用于可见照明的超宽带黄色荧光玻璃

报道了一种新的可用蓝光发光二极管（LED）有效激发的黄色发光玻璃.这种超宽带黄色荧光玻璃样品是在低硅钙铝酸盐玻璃基质中掺杂Ce³⁺,并采用熔融法制备的.通过对吸收光谱、激发光谱、荧光光谱以及不同激发源下荧光强度和峰值波长的测试,分析了样品的发光特性.并利用蓝光LED来激发样品,获得白光发射.从色坐标的计算和玻璃本身的优势来看,这一发光体系在照明和显示等方面具有很大的潜在应用价值.     

STUDY OF HETEROCYCLIC POLYMER COMPLEXES Ⅰ. POLYPHENYLQUINOXALINE-PLATINUM AND RHODIUM COMPLEXES*

Two new polyphenylquinoxaline-platinum and rhodium complexes were synthesized and iden-tified by X-ray photoelectron spectroscopy. Their catalytic properties on hydrosilylation and hy-drogenation of olefines have been investigated. It was found that these polymer complexes possessedhigh selective catalytic activities, and were easily recoverable after each reaction and could berepeatedly used for more than 10 times while maintaining the same effectiveness.     

Dy3+掺杂硼硅酸盐玻璃的发光特性

采用高温熔融法制备了Dy3+掺杂硼硅酸盐玻璃,通过测试激发光谱和发射光谱,研究了其光谱性质.研究了玻璃组分及Dy3+掺杂浓度对发射光谱及发光强度的影响,并计算了色坐标,均位于白光区域.通过改变玻璃组分及掺杂浓度,调节黄、蓝发射峰的强度比,在387 nm长紫外光激发下实现了单一基质上有效的白光发射.     

聚苯基单醚喹噁啉和铂铑络合物的研究

<正> 芳杂环高分子是一种耐高温高分子,诸如聚酰亚胺、聚苯基单醚喹噁啉等,都是耐高温优良的高分子,而后者还具有突出的耐高温水解性。鉴于芳杂环高分子主链结构上含N、S或O原子,它们都有未成键的电子,可以作为电子给体,而金属化合物中的金属有空轨道,可以作为电子受体,在合适条件发生电荷转移形成络合物。实验结果表明,聚苯     

不同分子量聚丙烯腈的制备及其高压静电纺丝研究

采用DMSO/H2O混合溶剂法制备了5种不同分子量的PAN,并以PAN为原料,DMF为溶剂,配成纺丝溶液,通过高压静电纺丝技术制备超细纤维毡(UFFM)。研究表明,相同单体组成和浓度、相同反应条件情况下,通过聚合制备PAN,随着混合溶剂中水含量的增加,生成的PAN粘均分子量相应增加,其转化率也增加。聚合所得的不同分子量PAN的热重分析显示,随着PAN分子量的增加,热重曲线的剧烈失重区会越来越明显,剧烈失重区的失重率也呈增加的趋势;高压静电纺丝研究发现,PAN-4和PAN-5纺丝溶液由于分子量过高而不可纺;另外,研究还发现,较高的纺丝电压有利于纤维直径的减小,但相应的纺丝稳定性减小,导致纤维直径分布的离散度增加。     

低温烧结制备氧化铝陶瓷膜支撑体

采用平均粒径为10.16 μm的α-Al2O3粉体为原材料,利用注浆成型技术制备陶瓷膜支撑体.设置正交实验,研究成孔剂、粘结剂、烧结助剂(硅酸钠+TiO2+CaCO3+MgO)含量及保温时间对支撑各性能的影响;在正交实验结论基础上,通过改变烧结温度,于低温条件下制备出性能良好的陶瓷膜支撑体.实验表明:硅酸钠用量、成孔剂用量、粘结剂用量和保温时间最佳组合分别为4;、6;、0.6;和2 h.在1400~1450 ℃温度区间内制得的支撑体各性能指标均相对较优,适宜作为陶瓷膜载体使用.