聚氯乙烯表面共价键合肝素及抗凝血性的研究

采用Ar等离子体引发聚乙二醇(PEG)在聚氯乙烯(PVC)表面固定化,进一步对固定PEG后的PVC进行肝素化处理,以改善PVC材料的抗凝血性能。探讨了PEG浓度对Ar等离子体固定化反应效果的影响。通过X射线光电子能谱(XPS)、衰减全反射红外光谱(ATR-FTIR)、扫描电镜(SEM)和接触角测定研究了固定PEG前后PVC的表面性能和表面形貌的变化。XPS分析证实肝素已成功地共价键合于PVC表面。采用体外凝血时间测定和血小板粘附实验对材料的抗凝血性能进行评价,结果表明,被修饰PVC材料的抗凝血性能显著提高。     

聚乙烯表面接枝聚合改性及抗凝血性的研究

聚乙烯(PE)膜经Ar等离子体预处理,无光引发剂紫外光照接枝甲基丙烯酸缩水甘油酯(GMA),然后进行肝素化处理,以改善PE的抗凝血性能。用正交实验确定接枝反应的最优条件。通过X-射线光电子能谱(XPS)、衰减全反射红外光谱(ATR-FTIR)、扫描电子显微镜(SEM)和接触角测定PE膜接枝GMA前后表面性能和表面形貌。用复钙时间、凝血酶原时间、部分凝血活酶时间、凝血酶时间和血小板粘附实验对其抗凝血性能进行评价,结果表明,被修饰PE膜的抗凝血性能显著提高。     

Novel surface fixation technology of hydrogel based on photochemical method: Heparin-immobilized hydrogelated surface

This article reports a novel photoinduced surface process technology enabling simultaneous hydrogel formation and its surface fixation on polymeric substrates. The process consists of layering two different types of photoreactive coatings on a polymeric surface, an azidophenyl-bearing polymer as an adhesive layer and cinnamoylated copolymer as a hydrogel layer, and subsequent UV irradiation. The photoreactive adhesive polymer coated on a substrate is poly(m-azidostyrene), in which photoreaction of phenyl azido groups is responsible for the chemical bonding between the substrate and hydrogel. N,N-dimethylacrylamide copolymer containing cinnamate moieties in their side chains, which undergo photocrosslinking via intermolecular dimerization, was applied as an overcoat on the adhesive layer. UV irradiation resulted in the formation of hydrogel chemically bonded onto the substrate. This was confirmed by ESCA measurements. A heparin-immobilized hydrogelated surface with controlled release characteristics was demonstrated. © 1993 John Wiley & Sons, Inc.     

SURFACE MODIFICATION OF BLEND FILMS COMPOSED OF SILK FIBROIN AND POLY（ETHYLENE GLYCOL） MACROMER AND THEIR IN VITRO ANTITHROMBOGENICITY

In order to improve the blood compatibility of silk fibroin (SF), poly(ethylene glycol) macromer (PEGM) in different amounts was added to the SF film to incorporate C=C group into the surface of blend films which were then modified by SO2 gas plasma treatment. ATR-FITR and XPS were used to analyze the chemical change which had occurred on the film‘s surface. When the content of sulfur on the surface of blend films surpasses 1.59%, the antithrombogenicity of plasma treated films increases remarkably due to surface sulfonation. This result implies that SF with blend of PEGM after SO2 plasma treatment have potential use for making blood-contacting biomaterials.     

Evaluation of antithrombogenicity of ion‐implanted silicone rubber

Ion implantations into silicone rods were performed at 150 keV with doses ranging from 1 × 10⁷ to 3 × 10¹⁷ ions/cm². The antithrombogenicity was tested by the superior vena cava (SVC) indwelling method for two days in rats with ¹¹¹In‐tropolone ‐ platelets, and by the inferior vena cava (IVC) indwelling method. Results of the SVC indwelling method showed that platelet accumulation on ion ‐ implanted specimens decreased. Macroscopic views of the ion‐implanted IVC specimens in dogs revealed little thrombus formation. In particular, SVC indwelling method revealed that O₂⁺, K⁺ and Kr⁺ (1 × 10¹⁷ ions/cm²) implantation was most effective in reducing platelet accumulation. Copyright © 1999 John Wiley & Sons, Ltd.