大规模制备Ni80Fe20纳米线阵列及其磁学特性研究

利用电化学沉积方法在高度有序纳米孔氧化铝模板中大规模制备了Ni80 Fe20纳米线阵列.该方法得到的Ni80Fe20纳米线产率高(约1012-1013/cm2),而且这些纳米线阵列具有(111)择优生长取向和很高的纵横比.与体材料相比,这些Ni80Fe20纳米线阵列具有更高的矫顽力和较大的剩磁比等性能,在微型磁性元件领域将具有广泛应用前景.     

Film Thickness Dependence of Rectifying Properties of La1.85Sr0.15CuO4/Nb-SrTiO3 Junctions

In this work, p-n junctions are made from directly depositing optimal doped La1.85Sr0.15CuO4 （LSCO） films on n-type Nb-doped SrTiO3 substrates. Film thickness controlled rectifying behaviors are strikingly displayed. The starting points of the diffusion voltage reduction Vd-on change clearly with varying film thickness. Vd-on and Tc coincide with each other when the film thickness is larger than 300 nm, indicating a close relation between the two parameters. However, when the film is very thin （〈 350 nm） a departure between the two parameters was also observed. A possible reason for this is discussed within the framework of an inhomogeneous Sehottky contact. Enhanced interface inhomogeneity due to the tensile strain appears to be the origin.     

广义Birkhoff自治系统平衡状态的流形稳定性

研究广义Birkhoff自治系统平衡状态流形稳定性.建立广义Birkhoff自治系统的受绕运动方程和平衡方程.由Liapunov稳定性理论给出广义Birkhoff自治系统的平衡状态流形稳定性的有关判据.举例说明结果的应用.     

Enhancing low-field magnetoresistance of La0.67Ca0.33MnO3 films deposited on anodized aluminium-oxide membranes

In this paper we report a new method to fabricate nanostructured films, La0.67Ca0.33MnO3 （LCMO） nanostructured films have been fabricated by using pulsed electron beam deposition （PED） on anodized aluminium oxide （AAO） membranes, The magnetic and electronic transport properties are investigated by using the Quantum Design physics properties measurement system （PPMS） and magnetic properties measurement system （MPMS）. The resistance peak temperature （Tp） is about 85 K and the Curie temperature （To） is about 250 K for the LCMO film on an AAO membrane with a pore diameter of 20nm. Large magnetoresistance ratio （MR） is observed near Tp. The MR is as high as 85% under 1 T magnetic field. The great enhancement of MR at low magnetic fields could be attributed to the lattice distortion and the grain boundary that are induced by the nanopores on the AAO membrane.     

大规模制备Ni80Fe20纳米线阵列及其磁学特性研究

利用电化学沉积方法在高度有序纳米孔氧化铝模板中大规模制备了Ni80₈₀Fe 20₂₀纳米线阵列.该方法得到的Ni80₈₀Fe20₂₀ 纳米线产率高（约1012^{12—101313/cm22）, 而且这些纳米线阵列具有（111）择优生 长取向和很高的纵横比.与体材料相比,这些Ni80₈₀Fe20₂₀纳 米线阵列具 关键词： 纳米线阵列 磁性}     

FIB快速加工纳米孔点阵的新方法

纳米尺度的点阵在纳米器件和基础科学研究方面都具有非常重要的应用.目前普遍采用的聚焦离子束和电子束曝光技术可以很方便的在衬底上加工纳米量级的微细结构，但大面积的图形加工过程需要花费太多的机时.介绍一种利用设计图形BMP文件的像素点阵和实际加工区域之间的匹配关系，通过聚焦离子束加工获得所需要的纳米孔点阵的新方法.采用这种方法可以在短时间内获得大面积的纳米点阵结构. 关键词： 聚焦离子束 电子束曝光 纳米孔点阵     

Fabrication and Characterization of YBa2Cu3Oy Superconducting Nanowires

Ordered YBa2Cu3Oy nanowires have been fabricated by filling YBa2Cu3Oy melting liquid into the pores of the anodized alumina templates. X-ray powder diffraction proves that YBa2Cu3Oy nanowires crystallized in the Y-123 structure. The temperature dependence of ac susceptibility indicates a superconducting transition at 91 K for the YBa2Cu3Oy nanowire array.     

改性光刻胶制备纳米压印模版

制备纳米压印中的模版是压印技术的基本条件.目前很多压印模版是利用高硬度材料制作的，但是这些材料比较难以加工，从而限制了纳米压印技术的发展.提出一种利用光刻胶制备纳米压印模版的方法.利用聚焦离子束对光刻胶的改性作用，控制加工的条件，将柔性的光刻胶改性为硬度很高的材料，从而形成纳米压印模版.这种方法具有速度快、制备简单等特点，是一种新颖的加工方式，扩展了聚焦离子束的加工范围，可用于其他的纳米加工领域. 关键词： 纳米压印 光刻胶 聚焦离子束 纳米孔阵列     

PED沉积La-Sr-Cu-O薄膜表面的有序纳米结构

采用脉冲电子束沉积(PED)技术在Si(100)衬底上生长La_Sr_Cu_O薄膜，在750℃生长温度下获得具有有序纳米结构的表面形貌.采用聚集离子束(FIB)技术对获得的纳米结构进行表征，结果表明，这种有序的纳米结构是由于Si衬底和La_Sr_Cu_O薄膜之间的热膨胀系数和晶格的 失配引起的纳米裂纹.在这些纳米裂纹处，La_Sr_Cu_O成核生长获得独立的纳米线.通过控制 这种有序的纳米结构的生长，这种有序的纳米结构可以用来构造弱连接形成的器件. 关键词： 脉冲电子束沉积 La_Sr_Cu_O薄膜 纳米结构