基于HEA封端聚氨酯大孔树脂颗粒的合成、表征及水声声学性能

制备了丙烯酸-β-羟乙酯（HEA）封端的聚氨酯（PUA）大分子单体,采用正庚烷作致孔剂,用悬浮聚合法合成了聚氨酯-苯乙烯（PUA-St）及聚氨酯-苯乙烯-甲基丙烯酸乙酯-二乙烯基苯（PUA-St-EMA-DVB）AB-交联共聚物大孔树脂颗粒。SEM表明：合成的PUA-St-EMA-DVB颗粒含有规整的、孔径较大的孔洞,...     

水热法制备高纯超细CeO2-ZrO2复合氧化物

Superfine composite powders of CeO₂-ZrO₂ (CZ) and CeO₂-ZrO₂-La₂O₃ (CZL) were prepared by hydrothermal method. The effects of pH、temperature and time for hydrothermal process on the performance of the resulting powders were studied. The optimized reaction parameters were on follows: the precursor′s pH≈9.0, hydrothermal temperature of 200 ℃ holding for 2 h. Thermal stable powders with average particle size smaller than 10 nm and specific surface area of 171 m²·g^-1 were obtained. A BET specific surface area was still at 44 m²·g^-1 after calcination at 1 000 ℃ for 6 hours.     

综合国力估量的前缘分析方法

把前缘分析方法引入国力估量,展示了这种方法在国力计算、比较测度和结构分析等方面的有效应用.     

用无机硅剂水热法合成纳米NiO/SiO2及其催化乙炔分解制备纳米碳管

以硅溶胶为硅源．水热法制备NiO／SiO2催化剂，用于化学气相沉积法(Chemical Vapor Deposition，CVD法)制备碳纳米管通过SEM表征，研究了催化剂原料及其配比，水热制备工艺条件对催化效果的影响．结果表明：用硅溶胶可替代正硅酸乙酯作为硅源；制备的最佳条件为：MSiO2：MNi（NO3）2=1：12～1：14，水热温度为180～200℃，压力为1．2～1．5MPa．保温时间为0．5～2h．     

吸光光度法测定乙酰氧基己烯酸

用吸光光度法分析了丁二烯电化学合成山梨酸的中间产物乙酰氧基己烯酸 (AA)。试验表明 ,AA测定的线性范围为 0～ 10 .1μg/ 10ml ,最大吸收波长λmax为 5 30nm ,摩尔吸光系数为 7 64× 10 4 L·mol- 1·cm- 1。催化剂CuCl最佳用量为 0 .75 μg/ 10ml ,最佳pH为 2 .7～ 3.3,温度条件为 2 7～37℃ ,水解时间为 30min ,样品测定结果满意 ,回收率达 92 .6%～ 10 3.2 %。     

在高纯氧氯化锆制取过程中絮凝剂对“二次除硅”的影响

高纯氧氯化锆是制取高纯锆化学品的重要原材料，目前国内外多采用锆英石为原料碱熔法生产，硅的去除分两步进行：第１步是用水浸洗碱熔分解产物，大约有８５％～９０％的硅以硅酸钠的形式进入水浸液，余下ＳｉＯ２需要“二次除硅”．因此，要生产高纯产品，“二次除硅”是...     

验证电能表的另一种方法

关于电能表的检测，笔者琢磨了好长一段时间，终于找到了一种用电子表检测的方法，现将该方法介绍如下。