氮气氛中高温退火对ZnO薄膜发光性质的影响

以二乙基锌和水汽分别作为锌源和氧源,用LP-MOCVD方法在p型Si(100)衬底上生长了单一取向的ZnO薄膜。对得到的样品在氮气气氛中进行高温热处理,退火温度分别为900,1000,1100℃。利用室温PL谱、XRD、AFM、XPS等方法对样品的性质进行了研究。研究表明:(1)随着退火温度的升高,样品的结晶性质也逐渐提高,从表面形貌观察到晶粒尺寸逐渐增大;(2)当退火温度从900℃升高至1000℃时,样品的光致发光谱中可见光波段的发光强度有所减弱,而紫外波段的发光强度明显增强;当退火温度升高至1100℃时,可见光波段的发光几乎完全被抑制,而紫外波段的发光强度急剧增强。分析认为,高温退火改善晶体结晶质量的同时调制了样品的Zn/O比,氮气气氛下的热处理使得样品内的氧原子逸出,来自受主缺陷OZn的可见发射随温度升高逐渐减弱,而当退火温度达到1000℃以上时样品成为富锌状态,此时与施主缺陷Zni有关的紫外发射急剧增强。     

Effect of Zn Interstitials on Enhancing Ultraviolet Emission of ZnO Films Deposited by MOCVD

ZnO films are grown on Si （111） substrates by a metal organic chemical vapor deposition method. Samples with different stoichiometric composition of Zn and 0 are obtained by varying Ⅱ/Ⅵ molar ratio between 3 and 1/3 in precursors. The x-ray photoelectron spectroscopy and photoluminescenee results show that the ultraviolet emission enhances with the increasing Zn/O composition ratio of the samples. It is suggested that the supertfluous Zn atoms pile up at interstitial positions to form Zn interstitial defects. The radiated recombination of the coupling of free exeitons with donor Zn interstitial enhances the ultraviolet emission of the samples.     

Effect of Annealing Temperature on Structural and Optical Properties of N-Doped ZnO Films

Nitrogen-doped ZnO （ZnO：N） films are prepared by thermal oxidation of sputtered Zn3N2 layers on A1203 substrates. The correlation between the structural and optical properties of ZnO：N films and annealing temperatures is investigated. X-ray diffraction result demonstrates that the as-sputtered Zn3N2 films are transformed into ZnO：N films after annealing above 600℃. X-ray photoelectron spectroscopy reveals that nitrogen has two chemical states in the ZnO：N films： the No acceptor and the double donor （N2）o. Due to the No acceptor, the hole concentration in the film annealed at 700℃ is predicted to be highest, which is also confirmed by Hall effect measurement. In addition, the temperature dependent photoluminescence spectra allow to calculate the nitrogen acceptor binding energy.     

Effect of High Temperature Annealing on Conduction-Type ZnO Films Prepared by Direct-Current Magnetron Sputtering

We experimentally find that the ZnO thin films deposited by dc-magnetron sputtering have different conduction types after annealing at high temperature in different ambient. Hall measurements show that ZnO films annealed at 1100℃ in N2 and in 02 ambient become n-type and p-type, respectiveIy. This is due to the generation of different intrinsic defects by annealing in different ambient. X-ray photoelectron spectroscopy and photolumineseence measurements indicate that zinc interstitial becomes a main defects after annealing at 1100℃ in N2 ambient, and these defects play an important role for n-type conductivity of ZnO. While the ZnO films annealed at 1100℃ in O2 ambient, the oxygen antisite contributes ZnO films to p-type.     

ZnO/Si异质结的光电转换特性研究

利用直流反应溅射方法在p型Si衬底上生长掺Al的n型ZnO薄膜,测量了由n型ZnO薄膜和p型Si衬底组成的异质结在黑暗和光照条件下的I-V特性,结果表明该异质结具有优良的整流特性,而且在光照条件下的反向电流迅速增大并很快趋于饱和.通过测量ZnO薄膜的光电流和异质结的光电压的光谱响应,初步分析了异质结的光电转换机理.测量结果显示,在入射光波长为380nm时光电流强度明显下降,反映出光电流与ZnO薄膜禁带宽度的密切关系;同时还发现,在与ZnO禁带宽度相对应的波长前后所产生的光生电压方向相反.推测这一现象与异质结的能带结构密切相关. 关键词： ZnO薄膜 异质结 光电转换 光谱响应