一种SO2固定及用于制备BaSO3或BaSO4的方法

在常温常压下,由乙二胺（EDA）和乙二醇及其衍生物（EGs）组成的混合体系可捕集SO₂并转化为一种SO₂储集材料（SO₂SM）。EDA+EGs体系呈现了强的捕集性能（0.364~0.662 g_SO2·gabsorbent^-1）。FTIR,XPS和XRD结果确证了SO₂SM为一种烷基亚硫酸盐。以EG-SO₂SM为原料制备具有多种形貌的BaSO₃或BaSO₄,在此过程中,EG-SO₂SM不仅提供了原材料,而且可以释放EDA和EG用作表面活性剂,调控晶体的结晶化过程。     

H2SO4处理的Nb2O5/γ -Al2O3催化剂表面酸性与催化性能研究

用Hammett指示剂法、红外光谱（IR）、示差扫描量热-热重法（DSC-TG）和微型催化反应装置等研究了H₂SO₄处理的负载型Nb₂O₅/γ-Al₂O₃催化剂表面酸性和催化异丁烯（IB）与异丁醛（IBA）反应生成2，5-二甲基-2，4-己二烯（DMHD）的催化性能。结果表明随所用H₂SO₄浓度增加，Nb₂O₅/γ-Al₂O₃催化剂表面酸性增强，B酸量增加，L酸量先增加后下降。经H₂SO₄处理的Nb₂O₅/γ-Al₂O₃催化剂的催化活性明显增加，但当H₂SO₄浓度超过0.05 mol·L^-1时催化活性又急剧下降，这可能是因为在H₂SO₄处理的催化剂表面形成的强酸中心上，产物分子进一步转化为积炭且封闭催化剂活性表面，导致催化活性下降。     

片状纳米结构CeO2晶体的制备及其吸附CO2性能

在室温下,将CeCl₃溶液与CO₂储存材料（CO₂SM）混合、搅拌0.5 h制备了片状碳酸铈前驱体（CCPs）,并在500℃下煅烧CCPs 4 h,制得平均尺寸为4.94 μm×0.92 μm,厚度为0.04~0.08 μm纳米结构片状CeO₂晶体。在此过程中,CO₂SM不但可以提供CO₃^2-,还能起到分散剂和结构导向剂的作用。反应过程中,系统地研究了CO₂SM用量、Ce³⁺浓度和搅拌时间3个因素对CCPs形态和大小的影响,得到最优制备条件：0.1 g CO₂SM和50 mL 0.03 mol·L^-1 Ce³⁺水溶液以1 000 r·min^-1转速在室温下搅拌0.5 h。煅烧CCPs后,所制备的片状CeO₂晶体在室温下CO₂吸附量可达0.554 mmol·g^-1。     

纳米SO42-/ZrO2的合成及其在酯交换反应中的催化性能

采用两步晶化-后浸渍法合成了纳米SO₄^2-/ZrO₂固体酸催化剂,并考察了其在植物油与甲醇酯交换反应中的催化性能。XRD、N₂吸附-脱附和TEM等结果表明,经过600℃焙烧,催化剂仍保持单一四方相,粒径大小为5~10 nm,比表面积为137 m²·g^-1,孔径为3.6 nm。NH₃-TPD结果表明,随着焙烧温度升高,催化剂表面的酸含量和酸强度逐渐增加,超强酸含量的增加,更有利于反应在温和条件下进行。在酯交换反应中,当醇油物质的量之比为20：1,反应温度为135℃,反应时间为6 h,600℃焙烧后催化剂用量为5%（w/w）时,植物油能够完全转化为脂肪酸甲酯。与传统的SO₄^2-/ZrO₂催化剂相比,该催化剂在低温反应条件下具有更高的催化性能和良好的重复使用性。     

纳米固体超强酸SO42-/Fe2O3的制备及其催化合成乙酸乙酯

将Fe₂O₃纳米粉体经一定浓度的H₂SO₄浸泡活化后制成纳米固体超强酸SO₄^2-/Fe₂O₃,将其用于催化合成乙酸乙酯以考察其活性。利用均匀设计分析了超强酸制备过程及酯化反应过程中各因素的影响,研究结果表明较好的制备条件是:H₂SO₄浓度:2.5mol·L^-1;浸泡时间:1h;活化温度:167℃;活化时间:1h,此时获得的固体超强酸SO₄^2-/Fe₂O₃的粒径小于50nm。当催化剂用量为冰乙酸质量的5%,n(乙醇)∶n(冰乙酸)为3∶1,反应3.5h后乙酸的转化率高于80%。该催化剂经H₂SO₄溶液浸泡、活化再生后可重新使用,推断出其酸强度H₀<-14.5。     

Cu/SO42-/La2O3-ZrO2-Al2O3催化剂的制备及其对C3H6选择还原NO的催化性能

以Al₂O₃为基质，添加ZrO₂和La₂O₃，制成La₂O₃-ZrO₂-Al₂O₃复合载体，然后采用SO₄^2-进行改性，再负载上Cu²⁺，制备了铜基SO₄^2-改性的复合载体催化剂(Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃)。考察了它在富氧条件下对丙烯选择还原NO的催化性能，并借助XRD、SEM、TG、Py-IR、NH₃-TPD、FTIR和TPR等方法研究了Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃的结构和性能的关系。结果表明，ZrO₂的加入主要有利于提高催化剂的低温活性；La₂O₃的加入则主要有利于提高催化剂的热稳定性和还原性能；SO₄^2-能够与Zr形成螯合双配位结构，大幅度促使催化剂表面酸量增加并且酸性增强；因此，有效地提高了Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃在富氧条件下对丙烯选择还原NO的催化活性和水热稳定性。在无水条件下，Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃能使NO的最大转化率高达84.3%，即使在275 ℃ 10%水蒸气存在的情况下，仍能使NO的转化率高达81.2%。     

快离子导体LiTi2(PO4)3在LiNi0.8Co0.1Mn0.1O2正极材料表面的原位反应包覆及其电化学性能

通过原位反应法,利用富镍层状金属氧化物LiNi_0.8Co_0.1Mn_0.1O₂（LNCM811）正极材料表面残余的氢氧化锂和碳酸锂,与C₈H₂₀O₄Ti和（NH₄）H₂PO₄反应,在LNCM811表面原位生成快离子导体LiTi₂（PO₄）₃（LTP）包覆层。这种原位反应的包覆方法有利于移除LNCM811表面有害的残留物氢氧化锂和碳酸锂。而且,获得的LTP均匀包覆层不仅可以有效地抑制LNCM811表面和电解液的直接接触及其副反应,还可以确保充放电循环过程中LNCM811正极材料的快速Li⁺传导。因此,在LTP包覆层的多重作用下,LTP包覆的LNCM811正极材料具有优异的循环稳定性和倍率性能：在0.2C时,首次放电比容量高达200.6 mAh·g^-1,200圈后的可逆容量依然有155.7 mAh·g^-1;在2C和5C的高电流密度下,200圈后的可逆容量仍然有126.4和111.9 mAh·g^-1。     

二维层状Ti3C2Tx-MXene@VS2用于高性能锂离子电池负极

为探索一种高性能的锂离子电池负极材料,采用酸刻蚀法制备了高导电性、高稳定性的二维层状Ti₃C₂T_x,通过溶剂热法制备了具有高理论比容量的花瓣状VS₂纳米片,再经过简单的液相混合得到了二维层状Ti₃C₂T_x-MXene@VS₂复合物。通过扫描电子显微镜、透射电子显微镜、X射线光电子能谱、X射线衍射和能谱分析对复合材料的形貌和结构进行了表征,采用循环伏安、恒流充放电、长循环和交流阻抗谱对复合材料的电化学性能进行了研究。结果表明：VS₂纳米片均匀地分布在Ti₃C₂T_x的层间及表面,该复合物具有高的可逆容量(电流密度为0.1A·g^-1时,比容量为610.5mAh·g^-1)、良好的倍率性能(电流密度为2A·g^-1时,比容量为197.1mAh·g^-1)和良好的循环稳定性(电流密度为0.2 A·g^-1时,循环600圈后比容量为874.9 mAh·g^-1;电流密度为2 A·g^-1时,循环1 500圈后比容量为115.9mAh·g^-1)。     

配合物Zn(Leu)SO4·0.5H2O的合成与热行为

在水-丙酮溶液中制备了Zn(Leu)SO₄·0.5H₂O的配合物。通过热重和红外分析,研究了它的热分解机理,可分为三步完成。第一阶段配合物的脱水过程在60～180℃,形成Zn(Leu)SO₄,第二阶段,Zn(Leu)SO₄进一步分解为Zn(Leu)SO₄·9ZnSO₄,随后其在728℃完全分解为ZnO。在不同线性升温5.0,10.0,15.0,20.0K·min^-1条件下,用两种积分法和三种微分法研究了题目化合物失去配体过程的非等温动力学,相应过程的表观活化能E为133.78kJ·mol^-1,指前因子A为10^8.19s^-1,配体失去过程为三维扩散机理控制,并建立了反应过程的动力学方程。     

纳米复合固体超强酸SO42-/CoFe2O4的制备和表征

采用纳米化学制备技术合成了新型的纳米复合固体超强酸催化剂ＳＯ４＾２－／ＣｏＦｅ２Ｏ４。用ＸＲＤ、ＴＥＭ、ＸＰＳ、红外光谱和比表面测定等技术研究了该催化剂的结构形态,结果表明：所研制的ＳＯ４＾２－／ＣｏＦｅ２Ｏ４２催化剂为晶态纳米粒子（〈５０ｎｍ）,比表面积很大（１５７ｍ＾２．ｇ＾－１）,ＳＯ４＾２－与氧化物的金属离子呈无机齿螯合状配位化合物的结合形式。以乙酸乙酯合成为模型反应考究了该催化剂的催化活     

AOT微乳液中通过水化电子产额调控合成BaSO_4纳米纤维

通过γ-辐照含有K2S2O8和BaCl2的二(2-乙基己基)琥珀酸酯磺酸钠(AOT)反相微乳液,将S2O82-通过辐射还原实现了SO42-的原位缓释,从而成功制备出BaSO4纳米纤维单晶,并进一步制得多层次的纳米纤维束结构.在此基础上,通过改变水与表面活性剂物质的量之比(ω值)、改变钡盐阴离子和在微乳液连续相添加芳香化合物等手段来调节水化电子(e-aq)产额,控制微乳液水池中S2O82-的还原和SO42-的缓释速率,成功实现了对BaSO4纳米粒子形貌的调控:随着ω值的增加或剂量率的增加,e-aq产额增加,从而加快了SO42-的释放,不利于BaSO4纳米纤维的生成;采用Ba(NO3)2为钡源时,NO3-能有效地降低e-aq产额和S2O82-的还原速率,因而在较高的剂量率和较高ω值下能得到BaSO4纳米纤维;在微乳液油相中加入甲苯来捕获油相中过量电子(e-oil),降低e-aq产额,从而在较高的剂量率下得到BaSO4纳米纤维.研究结果表明:通过e-aq产额调控纳米粒子形貌的机理在BaSO4纳米粒子的制备中得到很好体现.     

CO2 Fixation into Novel CO2 Storage Materials Composed of 1,2‐Ethanediamine and Ethylene Glycol Derivatives

A new CO₂ fixation process into solid CO₂‐storage materials (CO₂SMs) under mild conditions has been developed. The novel application of amine–glycol systems to the capture, storage, and utilization of CO₂ with readily available 1,2‐ethanediamine (EDA) and ethylene glycol derivatives (EGs) was demonstrated. Typically, the CO₂SMs were isolated in 28.9–47.5 % yields, followed by extensive characterization using ¹³C NMR, XRD, and FTIR. We found that especially the resulting poly‐ethylene‐glycol‐300‐based CO₂SM (PCO₂SM) product could be processed into stable tablets for CO₂ storage; the aqueous PCO₂SM solution exhibited remarkable CO₂ capturing and releasing capabilities after multiple cycles. Most importantly, the EDA and PEG 300 released from PCO₂SM were found to act as facilitative surfactants for the multiple preparation of CaCO₃ microparticles with nano‐layer structure.     

A novel method for preparing poly(ethylene terephthalate)/BaSO4 nanocomposites

We developed a novel method for preparing poly(ethylene terephthalate)/BaSO₄ nanocomposites, which were synthesized by in situ polymerization of terephthalic acid (TPA), ethylene glycol (EG) and BaSO₄ nanoparticles prepared by reacting H₂SO₄ with Ba(OH)₂ in ethylene glycol (EG). It was shown that the addition of BaSO₄ would not influence the synthesis of PET. The structure of the nanocomposites was characterized by transmission electron microscopy (TEM), and the nanoscale dispersion of BaSO₄ particles in the PET matrix was observed when the BaSO₄ content is below 4 wt%. Moreover, the thermal properties of the nanocomposites were investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The results suggest that the degree of dispersion of BaSO₄ particles in the PET matrix has important effect on the thermal properties of the nanocomposites. The existence of BaSO₄ nanoparticles enhances the crystallization rate of PET. Besides, it was found that the thermal stability of PET was improved by the addition of the BaSO₄ nanoparticles.     

CH3SO3裂解反应的机理和热力学性质

在G3XMP2//B3LYP/6-311+G(3df,2p)水平上对CH₃SO₃裂解反应的机理进行了研究, 获得了6 条通道(10 条路径), 并构建了其势能剖面. 同时采用单分子反应理论计算了各个通道在温度200-3000 K区间的速率常数. 研究结果表明, 在计算温度范围内, CH₃SO₃裂解反应的主产物为P1(CH₃+SO₃), 产物P2(CH₃O+SO₂)和P3(HCHO+HOSO)仅在温度大于3000 K时对总产物有贡献, 而产物P4(CHSO₂+H₂O), P5(CH₂SO₃+H)和P6(CHSO₃+H₂)贡献相对较少. 将裂解反应总的速率常数拟合为k_total=1.40×10¹²T^0.15exp(7831.58/T). 此外, 根据统计热力学原理, 预测了所有物种的生成焓(D_fH^Θ_{298 K}, D_fH_{0 K}), 熵(S^Θ_{298 K})和热容(C_p, 298-2000 K), 计算的结果与实验值较接近.     

SO42-改性后的TiO2(锐钛和/或金红石)表面上MoO3的分散性质研究

采用红外(IR)、拉曼(Raman)、X-射线衍射(XRD)、程序升温还原(TPR)等方法考察了经硫酸根改性后的金红石(SR)与锐钛矿(SA)的混合比例变化时的负载型催化剂，MoO₃ / TiO₂(SR+SA)，的一些物理化学性质(如活性组分MoO₃的分散行为、表面酸碱性、氧化还原性)的变化规律。结果表明：对于MoO₃ / TiO₂(SR+SA)样品，低含量MoO₃表面分散时倾向于优先与混合载体中的改性金红石(SR)发生作用；TiO₂载体表面SO₄^2-的存在，使得载体表面产生了新的酸性位，导致样品中表面分散的钼物种主要以聚合八面体状态存在。     

Spectroscopic properties of guanidinium zinc sulphate [C(NH2)3]2Zn(SO4)2 and ab initio calculations of [C(NH2)3]2 and HC(NH2)3

Raman and FTIR spectra of guanidinium zinc sulphate [C(NH₂)₃]₂Zn(SO₄)₂ are recorded and the spectral bands assignment is carried out in terms of the fundamental modes of vibration of the guanidinium cations and sulphate anions. The analysis of the spectrum reveals distorted SO₄²⁻ tetrahedra with distinct S–O bonds. The distortion of the sulphate tetrahedra is attributed to Zn–O–S–O–Zn bridging in the structure as well as hydrogen bonding. The CN₃ group is planar which is expressed in the twofold symmetry along the C–N (1) vector. Spectral studies also reveal the presence of hydrogen bonds in the sample. The vibrational frequencies of [C(NH₂)₃]₂ and HC(NH₂)₃ are computed using Gaussian 03 with HF/6-31G* as basis set.     

Al含量对Pt-SO2-4 /ZrO2-Al2O3固体超强酸催化

通过向SO^2-₄ /ZrO₂催化剂中同时引入适量的Pt和Al₂O₃, 制备出了具有较高催化性能和稳定性的Pt-SO^2-₄ /ZrO₂-Al₂O₃型固体超强酸催化剂. 以正戊烷异构化反应为探针, 考察了Al含量对催化剂性能的影响; 并采用X射线衍射(XRD)、比表面积测定(BET)、红外(IR)光谱、程序升温还原(TPR)、热重-差热分析(TG-DTA)和氨-程序升温脱附(NH₃-TPD)手段对催化剂进行了表征. 结果表明, Al能够提高ZrO₂的晶化温度, 抑制硫的分解, 增加催化剂的比表面积, 增强硫氧键的结合, 提高催化剂的还原性能, 增加催化剂的酸强度和酸总量. 当Al₂O₃含量(质量分数, w)为5.0%时, Pt-SO^2-₄ /ZrO₂-Al₂O₃固体超强酸催化剂的催化活性最好, 在100 h内异戊烷收率可稳定在52.0%以上, 选择性在98.2%以上.