CdTe/CdS共敏化TiO2电极材料的制备与光电性能

将电沉积法和化学浴沉积法结合,分别将CdTe和CdS量子点纳米晶材料引入到TiO_2纳米管阵列上制备CdTe/CdS量子点共敏化TiO_2光电极。利用扫描电镜、X射线衍射和X射线能量色散光谱等测试手段对所得样品的形貌、晶型和组分进行表征。在模拟太阳光照射条件下,通过电化学工作站测试其光电化学性能。研究结果表明,相对于单一量子点敏化CdS/TiO_2和CdTe/TiO_2光电极而言,共敏化CdTe/CdS/TiO_2光电极表现出更好的光电转化性能,短路电流密度和光电转换效率分别可以达到3.1 m A·cm~(-2)和1.85%。此外,采用电化学阻抗测试技术对材料性能提升的原因进行深入的探究。     

CdTe/CdS共敏化TiO2电极材料的制备与光电性能

将电沉积法和化学浴沉积法结合,分别将CdTe和CdS量子点纳米晶材料引入到TiO₂纳米管阵列上制备CdTe/CdS量子点共敏化TiO₂光电极。利用扫描电镜、X射线衍射和X射线能量色散光谱等测试手段对所得样品的形貌、晶型和组分进行表征。在模拟太阳光照射条件下,通过电化学工作站测试其光电化学性能。研究结果表明,相对于单一量子点敏化CdS/TiO₂和CdTe/TiO₂光电极而言,共敏化CdTe/CdS/TiO₂光电极表现出更好的光电转化性能,短路电流密度和光电转换效率分别可以达到3.1 mA·cm^-2和1.85%。此外,采用电化学阻抗测试技术对材料性能提升的原因进行深入的探究。     

三维有序结构In掺杂TiO_2薄膜的可见光催化活性

采用自组装生长聚苯乙烯胶体模板和溶胶-凝胶法,制备出三维(3D)有序结构In掺杂TiO2(IO-TiO2-In)薄膜可见光催化剂.光催化实验证明,IO-TiO2-In薄膜降解甲醛的可见光活性是TiO2和三维有序结构TiO2(IOTiO2)薄膜的5倍.利用X射线电子衍射(XRD)谱、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)和紫外-可见(UV-Vis)漫反射吸收光谱确定了催化剂的晶相结构、表面微结构和能带结构.结果表明,IO-TiO2-In薄膜具有锐钛矿型三维有序结构,与TiO2相比,增加了比表面积,提高光的利用率;掺入的In离子在薄膜表面形成In2O3和O-In-Clx(x=1,2)物种,既增强可见光的吸收,又有效地促进了光生载流子的分离,提高了光生载流子在固/气界面参加光催化反应的利用率,使催化剂的可见光催化活性显著提高.     

Gd-N共掺杂SrTiO3/TiO2复合纳米纤维制备及光催化性能

以静电纺丝技术制备的TiO_2纳米纤维为基质和反应物,结合一步水热法制得Gd-N共掺杂SrTiO_3/TiO_2复合纳米纤维光催化剂。利用X射线衍射(XRD)、扫描电子显微镜(SEM)、高分辨透射电镜(HRTEM)、X射线光电子能谱(XPS)、紫外-可见漫反射(UV-Vis DRS)和荧光光谱(PL)等方法对其微观结构、形貌和光学性能进行表征。结果表明:SrTiO_3和TiO_2形成异质结能够使光生电子和空穴得到很好的分离,而Gd-N共掺杂产生新带隙,可以拓宽光谱响应范围至可见光区,并引起晶格缺陷,成为光生电子-空穴对的浅势捕获阱。Gd-N共掺杂与异质结的协同作用有效提高了SrTiO_3/TiO_2复合纳米纤维的可见光催化活性。     

TiO2纳米管阵列光电催化氧化处理氨氮废水

用电化学阳极氧化法制备了高度有序的钛基二氧化钛纳米管阵列薄膜。用场发射扫描电镜(FE-SEM)、X射线衍射(XRD)表征样品的形貌与晶型特征。以二氧化钛纳米管阵列为光阳极,石墨为对电极,测试了不同pH值和外加偏压条件下的光电流响应和光电催化氧化降解NH4Cl水溶液(以N计,100 mg·L-1)的效率。结果表明:所制备的TiO2纳米管阵列具有锐钛矿和金红石的混晶结构,且主要晶型为锐钛矿。光电流响应的强弱与光电催化氧化效率的高低相对应,降解氨氮废水的最佳条件为pH=11,偏压为1.0 V。     

不同形貌Bi4Ti3O12粒子的可控合成及光催化性能

研究了用一步水热法制备的不同形貌的钛酸铋(Bi₄Ti₃O₁₂, BIT)粒子的光学和可见光催化性能, 并对其晶体结构和微观结构用X射线衍射(XRD)、场发射扫描电子显微镜(FESEM)、透射电子显微镜(TEM)和高分辨透射电子显微镜(HRTEM)等手段进行了表征. XRD结果表明, 所制备的BIT 样品为层状钙钛矿结构. FESEM结果表明, 通过控制水热过程的反应参数可以得到不同形貌的纳米粒子. 紫外-可见漫反射光谱(UV-Vis DRS)表明BIT 样品的带隙能约为2.88-2.93 eV. 利用可见光(λ>420 nm)照射下的甲基橙(MO)降解实验评价了BIT 样品的光催化性能. 结果表明, BIT 的光催化活性比掺氮TiO₂ (N-TiO₂)高得多. 研究了形貌对BIT 光催化性能的影响. 所制备的BIT纳米带光催化效率最高, 经可见光照射360 min, 甲基橙溶液的降解率可达到95.0%.     

玻璃微珠/Ag/TiO2可见光催化剂的制备与表征

通过离子交换法将Ag纳米颗粒负载于玻璃微珠的表面及浅表层,并以钛酸四丁酯的乙醇溶液为前驱体,将TiO₂负载于包含银的玻璃微珠表面,制得一种玻璃微珠/Ag/TiO₂复合光催化剂。由于纳米银的表面等离子体吸收效应,该复合光催化剂具有一定的可见光响应特性。利用XRD、SEM对样品进行表征,可发现玻璃微珠表面形成一层均匀多孔的锐钛矿TiO₂,其粒径均在50 nm左右。由漫反射光谱可得出该催化剂具有较强的可见光吸收,并在降解甲基橙溶液的试验中表现出较好的可见光催化活性。     

TiO2/Cu2O/Pt复合空心微球的制备及其光催化性能

以锐钛矿相TiO₂溶胶为基底,采用沉淀法和液相沉积法制备了TiO₂/Cu₂O/Pt复合空心微球,通过改变n₍Ti⁴⁺)∶n_Cu2+和H₂Pt Cl₆·6H₂O溶液的加入量对TiO₂的形貌和结构进行调控,采用不同的方法对不同样品的物相及结构、微观形貌和光学性能进行了对比分析。分析结果表明,复合材料中Pt与Cu₂O的引入产生协同效应,不仅在一定程度上阻止了电子-空穴的复合,还降低了禁带宽度,在可见光区域光吸收明显增强。与TiO₂、Cu₂O和TiO₂/Cu₂O光催化剂相比较,TiO₂/Cu₂O/Pt降解有机污染物的能力显著增强,首次光照120 min可降解93%的甲基橙(MO)溶液,4次循环后降解率为71%,具有良好的光催化...     

TiO2/Cu2O/Pt复合空心微球的制备及其光催化性能

以锐钛矿相TiO₂溶胶为基底,采用沉淀法和液相沉积法制备了TiO₂/Cu₂O/Pt复合空心微球,通过改变n_Ti⁴⁺∶ n_Cu²⁺和H₂PtCl₆·6 H₂O溶液的加入量对TiO₂的形貌和结构进行调控,采用不同的方法对不同样品的物相及结构、微观形貌和光学性能进行了对比分析。分析结果表明,复合材料中Pt与Cu₂O的引入产生协同效应,不仅在一定程度上阻止了电子-空穴的复合,还降低了禁带宽度,在可见光区域光吸收明显增强。与TiO₂、Cu₂O和TiO₂/Cu₂O光催化剂相比较,TiO₂/Cu₂O/Pt降解有机污染物的能力显著增强,首次光照120 min可降解93%的甲基橙(MO)溶液,4次循环后降解率为71%,具有良好的光催化稳定性能。     

Preparation of porous TiO2/silica composites without any surfactants

TiO₂-SiO₂ composites, with high specific surface area (up to 308 m²/g), large pore volume, and narrow distribution with average pore sizes of 3.2 nm, have been synthesized from wollastonite and titanium sulfate in the absence of any surfactants. Calcium sulfate, a microsolubility salt, plays an important role in the formation of pores in this porous TiO₂/silica composite. The microstructure and chemical composition of composite were characterized by X-ray diffractometry (XRD), transmission electron microscopy (TEM) equipped with energy-dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectrometer (XPS) and N₂ adsorption and desorption analysis. The as-prepared porous titanium dioxide-silicon dioxide composites with high specific surface area and well-crystallized anatase contents were used as an efficient photocatalyst.     

PVA在提高TiO2/CdSe异质结光催化活性与抗光腐蚀性能方面的应用及机理

通过阳极氧化法和电化学沉积制备了TiO_2/CdSe异质结膜,并通过旋涂结合后续热处理的方法,在TiO_2/CdSe异质结膜上制备适量脱水态的聚乙烯醇(PVA)来提高TiO_2/CdSe异质结抗光腐蚀性能。采用XRD,SEM,FTIR,UV-Vis,PL,电化学测试,光催化降解罗丹明B等方法对样品的晶体结构、微观形貌、光电化学性能、光催化性能等进行了表征,并通过测定光降解体系中Cd2+的浓度,研究了纳米复合材料的抗光腐蚀性能。结果表明,与TiO_2/CdSe相比,TiO_2/CdSe/PVA纳米复合材料不仅具有更好的可见光光催化活性,还具有良好的可见光光催化稳定性和抗光腐蚀性能。同时,PVA的存在对光催化反应中的二次污染物Cd2+也有抑制作用。     

Photoelectrochemical water splitting and simultaneous photoelectrocatalytic degradation of organic pollutant on highly smooth and ordered TiO2 nanotube arrays

The photoelectrochemical water splitting and simultaneous photoelectrocatalytic degradation of organic pollutant were achieved on TiO₂ nanotube electrodes with double purposes of environmental protection and renewable energy production under illumination of simulated solar light. The TiO₂ nanotube arrays (TiO₂ NTs) were fabricated by a two-step anodization method. The TiO₂ NTs prepared in two-step anodization process (2-step TiO₂ NTs) showed much better surface smoothness and tube orderliness than TiO₂ NTs prepared in one-step anodization process (1-step TiO₂ NTs). In the photoelectrochemical water splitting and simultaneous photoelectrocatalytic decomposition process, the 2-step TiO₂ NTs electrode showed both highest photo-conversion efficiency of 1.25% and effective photodecomposition efficiency with existing of methylene blue (MB) as sacrificial agent and as pollutant target. Those results implied that the highly ordered nanostructures provided direct pathway and uniform electric field distribution for effective charges transfer, as well as superior capabilities of light harvesting.     

微含水量电解液中高管径比TiO_2纳米管阵列的制备

通过阳极氧化法在微含水量为0.5wt%的NH4F/乙二醇/H2O酸性电解质体系中制备了管径大、高管径比的二氧化钛(TiO2)纳米管阵列。采用SEM、XRD等测试手段对TiO2纳米管阵列形貌及晶相进行表征,探讨了不同氧化时间、电压对纳米管阵列形貌的影响,微含水量下氧化电压可以适当增加,更容易得到规整的长纳米管阵列;通过测定样品的光电流和紫外-可见光漫反射吸收光谱,研究分析了含水量以及超声工艺对纳米管光吸收及光电流特性,微含水量下得到的纳米管阵列可见光吸收边红移至420nm,对480~700nm可见光有明显的光吸收,光电流显著增大;丙酮作为超声介质可有效去除纳米管阵列表面的集束,能进一步提高纳米管阵列的光电性能。     

GO/TiO2-g-C3N4纳米复合材料的制备及可见光催化性能

以水热法制备的20% g-C₃N₄/TiO₂（20%为质量分数）为基,将其与不同质量分数的氧化石墨烯（GO）复合制备出可见光催化性能优良的GO/TiO₂-g-C₃N₄三元复合材料。利用X射线衍射（XRD）、扫描电子显微镜（SEM）、X射线光电子能谱（XPS）、紫外-可见漫反射光谱（UV-Vis DRS）、光致荧光光谱（PL）、瞬态光电流响应等分析测试手段对样品的结构、形貌和光电性能进行表征。研究了不同质量分数GO的加入对GO/TiO₂-g-C₃N₄在可见光下降解亚甲基蓝（MB）溶液的影响。结果表明： g-C₃N₄/TiO₂与GO复合后,锐钛矿相TiO₂颗粒形成小团簇附着在g-C₃N₄和GO片层表面,且当GO含量为15%时,TiO₂形成的团簇最小,对可见光的吸收最多且光生电子-空穴对的复合率最低。可见光照射下,15% GO/TiO₂-g-C₃N₄复合材料对MB的降解率在3 h内可达98.4%,且其降解速率常数（0.022 4 min^-1）分别是纯TiO₂（0.001 5 min^-1）和g-C₃N₄/TiO₂（0.002 5 min^-1）的15倍和9倍。     

微含水量电解液中高管径比TiO2纳米管阵列的制备

通过阳极氧化法在微含水量为0.5wt%的NH₄F/乙二醇/H₂O酸性电解质体系中制备了管径大、高管径比的二氧化钛（TiO₂）纳米管阵列。采用SEM、XRD等测试手段对TiO₂纳米管阵列形貌及晶相进行表征,探讨了不同氧化时间、电压对纳米管阵列形貌的影响,微含水量下氧化电压可以适当增加,更容易得到规整的长纳米管阵列;通过测定样品的光电流和紫外-可见光漫反射吸收光谱,研究分析了含水量以及超声工艺对纳米管光吸收及光电流特性,微含水量下得到的纳米管阵列可见光吸收边红移至420nm,对480~700nm可见光有明显的光吸收,光电流显著增大;丙酮作为超声介质可有效去除纳米管阵列表面的集束,能进一步提高纳米管阵列的光电性能。     

三维有序大孔复合材料Bi2O3/TiO2制备与多模式下光催化降解结晶紫

以TiO2为基体,在聚苯乙烯(PS)胶球和EO20PO70EO20(P123)两种模板剂作用下通过溶胶-凝胶及煅烧后处理方法制备了三维有序大孔纳米复合材料Bi2O3/TiO2.经傅里叶变换红外(FT-IR)光谱、X-射线衍射(XRD)、等离子体原子发射光谱(ICP-AES)、紫外-可见漫反射吸收光谱(UV-Vis DRS)、X-射线光电子能谱(XPS)、扫描电子显微镜(SEM)和N2吸附-脱附等物理测试手段对其组成、结构、形貌及表面物理化学性能进行了表征.结果表明,该复合材料晶型结构良好,孔结构排列整齐有序,孔壁呈介孔结构,属于三维有序大孔材料(3DOM).与TiO2相比,3DOM-Bi2O3/TiO2对光的吸收至少红移60 nm,且红移至可见区.在紫外光、可见光以及微波辅助等多模式光催化降解结晶紫的实验中,复合材料3DOM-Bi2O3/TiO2表现出良好的光催化活性,其活性明显高于P25、Bi2O3和Bi2O3/TiO2.同时,该复合材料针对不同类型的染料均表现出较好的紫外光降解效果,且3次循环实验后,依旧保持较高活性.     

Ce掺杂Bi2MoO6/TiO2纳米纤维异质结的制备及可见光催化性能

以静电纺丝技术制备的TiO₂纳米纤维为基质,通过溶剂热法制备了异质结型稀土Ce掺杂Bi₂MoO₆/TiO₂复合纳米纤维。利用X射线衍射（XRD）、扫描电子显微镜（SEM）、X射线光电子能谱（XPS）、透射电镜（TEM）、紫外-可见漫反射光谱（UV-Vis DRS）以及荧光光谱（PL）等分析测试手段对样品的物相、形貌和光学性能等进行表征。以罗丹明B为模拟有机污染物,研究了样品的可见光催化性能。结果表明：在稀土掺杂样品中,Ce离子进入Bi₂MoO₆晶格,部分取代Bi³⁺,导致晶胞膨胀,晶格畸变,形成缺陷;与TiO₂复合形成异质结,有利于光生电荷的产生、转移和有效分离,从而提高TiO₂纳米纤维的光催化活性。可见光照射180 min,罗丹明B的降解率达到95.1%。经5次循环光催化降解活性基本不变,样品具有良好的光催化稳定性。     

中空Ta2O5/TiO2复合光催化剂的可控氧化制备及性能

以钛粉、钽粉为原料,炭黑作为反应性模板,通过熔盐法在炭黑表面原位生长了TaTiC₂纳米碳化物涂层,并以所得TaTiC₂/C复合物为碳化物前驱体,再经可控氧化制备出中空Ta₂O₅/TiO₂复合光催化剂。采用X射线粉末衍射（XRD）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）、紫外-可见（UV-Vis）漫反射（DRS）及N₂物理吸附等手段对所制备的光催化剂进行形貌、显微结构及孔结构表征。以高压汞灯为紫外光源,以亚甲基蓝为目标降解物,通过光催化降解实验评价中空Ta₂O₅/TiO₂复合光催化剂的光催化活性。结果表明,熔盐法生长碳化物涂层厚度均匀（20~30 nm）,碳化物主要以TaTiC₂晶相存在且具有纳米级的颗粒尺寸。中空Ta₂O₅/TiO₂复合光催化剂同时具有200 nm左右的中空大孔结构及壳层10 nm左右的介孔结构。中空大孔和介孔的存在提高了所制备催化剂对亚甲基蓝的吸附能力。此外,TiO₂与Ta₂O₅通过电子能带结构的耦合,有效提高了光生电子和空穴的分离效率,从而显著提高了光催化活性。n_Ti∶n_Ta=2.5∶1.5时,相应的中空Ta₂O₅/TiO₂复合光催化剂表现出最佳的光催化活性,对亚甲基蓝的紫外光催化降解率高达97%。     

Ce掺杂Bi2MoO6/TiO2纳米纤维异质结的制备及可见光催化性能

以静电纺丝技术制备的TiO_2纳米纤维为基质,通过溶剂热法制备了异质结型稀土Ce掺杂Bi_2MoO_6/TiO_2复合纳米纤维。利用X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)、透射电镜(TEM)、紫外-可见漫反射光谱(UV-Vis DRS)以及荧光光谱(PL)等分析测试手段对样品的物相、形貌和光学性能等进行表征。以罗丹明B为模拟有机污染物,研究了样品的可见光催化性能。结果表明:在稀土掺杂样品中,Ce离子进入Bi_2MoO_6晶格,部分取代Bi3+,导致晶胞膨胀,晶格畸变,形成缺陷;与TiO_2复合形成异质结,有利于光生电荷的产生、转移和有效分离,从而提高TiO_2纳米纤维的光催化活性。可见光照射180 min,罗丹明B的降解率达到95.1%。经5次循环光催化降解活性基本不变,样品具有良好的光催化稳定性。     

脉冲沉积制备Cu2O/TiO2纳米管异质结的可见光光催化性能

在用阳极氧化法制备有序排列TiO₂纳米管阵列薄膜的基础上,引入脉冲沉积工艺,成功实现了均匀、弥散分布的Cu₂O纳米颗粒修饰改性TiO₂纳米管阵列,形成Cu₂O/TiO₂ 纳米管异质结复合材料. 利用场发射扫描电镜（FESEM）、场发射透射电镜（FETEM）、X射线衍射（XRD）、X射线光电子能谱（XPS）和紫外-可见漫反射光谱（UV-Vis DRS）对样品进行表征,重点研究了Cu₂O/TiO₂ 纳米管异质结的光电化学特性和对甲基橙（MO）的可见光催化降解性能. 结果表明,Cu₂O纳米颗粒均匀附着在TiO₂纳米管阵列的管口和中部位置,所制备的Cu₂O/TiO₂ 纳米管异质结具有高效的可见光光催化性能;在浓度为0.01 mol·L^-1的CuSO₄溶液中制得的Cu₂O/TiO₂纳米管异质结表现出最好的电化学特性和光催化性能;另外,对Cu₂O纳米颗粒影响光催化活性的机理进行了讨论.