Neutron diffraction study on composite compound Nd2Co7

The crystallographic and the magnetic structures of the composite compound Nd₂Co₇ at 300 K are investigated by a combined refinement of X-ray diffraction data and high-resolution neutron diffraction data. The compound crystallizes into a hexagonal Ce₂Ni₇-type structure and consists of alternately stacking MgZn₂-type NdCo₂ and CaCu₅-type NdCo₅ structural blocks along the c axis. A magnetic structure model with the moments of all atoms aligning along the c axis provides a satisfactory fitting to the neutron diffraction data and coincides with the easy magnetization direction revealed by the X-ray diffraction experiments on magnetically pre-aligned fine particles. The refinement results show that the derived atomic moments of the Co atoms vary in a range of 0.7 μ_B-1.1 μ_B and the atomic moment of Nd in the NdCo₅ slab is close to the theoretical moment of a free trivalent Nd³⁺ ion, whereas the atomic moment of Nd in the NdCo₂ slab is much smaller than the theoretical value for a free Nd³⁺ ion. The remarkable difference in the atomic moment of Nd atoms between different structural slabs at room temperature is explained in terms of the magnetic characteristics of the NdCo₂ and NdCo₅ compounds and the local chemical environments of the Nd atoms in different structural slabs of the Nd₂Co₇ compound.     

R-site cation randomness effect in the A-site ordered Y0.5La0.5BaMn2O6 compound

The R/Ba-ordered and R-site mixed compound Y0.5La0.5BaMn2O6 is synthesized, in which (Y, La) and Ba are regularly arranged, while Y and La randomly occupy the R-site. Y0.5La0.5BaMn2O6 has a tetragonal unit cell with a space group of P4/mmm. A structural transition between tetragonal and orthorhombic is observed at about 325 K by X-ray powder diffraction (XRD). Thermal magnetic measurement shows the occurrence of an antiferromagnetic transition at the temperature TN～190 K. Anomalies in magnetization, resistivity and lattice parameters observed around 340 K indicate a charge/orbital order transition accompanying the structural phase transition. The R-site randomness effect is discussed to interpret the different properties of Y0.5La0.5BaMn2O6 between NdBaMn2O6 and SmBaMn2O6.     

北京同步辐射XAFS实验方法新进展

近年来基于现有的XAFS站线条件,与用户互相配合在发展实验方法,开拓XAFS的应用方面做了一些新的尝试.主要包括高温熔态XAFS实验、全反射XAFS方法、及发光XAFS实验方法.文中分别介绍了以上几种实验方法的意义,实验设置及实验结果,并进行了讨论.     

稀土富过渡族金属化合物的形成条件、晶体结构和磁性能(Ⅱ)

稀土(R)富过渡族金属(T)化合物是探索新型稀土永磁材料的主要研究对象,其磁性能与晶体结构密切相关。本文系统综述了我们近年来针对二元化合物不存在的情况下,通过第三组元M的稳定作用,合成和稳定具有CaCu5型衍生结构的化合物Rm-nT5m+2n(包括R(T,M)7,R2(T,M)17,R3(T,M)29和R(T,M)12),具有NaZn13型结构的化合物R(T,M)13,以及m层RT5和n层RT3B2组合的化合物Rm+nT5m+3nB2n等方面的主要研究结果。重点讨论了这些化合物的晶体结构、形成条件和磁性能,阐述了加入M对化合物的稳定作用机制,及M的晶体学占位对磁性能的影响。研究结果表明:M的加入不仅能够起到稳定化合物的作用,往往还可以显著改善化合物的磁性能。     

The crystal structures and physical properties of the solid solution compound Ba₅Y_8-xMn₄O_21-1.5x（x = 0,1）

New oxometallides with the formula Ba5Y8 xMn4O21 1.5x(x = 0,1) are prepared through an atmospherecontrolled solid-state reaction.Two single-phase samples with Ba/Y/Mn atomic ratios 5/8/4(Y8) and 5/7/4(Y7) are obtained.The crystal structures and the physical properties of the compounds are investigated by X-ray powder diffraction,magnetization,conductivity,and dielectricity measurements.The Ba5Y8 xMn4O21 1.5x compound is demonstrated to be a Y-deficient solid solution.The solid solution compound Ba5Y8 xMn4O21 1.5x crystallizes into tetragonal symmetry with the space group I4/m.Detailed structure analysis by Rietveld refinement of the X-ray powder diffraction data reveals that the Y vacancies occur preferentially at the Y(2) site.Thermal magnetization measurements indicate the presence of antiferromagnetic interaction between Mn ions in the compounds,and temperature-dependent resistivity measurements show that insulator-semiconductor transitions occur around 175 K and 170 K for the Y8 and Y7 samples,respectively.Strong frequency dependences of the dielectric constant are observed above ～175 K for the two compounds.     

Crystal structure and magnetic properties of Nd（Mn1-xFex）2Si2 compounds

X-ray powder diffraction,resistivity and magnetization studies have been performed on polycrystalline Nd(FexMn1-x)2Si2 (0 ≤ x ≤ 1) compounds which crystallize in a ThCr2Si2-type structure with the space group I4/mmm.The field-cooled temperature dependence of the magnetization curves shows that,at low temperatures,NdFe2Si2 is antiferromagnetic,while the other compounds show ferromagnetic behaviour.The substitution of Fe for Mn leads to a decrease in lattice parameters a,c and unit-cell volume V .The Curie temperature of the compounds first increases,reaches a maximum around x = 0.7,then decreases with Fe content.However,the saturation magnetization decreases monotonically with increasing Fe content.This Fe concentration dependent magnetization of Nd(FexMn1-x)2Si2 compounds can be well explained by taking into account the complex effect on magnetic properties due to the substitution of Mn by Fe.The temperature’s square dependence on electrical resistivity indicates that the curve of Nd(Fe0.6Mn0.4)2Si2 has a quasi-linear character above its Curie temperature,which is typical of simple metals.     

晶粒尺寸和应变的X射线粉末衍射法测定

文章介绍了根据X射线粉末衍射线形测定试样品粒度和点阵畸变(应变)的主要方法,并以Co<,3>O<,4>纳米材料晶粒度和应变的测量为例加以说明.通过与扫描电镜观察的统计结果进行比较,分析了各种方法计算晶粒尺寸的可靠性和适用性.     

Ga掺杂对Cu_3SbSe_4热电性能的影响

采用熔融-淬火方法制备了Cu_(2.95)Ga_xSb_(1-x)Se_4(x=0,0.01,0.02和0.04)样品,系统地研究了Ga在Sb位掺杂对Cu_3SbSe_4热电性能的影响.研究结果表明,少量的Ga掺杂(x=0.01)可以有效提高空穴浓度,抑制本征激发,改善样品的电输运性能.掺Ga样品在625 K时功率因子达到最大值10μW/cm·K~2,比未掺Ga的Cu_(2.95)SbSe_4样品提高了约一倍.但是随着Ga掺杂浓度的进一步提高,缺陷对载流子的散射增强,同时载流子有效质量增大,导致载流子迁移率急剧下降.因此Ga含量增加反而使样品的电性能恶化.在热输运方面,Ga掺杂可以有效降低双极扩散对热导率的贡献,同时掺杂引入的点缺陷对高频声子有较强的散射作用,因此高温区的热导率明显降低.最终该体系在664 K时获得最大ZT值0.53,比未掺Ga的样品提高了近50%.     

Sb2Te3 纳米结构的制备与表征

以室温热电性能优异的传统热电材料Sb₂Te₃为研究对象,利用化学气相沉积法制备Sb₂Te₃单晶纳米结构,并研究其生长机理.实验结果表明,不加催化剂时Sb₂Te₃易生长成六方纳米盘,在金催化剂条件下定向生长成纳米线.Sb₂Te₃的形貌与其晶体结构和生长机理有关.Sb₂Te₃为三角结构,Sb和     

Structure, dielectric and magnetodielectric properties of Bi1-xGdxFeO3 Ceramics

Different magnetodielectric effects were observed in Bi1-xGdxFeO3 ceramics depending on gadolinium content. A positive one was observed in the samples with x ≤0.10 at 295K and 16K, and a negative one in the sample with x = 0.4 at 16 K. Structure analysis by x-ray diffraction (XRD) reveals that the samples crystallize in the R3c structure (ferroelectrics) for x<0.08 and in the Pbnm structure (paraelectrics) for x≥0.3 at room temperature. Temperature-dependent dielectric response and x-ray diffraction confirm the occurrence of a structural transition in the Pbnm phase at low temperature for the samples with x ≤0.4. While the positive magnetodielectric effects can be attributed to a coupling of magnetic and crystallographic structures of the R3c phase, the observed negative magnetodielectric effect in the Pbnm phase can be associated with a low-temperature modification of the Pbnm structure. The observed dualsigned magnetodielectric effects suggest that the Bi1-xGdxFeO3 oxides are a good prototype for understanding the magnetodielectric coupling mechanism in this kind of materials.