As-doped p-type ZnO films grown on SiO2/Si by radio frequency magnetron sputtering

p-Type ZnO:As films with a hole concentration of 10¹⁶-10¹⁷ cm⁻³ and a mobility of 1.32-6.08 cm²/V s have been deposited on SiO₂/Si substrates by magnetron sputtering. XRD, SEM, Hall measurements are used to investigate the structural and electrical properties of the films. A p-n homojunction comprising an undoped ZnO layer and a ZnO:As layer exhibits a typical rectifying behavior. Our study demonstrates a simple method to fabricate reproducible p-type ZnO film on the SiO₂/Si substrate for the development of ZnO-based optoelectronic devices on Si-based substrates.     

Induction of p-type conduction in sputtered deposited Al-N codoped ZnO thin films

Al and N codoped ZnO thin films were grown on n-Si (100) substrate by sputtering technique. Hall effect measurements of as-grown films exhibited n-type conduction, however 500 °C Ar annealed codoped films showed p-type conductivity with a hole concentration of 9.9 × 10¹⁶ cm^− 3, resistivity of 15.95 Ω-cm and hole mobility of 3.95 cm²/Vs, respectively. Codoped ZnO thin films were found to be highly c-axis oriented with good crystal quality. A neutral acceptor-bound exciton and donor-acceptor-pair emissions that appeared at room temperature photoluminescence measurement verify p-type conduction in Al and N codoped ZnO film. The current-voltage characteristics of p-n heterojunction evidently showed a diode like rectifying behaviour.     

Ag-N doped ZnO film and its p-n junction fabricated by ion beam assisted deposition

Ag-N doped ZnO film was synthesized by ion beam assisted deposition and its electrical properties and annealing property were investigated. The films remained p-type even after annealing at 400 °C in air for 10 min. While the annealing temperature went up to 500 °C, the conduction type of these films shifted from p-type to n-type. The p-type ZnO film revealed low resistivity (0.0016 Ω cm), low Hall mobility (0.65 cm² V⁻¹ s⁻¹) and high carrier concentration (5.8 × 10²⁰ cm⁻³). ZnO p-n homojunction consisting of a p-type layer (Ag-N doped ZnO film) and an n-type layer (In-doped ZnO film) had been fabricated by ion beam assisted deposition. With electrical measurement, its current-voltage curve had a typical rectifying characteristic with current rectification ratio of 25 at bias ±5 V and a reverse current of 0.01 mA at −5 V. The depletion width was estimated 3.8 nm by using p-n junction equation.     

Investigation of p-type behavior in Ag-doped ZnO thin films by E-beam evaporation

Ag-doped ZnO (ZnO:Ag) thin films were grown on glass substrates by E-beam evaporation technique. The structural, electrical and optical properties of the films were investigated as a function of annealing temperature. The films were subjected to post annealing at different temperatures in the range of 350-650 °C in an air ambient. All the as grown and annealed films at temperature of 350 °C showed p-type conduction. The films lost p-type conduction after post annealing treatment temperature of above 350 °C, suggesting a narrow post annealing temperature window for the fabrication of p-type ZnO:Ag films. ZnO:Ag film annealed at 350 °C revealed lowest resistivity of 7.25 × 10⁻² Ω cm with hole concentration and mobility of 5.09 × 10¹⁹ cm⁻³ and 1.69 cm²/V s, respectively. Observation of a free-to-neutral-acceptor (e,A^o) and donor-acceptor-pair (DAP) emissions in the low temperature photoluminescence measurement confirms p-type conduction in the ZnO:Ag films.     

Structural, optical and electronic properties of P doped p-type ZnO thin film

P doped ZnO films were grown on quartz by radio frequency-magnetron sputtering method using a ZnO target mixed with 1.5 at% P₂O₅ in the atmosphere of Ar and O₂ mixing gas. The as-grown P doped ZnO film showed n-type conductivity, which was converted to p-type after 800 °C annealing in Ar gas. The P doped ZnO has a resistivity of 20.5 Ω cm (p∼2.0×10¹⁷ cm⁻³) and a Hall mobility of 2.1 cm² V⁻¹ s⁻¹. XRD measurement indicated that both the as-grown and the annealed P doped ZnO films had a preferred (0 0 2) orientation. XPS study agreed with the model that the P_Zn-2V_Zn acceptor complex was responsible for the p-type conductivity as found in the annealed P-doped ZnO. Temperature-dependent photoluminescence (PL) spectrum showed that the dominant band is located at 3.312 eV, which was attributed to the free electronic radiative transition to neutral acceptor level (FA) in ZnO. The P_Zn-2V_Zn acceptor complex level was estimated to be at E_V=122 meV.     

Fabrication of high hole-carrier density p-type ZnO thin films by N-Al co-doping

In order to obtain p-type ZnO thin films, effect of atomic ratio of Zn:N:Al on the electronic and structural characteristic of ZnO thin films was investigated. Hall measurement indicated that with the increase of Al doping, conductive type of as-grown ZnO thin films changed from n-type to p-type and then to n-type again, reasons are discussed in details. Results of X-ray diffraction revealed that co-doped ZnO thin films have similar crystallization characteristic (0 0 2 preferential orientation) like that of un-doping. However, SEM measurement indicated that co-doped ZnO thin films have different surface morphology compared with un-doped ZnO thin films. p-type ZnO thin films with high hole concentration were obtained on glass (4.6 × 10¹⁸ cm⁻³) and n-type silicon (7.51 × 10¹⁹ cm⁻³), respectively.     

Formation of Al-N co-doped p-ZnO/n-Si (1 0 0) heterojunction structure by RF co-sputtering technique

Al-N co-doped ZnO (ZnO:Al-N) thin films were grown on n-Si (1 0 0) substrate by RF co-sputtering technique. As-grown ZnO:Al-N film exhibited n-type conductivity whereas on annealing in Ar ambient the conduction of ZnO:Al-N film changes to p-type, typically at 600 °C the high hole concentration of ZnO:Al-N co-doped film was found to be 2.86 × 10¹⁹ cm⁻³ and a low resistivity of 1.85 × 10⁻² Ω-cm. The current-voltage characteristics of the obtained p-ZnO:Al-N/n-Si heterojunction showed good diode like rectifying behavior. Room temperature photoluminescence spectra of annealed co-doped films revealed a dominant peak at 3.24 eV.     

Improvement of electrical and optical properties of Ga and N co-doped p-type ZnO thin films with thermal treatment

Ga and N co-doped p-type ZnO thin films were epitaxially grown on sapphire substrate using magnetron sputtering technique. The process of synthesized Ga and N co-doped ZnO films was performed in ambient gas of N₂O. Hall measurement shows a significant improvement of p-type characteristics with rapid thermal annealing (RTA) process in N₂ gas flow, where more N acceptors are activated. The film rapid thermal annealed at 900 °C in N₂ ambient revealed the highest carrier concentration of 9.36 × 10¹⁹ cm⁻³ and lowest resistivity of 1.39 × 10⁻¹ Ω cm. In room and low temperature photoluminescence measurements of the as grown and RTA treated film, donor acceptor pair emission and exciton bound to acceptor recombination at 3.25 and 3.357 eV, respectively, were observed.     

The luminescence of ZnO film grown on GaAs interlayer by PA-MOCVD

ZnO film was firstly prepared by PA-MOCVD method on the substrate pre-coated with GaAs interlayer. Hall measurement found that the GaAs interlayer had important effects on the electrical behavior of the ZnO film. It could make the ZnO film convert to p-type conductivity. The XPS results confirmed that the acceptor was arsenic. And the acceptor level was 130 meV above the ZnO valence band maximum. Low-temperature PL measurement was introduced to investigate the optical properties of both as-grown n-type and arsenic doped p-type ZnO films. Then, based on this technology, ZnO homojunction light emitting device (LED) was fabricated with arsenic doped p-type ZnO and unintentionally doped n-type ZnO on GaAs/p⁺-Si substrate. Its current-voltage (I-V) character showed a typical rectification behavior, which was different from the n-ZnO/p⁺-Si structure. The UV-visible (385-580 nm) electroluminescence was detected under relatively low current injection condition from the n-ZnO/p-ZnO/p⁺-Si LED.     

Effects of annealing ambience on ZnO:N films grown by MOCVD and the p-type doping mechanism of ZnO:N films investigated by XANES

ZnO:N thin films were deposited on sapphire substrate by metal organic chemical vapor deposition with NH₃ as N-doping sources. The reproducible p-type ZnO:N film with hole concentration of ∼10¹⁷ cm⁻³ was successfully achieved by subsequent in situ thermal annealing in N₂O plasma protective ambient, while only weak p-type ZnO:N film with remarkably lower hole concentration of ∼10¹⁵ cm⁻³ was obtained by annealing in O₂ ambient. To understand the mechanism of the p-type doping behavior of ZnO:N film, X-ray photoelectron spectroscopy (XPS) and soft X-ray absorption near-edge spectroscopy (XANES) measurements have been applied to investigate the local electronic structure and chemical states of nitrogen atoms in ZnO:N films.     

p-Type conduction in phosphorus-doped ZnO thin films by MOCVD and thermal activation of the dopant

Phosphorus-doped p-type ZnO thin films have been realized by metalorganic chemical vapor deposition (MOCVD). The conduction type of ZnO films is greatly dependent on the growth temperature. ZnO films have the lowest resistivity of 11.3 Ωcm and the highest hole concentration of 8.84 × 10¹⁸ cm⁻³ at 420 °C. When the growth temperature is higher than 440 °C, p-type ZnO films cannot be achieved. All the films exhibited p-type conduction after annealing, and the electrical properties were improved comparing with the as-grown samples. Secondary ion mass spectroscopy (SIMS) test proved that phosphorus (P) has been incorporated into ZnO.     

Structural and electrical properties of nitrogen and aluminum codoped p-type ZnO films

To resolve the problem of p-type doping in ZnO, nitrogen and aluminum (N-Al) codoped ZnO films were prepared by the ultrasonic spray pyrolysis (USP) technique. The structural and electrical properties of N-Al codoped ZnO films were investigated. The results demonstrate that the undoped ZnO films exhibit the preferential orientation of (002) plane, while ZnO films show high orientation of (101) plane after codoping with N and Al. The N-Al codoped ZnO films under optimum conditions show p-type conduction, with a low resistivity of 1.7×10⁻²Ω cm, carrier concentration of 5.09×10¹⁸ cm⁻³ and high Hall mobility of 73.6 cm² V⁻¹ s⁻¹. A conversion from p-type conduction to n-type was observed during the increase of measurement temperature.     

Photoluminescence properties of nitrogen-doped ZnO films deposited on ZnO single crystal substrates by the plasma-assisted reactive evaporation method

Photoluminescence (PL) spectra of nitrogen-doped ZnO films (ZnO:N films) grown epitaxially on n-type ZnO single crystal substrates by using the plasma-assisted reactive evaporation method were measured at 5 K. In PL spectra, free exciton emission at about 3.375 eV was very strong and emissions at 3.334 and 3.31 eV were observed. These two emissions are discussed in this paper. The nitrogen concentration in ZnO:N films measured by secondary ion mass spectroscopy was 10^19-20 cm⁻³. Current-voltage characteristics of the junction consisting of an n-type ZnO single crystal substrate and ZnO:N film showed good rectification. Also, ultraviolet radiation and visible light were emitted from this junction under a forward bias at room temperature. It is therefore thought that ZnO:N films have good crystallinity and that doped nitrogen atoms play a role as acceptors in ZnO:N films to form a good pn junction. From these phenomena and the excitation intensity dependency of PL spectra, emissions at 3.334 and 3.31 eV were assigned to neutral acceptor-bound exciton (A⁰X) emission and a donor-acceptor pair (DAP) emission due to doped nitrogen, respectively.     

Effect of substrate temperature on properties of multilayer thin film based on ZnO and Mo-doped indium oxide

Zinc oxide/molybdenum-doped indium oxide/zinc oxide (ZnO/IMO/ZnO) multilayer thin films are grown using pulsed laser deposition technique. The effect of substrate temperature on structural, optical, and electrical properties of multilayer films is studied. It is observed that films grown at high substrate temperature are oriented along (0 0 2) and (2 2 2) direction for ZnO and IMO respectively. The crystallinity of these films increases with increase in substrate temperature. It is also seen that conductivity, carrier concentration, and mobility increase with increase in temperature. The multilayer film grown at 500 °C has low resistivity (7.67 × 10⁻⁵ Ω cm), high carrier concentration (3.90 × 10²⁰ cm⁻³), and high mobility (209 cm²/Vs).     

Electron transport in high quality undoped ZnO film grown by plasma-assisted molecular beam epitaxy

High quality ZnO films were grown on c-plane sapphire substrate using low temperature ZnO buffer layer by plasma-assisted molecular beam epitaxy. The film deposited at 720 °C showed the lowest value of full-width at half maximum for the symmetric (0002) diffraction peak of about 86 arcsec. The highest electron mobility in the films was about 103-105 cm²/V s. From temperature-dependent Hall effect measurements, the mobility strongly depends on the dislocation density at low temperature region and the polar optical phonon scattering at high temperature, respectively. Moreover, by obtaining the activation energy of the shallow donors, it was supposed that hydrogen was source of n-type conductivity in as-grown ZnO films.     

Rapid thermal annealing induced changes on the contact of Ni/Au to N-doped ZnO

N-doped p-type ZnO (p ∼ 10¹⁸cm^-3) was grown on sapphire(0 0 0 1) substrate by metal-organic chemical vapor deposition method. Ni/Au metal was evaporated on the ZnO film to form contacts. As-deposited contacts were rectifying while ohmic behavior was achieved after thermally annealing the contacts in nitrogen environment. Specific contact resistance was determined by circular transmission line method and a minimum specific contact resistance of 8 × 10⁻⁴ Ω cm² was obtained for the sample annealed at 650 °C for 30 s. However, Hall effect measurements indicate that, as the rapid thermal annealing temperature increased up to 550 °C or higher the samples’ conductive type have changed from p-type to n-type, which may be due to the instability nature of the present-day p-type N-doped ZnO or the dissociation of ZnO caused by annealing process in N₂ ambient. Evolution of the sample's electric characteristics and the increment of metal/semiconductor interface states induced by rapid thermal annealing process are supposed to be responsible for the improvement of electrical properties of Au/Ni/ZnO.     

Effects of growth temperature on Li-N dual-doped p-type ZnO thin films prepared by pulsed laser deposition

Li-N dual-doped p-type ZnO (ZnO:(Li,N)) thin films have been prepared by pulsed laser deposition. The introduction of Li and N was confirmed by secondary ion mass spectrometry measurements. The structural, electrical, and optical properties as a function of growth temperature were investigated in detail. The lowest room-temperature resistivity of 3.99 Ω cm was achieved at the optimal temperature of 450 °C, with a Hall mobility of 0.17 cm²/V s and hole concentration of 9.12 × 10¹⁸ cm⁻³. The ZnO:(Li,N) films exhibited good crystal quality with a complete c-axis orientation, a high transmittance (about 90%) in the visible region, and a predominant UV emission at room temperature. The two-layer-structure p-ZnO:(Li,N)/n-ZnO homojunctions were fabricated on a sapphire substrate. The current-voltage characteristics exhibited the rectifying behavior of a typical p-n junction.     

Transparent conductive ZnO:Al films grown by atomic layer deposition for Si-wire-based solar cells

Structural, electrical, and optical properties of atomic layer-controlled Al-doped ZnO (ZnO:Al) films grown by atomic layer deposition (ALD) on glass substrates were characterized at various growth temperatures for use as transparent electrodes. The Al atomic content in ZnO:Al films increased due to the reduced ZnO film growth rate with increasing temperature. The preferred orientation of ZnO:Al films was changed, and the optimum condition for best crystallinity was identified by varying the growth temperature. Furthermore, the carrier concentration of free electron was increased by substituting the Zn sites with Al atoms in the crystal, resulting from monolayer growth based on alternate self-limiting surface chemical reactions. The electrical resistivity of ZnO:Al film grown by ALD at 225 °C reached the lowest value of 8.45 × 10⁻⁴ Ω cm, with a carrier mobility of 9.00 cm² V⁻¹ s⁻¹ and optical transmittance of ∼93%. This result demonstrates that ZnO:Al films grown by ALD possess excellent potential for applications in electronic devices and displays as transparent electrodes and surface passivation layers.     

Realization of p-ZnO thin films by GaP codoping

An attempt has been made to realize p-ZnO by directly doping (codoping) GaP into ZnO thin films. GaP codoped ZnO thin films of different concentrations (1, 2 and 4 mol%) have been grown by RF magnetron sputtering. The grown films on sapphire substrate have been characterized by X-ray diffraction (XRD), Hall measurement, Photoluminescence (PL) and Energy dispersive spectroscopy (EDS) to validate the p-type conduction. XRD result shows that all the films have been preferentially oriented along (0 0 2) orientation. The decrease of full-width at half maximum (FWHM) with increase in GaP doping depicts the decrease in native donor defects. Hall measurement shows that among the three films, 2 and 4 mol% GaP doped ZnO shows p-conductivity due to the sufficient amount of phosphorous incorporation. It has been found that low resistivity (2.17 Ωcm) and high hole concentration (1.8×10¹⁸ cm⁻³) for 2% GaP codoped ZnO films due to best codoping. The red shift in near-band-edge (NBE) emission and donar-acceptor-pair (DAP) and neutral acceptor bound recombination (A°X) observed by room temperature and low temperature (10 K) PL, respectively, well acknowledged the formation of p-ZnO. The incorporated phosphorous in the film has been also confirmed by EDS analysis.     

Influence of sputter-etching of substrate on the microstructural and optical properties of ZnO films deposited by RF magnetron sputtering

ZnO films were prepared using radio frequency magnetron sputtering on Si(1 1 1) substrates that were sputter-etched for different times ranging from 10 to 30 min. As the sputter-etching time of the substrate increases, both the size of ZnO grains and the root-mean-square (RMS) roughness decrease while the thickness of the ZnO films shows no obvious change. Meanwhile, the crystallinity and c-axis orientation are improved by increasing the sputter-etching time of the substrate. The major peaks at 99 and 438 cm⁻¹ are observed in Raman spectra of all prepared films and are identified as E₂(low) and E₂(high) modes, respectively. The Raman peak at 583 cm⁻¹ appears only in the films whose substrates were sputter-etched for 20 min and is assigned to E₁(LO) mode. Typical ZnO infrared vibration peak located at 410 cm⁻¹ is found in all FTIR spectra and is attributed to E₁(TO) phonon mode. The shoulder at about 382 cm⁻¹ appearing in the films whose substrates were sputter-etched for shorter time (10-20 min) originates from A₁(TO) phonon mode. The results of photoluminescence (PL) spectra reveal that the optical band gap (Eg) of the ZnO films increases from 3.10 eV to 3.23 eV with the increase of the sputter-etching time of the substrate.