In the present research, magnesium aluminate spinel was prepared as catalyst support using a novel, facile, and efficient mechanochemical method. The Co-promoted catalysts with 20 wt.% of Ni were fabricated using an impregnation route and the samples were analyzed by the X-ray diffraction (XRD), N2 adsorption/desorption (BET), temperature-programmed reduction and desorption (H2-TPR and O2-TPD), and field emission scanning electron microscopy (FESEM) tests. The results confirmed that all samples have a mesoporous structure with a high specific surface area and the presence of cobalt caused complete CH4 oxidation at low temperatures, and no side reactions were observed. The results indicated that the 3%Co-20%Ni/MgAl2O4 catalyst was the optimal sample among the prepared catalysts, owing to the improvement of reduction features and oxygen mobility. The 50 and 90% of methane conversion was obtained at 530 and 600 °C, respectively. Also, the influence of calcination temperature, GHSV, and feed ratio was determined on the catalytic activity. The obtained outcomes revealed that the calcination temperature has a significant effect on the textural properties and catalytic efficiency. The sample calcined at 700 °C showed the weakest performance, which was related to the sintering of particles at high temperatures. The catalytic stability showed that the 3%Co-20%Ni/MgAl2O4 has acceptable stability during 600 min time of reaction.
Cu(II) Schiff base complex supported on Fe3O4@SiO2 nanoparticles was employed as a magnetic nanocatalyst (nanocomposite) with a phase transfer functionality for the one-pot preparation of α-aminonitriles (Strecker reaction). The desired α-aminonitriles were obtained from the reaction of aromatic or aliphatic aldehydes, aniline or benzyl amine, NaCN, and 1.6 mol% of the catalyst in water at room temperature and good to excellent yields were obtained for all substrates. The catalyst was characterized analytically and instrumentally including Fourier-transform infrared spectroscopy, X-ray diffraction, thermogravimetric, nuclear magnetic resonance, energy-dispersive X-ray spectroscopy, inductively coupled plasma spectroscopy, vibrating-sample magnetometry analysis, dynamic light scattering, Brunauer–Emmett–Teller surface area, field emission scanning electron microscopy, and transmission electron microscopy analyses. The reaction mechanism was investigated, in which the performance of the catalyst as a phase transition factor seems to be probable. The catalyst showed high activity, high turnover frequency (TOF)s, significant selectivity, and fast performance toward the Strecker synthesis. The nanocatalyst can be readily and quickly separated from the reaction mixture with an external magnet and can be reused for at least seven successive reaction cycles without significant reduction in efficiency. 相似文献
In this study, the analytical solutions of the radial Schr¨odinger equation for the central Woods-Saxon potential together with spin-orbit interaction and centrifugal terms have been derived by using Nikiforov-Uvarov method. The energy eigenvalues and corresponding eigenfunctions of nucleons have been obtained for various values of n,l, and j quantum numbers. The obtained results using this method are in satisfactory agreement with available data in the special case. 相似文献
Cellulose - The aggregation of silver nanoparticles (AgNPs) in colloidal solution and the oxidative cytotoxicity towards human cells are two major hindrances for their thriving medicinal... 相似文献
Pyrolysis is a commonly used method for the recovery of used lubricating oil (ULO), which should be kinetically improved by a catalyst, due to its high level of energy consumption. In this research, the catalytic effects of carbon nanotube (CNT) and graphene nanoplatelets on the pyrolysis of ULO were studied through thermogravimetric analysis. First, the kinetic parameters of ULO pyrolysis including activation energy were calculated to be 170.12 and 167.01 kJ mol?1 by FWO and KAS methods, respectively. Then, the catalytic effects of CNT and graphene nanoplatelets on pyrolysis kinetics were studied. While CNT had a negligible effect on the pyrolysis process, graphene nanoplatelets significantly reduced the temperature of maximum conversion during pyrolysis from 400 to 350 °C, due to high thermal conductivity and homogenous heat transfer in the pyrolysis process. On the other hand, graphene nanoplatelets maximized the rate of conversion of highly volatile components at lower temperatures (<?100 °C), which was mainly due to the high affinity of these components toward graphene nanoplatelets and also the effect of nanoplatelets’ edges which have free tails and can bond with other molecules. Moreover, graphene nanoplatelets decreased the activation energy of the conversion to 154.48 and 152.13 kJ mol?1 by FWO and KAS methods, respectively.
Oxidative coupling of methane is a direct way to obtain C2 hydrocarbon,and Mn-Na-W/SiO2 catalyst is the most promising among all the catalysts.The 2%Mn/5%Na2WO4/SiO2 catalyst was prepared by the incipient wetness impregnation method.A 7-step heterogeneous reaction model of the oxidative coupling of methane to C2 hydrocarbons was conducted by co-feeding methane and oxygen at a total pressure of 1 bar over the catalyst.The kinetic measurements were carried out in a micro-catalytic fixed bed reactor.The kinetic data were obtained at the appropriate range of reaction conditions (4 kPa<Po2 <20 kPa,20 kPa<PCZH4 <80 kPa,800℃<T<900℃).The proposed reaction kinetic scheme consists of three primary and four consecutive reaction steps.The conversions of hydrocarbons and carbon oxides were evaluated by applying Langrnuir-Hinshelwood type rate equations.Power-law rate equation was applied only for the water-gas shift reaction.In addition,the effects of operating conditions on the reaction rate were studied.The proposed kinetic model can predict the conversion of methane and oxygen as well as the yield of C2 hydrocarbons and carbon oxides with an average accuracy of ±15%. 相似文献
Super paramagnetic Fe3O4@SiO2 nanoparticle was incorporated into polyurethane rigid foams in order to prepare new corresponded magnetic nanocomposite foams via one-shot method. The core–shell-structured nanoparticles were prepared by sol–gel method and characterized by transmission electron microscopy, X-ray diffraction, as well as Fourier transform infrared spectroscopy techniques. Magnetic nanoparticles were used up to 3 % in the foam formulations and the samples prepared successfully. Thermal, mechanical, and magnetic properties of nanocomposites were studied and the results showed superior properties in comparison with pristine foams. 相似文献