Electrical Characterization of Metal-Insulator-Metal Capacitors with Atomic-Layer-Deposited HfO2 Dielectrics for Radio Frequency Integrated Circuit Application

Metal-insulator-metal （MIM） capacitors with atomic-layer-deposited HfO2 dielectric and TaN electrodes are investigated for rf integrated circuit applications. For 12nm HfO2, the fabricated capacitor exhibits a high capacitance density of 15.5fF/μm2 at 100kHz, a small leakage current density of 6.4 × 10^-9 A/cm^2 at 1.8V and 125℃, a breakdown electric field of 2.6 MV//cm as well as voltage coefficients of capacitance （VCCs） of 2110ppm/V^2 and -824 ppm/V at 100kHz. Further, it is deduced that the conduction mechanism in the high field range is dominated by the Poole-Frenkel emission, and the conduction mechanism in the low field range is possibly related to trap-assisted tunnelling. Finally, comparison of various HfO2 MIM capacitors is present, suggesting that the present MIM capacitor is a promising candidate for future rf integrated circuit application.     

Ta和TaN底电极对原子层淀积HfO2介质MIM电性能的影响

以Ta,TaN为衬底,采用原子层淀积方法制备高介电常数HfO2介质,比较研究了不同衬底电极对金属-绝缘体-金属(MIM)电容的性能影响.结果表明,采用TaN底电极能够获得较高的电容密度和较小的电容电压系数(VCC),在1MHz下的其电容密度为7.47fF/μm2,VCC为356ppm/V2和493ppm/V,这归因于TaN底电极与HfO2介质之间良好的界面特性.两种电容在3V时漏电流为5×10-8A/cm2左右,基于TaN底电极的MIM电容表现出具有较高的击穿强度,其在室温下的导电机理为肖特基发射.     

High density Al2O3/TaN-based metal--insulator-- metal capacitors in application to radio frequency integrated circuits

Metal-insulator-metal （MIM） capacitors with atomic-layer-deposited Al2O3 dielectric and reactively sputtered TaN electrodes in application to radio frequency integrated circuits have been characterized electrically. The capacitors exhibit a high density of about 6.05 fF/μm^2, a small leakage current of 4.8 × 10^-8 A/cm^2 at 3 V, a high breakdown electric field of 8.61 MV/cm as well as acceptable voltage coefficients of capacitance （VCCs） of 795 ppm/V2 and 268ppm/V at 1 MHz. The observed properties should be attributed to high-quality Al2O3 film and chemically stable TaN electrodes. Further, a logarithmically linear relationship between quadratic VCC and frequency is observed due to the change of relaxation time with carrier mobility in the dielectric. The conduction mechanism in the high field ranges is dominated by the Poole-Frenkel emission, and the leakage current in the low field ranges is likely to be associated with trap-assisted tunnelling. Meanwhile, the Al2O3 dielectric presents charge trapping under low voltage stresses, and defect generation under high voltage stresses, and it has a hard-breakdown performance.     

Ta和TaN底电极对原子层淀积HfO2介质MIM电性能的影响

以Ta,TaN为衬底,采用原子层淀积方法制备高介电常数HfO₂介质,比较研究了不同衬底电极对金属-绝缘体-金属（MIM）电容的性能影响.结果表明,采用TaN底电极能够获得较高的电容密度和较小的电容电压系数（VCC）,在1MHz下的其电容密度为7.47fF/μm²,VCC为356ppm/V²和493ppm/V,这归因于TaN底电极与HfO₂介质之间良好的界面特性.两种电容在3?V时漏电流为5×10^-8关键词： 高介电常数 MIM电容 2薄膜')" href="#">HfO₂薄膜 电极