V_2O_5/C电化学电容器有机电解液的性能研究

以偏钒酸铵为反应原料,采用液相沉淀法制备出不定型V2O5电极材料.以V2O5为正极,石墨为负极,分别选用1.0 mol/L LiClO4/EC+DMC、1.0 mol/L LiPF6/EC+DEC+DMC、1.6 mol/L Et4NBF4/AN 3种有机电解液组成不对称电化学电容器,恒流充放电、循环伏安和交流阻抗等测试该模拟电容器,如以1.0 mol/LLiClO4/EC+DMC作电解液则具有良好的循环性能和较小的阻抗,且在500 mA/g电流密度下比能量达到8.4Wh/kg,充放电效率达98%.     

Li_4Ti_5O_(12)纳米片的合成及储锂性能研究

以无定形的水合二氧化钛为前驱物,水热法合成了200～400nm大小的Li4Ti5O12纳米片作为锂离子电池负极材料.XRD(X射线衍射)、SEM(扫描电子显微镜)和TEM(透射电镜)分析表征样品的物相结构、表观形貌;循环伏安、充放电循环和电化学交流阻抗技术分别测定该纳米Li4Ti5O12在有机电解液和室温离子液体S114TFSI电解液中的电化学性能.结果表明,该材料具有较高的放电容量和良好的循环性能,有望成为锂二次电池新型负极材料.     

LiBOB-PC/DEC电解液性质研究

合成锂离子电池新型电解质锂盐L iBOB,并与PC/DEC溶剂配成电解液.室温下研究了L iBOB-PC/DEC电解液电导率随锂盐浓度的变化规律及其用于L i/ARG电池充放电循环性能的最佳组成配比,为0.5mol.L-1L iBOB-PC/DEC(3∶7).应用交流阻抗和循环伏安法研究了该最佳电解液的电化学性质及其电极/界面状态,结果显示,石墨电极在这种电解液中可形成良好的SEI膜.     

离子液体/凝胶聚合物电解质的制备及其与LiFePO_4的相容性

以1-甲基-3-乙基咪唑六氟磷酸盐(EMIPF6)、聚偏氟乙烯-六氟丙烯(P(VDF-HFP))和六氟磷酸锂(LiPF6)为原料,采用溶液浇铸法制备了离子液体/凝胶聚合物电解质(ILGPE).通过循环伏安(CV)、计时电流法、恒流充放电、电化学阻抗法(EIS)研究了该电解质的离子传输特性以及与锂离子电池正极材料LiFePO4的相容性.结果表明,离子液体/凝胶聚合物电解质的室温电导率为1.650×10-3S·cm-1,电化学稳定窗口达到5.0V.在充放电循环过程中,电极表面形成的钝化膜改善了锂离子脱、嵌可逆性和电极/电解质的界面性质.     

LiNi_(0.8-y)Ti_yCo_(0.2)O_2电极材料中钛离子掺杂作用机理的研究

应用恒流充放电、非现场X射线粉末衍射 (ex situXRD)、电化学交流阻抗 (EIS)、程序控温脱附 质谱联用(TPD MS)等实验方法研究LiNi0. 8-yTiyCo0. 2O2电极材料钛离子的掺杂作用机理.结果表明,掺钛后的电极材料于充放电过程中的结构相变和晶格的膨胀收缩受到抑制,在高电位下的界面反应活性减弱,从而减小了由结构变化和界面反应引起的容量损失;同时,钛的掺杂增强了电极材料在脱锂状态下的结构稳定性,抑制了电极材料和电解液的分解或氧化反应,以上两个方面分别改善并提高了电极材料的充放电循环性能及其热稳定性.     

LiBOB对Li_(1.15)Ni_(0.68)Mn_(1.32)O_4电极电化学行为的影响

采用恒电流充放电技术研究了锂离子电池电解液添加剂双草酸硼酸锂(Li BOB)对Li1.15Ni0.68Mn1.32O4电极电化学性能的影响,用X射线衍射(XRD)、衰减全反射傅里叶变换红外光谱(FTIR-ATR)、电感耦合等离子体发射光谱(ICP)、扫描电子显微镜(SEM)和电化学阻抗谱(EIS)分析了Li BOB对Li1.15Ni0.68Mn1.32O4电极性能的影响.结果显示,Li BOB作为电解液添加剂能显著改善Li1.15Ni0.68Mn1.32O4电极的循环性能,原因是Li BOB在充放电过程中会在Li1.15Ni0.68Mn1.32O4电极表面发生分解,分解产物在电极表面沉积形成固体电解质界面(SEI)膜,SEI膜能够有效抑制Li1.15Ni0.68Mn1.32O4电极材料中Mn的溶解,确保其晶体结构的稳定性,从而提高Li1.15Ni0.68Mn1.32O4电极的循环性能.     

五种1-烷基-2,3-二甲基咪唑型离子液体的合成及作为Li/LiFeO_4电池电解液的研究

合成了五种新的1-烷基-2,3-二甲基咪唑二(三氟甲基磺酰)亚胺离子液体(alkyl-DMimTFSI).以离子液体作为Li/LiFeO4电池电解液,分别考察不同烷基(正丁基、正戊基、正辛基、异辛基和正癸基)对电解液理化性质、界面性质和电池行为的影响.结果表明离子液体的电化学窗口都可以达到5.6V(-0.4～5.2Vvs.Li+/Li),显示它们具有较好的电化学稳定性.加入碳酸亚乙烯酯作为添加剂后,离子液体电解液在Li负极形成稳定的固体电解质相界面膜(SEI),从而提高了Li负极的稳定性,保护了Li片不受腐蚀.电化学阻抗和循环伏安分析进一步揭示LiFeO4正极与离子液体电解液也有良好的兼容性.此外,研究还表明离子液体中烷基种类严重影响它们的电池行为.采用butyl-DMimTFSI和amyl-DMimTFSI电解液体系的电池充放电容量和可逆性明显优于另外三种离子液体,它们的首次放电容量分别达到145和152.6mAh/g,并表现出良好的充放电循环性能.因粘度最大,采用isooctyl-DMimTFSI电解液的电池首次放电容量仅为8.3mAh/g,但添加碳酸丙烯酯(质量比1∶1)稀释后首次放电容量上升至132.4mAh/g.     

MnO_2/C复合材料的电化学电容特性研究

应用乙炔黑直接还原高锰酸钾制备MnO2/C复合材料.样品结构及性能由XRD和SEM表征.研究了MnO2/C电极(正极)在不同电解液中的法拉第"准电容行为",及其循环伏安、交流阻抗与恒电流充放电等性能.实验表明,MnO2/C复合材料具有良好的电化学电容特性.在1 mol/L的KOH电解液中和电流密度为5 mA/cm2下,MnO2/C复合材料的比电容量可达258 F/g,并表现出良好的循环性能.     

温度对尖晶石LiMn2O4中锂离子嵌脱过程的影响

运用电化学阻抗谱研究了商品化尖晶石LiMn₂O₄电极在1 mol/L LiPF₆-EC(碳酸乙烯酯):DEC(碳酸二乙酯)电解液中―10～30 ℃范围内的阻抗谱特征、固体电解质相界面(SEI)膜阻抗、电子电阻和电荷传递电阻等随温度的变化. 研究结果表明, 尖晶石LiMn₂O₄电极的阻抗谱特征与温度有关, 随温度的升高, 与活性材料电子电导率相关的半圆和与SEI膜相关的半圆会发生重叠而成为一个半圆. 通过选取适当的等效电路拟合了实验所得的电化学阻抗谱数据, 测得尖晶石LiMn₂O₄电极在1 mol/L LiPF₆-EC:DEC 电解液中, 锂离子迁移通过SEI膜的离子跳跃能垒平均值为15.49 kJ/mol; 电子电导率的热激活化能平均值为24.21 kJ/mol; 嵌入反应活化能平均值为53.07 kJ/mol.     

哌啶型离子液体混合电解液在Li/LiCoO2电池中的性能研究

合成并考察了N-甲基-N-乙（丙,丁）基哌啶-二( 三氟甲基磺酰) 亚胺三种离子液体( PP12（3,4）TFSI )作为电解液添加剂的影响. 使用热分析和电化学技术研究了离子液体混合电解液的热稳定性和电化学性能.实验表明,哌啶型离子液体可以提高有机电解液的热稳定性,并且侧链的长短对 LiCoO₂ 电极的电化学性能有重要的影响.当以PP13TFSI配成的混合电解液,在3.0~4.35 V之间、电流密度为150 mA•g^-1时, LiCoO₂ 电极的首次放电容量为156.6 mAh•g^-1,200周循环后容量为133.9mAh•g^-1,容量保持率为85.5%,远远优于在传统有机电解液中的循环性能.     

Temperature effects on the electrochemical behavior of spinel LiMn(2)O(4) in quaternary ammonium-based ionic liquid electrolyte

Temperature dependence of the physiochemical characteristics of a room-temperature ionic liquid consisting of trimethylhexylammonium (TMHA) cation and bis(trifluoromethane) sulfonylimide (TFSI) anion containing different concentrations of LiTFSI salt was examined. Electrochemical properties of a spinel LiMn(2)O(4) electrode in 1 M LiTFSI/TMHA-TFSI ionic electrolyte were investigated at different temperatures by using cyclic voltammetry, galvanostatic measurements, and electrochemical impedance spectroscopy. The Li/ionic electrolyte/LiMn(2)O(4) cell exhibited satisfactory electrochemical properties with a discharge capacity of 108.2 mA h/g and 91.4% coulombic efficiency in the first cycle under room temperature. At decreased temperature, reversible capacity of the cell could not attain a satisfactory value due to the high internal resistance of the cell and the large activation energy for lithium ion transfer through the electrode/electrolyte interface. Anodic electrolyte oxidation results in the decrease of coulombic efficiency with increasing temperature. Irreversible structural conversion of the spinel LiMn(2)O(4) in the ionic electrolyte, possibly associated with the formation of TMHA intercalated compounds and/or Jahn-Teller distortion, was considered to be responsible for the electrochemical decay with increasing cycles.     

电解液组成对尖晶石LiMn_2O_4中锂离子嵌脱过程的影响

运用电化学阻抗谱(EIS)研究了尖晶石LiMn2O4正极在1mol·L-1LiPF6-EC(碳酸乙烯酯)∶DEC(碳酸二乙酯)∶DMC(碳酸二甲酯),1mol·L-1LiPF6-EC∶DEC∶EMC(碳酸甲乙酯)和1mol·L-1LiPF6-EC∶DMC三种不同电解液中,-20-20℃范围内的阻抗谱特征随温度的变化.研究结果表明,温度强烈影响尖晶石LiMn2O4正极的阻抗谱特征,而电解液组成对尖晶石LiMn2O4正极阻抗谱特征的影响较小,但电解液组成对锂离子在尖晶石LiMn2O4正极中嵌入脱出过程相关动力学参数影响较大.测得尖晶石LiMn2O4正极在上述三种电解液中,锂离子迁移通过固体电解质相界面(SEI)膜的离子跳跃能垒平均值分别为7.60、16.40和18.40kJ·mol-1;电子电导率的热激活化能平均值分别为44.77、35.47和68.06kJ·mol-1;嵌入反应活化能平均值分别为52.19、46.19和69.86kJ·mol-1.     

尖晶石锂锰氧化物电极首次脱锂过程的EIS研究

研究了尖晶石锂锰氧化物电极首次脱锂过程中的电化学阻抗特征. 通过选取适当的等效电路拟合实验所得的电化学阻抗谱数据, 获得了首次脱锂过程中固体电解质相界面膜(SEI膜)的电阻、电容以及电荷传递电阻、双电层电容等随电极极化电位的变化规律.     

Impedance Studies of Spinel LiMn2O4 Electrode/electrolyte Interfaces

The formation process of solid electrolyte interphase（SEI） film on spinel LiMn2O4 electrode surface was studied by electrochemical impedance spectroscopy（EIS） during the initial storage in 1 mol/L LiPF6-EC：DMC：DEC electrolyte and in the subsequent first charge-discharge cycle. It has been demonstrated that the SEI film thickness increased with the increase of storage time and spontaneous reactions occurring between spinel LiMn2O4 electrode and electrolyte can be prevented by the SEI film. In the first charge-discharge cycle succeeding the storage, the electrolyte oxidation coupled with Li-ion insertion is evidenced as the main origin to increase the resistance of SEI film. The results also confirm that the variations of the charge transfer resistance（Rot） with the electrode potential（E） can be well described using a classical equation.     

尖晶石LiMn2O4锂充放电池的电化学研究

本文报导尖晶石型ＬｉＭｎ２Ｏ４化合物的制备方法，用循环伏安法和交流阻抗技术研究了Ｌｉ／有机电解液／ＬｉＭｎ２Ｏ４电池的电化学行为，用分形理论首次考察和进一步讨论电极材料的阻抗行为随锂离子嵌入或脱嵌电极时的变化。     

LiMn2O4正极在高温下性能衰退现象的研究

采用恒流充放电方法测量了温度升高导致ＬｉＭｎ２Ｏ４正极容量衰减的情况。发现当环境温度上升到５０℃时,ＬｉＭｎ２Ｏ４电极出现严重的容量损失和性能衰退,充电态的电极受影响的程度最为严重。对电解液的原子发射和红外光谱分析,电极晶相结构Ｘ－射线衍射及循环伏安实验速增加,电解液出现催化氧化是导致容量不可逆衰砬的原因。采用富锂尖晶石材料是抑制ＬｉＭｎ２Ｏ４高温性能下降的一种有效方法。     

正尖晶石LiMn_2O_4电化学性能研究

采用高温固相反应合成了尖晶石LiMn2 O4 锂离子电池正极材料 ,并对其性能进行研究 .综合考察了影响材料电化学性能的主要因素 ,诸如原材料的选择、合成温度、Li/Mn比以及添加金属元素Co等 .研究了材料在高温下的电化学性能和影响因素 ,并分析了LiMn2 O4 在电解质中的溶解和引起容量衰减的原因     

尖晶石LiMn_2O_4高温电化学容量衰减及改进

综述了高温下尖晶石ＬｉＭｎ２Ｏ４容量衰减的原因、机理研究和改进它的高温性能的方法以及目前的进展,且指出了可能的提高它的高温性能的途径。     

尖晶石LiMn2O4中锂离子嵌入脱出过程的电化学阻抗谱研究

运用电化学阻抗谱(EIS)研究了尖晶石LiMn2O4电极的首次充放电过程. 发现EIS谱高频区域拉长压扁的半圆是由两个半圆相互重叠而成的, 分别归属于与锂离子通过固体电解质相界面膜(SEI膜)的迁移和与尖晶石LiMn2O4材料的电子电导率相关的特征. 通过选取适当的等效电路, 对实验所得的电化学阻抗谱数据进行拟合, 获得尖晶石LiMn2O4电极首次充放电过程中SEI膜电阻、电子电阻和电荷传递电阻等随电极极化电位变化的规律. 根据研究结果提出了嵌锂物理机制模型.     

Li_3PO_4包覆LiMn_2O_4正极材料的结构表征和电化学性能

采用共沉淀法在尖晶石LiMn2O4颗粒表面包覆Li3PO4.XRD、SEM研究结果表明,包覆后的材料仍为尖晶石结构,粒径均匀.电化学性能测试表明,Li3PO4包覆层的存在,减少了正极材料与电解液的直接接触,抑制了高温下电解液对LiMn2O4材料的侵蚀,从而有效改善了高温下材料的循环性能.在40℃时,包覆样品的比容量衰减率都低于未包覆样品,其中包覆1%Li3PO4的样品的初始比容量为110.4mAh/g,50次循环后比容量为84.1mAh/g.