GISAXS and SAXS studies on the spatial structures of Co nanowire arrays

The spatial structures of magnetic Co nanowire array embedded in anodic aluminium membranes were investigated by grazing incidence small angle X-ray scattering (GISAXS) and conventional small angle X-ray scattering (SAXS) techniques. Compared with SEM observation, the GISAXS and SAXS measurements can get more overall structural information in a large-area scale. In this study, the two-dimensional GISAXS pattern was well reconstructed by using the IsGISAXS program. The results demonstrate that the hexagonal lattice formed by the Co nanowires is distorted (a ≈ 105 nm, b ≈ 95 nm). These Co nanowires are isolated into many structure domains with different orientations with a size of about 2 μm. The SAXS results have also confirmed that the nanopore structures in the AAM can be retained after depositing Co nanowires although the Co nanowires can not completely but only just fill up the nanopores. These results are helpful for understanding the global structure of the Co nanowire array.     

Characterization of the nanopore structures of PAN-based carbon fiber precursors by small angle X-ray scattering

The nanopore structures in precursors are crucial to the performance of PAN-based carbon fibers. Four carbon-fiber precursors are prepared. They are bath-fed filaments (A), water-washing filaments (B), hot-stretching filaments (C) and drying-densification filaments (D). Synchrotron radiation small angle X-ray scattering is used to probe and compare the nanopore structures of the four fibers. The nanopore size, discrete volume distribution, nanopore orientation degree along the fiber axis and the porosity are obtained. The results demonstrate that the nanopores are mainly formed in the water-washing stage. During the processes of the subsequent production technologies, the slenderness ratio of nanopores and their orientation degree along the fiber axis increase further and simultaneously, the porosity decreases. These results are helpful for improving the performance of the final carbon fibers.     

Hierarchical structure and biomineralization in cricket teeth

The cricket is a truculent insect with stiff and sharp teeth as a fighting weapon. The structure and possible biomineralization of cricket teeth are always interesting. Synchrotron radiation X-ray fluorescence, X-ray diffraction, and small angle X-ray scattering techniques were used to probe the element distribution, possible crystalline structures and size distribution of scatterers in cricket teeth. A scanning electron microscope was used to observe the nanoscaled structure. The results demonstrate that Zn is the main heavy element in cricket teeth. The surface of a cricket tooth has a crystalline compound like ZnFe2(AsO4)2(OH)2(H2O)4 . The interior of the tooth has a crystalline compound like ZnCl2 , which is from the biomineralization. The ZnCl2-like biomineral forms nanoscaled microfibrils and their axial direction points towards the top of the tooth cusp. The microfibrils aggregate randomly into intermediate filaments, forming a hierarchical structure. A sketch map of the cricket tooth cusp is proposed and a detailed discussion is given in this paper.