Nanocomposite hydrogel consisting of Na‐montmorillonite with enhanced mechanical properties

A new kind of nanocomposite (NC) hydrogel with Na‐montmorillonite (MMT) is presented in this article. The NC hydrogels were synthesized by free radical copolymerization of acrylamide and (3‐acrylamidopropyl) trimethylammonium chloride (ATC) in the presence of MMT and N,N′‐methylene‐bis‐acrylamide used as chemical cross‐linker. Due to the cation‐exchange reaction between MMT and ATC (cationic monomer) during the synthesis of NC hydrogels, MMT platelets were considered chemical “plane” cross‐linkers, different from “point” cross‐linkers. With increasing amount of MMT, the crosslinking degree enhanced, causing a decrease of the swelling degree at equilibrium. Investigations of mechanical properties indicated that NC hydrogels exhibited enhanced strength and toughness, which resulted from chemical interaction between exfoliated MMT platelets and polymer chains in hydrogels. Dynamic shear measurements showed that both storage modulus and loss modulus increased with increasing MMT content. The idea described here provided a new route to prepare hydrogels with high mechanical properties by using alternative natural Na‐MMT. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1020–1026     

Naphthalimide‐phthalimide derivative based photoinitiating systems for polymerization reactions under blue lights

Naphthalimide‐phthalimide derivatives (NDPDs) have been synthesized and combined with an iodonium salt, N‐vinylcarbazole, amine or 2,4,6‐tris(trichloromethyl)‐1,3,5‐triazine to produce reactive species (i.e., radicals and cations). These generated reactive species are capable of initiating the cationic polymerization of epoxides and/or the radical polymerization of acrylates upon exposure to very soft polychromatic visible lights or blue lights. Compared with the well‐known camphorquinone based systems used as references, the novel NDPD based combinations employed here demonstrate clearly higher efficiencies for the cationic polymerization of epoxides under air as well as the radical polymerization of acrylates. Remarkably, one of the NDPDs (i.e., NDPD2) based systems is characterized by an outstanding reactivity. The structure/reactivity/efficiency relationships of the investigated NDPDs were studied by fluorescence, cyclic voltammetry, laser flash photolysis, electron spin resonance spin trapping, and steady state photolysis techniques. The key parameters for their reactivity are provided. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 665–674     

非傍轴平顶高斯光束M2因子两种定义的比较研究

基于功率密度的二阶矩方法,推导出了非傍轴平顶高斯(FG)光束束宽和远场发散角的解析表达式·研究表明,当w0/λ→0时,远场发散角趋于渐近值θmax=63.435°,与阶数无关·使用非傍轴高斯光束代替傍轴高斯光束作为理想光束,研究了非傍轴FG光束的M2因子,并与传统定义的M2因子作了比较·在非傍轴范畴,非傍轴FG光束的M2因子不仅与阶数N有关,而且与w0/λ有关·按照定义,当w0/λ→0时,非傍轴FG光束的M2因子不等于0,对阶数N=1,2,3时,M2因子分别趋于0.913,0.882和0.886·当N→∞时,M2因子取最小值M2min=0.816·     

非傍轴平顶高斯光束M2因子两种定义的比较研究

基于功率密度的二阶矩方法，推导出了非傍轴平顶高斯(FG)光束束宽和远场发散角的解析表达式.研究表明，当w0/λ→0时，远场发散角趋于渐近值θmax=63.435°，与阶数无关.使用非傍轴高斯光束代替傍轴高斯光束作为理想光束，研究了非傍轴FG光束的M2因子，并与传统定义的M2因子作了比较.在非傍轴范畴，非傍轴FG光束的M2因子不仅与阶数N有关，而且与w0/λ有关.按照定义，当w0/λ→0时，非傍轴FG光束的M2因子不等于0，对阶数N=1, 2, 3时，M2因子分别趋于0.913,0.882和0.886.当N→∞时，M2因子取最小值M2min=0.816.     

UV‐ignited frontal polymerization of an epoxy resin

By combining frontal polymerization and radical‐induced cationic polymerization, it was possible to cure thick samples of an epoxy monomer bleached by UV light. The effect of the relative amounts of cationic photoinitiator and radical initiator was thoroughly investigated and was related to the front's velocity and its maximum temperature. The materials obtained were characterized by quantitative conversion also in the deeper layers, not reached by UV light. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2066–2072, 2004     

Cationic polymerization of styrene in a neutral ionic liquid

The cationic polymerization of styrene in a neutral ionic liquid, 1‐butyl‐3‐methylimidazolium hexafluorophosphate, with a 1‐phenetyl chloride/TiCl₄ initiating system is reported. The polymerization proceeds to a high conversion, but an analysis of the matrix‐assisted laser desorption/ionization time‐of‐flight spectra of the polymers indicates that chain transfer is significant, leading to a lack of control over the molecular weight and molecular weight distribution. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3230–3235, 2004     

Dark cure studies of cationic photopolymerizations of epoxides: Characterization of kinetic rate constants at high conversions

The effective propagation rate constant (k_p; averaged over all the propagating active centers) was characterized for solvent‐free cationic photopolymerizations of phenyl glycidyl ether over the entire range of conversions, including the high conversion regime in which mass transfer limitations become important. The profile for the k_p as a function of conversion was found to exhibit a constant plateau value at low to intermediate conversions, followed by a monotonic increase above a threshold value of conversion. To explain this trend, it is proposed that at high conversion the diffusional mobility of the photoinitiator counterion is reduced whereas the mobility of the cationic active center remains high because of reactive diffusion. Therefore, with increasing conversion, the average distance between the active centers and counterions may increase, resulting in an increase in the propagation rate constant. The profiles for the k_p values were investigated as a function of the temperature, photoinitiator anion, and photoinitiator concentration. As the photoinitiator concentration was increased, the plateau value of the effective propagation rate constant decreased whereas the threshold conversion increased. All of the experimental trends are consistent with the proposed increase in ion separation at high conversions. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4409–4416, 2004     

Tetrafunctional initiators for cationic polymerization of olefins

3,3′,5,5′‐Tetrakis(2‐chloro‐2‐propyl)biphenyl (biphenyl tetracumyl chloride, BPTCC) and 1,3‐bis[3,5‐bis(2‐chloro‐2‐propyl)phenoxy]propane (diphenoxypropane tetracumyl chloride, DPPTCC) were synthesized as initiators for quasiliving cationic polymerization of isobutylene (IB). In the synthesis of BPTCC, tetrafunctionality was achieved via the coupling of dimethyl 5‐bromoisophthalate (DMBI) using nickel dibromide bis(triphenylphosphine) and zinc in the presence of a base; in the synthesis of DPPTCC, two equivalents of dimethyl 5‐hydroxyisophthalate were linked via reaction with 1,3‐dibromopropane in the presence of potassium carbonate. Both initiators were used to initiate the polymerization of IB under quasiliving cationic polymerization conditions. PIB initiated from BPTCC revealed a chain end/molecule value (as determined by ¹H‐NMR) of 3.85, verifying the nearly exclusive production of 4‐arm polyisobutylene (PIB). GPC analysis revealed a narrow peak representing the target four‐arm PIB, with a slight shoulder at high elution volumes (low molecular weights). GPC analysis of the PIB initiated by DPPTCC revealed multimodal distributions, suggesting the formation of two‐, three‐, and four‐arm star polymers during the polymerization. This behavior was attributed to Friedel–Crafts alkylation of the initiator core after the addition of one IB unit, which was activated by the electron‐donating oxytrimethyleneoxy linking moiety. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5942–5953, 2004     

Synthesis of Cationic PEM Emulsion and Application in Waste Water Treatment

Cationic polymer as a kind of flocculant is widely applied in purification treatment of waste water. Because it has positive charge group, it is able to connect strongly the suspended matters, short cellulose and other microparticles. The research on synthesis of cationic polymer and application in treatment of waste water is very universal abroad. But domestic research on those is not general. The technology of synthesis of PEM is simple, and the production cost is low. It is easy to apply in treatment of waste water.Synthesis of PEM Emulsion FlocculantSome distilled water, PVA(poly(vinyl alcohol)), EA(ethyl acrylate), and K2S2O8(potassium persulfate) were put into reaction vessel. Kept stirring up under nitrogen. When heated the solution to 40℃, dropped the water solution of MTA[(2-methacryloxylethyl)trimethyl ammonium].Maintained the temperature at 70℃, reacted about 7-8 hours. Then got the PEM emulsion. Changed the ratio of EA and MTA. Obtained a series of PEM emulsions.Stability and Convertibility of PEM EmulsionThe test results showed that when the EA/MTA was 85/15, the PEM emulsion was most stable.When the total monomer quantity was 35%, the convertibility of PEM emulsion was the highest,i.e.98.6%.The MTA Copolymerization Ratio and Morphology of PEM EmulsionWhen the monomers EA/MTA=85/15 and total monomer quantity was 35%, the MTA copolymerization ratio of PEM emulsion was 95.15%(the highest), and the PEM emulsion was some microspheres with 100-180nm of diameter.The Test Results of PEM Emulsion in Treatment of Waste Water The PEM emulsion flocculant was applied in treatment of waste water of paper mill, and measured the precipitation time(t) and transmittancy(T). The test results were showed in table 1. The optimum value of PEM which was able to make the waste water of paper mill into clear water was 0.008%.     

Hybrid free radical/cationic frontal photopolymerizations

The irradiation of hybrid photopolymer systems consisting of a free radically polymerizable multifunctional acrylate monomer and a cationically polymerizable epoxide or oxetane monomer was conducted under conditions where only the free radical polymerization takes place. This results in the formation of a free‐standing polyacrylate network film containing quiescent oxonium ions along with the unreacted cyclic ether monomer. The subsequent application of a point source of heat to the film ignites a cationic ring‐opening frontal polymerization that emanates from that site and propagates to all portions of the irradiated sample. This article examines the impact of various molecular structural and experimental parameters on these novel hybrid frontal polymerizations that produce interpenetrating network polymers. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4331–4340, 2007