Af-AaDd型氢键体系的网络结构参数

利用溶胶-凝胶分配理论对氢键溶液的模型体系进行研究, 给出了凝胶点后氢键网络中各结构参数的计算方案, 并进行相应的数值计算. 结果表明, 因受体基团本身的性质及两类质子受体基团的数量比不同, 受体基团的竞争作用对网络结构有明显影响, 这提供了控制氢键网络结构特征的可能方法.     

对-RTlnKco=ΔrGmo(T,co)的理论探讨

应用热力学特性函数、齐次函数定理和勒让德变换等概念和方法从理论上探讨了热力学公式RTlnKco=ΔrGmo（T,co）在推导和应用方面的问题。严格的数学论证表明该式是背离热力学原理的,它近似地适用于液相,但应用于气相则可能产生较大偏差。     

LixNi0.8-yCo0.2ZnyOp的合成及电化学性能研究

A series of single-phase Li_xNi_0.8-yCo_0.2Zn_yO_p(0.96 ≤x≤ 1.10， 0 ≤y≤ 0.05， 2 ≤p≤ 2(1+y) ) (different in the y values) were synthesized by a two-step solid state reaction method， in which LiOH·H₂O， Zn-doped spherical Ni(OH)₂ and Co₂O₃ were used as the precursors. The ICP-AES analyses proved that the Zn-doped compounds synthesized had the nonstoichiometric form. The results of the XRD， SEM identified that the uniform particles of the as-prepared materials having a good layered structure were fine， narrowly distributed and well crystallized. The electrochemical performance test was carried out and the results showed that the as-prepared Zn-doped materials had not only a high capacity， but also a better cycling stability characterization than the un-doped one. The Li_1.06Ni_0.75Co_0.22Zn_0.03O_2.03 material has an initial reversible capacity as high as 160.5mAh·g^-1; and a first discharge efficiency 89.2%， and exhibits satisfactory cyclic stability with 90% retainable capacity after 50 cycles.     

LixZryOz三元化合物的制备及表征

采用高温固相法制备了4种高纯度晶相组成的LixZryOz三元化合物,研究了焙烧温度、时间、反应物的种类和初始反应物物质的量比对产物组成的影响,进一步用XRD、SEM及BET分析方法对产物的晶相结构、表面形貌及比表面积进行了表征.实验结果表明,Li2CO3与ZrO2在适当条件下可以合成得到单斜相Li3ZrO3;以LiOH替代Li2CO3,在适当条件下可以分别合成得到四方相Li2ZrO3和三斜/单斜相Li6Zr2O7;进一步以Zr(NO3)4·5H2O代替Zr02,可将单斜相Li6Zr2O7的制备时间由96 h缩短至24 h.SEM照片显示产物硬团聚明显,粒径分布在1～10μm间,BET分析表明样品比表面积处于1.0～9.0 m2·g-1间分布,反应过程中锂的过量以及长时间高温焙烧是引起产物粒径长大和产生硬团聚的主要原因.     

Zr1-xMxWMoO8-x/2和Zr1-xMxW2O8-x/2固溶体的晶胞参数与晶格畸变的关系

合成了Zr1-xMxWMoO8-x/2(M=Er,Tm,Yb,Sc,In,Ga,Al)和Zr1-xMxW2O8-x/2(M=Eu,Er,Yb,Sc,In,Ga,Al)2个系列的固溶体,前者具有β-ZrW2O8结构类型(简称β相);后者具有α-ZrW2O8结构类型(简称α相)。建立了相和相的晶胞参数与M3+离子浓度的Vegard方程,测定了上述固溶体的固溶度。讨论了M3+离子的化学性质与Vegard斜率SV的关系。分析了α相的SαA与β相的SβA的关系;揭示了α-Zr1-xMxW2O8-x/2晶格中2[WO4]四面体对的取向有序程度对晶格畸变的贡献。提出上述固溶体的晶胞参数随溶质浓度增加而减小,主要是由于氧空位缺陷相互作用的结果。     

橙红色荧光粉Ca1-x-ySmxBiySiO3的制备及其发光性能

以Sm³⁺作为激活剂,Bi³⁺作为辅助激活剂,采用水热法合成Ca_1-x-ySm_xBi_ySiO₃前驱体,然后在1 100 ℃焙烧得到系列橙红色荧光粉.用X-射线衍射仪、扫描电镜和荧光分光光度计和傅里叶变换红外光谱等手段对样品的组成、结构和形貌及其发光性质进行分析和表征.分析结果表明：产物都为三斜晶系结构的Ca_1-x-ySm_xBi_ySiO₃和四方结构的方石英SiO₂共熔体.在405 nm近紫外光激发下,产物的发射光谱由3个峰组成,发射峰值位于566、606和650 nm处,分别归属于Sm³⁺的⁴G_5/2→⁶H_J/2(J=5,7,9)跃迁.产物的激发光谱在405 nm有很强的发射带,与近紫外LED芯片匹配.随着Sm³⁺掺量的增加,样品发光强度先增强后减弱,当Sm³⁺的物质的量分数为3%时发光强度达到最大,浓度猝灭机理为电偶极-电偶极相互作用.当Bi³⁺的物质的量分数在0.3%~1.5%时,对产物Ca_0.97Sm_0.03SiO₃的荧光强度起敏化作用.Sm³⁺和Bi³⁺的最佳物质的量分数分别为3%和0.5%.     

直接Z型Zn2SnO4-xNx/ZnO1-yNy异质结光催化剂的制备及机理

采用微波溶剂热法成功制备直接Z型Zn_2SnO_(4-x)N_x/ZnO_(1-y)N_y核壳结构异质结光催化剂。2种物质不同的功函数改变了其表面电荷密度,并在界面处形成内建电场,导致其从传统的Ⅰ型镶嵌异质结转变为Ⅱ型异质结,再转变为Z型异质结构。N杂质原子替代O原子进入Zn_2SnO_4和ZnO的晶格,在两者的价带(VB)顶部形成双杂质能级。核壳结构的Z型异质结光催化剂对罗丹明B的降解速率为纯相Zn_2SnO_(4-x)N_x的1.40～1.43倍,同时具有良好的循环稳定性,且可以降解亚甲基蓝、甲基橙、水杨酸等污染物。Z型异质结的形成使其光生电子-空穴对具有较强的氧化还原能力,而双杂质能级的存在可以拓宽其光响应范围并提高载流子的分离效率。因此,Zn_2SnO_(4-x)N_x/ZnO_(1-y)N_y异质结光催化剂高的光催化活性归因于Z型异质结和双杂质能级的协同作用。     

纳米钙钛矿LaxSr1-xFe1-yCoyO3复合氧化物的制备和表征

用甘氨酸-硝酸盐燃烧合成法，制备La_xSr_1-xFe_1-yCo_yO₃复合氧化物的陶瓷粉末，对该钙钛矿型氧化物进行了XRD、IR、紫外漫反射光谱及循环伏安曲线分析。结果表明：该复合氧化物粉体平均晶粒为15.3～29.8 nm,为立方和正交晶系。该氧电极具有双功能催化特性，但不完全可逆。对水溶液染料进行光解实验，利用紫外-可见、人工神经网络光度法研究La_xSr_1-xFe_1-yCo_yO₃的催化性能。结果表明：CO²⁺的加入可使La_xSr_1-xFeO₃的光催化活性有所提高，B位离子(Fe³⁺，CO²⁺)改变与加入，使La_xSr_1-xFe_1-yCo_yO₃(x=0.7，0.3；y=0.3，0.9，1)光催化活性高于La_xSr_1-xFeO₃。同时，对5种染料进行紫外光解，在0.75 h，脱色率大于91%，并为动力学一级反应。     

多元掺杂尖晶石型Li1.02MxMn2-xQyO4-y正极材料的电化学特性

The effect of doping on the electrochemical performance was studied for spinel type Li_1.02M_xMn_2-xQ_yO_4-y used as cathode material in lithium-ion battery. TG/DTA curves of the precursor(the raw materials) doped with different elements were studied. The spinel materials Li_1.02Mn₂O₄, Li_1.02Co_0.02Cr_0.01La_0.01Mn_1.96F_0.02O_3.98, Li_1.02Co_0.02Cr_0.01 La_0.01Mn_1.96Cl_0.02O_3.98, Li_1.02Co_0.02La_1.02Mn_1.97Cl_0.02O_3.98, Li_1.02Co_0.02Cr_0.01Mn_1.97O₄, were prepared by solid-state reaction method after the pretreatment of conversion under low temperature and uniform mixing. X-ray diffraction patterns showed that all the samples had perfect spinel structure. SEM indicated that the particles of the samples had uniform size and were distributed evenly. The results of the charge/discharge curves showed that Li_1.02Co_0.02Cr_0.01La_0.01Mn_1.96F_0.02O_3.98 had better performance than other materials according to the inhibition of decline of reversible capacity of spinel Li_1.02M_xMn_2-xQ_yO_4-y. Therefore, cycle performance had been improved so obviously that 93.9% of the initial capacity were preserved after 100 cycles. Furthermore, electrochemical impedance tests were carried out with the spinel Li_1.02Co_0.02Cr_0.01La_0.01Mn_1.96F_0.02O_3.98 as working electrode, Lithium as counter electrode and reference electrode. Results showed that this material possessed good charge/discharge reversible capability and had the lowest impedance in 3.95～4.25 V range (on the stage of charge / discharge).     

ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.     

SinH/SinH-(n=3～8)的结构和电子亲合能的研究

选用四种不同的密度泛函理论方法(B3LYP，B3P86，BLYP，BP86)，在全电子的双ξ加极化加弥散函数基组(DZP )下，对SinH／SinH^-(n=3～8)体系进行研究，获得它们的基态结构和电子亲合能。预测Si3H／Si3H^-,Si4H／Si4H^-,Si5H／Si5H^-,Si6H／Si6H^-，Si7H／Si7H^-和Si8H／Si8H^-的基态结构分别为C2v(^2B2)／C2v(1^A1)氢桥结构，Cs(^2A’)／C(^1A’)，C2v(^2B2)／C2v(^1A1)，C2v(^2B2或^2B1)／C4v(^1A1)，C5v(^2A1)／C5v(^1A1)和C5(^2A‘‘)／C3v(^1A1)。在电子亲合能方面，B3LYP方法预测的电子亲合能是最可靠的，预测Si3H，Si4H，Si5H，Si6H，Si7H和Si8H的电子亲合能分别为2．56，2．59，2．84，2．86，3．19和3．14eV。     

nFe3+/nSr2+和nOH-/nNO3-对锶铁氧体纳米片结构及磁性能的影响

采用改进的水热法成功合成了单分散的纯相锶铁氧体纳米片。借助DLS、XRD、FTIR、SEM、EDS和VSM等分析测试手段对SrFe₁₂O₁₉铁氧体粉体的粒度、结构、形貌和磁性能进行表征。研究结果表明,在240℃保温5 h,物质的量之比n_Fe³⁺/n_Sr²⁺(R_F/S)和n_OH^-/n_NO^-(R_O/N)分别为5和2时,所得产物为单分散的纯相六角SrFe₁₂O₁₉铁氧体纳米片。随着R_F/S和R_O/N的变化,合成样品中有少量SrCO₃和Fe₂O₃杂相存在,这主要与反应条件和离子比例有关。磁性能测试结果显示,所得纯相的六角SrF₁₂O₁₉铁氧体纳米片具有优异的磁性能,其饱和磁化强度和矫顽力分别达到60.91 emu·g^-1和94.83 kA·m^-1,使其在医疗、催化和生物等高技术领域具有潜在的应用。     

Pd/CuxCo3-xOn界面的可控制备及高效催化甲苯燃烧反应

采用水热合成法制备了形貌规整且主要暴露晶面为(112)面的Co_3O_4六角片,在此基础上掺杂了适量的Cu元素,并且可控沉积了窄尺寸分布的Pd粒子。制备过程简单、绿色且产率高。所得材料应用于催化甲苯完全氧化反应时表现出优异的催化性能,其中Pd/h-Cu_(0.18)Co_(2.82)O_n的T_(90)(甲苯的转化率达到90%时的反应温度)低至198℃。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、比表面积测试(BET)、H2程序升温还原(H2-TPR)、X射线光电子能谱(XPS)对催化剂的结构和理化性质进行了表征。结果表明,适宜量的Cu掺杂后Co_3O_4基底氧空位增多,活化氧的能力增强,表面存在丰富的吸附氧物种,表现出与贵金属基催化剂相媲美的催化活性。引入的Pd组分主要以PdO形式存在,基底Cu掺杂进一步提升了Pd的氧化态,表面高反应性的氧种更多,反应活性更高。     

nFe3+/nSr2+和nOH-/nNO3-对锶铁氧体纳米片结构及磁性能的影响

采用改进的水热法成功合成了单分散的纯相锶铁氧体纳米片。借助DLS、XRD、FTIR、SEM、EDS和VSM等分析测试手段对SrFe₁₂O₁₉铁氧体粉体的粒度、结构、形貌和磁性能进行表征。研究结果表明,在240℃保温5 h,物质的量之比n_Fe³⁺/n_Sr²⁺(R_F/S)和n_OH^-/n_NO3^-(R_O/N)分别为5和2时,所得产物为单分散的纯相六角SrFe₁₂O₁₉铁氧体纳米片。随着R_F/S和R_O/N的变化,合成样品中有少量SrCO₃和Fe₂O₃杂相存在,这主要与反应条件和离子比例有关。磁性能测试结果显示,所得纯相的六角SrF₁₂O₁₉铁氧体纳米片具有优异的磁性能,其饱和磁化强度和矫顽力分别达到60.91 emu·g^-1和94.83 kA·m^-1,使其在医疗、催化和生物等高技术领域具有潜在的应用。     

Pt-CeOx/CNxNT催化剂的高稳定性和高效氧还原性能

通过简便的方法合成出了Pt-CeO_x/CN_xNT催化剂。该催化剂以聚吡咯纳米管碳化后的含氮碳纳米管作为载体,以氧化铈作为助催化剂。实验表明,由于二氧化铈的储氧性能,也由于CN_xNT载体中氮元素的促进作用和其本身独特的一维中空结构,Pt-CeO_x/CN_xNT催化剂的氧还原性能明显高于商业Pt/C。而催化剂优秀的稳定性则源于二氧化铈对Pt纳米颗粒和载体的保护作用。     

GCE/DNA/PFS/RTIL/HRP修饰电极的制备及其电催化行为

将辣根过氧化物酶（HRP）固定在室温离子液体（RTIL）/聚二茂铁硅烷（PFS）/DNA复合材料修饰的玻碳电极（GCE）表面,构建了GCE/DNA/PFS/RTIL/HRP修饰电极,详细地研究了该修饰电极的电催化行为,优化了电解质溶液的pH值和RTIL的体积对催化过氧化氢（H2O2）的影响。 电化学实验结果表明,DNA、PFS和RTIL复合膜既为HRP提供了一个生物兼容的微环境;又有效地促进了电子在HRP和电极表面之间的传递。 在最优实验条件下,该修饰电极对H2O2具有快速的催化响应,在2 s内即可达到稳态电流的95%,其响应在3.25 μmol/L~1.47 mmol/L（r=0.999,n=10）和1.86~5.35 mmol/L（r=0.996,n=12）范围内呈良好的线性关系,检出限为0.86 μmol/L。 该传感器灵敏度高、重现性和稳定性好。 此外,该修饰电极还能催化O2还原。     

TixNy团簇结构的密度泛函研究

采用杂化密度泛函方法(B3LYP)和有效核势基组预测了Ti_xN_y (x≤3, y≤2)团簇的结构及稳定性, 并分析了可能存在构型的电子结构. 结果表明Ti₂N中体系的自旋多重度由Ti原子决定. Ti₃N中随着N的配位数增加, N的负电荷增加, 平均每个Ti向N提供约0.3个电子. 从Ti₂N₂可能稳定构型分析, 成键数目越多, 能量上越有利, 且Ti—N键的数目的增加, 将削弱N—N间的成键.     

FexOy/SBA-15介孔分子筛的合成以及性能研究

在酸性溶液中利用溶胶凝胶-pH值控制两步法直接合成Fe_xO_y/SBA-15介孔分子筛，同时利用场发射扫描电子显微镜(FESEM)、小角度X射线衍射(Low-angle XRD)、透射电子显微镜(TEM)以及振动样品磁强计(VSM)对制备的各种SBA-15介孔分子筛进行结构以及性能的测试、表征。结果显示Fe_xO_y均匀地分散在SBA-15的骨架中，而且会对SBA-15介孔分子筛起钉轧作用。而后着重研究了Fe_xO_y的加入对SBA-15介孔分子筛的热稳定性、催化特性以及磁学性能的影响。Fe_xO_y的引入可以增加制备的SBA-15介孔分子筛的热稳定性;Fe_xO_y的引入可以改善SBA-15介孔分子筛的催化活性，得到了开口的、石墨化程度较好的纳米碳管。Fe_xO_y的引入使SBA-15介孔分子筛具有明显的铁磁性。