由畴壁钉扎造成的。研究了 _iH_c与温度的变化关系,并估算了钉扎位垒的强度。测量了Nd₂(Fe_1-xMn_x)₁₄B的居里温度和饱和磁化强度。在此赝三元化合物中,交换作用随Mn对Fe的替换而急剧降低。这使得畴壁厚度变窄。Nd₂(Fe_1-xMn_x)₁₄B的磁化和反磁化行为可用窄畴壁的特征来解释。 关键词：