Optical spectroscopy of Ca3Sc2Si3O12, Ca3Y2Si3O12 and Ca3Lu2Si3O12 doped with Pr

The silicates Ca₃Sc₂Si₃O₁₂, Ca₃Y₂Si₃O₁₂ and Ca₃Lu₂Si₃O₁₂, both undoped and doped with Pr³⁺ ions, have been synthesized by solid-state reaction at high temperature. The luminescence spectroscopy and the excited state dynamics of the materials have been studied upon VUV and X-ray excitation using synchrotron radiation. All doped samples have shown efficient 5d-4f emission upon direct VUV excitation of 5d levels, but only Ca₃Sc₂Si₃O₁₂:Pr³⁺ shows luminescence upon interband VUV or X-ray excitation. The VUV excited emission spectra of Ca₃Y₂Si₃O₁₂:Pr³⁺ and Ca₃Lu₂Si₃O₁₂:Pr³⁺ show features attributed to emission from two distinct sites accommodating the Pr³⁺ dopant. The decay kinetics of the Pr³⁺ 5d-4f emission in Ca₃Sc₂Si₃O₁₂:Pr³⁺ upon VUV excitation across the band gap are characterized by decay times in the range 25-28 ns with no significant rise after the excitation pulse. They appear to be faster upon X-ray irradiation than for VUV excitation. Weak afterglow components are attributed to defect luminescence.     

La0.67Ca0.33MnO3薄膜皮秒光电效应

在1064 nm波长脉冲激光（脉宽25 ps）的照射下，钙钛矿氧化物薄膜La0.67Ca0.33MnO3/SrTiO3具有超快光电效应，对激光脉冲显示ps量级的响应时间，上升沿响应时间300 ps，半高宽700 ps，同时，对激光能量的响应灵敏度为500 mV/mJ。     

合成反铁磁Ni81Fe19/Co90Fe10/Ru/Co90Fe10/Ni81Fe19的研究

采用直流磁控溅射方法制备了一系列的合成反铁磁及以其为自由层的自旋阀.研究发现,在Ni₈₁Fe₁₉与Ru层之间插入适当厚度的Co₉₀Fe₁₀层后,可有效地提高合成反铁磁两磁性层间的反铁磁耦合强度,得到具有饱和场H_s更高、饱和磁化强度M_s更低、热稳定性更好的合成反铁磁.另外,以这种合成反铁磁作自旋阀的自由层时,可有效提高自旋阀的稳定性. 关键词： 合成反铁磁 退火 自旋阀     

Multilayer Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 thin films for tunable microwave applications

Bi_1.5Zn_1.0Nb_1.5O₇/Ba_0.6Sr_0.4TiO₃/Bi_1.5Zn_1.0Nb_1.5O₇ tunable multilayer thin film has been fabricated by pulsed laser ablation and characterized. Phase composition and microstructure of multilayer films were characterized by X-ray diffraction, scanning electron microscopy (SEM) and atomic force microscopy (AFM). The film has very smooth surface with RMS roughness of 1.5-2 nm and grain size of 100-150 nm. Total film thickness has been measure to be 375 nm. The BZN thin films at 300 K, on Pt(1 1 1)/SiO₂/Si substrate showed zero-field dielectric constant of 105 and dielectric loss tangent of 0.002 at frequency of 0.1 MHz. Thin films annealed at 700 °C shows the dielectric tunability of 18% with biasing field 500 kV/cm at 0.1 MHz. The multilayer thin film shows nonferroelectric behavior at room temperature. The good physical and electrical properties of multilayer thin films make them promising candidate for tunable microwave device applications.     

Depolarization currents in the Na0.5Bi8.5Ti2Nb4O27 and Na0.5Bi8.5Ti2Ta4O27 layered ferroelectrics

The influence of the prehistory on the electrical properties of layered ferroelectrics is investigated. It is established that the heating of short-circuited samples of the nonpolarized ceramic material Na_0.5Bi_8.5Ti₂Nb₄O₂₇ leads to the appearance of maxima of the current at temperatures below the Curie point only in the case of preliminary ageing of the samples. Original Russian Text ? A.I. Burkhanov, Yu.V. Kochergin, K. Bormanis, A. Kalvane, M. Dambekalne, 2009, published in Fizika Tverdogo Tela, 2009, Vol. 51, No. 7, pp. 1393–1394.     

Structure and magnetic order in La0.7Ca0.3Mn0.5Co0.5O3 and La0.8Sr0.2Mn0.5Co0.5O3 perovskites

In this paper we report the study of the perovskites La_0.7Ca_0.3Mn_0.5Co_0.5O₃ and La_0.8Sr_0.2Mn_0.5Co_0.5O₃ by neutron powder diffraction at various temperatures and magnetization measurements in zero applied field and at low cooling regimes. The replacement of half Mn by Co in La_0.7Ca_0.3MnO₃ and La_0.8Sr_0.2MnO₃ destroys their long-range ferromagnetism exhibiting a cluster glass ferromagnetic order similar to the one observed in many cobaltites.     

Cross section determination for the reaction K+p → K+pπ+π−π0 and K+π+π+π−n at 8.2 and 16 GeV/c

The cross sections for the reactions: (a) K⁺p → K⁺pπ⁺π^?π⁺ and (b) K⁺p → K⁺π⁺π⁺π^?n have been determined at 8.2 and 16 GeV/c with the following results:at 8.2 GeV/c: (a) 0.99 ± 0.07 mb, (b) 0.41 ± 0.04 mb;at 16 GeV/c: (a) 0.72 ± 0.05 mb, (b) 0.28 ± 0.05 mb.Using the available data at other energies, the cross-section dependence of these reactions on the incident momentum is discussed.     

Phase formation and characterization of Sr3Y2Ge3O12, Sr3In2Ge3O12, and Ca3Ga2Ge3O12 doped by trivalent europium

This work reports on the phase formation during a solid-state reaction of Eu³⁺-doped garnets with the general formula A₃B₂Ge₃O₁₂ (A=Ca, Sr and B=Ga, In, Y) and their luminescent properties. It is shown by XRD and DTA/TG experiments that the garnet-phase formation is completed at 1100-1200 °C. Moreover, it turned out that the position of the oxygen to europium charge-transfer band and the intensity of the forbidden 4f-4f transitions of Eu³⁺ is dependent on the covalent interaction between the Eu³⁺ activator and the surrounding oxygen anions. The investigated red-emitting luminescent materials show high lumen equivalents and deep red emission at the same time, which makes them attractive for the application in LEDs (light emitting diodes), in particular for near UV-emitting LEDs.     

Appearance of an inhomogeneous superconducting state in La0.67Sr0.33MnO3-YBa2Cu3O7-La0.67Sr0.33MnO3 trilayers

An experimental study of proximity effect in La_0.67Sr_0.33MnO₃-YBa₂CU₃O₇-La_0.67Sr_0.33MnO₃ trilayers is reported. Transport measurements on these samples show clear oscillations in critical current (I _c) as the thickness of La_0.67Sr_0.33MnO₃ layers (d _F) is scanned from ∼50 ? to ∼ 1100 ?. In the light of existing theories of ferromagnet-superconductor (FM-SC) heterostructures, this observation suggests a long range proximity effect in the manganite, modulated by its weak exchange energy (∼2 meV). The observed modulation of the magnetic coupling between the ferromagnetic LSMO layers as a function of d _F, also suggests an oscillatory behavior of the SC order parameter near the FM-SC interface.      

Electrical transport and superconductivity in the Al2O3-Bi2Sr1.8Ca1.2Cu2Oy and MgO-Bi2Sr1.8Ca1.2Cu2Oy composites

We have measured the resistivities of Al₂O₃-Bi₂Sr_1.8Ca_1.2Cu₂O_y and MgO-Bi₂Sr_1.8Ca_1.2Cu₂O_y composites with the nominal Bi₂Sr_1.8Ca_1.2Cu₂O_y volume fraction, ₂₂₁₂, ranging from 0.15 to 1.00. For the Al₂O₃-Bi₂Sr_1.8Ca_1.2Cu ₂O_y composites, we find for the samples with ₂₂₁₂≥0.6 that the superconducting transition temperature, T_c, is not disturbed by the addition of Al₂O₃. For ₂₂₁₂<0.3, no zero-resistivity state is observed. For the MgO-Bi₂Sr_1.8Ca_1.2Cu₂O_y composites, T_c is barely disturbed for the samples with ρ₂₂₁₂≥0.7. No superconducting state is observed for the samples with ρ₂₂₁₂<0.35. The variation of (300 K) with ρ₂₂₁₂ indicates a three-dimensional percolating Bi-Sr-Ca-Cu-O matrix occurring at ρ₂₂₁₂≈0.19 and ≈0.15 in Al₂O₃-Bi₂Sr_1.8Ca_1.2 Cu₂O_y and MgO-Bi₂Sr_1.8Ca_1.2Cu₂O_y, respectively. Both resistivity and magnetization measurements suggest that the reactions of Bi₂Sr_1.8Ca_1.2Cu₂O_y with MgO are weaker than with Al₂O₃.     

An investigation of the processes e+e−→μ+μ−γ and e+e−→e+e−γ

The reactions e⁺e^?→μ⁺μ^?γ and e⁺e^?→e⁺e^?γ have been studied with the CELLO detector at the PETRA storage ring. Data have been collected from $\text{s}\text{=14}\text{GeV up to}\text{46.8}\text{GeV}$. In a Dalitz plot analysis of the data, good agreement is found with QED, except for the region Mx_μγe>0.8 where the probability that QED describes the high energy data is at the percent level.     

The ν3 band of 16O12C34S and 16O13C34S

The ν₃ fundamental of OCS has been measured with a resolution of about 0.03 cm^?1 for the isotopic species ¹⁶O¹²C³⁴S and ¹⁶O¹³C³⁴S. The associated transition 01¹1-01¹0 has also been measured. The transition 10⁰1-00⁰0 is also reported for the ¹⁶O¹²C³⁴S species.     

Incommensurate modulations in Ba2TiSi2O8, Sr2TiSi2O8, and Ba2TiGe2O8

Incommensurate modulations in Ba₂TiSi₂O₈, Sr₂TiSi₂O₈, and Ba₂TiGe₂O₈ are compared based on their corresponding electron diffraction patterns. The dependence of the modulations on chemical composition provides a suitable model system for the investigation of incommensurations in framework structures using high-resolution transmission electron microscopy (HRTEM). A widening of quantitative HRTEM utilising the concept of rigid units is proposed allowing for a determination of atomistic displacements responsible for the formation of incommensurately modulated structures.     

X-ray study of phase transitions in the system of solid solutions K2Pb4Nb10O30-Na2Pb4Nb10O30-K6W4Nb6O30

Boundaries of morphotropic phase transitions region in the system of solid solutions K₂Pb₄Nb₁₀O₃₀-Na₂Pb₄Nb₁₀O₃₀-K₆W₄Nb₆O₃₀ with the structure of the tetragonal tungsten bronze have been specified. Presence of the second morphotropic phase transition, perpendicular to the first one has been revealed. The temperature dependences of the structural parameters of some compounds have been investigated. The compounds with high values of Curie temperatures and working temperatures have been obtained.     

Zeros of the π+π− → π+π− amplitude

Recent data on the reaction $\text{p}\text{p}\text{→ π}{}^{\mathrm{?}}\text{π}{}^{\mathrm{+}}$ show four conspicuous dips in the angular distribution at fixed values of ν = t?u. The conjecture is made that the channel π^?π⁺ → π^?π⁺ has zeros at the same ν values. Using data of the CERN-Munich group, one can follow the zeros through the whole Mandelstam plane. The zeros pass through the intersections of s and t channel poles, as the Veneziano model predicts; however, away from these intersections, they propagate in a fashion systematically quite different from Veneziano's ansatz.     

The ν9 + ν11 − ν11, ν10 + ν11 − ν11 hot band system in allene-d4

The hot band system ν₉ + ν₁₁ ? ν₁₁, ν₁₀ + ν₁₁ ? ν₁₁ in allene-d₄ was studied at a resolution near 0.010 cm^?1. About 1500 partly overlapped hot band rotational lines were assigned and fitted to a model taking into account z-Coriolis resonance between the combination levels ν₉ + ν₁₁ and ν₁₀ + ν₁₁ as well as vibrational l-type resonances within these levels. Upperstate constants have been derived from an analysis in which the constants for the ν₁₁ level were constrained. A detailed study of rotational as well as vibrational l-type doublings occurring in the KΔK = ?1 subband is presented, and the sign of vibrational l-type doubling constants for the ν₁₀ + ν₁₁ level is determined. A localized (x, y)-Coriolis resonance between ν₁₀ + ν₁₁ and ν₄(B₁) + ν₁₁ is discussed and the interaction parameter is obtained as well as some constants for ν₄ + ν₁₁.     

BaO-Li2O-B2O3三元系中BaB2O4-Li2B2O4和BaB2O4-Li2O截面相平衡关系的研究

本文用X射线和差热分析方法对BaO-Li₂O-B₂O₃三元系中的两个截面:BaB₂O₄-Li₂B₂O₄和BaB₂O₄-Li₂O作了研究。在BaB₂O₄-Li₂B₂O₄赝二元系中发现了一个新的化合物4BaB₂O₄·Li₂B₂O₄。化合物在930±3℃由包晶反应形成,并与Li₂B₂O₄形成共晶反应。共晶温度为797±3℃,共晶点组分为79mol％Li₂B₂O₄。在BaB₂O₄-Li₂O截面中也存在化合物4BaB₂O₄·Li₂B₂O₄,其包晶反应温度从930±3℃随Li₂O含量增加下降到908±3℃。在组分60mol％Li₂O处形成另一个新的化合物2BaB₂O₄·3Li₂O。该化合物在630±3℃也是由包晶反应形成,并与Li₂O和Li₂CO₃分别形成共晶反应,共晶温度分别为400±3℃和612±3℃。在BaB₂O₄-Li₂B₂O₄和BaB₂O₄-Li₂O体系中都没有观察到固溶体。用计算机程序分别对化合物4BaB₂O₄·Li₂B₂O₄和2BaB₂O₄·3Li₂O的X射线粉末衍射图案进行了指标化,其结果:4BaB₂O₄·Li₂B₂O₄的空间群为Pmma,a=13.033?,b=14.630?,c=4.247?,每个单胞包含两个化合式单位;2BaB₂O₄·3Li₂O的空间群为Pmmm,a=4.814?,b=9.897?,c=11.523?,每个单胞也含有两个化合式单位。 关键词：     

Orbital ordering in Mott-insulators La2O3Fe2Se2 and La2O3Co2Se2

The electronic structure and magnetic properties of new layered oxyselenide compounds La₂O₃Fe₂Se₂ and La₂O₃Co₂Se₂ are studied by first-principles calculations. Our results indicate that both compounds are Mott-insulators with orbital ordering. The ground states of both compounds are the checkerboard antiferromagnetic states, which are different from the iron pnictide superconductors, although their structures are similar to those of the Fe-As-based superconductors.     

Analysis of FTIR spectra of CH2BrCl; the ν4 and ν5 fundamentals and their hot-bands ν4+ν6−ν6 and ν5+ν6−ν6

The infrared spectrum of isotopically pure CH₂⁷⁹BrCl has been recorded at a resolution of 0.0023 cm⁻¹ (FWHM) in the range 550-800 cm⁻¹ with a Bruker IFS 120 HR Fourier transform spectrometer in Wuppertal. Here we report the full rotational analysis of the ν₄ and ν₅ fundamentals and of the hot-bands ν₄+ν₆−ν₆ and ν₅+ν₆−ν₆. Ground state combination differences were constructed for all bands, yielding improved ground state constants, up to quartic terms, as well as reliable rotational constants for the ν₄, ν₅, and ν₆ states.     

High-resolution infrared spectrum of the ν3 and ν2 + ν3 − ν2 bands of 14N16O2

The infrared absorption spectrum of the ν₃ band of ¹⁴NO₂ has been recorded with a resolution and a frequency accuracy much improved over the previous investigations. The K- and N-line assignments have been greatly extended and a more accurate set of spectroscopic constants derived. Several lines in the subbands with K_a ≥ 3 have been observed to be doubled by spin-rotation interaction and spin-rotation interaction constants have been obtained. Several weak series of lines in the spectrum (K_a = 0, 1, 2, and 3) have been unambiguously assigned to the “hot band” ν₂ + ν₃ ? ν₂. Lines of the K_a = 3, 4, 5, and 6 sub-bands of ν₃ have been found to be perturbed by a Coriolis interaction with the K_a = 4, 5, 6, and 7 levels of 2ν₂.