掺镱石英光纤预制棒的制备与表征

采用改进化学汽相沉积结合溶液掺杂法制备了掺镱石英光纤预制棒,并研究了不同镱掺杂浓度下的吸收光谱和发光光谱.吸收光谱和发光光谱的强度随着YbCl₃溶液浓度的增大而增强.在不产生失透的前提下,得到预制棒芯层能够掺杂的YbCl₃溶液最大浓度为0.057 mol/L.     

Yb/P/Al共掺双包层光纤的制备与激光性能

采用改进化学汽相沉积结合溶液掺杂法制备了Yb/P/Al共掺的石英光纤预制棒,通过光纤芯层的组份和制备工艺的优化,实现了Yb3+的高浓度掺杂和均匀掺杂.预制棒芯层Yb2O3掺杂浓度达到～4wt.％,Yb3+在1 080 nm处荧光寿命为1 780μs.成功拉制出内包层截面形状为八边形的双包层光纤,纤芯直径为7.5 μm,包层吸收系数达到～5 dB/m@976 nm.利用拉制的掺镱双包层光纤开展了全光纤结构的掺镱光纤激光器性能测试实验,实现了5.15W的激光输出,斜率效率达到76％.     

Broadband Infrared Luminescence of Ni^2＋ in Petalite-Type Transparent Glass Ceramics

Transparent Ni^2＋-doped magnesium aluminosilicate glass ceramics are prepared. The formation of petalite-type crystallites in the glass ceramics is confirmed by x-ray diffraction. Broadband infrared luminescence centred at around 1235nm with full width at half maximum （FWHM） of about 300nm is observed from the Ni^2＋-doped glass ceramics. The observed infrared emission could be attributed to the ^3T2（F） → ^3A2（F） transition of octahedral Ni^2＋ ions in petalite-type crystallites. Theproduct of the fluorescence lifetime and the stimulated emission cross sections is 1.2 ×10-24 cm^2s.     

掺镱石英光纤预制棒的制备与表征

采用改进化学汽相沉积结合溶液掺杂法制备了掺镱石英光纤预制棒,并研究了不同镱掺杂浓度下的吸收光谱和发光光谱.吸收光谱和发光光谱的强度随着YbCl3溶液浓度的增大而增强.在不产生失透的前提下,得到预制棒芯层能够掺杂的YbCl3溶液最大浓度为0.057mol/L.