Study on the electrical and optical properties of Ag/Al-doped ZnO coatings deposited by electron beam evaporation

A layer of silver was deposited onto the surface of glass substrates, coated with AZO (Al-doped ZnO), to form Ag/AZO film structures, using e-beam evaporation techniques. The electrical and optical properties of AZO, Ag and Ag/AZO film structures were studied. The deposition of Ag layer on the surface of AZO films resulted in lowering the effective electrical resistivity with a slight reduction of their optical transmittance. Ag (11 nm)/AZO (25 nm) film structure, with an accuracy of ±0.5 nm for the thickness shows a sheet resistance as low as 5.6 ± 0.5 Ω/sq and a transmittance of about 66 ± 2%. A coating consisting of AZO (25 nm)/Ag (11 nm)/AZO (25 nm) trilayer structure, exhibits a resistance of 7.7 ± 0.5 Ω/sq and a high transmittance of 85 ± 2%. The coatings have satisfactory properties of low resistance, high transmittance and highest figure of merit for application in optoelectronics devices including flat displays, thin films transistors and solar cells as transparent conductive electrodes.     

Effects of post-annealing on structural, optical and electrical properties of Al-doped ZnO thin films

Aluminum-doped zinc oxide (AZO) films were deposited at 400 °C by radio-frequency magnetron sputtering using a compound AZO target. The effects of annealing atmospheres as well as hydrogen annealing temperatures on the structural, optical and electrical properties of the AZO films were investigated. It was found that the electrical resistivity varied depending on the atmospheres while annealing in air, nitrogen and hydrogen at 300 °C, respectively. Comparing with that for the un-annealed films, the resistivity of the films annealed in hydrogen decreased from 9.8 × 10⁻⁴ Ω cm to 3.5 × 10⁻⁴ Ω cm, while that of the films annealed in air and nitrogen increased. The variations in electrical properties are ascribed to both the changes in the concentration of oxygen vacancies and adsorbed oxygen at the grain boundaries. These results were clarified by the comparatively XPS analyzing about the states of oxygen on the surface of the AZO films. There was great increase in electrical resistivity due to the damage of the surfaces, when AZO films were annealed in hydrogen with a temperature higher than 500 °C, but high average optical transmittance of 80-90% in the range of 390-1100 nm were still obtained.     

Deposition of quasi-crystal Al-doped ZnO thin films for photovoltaic device applications

Quasi-crystal aluminum-doped zinc oxide (AZO) films were prepared by in situ radio frequency (RF) magnetron sputtering (sputtering without annealing) on glass substrates. The influence of deposition parameters on the optoelectronic and structural properties of the in situ deposited quasi-crystal AZO films was investigated in order to compare resulting samples. X-ray diffraction (XRD) patterns show that the quasi-crystal AZO thin films have excellent crystallization improved with increase of the RF power and substrate temperature, with an extremely preferential c-axis orientation exhibit sharp and narrow XRD pattern similar to that of single-crystal. Field emission scanning electron microscopy (FESEM) images show that quasi-crystal AZO thin films have uniform grains and the grain size increase with the increase of RF power and substrate temperature. Craters of irregular size with the columnar structure are observed in the quasi-crystal AZO thin films at a lower substrate temperature while many spherical shaped grains appeared at a higher substrate temperature. The average optical transmittance of all the quasi-crystal AZO films was over 85% in the 400-800 nm wavelength range. The resistivity of 4.176 × 10⁻⁴ Ω cm with the grain size of 76.4891 nm was obtained in the quasi-crystal AZO thin film deposited at 300 °C, under sputtering power of 140 W.     

High work function of Al-doped zinc-oxide thin films as transparent conductive anodes in organic light-emitting devices

Deposition of Al-doped ZnO (AZO) films with various film thicknesses on glass substrates was performed to investigate the feasibility of using AZO films as anode electrodes in organic light-emitting devices (OLEDs). The electrical resistivity of the AZO films with a 180-nm thickness was 4.085 × 10⁻² Ω cm, and the average optical transmittance in the visible range was 80.2%. The surface work function for the AZO films, determined from the secondary electron emission coefficients obtained with a focused ion beam, was as high as 4.62 eV. These results indicate that AZO films grown on glass substrates hold promise for potential applications as anode electrodes in high-efficiency OLEDs.     

Optimization of the optical and electrical properties of electron beam evaporated aluminum-doped zinc oxide films for opto-electronic applications

Aluminum-doped zinc oxide (AZO) thin films have been deposited by electron beam evaporation technique on glass substrates. The structural, electrical and optical properties of AZO films have been investigated as a function of annealing temperature. It was observed that the optical properties such as transmittance, reflectance, optical band gap and refractive index of AZO films were strongly affected by annealing temperature. The transmittance values of 84% in the visible region and 97% in the NIR region were obtained for AZO film annealed at 475 °C. The room temperature electrical resistivity of 4.6×10⁻³ Ω cm has been obtained at the same temperature of annealing. It was found that the calculated refractive index has been affected by the packing density of the thin films, whereas, the high annealing temperature gave rise to improve the homogeneity of the films. The single-oscillator model was used to analyze the optical parameters such as the oscillator and dispersion energies.     

Influence of various thickness metallic interlayers on opto-electric and mechanical properties of AZO thin films on PET substrates

Various thickness metallic interlayers to improve the opto-electric and mechanical properties of aluminum-doped zinc oxide (AZO) thin films deposited on flexible polyethylene terephtalate (PET) substrates are studied. The effects of the interlayers on the resistance and transmittance of the AZO thin films are discussed. The result shows that the metallic interlayers effectively improve the electric resistance but reduce the optical transmittance of the AZO thin films. These phenomena become more obvious as the interlayer thickness increases. However, the AZO with an aluminum interlayer still behaves an acceptable transmittance. Moreover, mechanical tests indicate that the aluminum interlayer increases the hardness and modulus, and reduce the residual stress of the AZO thin films. In contrast, the silver and copper interlayers decrease the AZO's mechanical properties. Comparing to those without any interlayer, the results show that the best interlayer is the 6 nm thick aluminum film.     

粉末靶制备的AZO/Ag/AZO透明导电薄膜的光电性能

室温下,采用射频磁控溅射AZO粉末靶和Ag靶在玻璃基底上制备Ag层厚度分别为12 nm和15 nm两组对称结构掺铝氧化锌/银/掺铝氧化锌(AZO/Ag/AZO)透明导电薄膜,研究了Ag层和AZO层厚度对薄膜光电性能的影响。结果表明:3层薄膜的可见光区平均透光率达到了80%,550 nm处的最高透过率达到了88%,方块电阻小于5 Ω/□。Ag层厚度是影响AZO/Ag/AZO薄膜光电性能的主要因素,AZO层的厚度对薄膜光学性能影响较大。     

Optical and electrical characteristics of Al-doped ZnO thin films prepared by aqueous phase deposition

Transparent conducting Al-doped ZnO (AZO) thin films have been deposited by sol-gel route. Starting from an aqueous solution of zinc acetate by adding aluminum chloride as dopant, a c-axis oriented polycrystalline ZnO thin film 100 nm in thickness could be spin-coated on glass substrates via a two-step annealing process under reducing atmosphere. The effects of thermal annealing and dopant concentration on the structural, electrical and optical properties of AZO thin films were investigated. The post-treated AZO films exhibited a homogenous dense microstructure with grain sizes less than 10 nm as characterized by SEM photographs. The annealing atmosphere has prominent impact on the crystallinity of the films which will in turn influence the electrical conductivity. By varying the doping concentrations, the optical and electrical properties could be further adjusted. An optimal doping concentration of Al/Zn = 2.25 at.% was obtained with minimum resistivity of 9.90 × 10⁻³ Ω-cm whereas the carrier concentration and mobility was 1.25 × 10²⁰ cm⁻³ and 5.04 cm² V⁻¹ s⁻¹, respectively. In this case, the optical transmittance in the visible region is over 90%.     

Electrical and optical properties of Al-doped ZnO thin films by sol-gel process

Al-doped ZnO (AZO) thin films oriented along the (0 0 2) plane have been prepared by the sol-gel process and their electrical and optical properties with post-deposition heating temperature were investigated. The preferred c-axis orientation along the (0 0 2) plane was enhanced with increasing post-deposition heating temperature and the surface of the films showed a uniform and nano-sized microstructure. The electrical resistivity of the films decreased from 73 to 22 Ω cm as the post-deposition heating temperature increased from 500 to 650 °C; however, the film postheated at 700 °C increased greatly to 580 Ω cm. The optical transmittance of the films postheated below 650 °C was over 86%, but it decreased at 700 °C. The electrical and optical properties of the AZO films with post-deposition heating temperature are discussed.     

Room-temperature deposition of transparent conducting Al-doped ZnO films by RF magnetron sputtering method

Transparent conductive Al-doped zinc oxide (AZO) films with highly (0 0 2)-preferred orientation were deposited on quartz substrates at room temperature by RF magnetron sputtering. Optimization of deposition parameters was based on RF power, Ar pressure in the vacuum chamber, and distance between the target and substrate. The structural, electrical, and optical properties of the AZO thin films were investigated by X-ray diffraction, Hall measurement, and optical transmission spectroscopy. The 250 nm thickness AZO films with an electrical resistivity as low as 4.62 × 10⁻⁴ Ω cm and an average optical transmission of 93.7% in the visible range were obtained at RF power of 300 W, Ar flow rate of 30 sccm, and target distance of 7 cm. The optical bandgap depends on the deposition condition, and was in the range of 3.75-3.86 eV. These results make the possibility for light emitting diodes (LEDs) and solar cells with AZO films as transparent electrodes, especially using lift-off process to achieve the transparent electrode pattern transfer.     

Effect of Cr and V dopants on the chemical stability of AZO thin film

The effect of the dopants of Cr and V on the optoelectronic properties of AZO thin film by pulsed DC magnetron sputtering has been investigated. We also use HCl and KOH solutions to conduct the chemical stability of AZO:Cr:V thin film. The experimental results show that the optimum AZO optoelectronic properties without Cr and V doping obtain the resistivity of 9.87 × 10⁻⁴ Ω cm, optical transmittance of 84% and surface roughness rms value of 2.6 nm. The chemical stability of AZO will increase after Cr and V doping. Under the added V = 0.19 wt.%, Cr = 0.56 wt.%, AZO:Cr:V thin film showed 52% increased chemical stability and 128% decrease in surface roughness after etching (the resistivity was 3.62 × 10⁻³ Ω cm and optical transmittance 81%). From the experimental results, the higher resistivity obtained after KOH etching compared with after HCl etching. The reason is that the Zn/Al ratio will reduce after etching and cause the AZO film carrier density to reduce as well. However, the optical transmittance obtained after KOH etching will be higher than that after HCl etching. This is because that a better surface roughness after KOH etching obtained than after HCl etching.     

Microstructure, hydrogenation and optical behavior of Mg-Ni multilayer films deposited by magnetron sputtering

Mg-Ni multilayer films with sequential Mg and Ni layers were prepared by direct current magnetron sputtering. The substrate temperature influences the microstructure of the films greatly. The film deposited at 298 K exhibits multilayered structure, while the film shows nanocrystalline/amorphous composite structure at the deposition temperature of 473 K. The optical properties between hydrogenation/dehydrogenation states of the films were performed using spectrophotometer in visible light region. The film deposited at 473 K can switch from mirror-like metallic state towards brownish yellow transparent state under 0.6 MPa H₂ at 298 K, and the optical transmittance modulation reaches up to 20% both at a wavelength of 770 nm and IR region, while the film deposited at 298 K exhibits low optical change, and the optical switching behavior can hardly be found. The extra free energy stored in the boundary of the nanocrystallines benefits the formation of magnesium-based hydride, resulting in the enhancement of the optical switching properties of the Mg-Ni film deposited at 473 K.     

The enhanced conductivity and stability of AZO thin films with a TiO2 buffer layer

Aluminum doped zinc oxide (AZO) films were substitutes of the SnO₂:F films on soda lime glass substrate in the amorphous thin-film solar cells due to good properties and low cost. In order to improve properties of AZO films, the TiO₂ buffer layer had been introduced. AZO films with and without TiO₂ buffer layer were deposited on soda lime glass substrates by r.f. magnetron sputtering. Subsequently, one group samples were annealed in vacuum (0.1 Pa) at 500 °C for 120 s using the RTA system, and the influence of TiO₂ thickness on the properties of AZO films had been discussed. The XRD measurement results showed that all the films had a preferentially oriented (0 0 2) peak, and the intensity of (0 0 2) peak had been enhanced for the AZO films with TiO₂ buffer layer. The resistivity of TiO₂ (3.0 nm)/AZO double-layer film is 4.76×10⁻⁴ Ω cm with the maximum figure merit of 1.92×10⁻² Ω⁻¹, and the resistivity has a remarkable 28.7% decrease comparing with that of the single AZO film. The carrier scattering mechanism of TiO₂ (3.0 nm)/AZO double-layer film had been described by Hall measurement in different temperatures. The average transmittance of all the films exceeded 92% in the visible spectrum. Another group samples were heat treated in the quartz tube in air atmosphere, and the effect of TiO₂ thickness on thermal stability of AZO films had been discussed.     

Thickness dependence of structural, electrical and optical properties of indium tin oxide (ITO) films deposited on PET substrates

Without intentionally heating the substrates, indium tin oxide (ITO) thin films of thicknesses from 72 nm to 447 nm were prepared on polyethylene terephthalate (PET) substrates by DC reactively magnetron sputtering with pre-deposition substrate surfaces plasma cleaning. The dependence of structural, electrical, and optical properties on the films thickness were systematically investigated. It was found that the crystal grain size increases, while the transmittance, the resistivity, and the sheet resistance decreases as the film thickness was increasing. The thickest film (∼447 nm) was found of the lowest sheet resistance 12.6 Ω/square, and its average optical transmittance (400-800 nm) and the 550 nm transmittance was 85.2% and 90.4%, respectively. The results indicate clearly that dependence of the structural, electrical, and optical properties of the films on the film thickness reflected the improvement of the film crystallinity with the film thickness.     

ZnO/Ag/ZnO multilayer films for the application of a very low resistance transparent electrode

Transparent conductive ZnO/Ag/ZnO multilayer electrodes having much lower electrical resistance than the widely used transparent electrodes were prepared by simultaneous RF magnetron sputtering of ZnO and DC magnetron sputtering of Ag. An Ag film with different thickness was used as intermediate metallic layers. The optimum thickness of Ag thin films was determined to be 6 nm for high optical transmittance and good electrical conductivity. With about 20-25 nm thick ZnO films, the multilayer showed high optical transmittance in the visible range of the spectrum and had color neutrality. The electrical and optical properties of the multilayers were changed mainly by Ag film properties. A high quality transparent electrode, having sheet resistance as low as 3 ohm/sq and high transmittance of 90% at 580 nm, was obtained and could be reproduced by controlling the preparation parameter properly. The above property is suitable as transparent electrode for dye sensitized solar cells (DSSC).     

Transparent conductive and near-infrared reflective Cu-based Al-doped ZnO multilayer films grown by magnetron sputtering at room temperature

Cu-based Al-doped ZnO multilayer films were deposited on glass substrates by DC magnetron sputtering at room temperature. Three kinds of multilayer structures (AZO/Cu, AZO/Cu/AZO, and Cu/AZO) were designed for comparison, and the effects of the Cu layer thickness on photoelectrical properties of the multilayer films were investigated. The results revealed that the transparent-conductive property and near-infrared reflectance of the films are closely correlated with the Cu layer thickness, and among the three structures, AZO/Cu bi-layer films exhibited preferable photoelectrical properties. The AZO/Cu bi-layer film with a Cu layer thickness of 7 nm displayed the highest figure of merit of 4.82 × 10⁻³ Ω⁻¹, with a low sheet resistance of 21.7 Ω/sq and an acceptable visible transmittance of 80%. The near infrared reflectance above 50% can be simultaneously obtained. The good performance of the coatings indicates that they are promising for coated glasses, thin film solar cells and heat-reflectors.     

用粉末靶在玻璃和PI衬底上制备AZO/Ag/AZO薄膜

室温下在玻璃和聚酰亚胺两种不同衬底上, 采用射频磁控溅射法溅射掺铝氧化锌(AZO)粉末靶和固体Ag靶, 制备了两组AZO/Ag/AZO 3层透明导电薄膜, 研究了AZO层厚度对不同衬底3层膜结构和光电性能的影响.结果表明:不同衬底的两组AZO/Ag/AZO薄膜均为多晶膜.当Ag层厚度不变时, 随着AZO层厚度的增加, 两组薄膜电学性能变化不大, 透射峰向长波方向移动.玻璃和PI衬底上制备的AZO(30 nm)/Ag(14 nm)/AZO(30 nm)薄膜, 在550 nm处的透光率分别为85%和70%, 方块电阻分别为2.6 Ω/□和4.6 Ω/□.     

Substrate temperature dependence of the properties of scandium-doped ZnO films deposited by sputtering

Structural and optical properties of Sc-doped ZnO films grown by RF magnetron sputtering at different substrate temperatures were investigated. All the ZnO:Sc films are polycrystalline with the hexagonal wurtzite structure. X-ray diffraction patterns of the films showed that the doped-films have (0 0 2) as preferred orientation when the deposition temperature was increased from 250 °C to 300 °C. All the films are in a state of compressive stress, whereas the stress decreases gradually with increasing substrate temperature. The average transmittance of these films was above 90% in the wavelength range from 400 nm to 800 nm. The optical band gap of these films was determined. The optical constants of these films were determined using transmittance and reflectance spectra.     

Effects of hydrogen flux on the properties of Al-doped ZnO films sputtered in Ar + H2 ambient at low temperature

Al-doped ZnO (AZO) transparent conductive thin films were grown by magnetron sputtering with AZO (98 wt.% ZnO, 2 wt.% Al₂O₃) ceramic target in Ar + H₂ ambient at a relatively low temperature of 100 °C. To investigate the dependence of crystalline and properties of as-grown AZO films on the H₂-flux, X-ray diffraction (XRD), X-ray photoemission spectrometer (XPS), Hall and transmittance spectra measurements were employed to analyze the AZO samples deposited with different H₂-flux. The results indicate that H₂-flux has a considerable influence on the transparent conductive properties of AZO films. The resistivity of 4.15 × 10⁻⁴ Ω cm and the average transmittance of more than 94% in the visible range were obtained with the optimal H₂-flux of 1.0 sccm. Such a low temperature growing method present here may be especially useful for some low-melting point photoelectric devices and substrates.     

Influence of substrate temperature and post-treatment on the properties of ZnO:Al thin films prepared by pulsed laser deposition

Highly transparent conductive Al₂O₃ doped zinc oxide (AZO) thin films have been deposited on the glass substrate by pulsed laser deposition technique. The effects of substrate temperature and post-deposition annealing treatment on structural, electrical and optical properties of AZO thin films were investigated. The experimental results show that the electrical resistivity of films deposited at 240 °C is 6.1 × 10⁻⁴ Ω cm, which can be further reduced to as low as 4.7 × 10⁻⁴ Ω cm by post-deposition annealing at 400 °C for 2 h in argon. The average transmission of AZO films in the visible range is 90%. The optical direct band gap of films was dependent on the substrate temperature and the annealing treatment in argon. The optical direct band gap value of AZO films increased with increasing annealing temperature.