Hydrothermal Synthesis and Structure of a Novel Coordination Polymer Co_3(tma)(pda)_2(H_2O)_3]n·nH_2O

1INTRODUCTION Recently,the design and preparation of coordina-tion polymers with new porous frameworks are of great interest due to their potential functionalities such as catalysis,gas absorption,separation and molecu-lar recognition.In designing1-D,2-D and3-D porous coordination polymers,the selection of appropriate ligands is crucial for determining the structure.The mixed-linker systems of both carboxylates and pyri-dyls have proved to be effective for the preparation of novel coordi…     

A New Cadmium（Ш） Polymer Based on 3,5-Pyrazoledicarboxylic Acid：Hydrothermal Synthesis and Crystal Structure

The reaction of CdCl3.2.5H2O with 3,5-pyrazoledicaiboxylic acid under hydrother-mal conditions produce a novel three-dimensional(3-D) coordination polymer [Cd2(C5H2O4N2)2.2H2O]n.The title compound crystallizes in the monoclinic system,space group P21/c with a = 6.422(4),b = 12.334(7),c = 8.936(6) ,β = 104.793(7)°,V = 684.4(7) 3,Z = 4,Dc = 2.761 g/cm3,μ = 3.181 mm-1,F(000) = 544,R = 0.0248 and wR = 0.0624.In the crystal structure of the title compround,molecules are linked through N-H...O hydrogen bonds,forming chains running along the a axis.Every Cd(Ш) coordinates with four molecules of ligand and one water molecule,forming a pentagomal-bipyramidal geometry.     

新型三维配位聚合物[La(C5H4NCOO)3(H2O)2]n的水热合成和晶体结构

在水热反应条件下,设计合成了一种新型三维配位聚合物[La(C5H4NCOO)3(H2O)2]n的单晶体,对其进行了元素分析、热重分析、红外光谱表征、X射线单晶衍射测定.该配位聚合物属单斜晶系,P2(1)/c空间群,晶胞参数为a=0.9747(4)nm,b=1.9904(7)nm,c=1.1613(4)nm,α=90°,β=111.761(6)°,γ=90°,V=2.0925(13)nm3,Z=4,dc=1.718g/cm3,μ=2.090mm-1,F(000)＝1064,R1=0.0374, wR2=0.0683.X射线衍射结果显示La3+离子之间以4-氰基吡啶的羧基为桥形成一维链状结构,通过4-氰基吡啶的吡啶基与配位的水分子之间的氢键形成三维的网络结构.热重分析表明该配位聚合物在230℃下稳定.     

二维互穿配位聚合物[Co3(2,6-nda)3(4,4''''-bpy)1.5]n的合成和晶体结构

在中温水热反应条件下,以CoCl2·6H2O、2,6-萘二羧酸(2,6-pda)和4,4'-bpy为原料,合成了一种二维互穿配位聚合物[Co3(2,6-nda)3(4,4'-bpy)1.5]n晶体,对其进行了元素分析、红外光谱表征、TGA-GTA分析和X射线单晶衍射测定.该配位聚合物属单斜晶系,C2/m空间群,晶胞参数为a=1.7285(11)nm,b=1.9965(13)nm,c=1.3994(9)nm,α=90°,β=95.822(11)°,γ=90°,V=4.804(5)nmm3,Z=4,dc=1.457g/cm3,μ=1.089mm-1,F(000)=2136,R1=0.0594,wR2=0.1605.结果显示形成一个二维互穿的网络结构.     

多孔配位聚合物[Nd2(C6H8O4)3(H2O)2]n·n(4,4'-bpy)的合成及晶体结构

合成了标题配位聚合物, 借助于元素分析、 红外光谱和X射线单晶衍射等分析方法确定了其晶体结构, 并测定了其TDA-DTA. 该配位聚合物属正交晶系, Pbcn空间群, 晶胞参数为a=2.201 2 nm(6), b=0.777 8 nm(2), c=1.972 4 nm(5), α=β=γ=90°, V=337.70 nm(15)3, Z=4, Dc=1.796 g·cm-3, μ=3.108 mm-1, F(000)=1 800, R1=0.043 0, wR2=0.056 0. 波谱分析结构显示, 通过己二酸配体羧基氧原子桥联Nd3+离子形成三维多孔结构, 4,4'-bpy通过氢键连接存在于孔道中.     

新型配位聚合物[Co(pda)2(H2O)2]n的水热合成和晶体结构

以CoCl2·6H2O和3-(3-吡啶基)丙烯酸(pda)为原料,在中温水热反应条件下,合成了一种新型配位聚合物[Co(pda)2(H2O)2]n单晶体,并对其进行了元素分析、红外光谱表征、TGA-GTA分析和X射线单晶衍射测定.该配位聚合物属单斜晶系,P2(1)/c空间群,晶胞参数为a=1.6958(8)nm;b=0.5466(3)nm;c=1.8034(8)nm;α=90°;β=106.209(7)°;γ=90°;Mr=391.24;V=1.6051(13)nm3;Z=4;dc=1.619g/cm3;μ=1.106mm-1;F(000)=804;R1=0.0367;wR2=0.0711.该晶体通过配位键的连接形成二维结构,又通过分子间氢键和π-π相互作用形成三维的网状结构.     

纳米TiO2-MnO2复合材料的合成、结构与光催化性能

以TiCl₄, MnSO₄·H₂O, NH₃·H₂O为原料, 把TiCl₄和MnSO₄·H₂O按照化学计量比共同水解, 得到的水合氧化物中间体放入高压釜中在150℃, 0.5 MPa下进行反应, 经过滤、洗涤、烘干, 得到纳米TiO₂-MnO₂复合材料. XRD结合DTA-TG分析证明产品为非晶态, 780℃以上转变为金红石型的Ti_1-xMn_xO₂. TEM形貌观察, 粒子基本为球形, 平均粒径20 nm; 将样品均匀分散在甘油-水混合液中, 利用UV-1200紫外-可见分光光度计测试了样品的光吸收性能, 发现该纳米复合材料秉承了纳米TiO₂和MnO₂两者的优点, 对紫外光和可见光均有很强的吸收. 利用该纳米复合材料作为光催化剂对有机染料溶液进行了降解实验, 发现在日光照射60 min后, 对酸性红B、酸性黑234以及两者混合染料的降解率可达100%.     

三维配位聚合物[Co(pda)(SCN)(H2O)]n [pda=3-(3-吡啶基)丙烯酸]的合成和晶体结构

以CoCl2、3-(3-吡啶基)丙烯酸(pda)和KSCN为原料,在水热反应条件下,合成了一种三维配位聚合物[Co(pda)(SCN)(H2O)]n晶体,对其进行了元素分析、红外光谱表征、X射线单晶衍射测定和热重分析.该配位聚合物属三斜晶系,P-1空间群,晶胞参数为a=0.7309(5)nm,b=0.8799(6)nm,c=0.9634(6)nm,α=68.128(10)°,β=73.241(11)°,γ=71.218(12)°,V=0.5343(6)nm3,Z=2,dc=1.760g/cm3,μ=1.792mm-1,F(000)＝268,R1=0.0450, wR2= 0.1035.X射线单晶衍射显示形成一个三维的网络结构.     

一维链状配位聚合物[Nd(C_8H_7NO_2)_3(H_2O)]_n的水热合成和晶体结构

利用Nd(NO)36H2O和3-(3-吡啶基)丙烯酸在水热反应条件下反应,合成了一种新型一维链状配位聚合物[Nd(C8H7NO2)3(H2O)]n。用元素分析、IR和TGA-DTA进行了表征, 并用X-射线衍射法测定了晶体结构。结果表明,该晶体属三斜晶系,(分子式C24H23N3O7Nd),P空间群,晶胞参数为a = 6.275(2),b = 12.757(4), c = 15.714(5) 牛琣 = 111.966(5), b = 90.338(6),g = 94.960(6),V = 1161.2(7) ?,Z = 2,Dc = 1.735 g/cm3,m = 2.286 mm-1,Mr = 606.67, F(000) = 602,R = 0.0355, wR = 0.0757。通过3-(3-吡啶基)丙烯酸配体羧基氧原子桥联形成一维链状结构,同时链与链通过氢键及-相互作用形成了三维的网络结构。