Formation of Al-N co-doped p-ZnO/n-Si (1 0 0) heterojunction structure by RF co-sputtering technique

Al-N co-doped ZnO (ZnO:Al-N) thin films were grown on n-Si (1 0 0) substrate by RF co-sputtering technique. As-grown ZnO:Al-N film exhibited n-type conductivity whereas on annealing in Ar ambient the conduction of ZnO:Al-N film changes to p-type, typically at 600 °C the high hole concentration of ZnO:Al-N co-doped film was found to be 2.86 × 10¹⁹ cm⁻³ and a low resistivity of 1.85 × 10⁻² Ω-cm. The current-voltage characteristics of the obtained p-ZnO:Al-N/n-Si heterojunction showed good diode like rectifying behavior. Room temperature photoluminescence spectra of annealed co-doped films revealed a dominant peak at 3.24 eV.     

Structural and electrical properties of nitrogen and aluminum codoped p-type ZnO films

To resolve the problem of p-type doping in ZnO, nitrogen and aluminum (N-Al) codoped ZnO films were prepared by the ultrasonic spray pyrolysis (USP) technique. The structural and electrical properties of N-Al codoped ZnO films were investigated. The results demonstrate that the undoped ZnO films exhibit the preferential orientation of (002) plane, while ZnO films show high orientation of (101) plane after codoping with N and Al. The N-Al codoped ZnO films under optimum conditions show p-type conduction, with a low resistivity of 1.7×10⁻²Ω cm, carrier concentration of 5.09×10¹⁸ cm⁻³ and high Hall mobility of 73.6 cm² V⁻¹ s⁻¹. A conversion from p-type conduction to n-type was observed during the increase of measurement temperature.     

Induction of p-type conduction in sputtered deposited Al-N codoped ZnO thin films

Al and N codoped ZnO thin films were grown on n-Si (100) substrate by sputtering technique. Hall effect measurements of as-grown films exhibited n-type conduction, however 500 °C Ar annealed codoped films showed p-type conductivity with a hole concentration of 9.9 × 10¹⁶ cm^− 3, resistivity of 15.95 Ω-cm and hole mobility of 3.95 cm²/Vs, respectively. Codoped ZnO thin films were found to be highly c-axis oriented with good crystal quality. A neutral acceptor-bound exciton and donor-acceptor-pair emissions that appeared at room temperature photoluminescence measurement verify p-type conduction in Al and N codoped ZnO film. The current-voltage characteristics of p-n heterojunction evidently showed a diode like rectifying behaviour.     

Improvement of electrical and optical properties of Ga and N co-doped p-type ZnO thin films with thermal treatment

Ga and N co-doped p-type ZnO thin films were epitaxially grown on sapphire substrate using magnetron sputtering technique. The process of synthesized Ga and N co-doped ZnO films was performed in ambient gas of N₂O. Hall measurement shows a significant improvement of p-type characteristics with rapid thermal annealing (RTA) process in N₂ gas flow, where more N acceptors are activated. The film rapid thermal annealed at 900 °C in N₂ ambient revealed the highest carrier concentration of 9.36 × 10¹⁹ cm⁻³ and lowest resistivity of 1.39 × 10⁻¹ Ω cm. In room and low temperature photoluminescence measurements of the as grown and RTA treated film, donor acceptor pair emission and exciton bound to acceptor recombination at 3.25 and 3.357 eV, respectively, were observed.     

Investigation of p-type behavior in Ag-doped ZnO thin films by E-beam evaporation

Ag-doped ZnO (ZnO:Ag) thin films were grown on glass substrates by E-beam evaporation technique. The structural, electrical and optical properties of the films were investigated as a function of annealing temperature. The films were subjected to post annealing at different temperatures in the range of 350-650 °C in an air ambient. All the as grown and annealed films at temperature of 350 °C showed p-type conduction. The films lost p-type conduction after post annealing treatment temperature of above 350 °C, suggesting a narrow post annealing temperature window for the fabrication of p-type ZnO:Ag films. ZnO:Ag film annealed at 350 °C revealed lowest resistivity of 7.25 × 10⁻² Ω cm with hole concentration and mobility of 5.09 × 10¹⁹ cm⁻³ and 1.69 cm²/V s, respectively. Observation of a free-to-neutral-acceptor (e,A^o) and donor-acceptor-pair (DAP) emissions in the low temperature photoluminescence measurement confirms p-type conduction in the ZnO:Ag films.     

Ag-N doped ZnO film and its p-n junction fabricated by ion beam assisted deposition

Ag-N doped ZnO film was synthesized by ion beam assisted deposition and its electrical properties and annealing property were investigated. The films remained p-type even after annealing at 400 °C in air for 10 min. While the annealing temperature went up to 500 °C, the conduction type of these films shifted from p-type to n-type. The p-type ZnO film revealed low resistivity (0.0016 Ω cm), low Hall mobility (0.65 cm² V⁻¹ s⁻¹) and high carrier concentration (5.8 × 10²⁰ cm⁻³). ZnO p-n homojunction consisting of a p-type layer (Ag-N doped ZnO film) and an n-type layer (In-doped ZnO film) had been fabricated by ion beam assisted deposition. With electrical measurement, its current-voltage curve had a typical rectifying characteristic with current rectification ratio of 25 at bias ±5 V and a reverse current of 0.01 mA at −5 V. The depletion width was estimated 3.8 nm by using p-n junction equation.     

p-Type conduction in phosphorus-doped ZnO thin films by MOCVD and thermal activation of the dopant

Phosphorus-doped p-type ZnO thin films have been realized by metalorganic chemical vapor deposition (MOCVD). The conduction type of ZnO films is greatly dependent on the growth temperature. ZnO films have the lowest resistivity of 11.3 Ωcm and the highest hole concentration of 8.84 × 10¹⁸ cm⁻³ at 420 °C. When the growth temperature is higher than 440 °C, p-type ZnO films cannot be achieved. All the films exhibited p-type conduction after annealing, and the electrical properties were improved comparing with the as-grown samples. Secondary ion mass spectroscopy (SIMS) test proved that phosphorus (P) has been incorporated into ZnO.     

Preparation and characteristics of transparent p-type ZnO film by Al and N co-doping method

Al-N co-doped ZnO films were fabricated by gaseous ammonia annealing at various temperatures. The structure and the electrical properties of Al-N-doped ZnO films strongly depend on the annealing temperature. XRD and SEM analysis indicate that the ZnO films possess a good crystallinity with c-axis orientation, uniform thickness and dense surface. Optical transmission spectra show a high transmittance (∼85%) in the visible region. Hall measurement demonstrates that ZnO films have p-type conduction with high carrier concentration of 8.3 × 10¹⁸ cm⁻³ and low resistivity of 25.0 Ω cm when the annealing temperature is 700 °C. Also the growth process of Al-N co-doped at various temperatures is discussed in detail.     

Fabrication and characterization of magnetron sputtered arsenic doped p-type ZnO epitaxial thin films

Arsenic doped p-type ZnO thin films were grown on sapphire substrate by magnetron sputtering. As grown films reveal p-type conduction confirmed by Hall-effect and photoluminescence measurements. The p-type film with a hole concentration of 2.16× 10¹⁷ cm⁻³, mobility of 1.30 cm²/V.s and resistivity of 22.29 Ω-m were obtained at substrate temperature of 700 °C. ZnO homojunction synthesized by in-situ deposition of As doped p-ZnO layer on Al doped n-ZnO layer showed p-n diode like characteristics. X-ray pole figure and Transmission Electron Microscope studies confirm epitaxial nature of the films. Photoluminescence results exhibit the peaks associated with donor acceptor pair emission.     

Preparation and characterization of n-type conductive (Al, Co) co-doped ZnO thin films deposited by sputtering from aerogel nanopowders

Highly transparent, n-type conducting ZnO thin films were obtained by low temperature magnetron sputtering of (Co, Al) co-doped ZnO nanocrystalline aerogels. The nanoparticles of ∼30 nm size were synthesized by a sol-gel method using supercritical drying in ethyl alcohol. The structural, optical and electrical properties of the films were investigated. The ZnO films were polycrystalline textured, preferentially oriented with the (0 0 2) crystallographic direction normal to the film plane. The films show within the visible wavelength region an optical transmittance of more than 90% and a low electrical resistivity of 3.5 × 10⁻⁴ Ω cm at room temperature.     

Enhanced hardness in B-doped ZnO thin films on fused quartz substrates by pulsed-laser deposition

B-doped ZnO thin films have been fabricated on fused quartz substrates using boron-ZnO mosaic target by pulsed-laser deposition technique, and the mechanical properties have been studied by nanoindentation continuous stiffness measurement technique and transmission electron microscope (TEM). Nanoindentation measurement revealed that the hardness of B-doped ZnO films, 9.32 ± 0.90 to 12.10 ± 1.00 GPa, is much greater than that of undoped ZnO films and very close to that of traditional semiconductor Si. The mean transmittance (%) is larger than 81% in the visible range (380-780 nm) for all the films, and the Hall effect measurement showed that the carrier density is around 2 × 10²⁰ cm⁻³ and the resistivity lower than 3 × 10⁻³ Ω cm. TEM characteristics show undoped thin films have more amorphous area between grains while the B-doped ZnO films have thin grain boundaries. We suggest that the grain boundaries act as the strain compensation sites and the decrease in thickness of grain boundaries enhances the hardness of the B-doped ZnO films.     

Structural, optical and electronic properties of P doped p-type ZnO thin film

P doped ZnO films were grown on quartz by radio frequency-magnetron sputtering method using a ZnO target mixed with 1.5 at% P₂O₅ in the atmosphere of Ar and O₂ mixing gas. The as-grown P doped ZnO film showed n-type conductivity, which was converted to p-type after 800 °C annealing in Ar gas. The P doped ZnO has a resistivity of 20.5 Ω cm (p∼2.0×10¹⁷ cm⁻³) and a Hall mobility of 2.1 cm² V⁻¹ s⁻¹. XRD measurement indicated that both the as-grown and the annealed P doped ZnO films had a preferred (0 0 2) orientation. XPS study agreed with the model that the P_Zn-2V_Zn acceptor complex was responsible for the p-type conductivity as found in the annealed P-doped ZnO. Temperature-dependent photoluminescence (PL) spectrum showed that the dominant band is located at 3.312 eV, which was attributed to the free electronic radiative transition to neutral acceptor level (FA) in ZnO. The P_Zn-2V_Zn acceptor complex level was estimated to be at E_V=122 meV.     

Electrical and optical properties of ZnO films prepared by sputtering of ZnO targets containing AlN

ZnO films prepared from the ZnO target containing 2% AlN are transparent irrespective of radio frequency (RF) power. The obtained ZnO films have the carrier density of 3.8 × 10²⁰ cm⁻³ or less and the low mobility of 5.3-7.8 cm²/(V s). In the case of 5% AlN target, ZnO films prepared at 40, 60 and 80 W are transparent, whereas ZnO films prepared at 100 and 120 W are colored. As RF power increases from 40 to 120 W, the carrier density increases straightforwardly up to 5.5 × 10²⁰ cm⁻³ at 100 W and is oppositely reduced to 3.2 × 10²⁰ cm⁻³ at 120 W. In the case of 10% AlN target, ZnO films prepared at 60 W or more are colored, and have the carrier density of 4 × 10²⁰ cm⁻³ or less. The N-concentration in these colored films is estimated to be 1% or less. The Al-concentration in the ZnO films prepared from the 5 and 10% AlN targets is higher than 2%. The carrier density of the ZnO films containing Al and N atoms is nearly equal to that of ZnO films doped with Al atoms alone. There is no evidence in supporting the enhancement of the carrier density via the formation of N-Al_xZn_4−x clusters (4 ≥ x ≥ 2).     

Fabrication of Sb-doped p-type ZnO thin films by pulsed laser deposition

p-Type ZnO thin films have been realized via monodoping antimony (Sb) acceptor by using pulsed laser deposition. The obtained films with the best electrical properties show a hole concentration in the order of 10¹⁸ cm⁻³ and resistivity in the range of 2-4 Ω cm. X-ray diffraction measurements revealed that all the films possessed a good crystallinity with (0 0 2)-preferred orientation. Guided by X-ray photoemission spectroscopy analysis and a model for large-sized-mismatched group-V dopant in ZnO, an Sb_Zn-2V_Zn complex is believed to be the most possible acceptor in the Sb-doped p-type ZnO thin films.     

Characteristics of ZnO:Al thin films co-doped with hydrogen and fluorine

Fluorine and hydrogen co-doped ZnO:Al (AZO) films were prepared by radio frequency (rf) magnetron sputtering of ZnO targets containing 1 wt.% Al₂O₃ on Corning glass at substrate temperature of 150 °C with Ar/CF₄/H₂ gas mixtures, and the structural, electrical and optical properties of the as-deposited and the vacuum-annealed films were investigated. In as-deposited state, films with fairly low resistivity of 3.9-4 × 10⁻⁴ Ω cm and very low absorption coefficient below 900 cm⁻¹ when averaged in 400-800 nm could be fabricated. After vacuum-heating at 300 °C, the minimum resistivity of 2.9 × 10⁻⁴ Ω cm combined with low absorption loss in visible region, which enabled the figure of merit to uplift as high as 4 Ω⁻¹, could be obtained for vacuum-annealed film. It was shown that, unlike hydrogenated ZnO films which resulted in degradation upon heating in vacuum at moderately high temperature, films with fluorine addition could yield improved electrical properties mostly due to enhanced Hall mobility while preserving carrier concentration level. Furthermore, stability in oxidizing environment could be improved by fluorine addition, which was ascribed to the filling effect of dangling bonds at the grain boundaries. These results showed that co-doping of hydrogen and fluorine into AZO films with low Al concentration could be remarkably compatible with thin film solar cell applications.     

Comparison of ferromagnetism in n- and p-type magnetic semiconductor thin films of ZnCoO

Both n- and p-type diluted magnetic semiconductor ZnCoO are made by magnetron co-sputtering with, respectively, dopants of Al and dual dopants of Al and N. The two sputtering targets are compound ZnCoO with 5% weight of Co and pure metal Al. Sputtering gases for n- and p-type films are pure Ar and N₂, respectively. These films are magnetic at room temperature and possess free electron- and hole-concentration of 5.34×10²⁰ and 5.27×10¹³ cm⁻³. Only the n-type film exhibits anomalous Hall-effect signals. Magnetic properties of these two types of films are compared and discussed based on measurements of microstructure and magneto-transport properties.     

Rapid thermal annealing induced changes on the contact of Ni/Au to N-doped ZnO

N-doped p-type ZnO (p ∼ 10¹⁸cm^-3) was grown on sapphire(0 0 0 1) substrate by metal-organic chemical vapor deposition method. Ni/Au metal was evaporated on the ZnO film to form contacts. As-deposited contacts were rectifying while ohmic behavior was achieved after thermally annealing the contacts in nitrogen environment. Specific contact resistance was determined by circular transmission line method and a minimum specific contact resistance of 8 × 10⁻⁴ Ω cm² was obtained for the sample annealed at 650 °C for 30 s. However, Hall effect measurements indicate that, as the rapid thermal annealing temperature increased up to 550 °C or higher the samples’ conductive type have changed from p-type to n-type, which may be due to the instability nature of the present-day p-type N-doped ZnO or the dissociation of ZnO caused by annealing process in N₂ ambient. Evolution of the sample's electric characteristics and the increment of metal/semiconductor interface states induced by rapid thermal annealing process are supposed to be responsible for the improvement of electrical properties of Au/Ni/ZnO.     

Effects of growth temperature on Li-N dual-doped p-type ZnO thin films prepared by pulsed laser deposition

Li-N dual-doped p-type ZnO (ZnO:(Li,N)) thin films have been prepared by pulsed laser deposition. The introduction of Li and N was confirmed by secondary ion mass spectrometry measurements. The structural, electrical, and optical properties as a function of growth temperature were investigated in detail. The lowest room-temperature resistivity of 3.99 Ω cm was achieved at the optimal temperature of 450 °C, with a Hall mobility of 0.17 cm²/V s and hole concentration of 9.12 × 10¹⁸ cm⁻³. The ZnO:(Li,N) films exhibited good crystal quality with a complete c-axis orientation, a high transmittance (about 90%) in the visible region, and a predominant UV emission at room temperature. The two-layer-structure p-ZnO:(Li,N)/n-ZnO homojunctions were fabricated on a sapphire substrate. The current-voltage characteristics exhibited the rectifying behavior of a typical p-n junction.     

Oxygen influence on sputtered high rate ZnO:Al films from dual rotatable ceramic targets

In this study, the influence of oxygen on high rate (up to 110 nm m/min) sputtered aluminum doped zinc oxide films (ZnO:Al) was systematically investigated. Different oxygen gas flows from 0 sccm to 8 sccm were inputted into the chamber during the preparation of ZnO:Al films from dual rotatable ceramic targets under high discharge power (14 kW). The resistivity increases from 4.2 × 10⁻⁴ Ω cm to 4.3 × 10⁻² Ω cm with the rising oxygen gas flow. While both the carrier concentration and mobility drop by one order of magnitude from 3.4 × 10²⁰ cm⁻³ to 2.5 × 10¹⁹ cm⁻³ and from 43.5 cm²/V s to 5.6 cm²/V s, respectively. The as-grown ZnO:Al films and after-etched ZnO:Al films after a chemical wet etching step in diluted HCl solution (0.5%) exhibit different surface structures. All films show high light transmission and low light absorption but different light scattering properties (diffusion and haze) because of different surface structures. Moreover, ZnO:Al films display different optical bandgaps between 3.51 eV and 3.27 eV, which are corresponding to different carrier concentrations. The variation of mobility and morphology is related with chemisorption of oxygen in the grain boundaries as well as high energetic oxygen ions bombardment.     

Nitrogen-doped ZnO prepared by capillaritron reactive ion beam sputtering deposition

Nitrogen-doped ZnO thin films have been prepared by reactive ion beam sputtering deposition utilizing a capillaritron ion source. X-ray diffraction (XRD) analysis of the as-deposited film exhibits a single strong ZnO (002) diffraction peak centred at 34.40°. Post-growth annealing causes increase of grain size and decrease of c-axis lattice constant. Micro-Raman spectroscopy analysis of the as-deposited film shows strong nitrogen-related local vibration mode at 275, 582, 640 and 720 cm⁻¹, whereas the E₂ mode of ZnO at 436 cm⁻¹ can barely be identified. Annealing at 500-800 °C causes decrease of 275, 582, 640 and 720 cm⁻¹ and increase of 436 cm⁻¹ intensity, indicating out-diffusion of nitrogen and improvement of ZnO crystalline quality. Unlike un-doped ZnO, the surface roughness of nitrogen-doped ZnO deteriorates after annealing, which is also attributed to the out-diffusion of nitrogen. A nitrogen concentration of ∼10²¹/cm³ was observed while type conversion from n-type to p-type was not achieved, which is likely due to the formation of Zn_I-N_O or (N₂)_O that act as donor/double donors.