热损伤奥克托金(HMX) 缺陷的X射线小角散射研究

奥克托金(HMX) 在温度作用下, 会发生热膨胀、 相转变、 热分解等物理、 化学变化, 导致在材料内部产生大量缺陷, 进而会对其宏观性能造成明显影响. 为了深入了解热损伤HMX内部的缺陷演化, 本文采用X射线小角散射和原子力显微技术研究了热损伤HMX的内部缺陷. 结果发现HMX在180 °C相变过程中散射曲线有明显的变化, 颗粒内部生成了大量10nm左右的孔洞, 随着加载时间延长, 其尺寸增大到25nm, 数量明显降低. 当HMX在190 °C、 200 °C保温5h时, 由于HMX热分解内部有新缺陷生成, 小角散射发现其尺寸约为5至8nm, 随着加载温度升高, 其数量增加.     

Small-angle X-ray analysis of the effect of grain size on the thermal damage of octahydro-1, 3, 5, 7-tetranitro-1, 3, 5, 7 tetrazocine-based plastic-bounded expolsives

The microstructure evolution of plastic-bonded explosives(PBXs) after thermal stimulus plays a key role in PBX performance. In this paper, the nanoscale pores of thermal-treated octahydro-1,3,5,7-tetranitro-1,3,5,7 tetrazocine(HMX)-based PBXs with different HMX particle sizes [approximately 40(FHP) and 100 μm(LHP)] were measured using smallangle X-ray scattering(SAXS). No obvious pore variations were found in the LHP samples heated at 160℃ for 6 h,whereas the amount of pores of FHP decreased when subjected to 160℃ for 6 h. At 180℃, the average pore radii of FHP and LHP decreased from approximately 45 nm to 25 nm, and the total pore volume increased distinctively because of phase transformation. The LHP sample reached a high level of pore content after being held at 180℃ for 1 h, whereas FHP required 3 h. Both FHP and LHP had relatively high pore volumes when subjected to 200℃ for 1 and 3 h.     

蠕变镍基单晶高温合金微观结构与界面特征的X射线小角散射研究

利用SAXS技术对蠕变过程中不同尺度范围的微观结构变化分析表明X射线小角散射(SAXS)与中子小角散射(SANS)测量的二维散射图具有明显的差异,由散射强度曲线的变化说明了蠕变过程中二次析出γ'相形貌和不同区域尺寸特征的改变情况.分析结果表明二次析出γ'相存在两类特征尺寸,在蠕变过程中沿[100]或[010]方向的变化趋势类似,均是在第一和第二阶段有所减小,在第三阶段又有所增大,相较而言,特征尺寸较大的γ'相变化也较为显著.二次析出γ'相在蠕变第二阶段元素扩散最严重,相表面最粗糙,在第三阶段两相界面又进一 关键词： 单晶高温合金 二次析出γ'相 X射线小角散射 微观结构