噻吩加氢脱硫和四氢萘催化加氢反应中的载体和助剂的影响

 为了更好地认识加氢脱硫和催化加氢反应中的载体影响和助剂效应，在同样的催化剂制备方法及反应条件下，研究了噻吩加氢脱硫（HDS）和四氢萘催化加氢（HYD）反应．结果表明，对于无助剂的Mo和W催化剂，载体对催化活性的影响顺序为TiO2－Al2O3＞ZrO2＞Al2O3．助剂的添加改变了催化剂活性顺序．Ni助剂催化剂的活性明显高于Co助剂催化剂．ZrO2担载的添加Ni的Mo和W催化剂分别获得了最佳的HDS和HYD活性．然而，添加Pt的Mo和W催化剂其HDS和HYD活性仅是Pt与Mo（W）二者的加和，Pt与Mo（W）之间没有协同效应．先将担载的Mo和W预硫化再将助剂引入体系的催化剂制备方法可以避免Ni和Co过早硫化形成类硫化镍（或硫化钴）物相，与采用螯合物分子方法制备的催化剂间有一定的相似性．     

加氢处理催化剂的制备和表征 Ⅰ.MoNiP/Al2O3催化剂的制备及助剂的作用

 采用专利方法制备出一种新型的γ－Al2O3,并以其为载体,制备出加氢处理催化剂MoNiP／Al2O3．用PAS－CA,XPS,DRS,TPR和微型反应色谱等技术对γ－Al2O3和催化剂进行了表征,考察了Ni和P两种助剂的作用．结果表明,γ－Al2O3具有较大的孔径,集中的孔分布和较高的机械强度;活性金属Mo在γ－Al2O3表面上的化学分散量（分散阈值）可达5．04～5．82μmol／m2．因而特别适合用作高活性加氢处理催化剂的载体．引入的Ni主要是同Mo／Al2O3催化剂表面上较稳定的金属－载体相互作用复合物反应,并生成类NiMoO4化合物;在MoNi／Al2O3催化剂中引入P,有利于抑制四面体配位结构的物种Mo［T］,增加八面体配位结构的物种Mo［O］,改善催化剂的还原性能,从而提高催化剂的加氢处理活性．助剂Ni和P的最佳含量分别为w（Ni）＝4．0％和w（P）＝2．6％．     

Mo助剂含量对Mo-Ni2P/SBA-15/堇青石整体式催化剂加氢脱硫性能的影响

 采用共浸渍法制备了 P/Ni 摩尔比为 2 的 Ni2P/SBA-15, 再通过二次浸渍引入助剂 Mo 制得 Mo-Ni2P/SBA-15, 将它调制成活性胶后均匀涂敷于预处理后的载体表面, 干燥焙烧后在氢气流中采用程序升温还原法, 制备了一系列 Mo-Ni2P/SBA-15/堇青石整体式催化剂. 采用 X 射线衍射、N2 吸附-脱附和 X 射线光电子能谱对催化剂结构进行了表征, 以二苯并噻吩为模型含硫化合物, 考察了催化剂的加氢脱硫性能. 结果表明, Mo 的加入增大了催化剂的比表面积, 在催化剂表面形成了 MoNiP2, 且 Ni2P 为主要活性物相. Mo 在催化剂表面主要以 Mo6+和 Moδ+形式存在; 当 w(Mo) = 4.2% 时, n(Mo)/n(Ni+Mo) = 0.18 的整体式催化剂上二苯并噻吩的转化率最高, 且在较低反应温度时以直接脱硫机理为主, 而较高反应温度时以加氢脱硫机理为主.     

Ni对MoS_2基催化剂活性相及加氢脱氮脱硫性能的影响

为了获得较多高活性II型MoS_2活性相,采用四硫代钼酸铵原位热分解法制备了MoS_2基催化剂,对比分析了Ni源引入方式和热分解气氛对MoS_2活性相微观结构、表面元素化学状态和加氢脱氮脱硫性能等的影响。结果表明,同时引入Mo源和Ni源原位沉淀生成无定形NiMoS_4后,再热分解有利于Ni取代MoS_2片晶边缘的Mo原子,被修饰后的MoS_2片晶保持较高的分散度、适宜的长度(3-5 nm)和堆叠层数(2-4层),从而在边缘暴露较多具有加氢和氢解活性的rim和corner活性位点。热分解气氛H_2比N_2更有利于Ni在热分解过程中取代MoS_2边缘的Mo原子,形成更多II型NiMo-S活性结构,有利于喹啉和二苯并噻吩的吸附活化和加氢反应。当加氢反应温度340℃、氢压3 MPa、重时空速23.4 h~(-1)、氢油比为600和使用0.1 g NMS-H_2催化剂时,喹啉加氢脱氮转化率达23.8%,二苯并噻吩加氢脱硫转化率达93.3%。     

Ni2P加氢脱硫催化剂

环境法规对硫氧化物脱出的限制日益严格以及原油品质的不断下降,使得有必要研发高效的加氢脱硫催化剂。Ni2P由于具有优异的加氢脱硫活性和稳定性,引起了广泛的关注。本文综述了Ni2P加氢脱硫催化剂的特性、反应活性相、制备方法、改进和加氢脱硫活性等方面的研究进展。在Ni2P中存在两种不同的初始活性位,四面体几何构型的Ni(1)初始活性位在加氢脱硫反应中参与直接脱硫反应,四方锥几何构型的Ni(2)初始活性位则与催化剂的高加氢活性有关。在加氢脱硫反应中,催化剂表面生成的NixSyP相被认为是真正的活性相。制备Ni2P的方法主要是程序升温还原和液相合成。载体、助剂和络合剂对Ni2P活性相的形成和催化剂的活性有重要影响。相比于商用硫化物催化剂,Ni2P催化剂对噻吩、二苯并噻吩和4,6-二甲基二苯并噻吩均表现出更高的加氢脱硫活性。     

Ni2P/HZSM5上噻吩加氢脱硫性能研究

采用程序升温还原方法制备了Ni2P/HZSM5催化剂。用X射线衍射 (XRD)、低温N2吸附（BET）、扫描电镜(SEM)等技术对催化剂样品的物相、比表面积、形貌等性质进行了表征。在连续微反系统中测定了Ni2P/HZSM5催化剂对噻吩加氢脱硫催化活性；研究了Ni2P负载量、前驱体中Ni/P摩尔比对催化剂的物相及性能的影响，考察了空速、反应温度、反应压力等操作条件对催化剂上噻吩加氢脱硫性能的影响。实验结果表明，Ni2P/HZSM5催化剂对噻吩加氢脱硫反应具有较高的活性和稳定性。随着Ni2P负载量、前驱体中Ni/P摩尔比的增加，催化剂的活性和稳定性先升高后降低。反应温度和体积空速对Ni2P/HZSM5催化剂的噻吩加氢脱硫性能有较明显的影响，反应压力和进料氢油比的影响相对较小。     

磷对CoMoP浸渍液及催化剂活性组分结构影响的激光拉曼光谱法研究

采用激光拉曼光谱技术(LRS)对CoMoP浸渍液以及浸渍后的样品进行表征,研究了磷含量对CoMoP浸渍液中活性相前躯体结构的影响以及在浸渍后处理过程中对活性相结构的影响.实验结果表明,当CoMoP浸渍液中磷含量较低时,活性组分主要以CoxH6-2x[P2Mo5O23]、CoxH7-2x[PMo11O39]或CoxH3-2x[PMo9O31]以及CoxH3-2x[PMo12O40]结构存在,随着磷添加量的增加,后3种结构转化成CoxH6-2x[P2Mo5O23].提高磷含量有利于抑制活性组分在氧化铝表面分解成七聚钼酸盐.活性组分在载体吸附和催化剂焙烧过程中,在Mo和P之间存在相互作用,[P2Mo5O23]6-结构在焙烧过程中会发生解离.干燥样品经过高温焙烧后,催化剂中出现四面体配位和八面体配位的钼物种.     

加氢脱硫反应后催化剂βMo2N0.78的研究

在对βMo2N0.78催化剂加氢脱硫催化性能进行考察的基础上，对反应使用后催化剂的组成、结构变化、以及反应后催化剂再处理对活性的影响等几方面进行了研究。结果表明，在噻吩加氢脱硫条件下，βMo2N0.78 催化剂的氮含量下降，表层被硫化，而且钝化过程中产生的氮氧化物被消耗，但体相结构没有发生变化，表现了较强的抗硫化性能；脱硫反应前后催化剂的氢还原处理不能改善催化剂的活性，但预硫化催化剂在反应起始的活性与钝化催化剂在反应稳定时活性相近，加氢脱硫反应后催化剂的再次氮化处理，可以较大程度的恢复催化剂的初始活性。     

助剂镍/钴对磷化钨催化剂加氢精制性能的影响

在共浸渍法制备磷化钨／γ-Al2O3催化剂基础上，分别加人1％、3％、5％、7％和9％(占活性组分比例)的助剂镍或钴，制得负载30％含助剂镍／钴磷化钨／γ-Al2O3系列催化剂，考察了助剂及其加人比例对催化剂加氢脱硫和加氢脱氮性能的影响．结果表明，加人适当比例的助剂镍或钴，有利于提高磷化钨／γ-Al2O3催化剂的加氢脱硫活性，当助剂含量分别为5％镍或7％钴时，催化剂的噻吩加氢脱硫率最高；助剂镍对磷化钨／γ-Al2O3催化剂的加氢脱氮反应不利，而加人适当比例助剂钴有利于提高催化剂加氢脱氮活性，当助剂钴含量为5％时，催化剂吡啶加氢脱氮率最高．温度对磷化钨／γ-Al2O3催化剂加氢精制性能有一定影响，高温有利于加氢脱硫反应，低温有利于加氢脱氮反应．     

磷含量对NiMo/γ-Al_2O_3催化剂活性相结构的影响

采用程序升温还原(TPR)、高分辨透射电镜(HRTEM)和X射线光电子能谱(XPS)表征手段对共浸渍法制备的不同磷含量NiMo/γ-Al2O3催化剂进行了表征,研究了磷含量对NiMo/γ-Al2O3催化剂活性相结构的影响。TPR研究表明,磷能够减少四面体配位Mo物种的数量,增加八面体配位Mo物种的数量,促进高活性Ⅱ型"Ni-Mo-S"活性相的形成。HRTEM研究表明,随磷含量的增加,MoS2颗粒堆积层数增加,催化剂的加氢选择性提高;适量磷能够增加边角位有效Mo原子的分散度(fMo),增加催化剂表面加氢脱硫(HDS)和加氢脱氮(HDN)活性位的数量。上述结论得到了XPS表征的证实:适量磷增加了催化剂表面Mo原子浓度、提高有效助剂比率(PR)和提升比率(Ni/Mo),相应催化剂表现出最高的HDS和HDN活性;但过高磷含量能够引起MoS2颗粒过度堆积,片层长度过长,导致活性位数量减少,催化活性降低。     

磷含量对NiMo/γ-Al2O3催化剂活性相结构的影响

采用程序升温还原（TPR）、高分辨透射电镜（HRTEM）和X射线光电子能谱（XPS）表征手段对共浸渍法制备的不同磷含量NiMo/γ-Al₂O₃催化剂进行了表征,研究了磷含量对NiMo/γ-Al₂O₃催化剂活性相结构的影响。TPR研究表明,磷能够减少四面体配位Mo物种的数量,增加八面体配位Mo物种的数量,促进高活性Ⅱ型"Ni-Mo-S"活性相的形成。HRTEM研究表明,随磷含量的增加,MoS₂颗粒堆积层数增加,催化剂的加氢选择性提高;适量磷能够增加边角位有效Mo原子的分散度(fMo),增加催化剂表面加氢脱硫（HDS）和加氢脱氮（HDN）活性位的数量。上述结论得到了XPS表征的证实：适量磷增加了催化剂表面Mo原子浓度、提高有效助剂比率（PR）和提升比率（Ni/Mo）,相应催化剂表现出最高的HDS和HDN活性;但过高磷含量能够引起MoS₂颗粒过度堆积,片层长度过长,导致活性位数量减少,催化活性降低。     

MoNiP/Al2O3加氢脱氮催化剂的研究:金属分散状态对催化剂活性的影响

采用ＰＡＳＣ Ａ，ＸＰＳ，ＳＴＥＭ和微型反应色谱等技术，研究了一系列ＭｏＮｉＰ／Ａｌ２Ｏ３催化剂表面活性组分的分散状态及其对催化剂ＨＤＮ反应活性的影响。     

Synthesis of Ni2P promoted trimetallic NiMoW/γ-Al2O3 catalysts for diesel oil hydrotreatment

The Ni2P promoted and γ-Al2O3 supported NiMoW sulfide catalyst consisting of 4 wt% Mo, 22 wt% W, 2 wt% Ni and 2.5 wt% Ni2P was synthesized by a co-impregnation method. The catalysts were characterized by N2 adsorption-desorption, X-ray diffraction (XRD), diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy, NH3 temperature-programmed desorption (NH3-TPD) and transmission electron microscopy (TEM). The results showed that Ni2P, Ni, Mo and W species were highly dispersed over γ-Al2O3. The hydrodesulfurization (HDS) of dibenzothiophene (DBT) showed that the presence of Ni2P brought a strong promotional effect on the HDS activity, which was further confirmed by the HDS and hydrodenitrogenation (HDN) of diesel oil under industrial conditions. The enhancement in HDN activity and stability by Ni2P addition could be attributed more to the effect of new active sites of Ni2P than that of acidity modification. The as-prepared Ni2P-NiMoW/γ-Al2O3 catalyst showed better hydrotreating performance than NiMoW/γ-Al2O3 and commercial catalysts.     

Hydrothermal synthesis, structure and quantum chemistry of transition metal complex supported by metal-oxo cluster [{Ni(phen)2}2(x-Mo8O26)]

A nickel-1,10-phenanthroline complex supported on an octamolybdate, [{Ni(phen)2}2(x- Mo8O26)], has been hydrothermally synthesized with MoO3, H2MoO4, Ni(OAc)2· 6H2O and 1,10-phenathroline (1,10-phen) as raw materials. The crystals of the compound belong to monoclinic P21/n space group, a = 1.2952(2), b = 1.6659(10), c = 1.3956(12) nm, b =106.273(8)°, V = 2.8906(5) nm3, Z = 2. 5604 observable reflections (I ＞2s(I)) were used for structure resolution and refinements to converge to final R1 = 0.0414, wR2 = 0.0815. The result of structure determination shows that the compound contains octamolybdate possessing a novel structure type (named as x-isomer). The feature of x-[Mo8O26]4- is that it is composed of Mo6O6 ring and two MoO6 octahedra located at cap positions on opposite faces. The Mo6O6 ring contains two octahedral and four trigonal-bipyramidal MoVI atoms. Each x-[Mo8O26]4- unit is bonded with two [Ni(phen)2]2+ through terminal oxygen atoms of octahedral and neighbouring trigonal-bipyramidal Mo atom in the Mo6O6 ring. IR and UV-Vis spectra of the compound were measured and its electronic structure was studied by EHMO method.     

Mo（W）－Co（Ni，Fe）簇合物的加氢脱硫催化活性

对线型、立方烷型和笼状３种不同构型的Ｍｏ（Ｗ）－Ｃｏ（Ｎｉ，Ｆｅ）－Ｓ（Ｏ）簇共１２种化合物进行了噻吩加氢脱硫和环己烯加氢的催化活性研究．讨论了簇合物的组成，金属原子的配比、价态与催化活性的关系．探讨了不同构型对活性的影响．     

镍钼杂多酸制备NiMo/γ-Al2O3催化剂及硼、钴或镍改性氧化铝的影响（英文）

A hydrotreating NiMo/γ-Al2O3 catalyst(12 wt% Mo and 1.1 wt% Ni) was prepared by impregnation of the support with the Anderson-type heteropolyoxomolybdate(NH4)4Ni(OH)6Mo6O18.Before impregnation of the support,it was modified with an aqueous solution of H3BO3,Co(NO3)2,or Ni(NO3)2.The catalysts were investigated using N2 adsorption,O2 chemisorption,X-ray diffraction,UV-Vis spectroscopy,Fourier transform infrared spectroscopy,temperature-programmed reduction,temperature-programmed desorption,and X-ray photoelectron spectroscopy.The addition of Co,Ni,or B influenced the Al2O3 phase composition and gave increased catalytic activity for 1-benzothiophene hydrodesulfurization(HDS).X-ray photoelectron spectroscopy confirmed that the prior loading of Ni,Co or B increased the degree of sulfidation of the NiMo/γ-Al2O3 catalysts.The highest HDS activity was observed with the NiMo/γ-Al2O3 catalyst with prior loaded Ni.     

Mo-Ni2P/SBA-15催化剂的制备、表征及加氢脱硫催化性能

以介孔分子筛SBA-15 为载体, 通过分步浸渍硝酸镍、磷酸氢二铵、钼酸铵, 然后在H₂气流下程序升温还原(H₂-TPR), 制备了一系列不同Mo 含量的Mo-Ni₂P/SBA-15 催化剂. 采用X 射线衍射(XRD)、氮气吸脱附(BET)、透射电子显微镜(TEM)和X射线光电子能谱(XPS)对催化剂的结构进行了表征, 评价了催化剂对二苯并噻吩(DBT)的加氢脱硫(HDS)活性. 结果表明, Mo-Ni₂P/SBA-15 催化剂仍然保留有介孔结构, 催化剂的物相主要是Ni₂P. 催化剂表面的Ni 以Ni^δ+和Ni²⁺形式存在; P以P^δ-和P⁵⁺形式存在; Mo以Mo^δ+和Mo⁶⁺形式存在. Mo能促进催化性能的提高, 其中Mo含量为1% (w, 质量分数)的Mo-Ni₂P/SBA-15 催化剂具有最好的二苯并噻吩加氢脱硫催化活性, 在反应温度为380 ℃, 反应压力为3.0 MPa的条件下, 二苯并噻吩的转化率可达99.03%, 所有考察的Mo-Ni₂P/SBA-15都以直接加氢脱硫(DDS)途径为主.     

Al-Ni2P/SBA-15催化剂的制备、表征及加氢脱硫催化性能

以磷酸氢二铵为磷源,硝酸镍为镍源,硝酸铝为助剂铝源,制备了n_P/n_Ni=0.8,Al含量为1.06wt%~6.35wt%的一系列Al-Ni₂P/SBA-15催化剂。采用XRD、TEM和N₂吸脱附等技术对催化剂的结构进行了表征研究,以二苯并噻吩(DBT)作为模型化合物,在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价。结果表明,Al修饰的Al-Ni₂P/SBA-15催化剂仍然保持介孔结构,当Al含量低于5.29wt%时,催化剂的物相主要是Ni₂P,当Al含量在5.29wt%-6.35wt%之间时,催化剂的物相为Ni₂P和Ni₁₂P₅。Al含量为4.24wt%的3-Al-Ni₂P/SBA-15催化剂具有最好的二苯并噻吩加氢脱硫催化活性,在反应温度为360 ℃,反应压力为3.0 MP的条件下,3-Al-Ni₂P/SBA-15催化剂对二苯并噻吩的转化率可达99.0%。     

负载型TiO2-Al2O3复合载体在超深度加氢脱硫中的应用

运用HRTEM、FT-Raman、TPR等方法表征了Mo活性组分在负载型TiO2-Al2O3复合载体和Al2O3上不同形态和性质。比较了TiO2-Al2O3复合载体同传统Al2O3载体对CoMo催化剂结构的影响,并以4,6-二甲基二苯并噻吩（4,6-DMDBT）为探针考察了催化剂的超深度加氢脱硫（UHDS）性能。结果表明,在负载型TiO2-Al2O3复合载体中, MoO3同载体之间的相互作用较弱,这种弱的相互作用使MoO3更多的以八面体配位Mo物种（MoⅥ）及其二维的聚合物的形式存在。二维聚合物有利于形成具有更高活性的多层MoS2结构,明显提高催化剂的超深度加氢脱硫催化活性。