对分布布拉格反射镜(DBR)的原理和特征进行了分析,使用传输矩阵方法计算了不同对数GaAs/AlAs反射镜的反射率曲线.利用分子束外延(MBE)设备生长了波长为920nm和980nm的半导体多层膜DBR反射镜,分析了实验测得的反射谱与理论拟合曲线之间的差异及其产生原因,实现了材料的优化生长,获得了反射率大于99;、中心波长和带宽接近理论计算值的DBR材料.该DBR的反射谱拟合与优化生长研究可应用于VCSEL和VECSEL激光器. 相似文献
3.
A GaAs/AlGaAs two-dimensional electron gas (2DEG) structure with the high mobility of μ2K= 1.78 × 10^6 cm^2/Vs has been studied by low-temperature Hall and Shubnikov de Hags (SdH) measurements. Quantum lifetimes related to all-angle scattering events reduced from 0.64 ps to 0.52 ps after i11uminating by Dingle plots, and transport lifetimes related to large-angle scattering events increasing from 42.3ps to 67.8ps. These results show that small-angle scattering events become stronger. It is clear that small-angle scattering events can cause the variation of the widths of the quantum Hall plateaus. 相似文献
4.
5.
6.
7.
8.
9.
采用分子束外延技术,分别在480,520℃的生长温度下,制备了淀积厚度2.7ML的InAs/GaAs量子点。用原子力显微镜对样品进行形貌测试和统计分布。结果表明,在相应的生长温度下,量子点密度分别为8.0×1010,5.0×109cm-2,提高生长温度有利于获得大尺寸的量子点,并且量子点按高度呈双模分布。结合光致发光谱的分析,在480℃的生长条件下,最近邻量子点之间的合并导致了量子点尺寸的双模分布;而在525℃的生长温度下,In偏析和InAs解析是形成双模分布的主要原因。 相似文献
10.
固态源MBE系统生长高质量的调制掺杂GaAs结构材料和InP/InP外延材料的兼容性研究 总被引:1,自引:0,他引:1
通过固态源的分子束外延系统生长了调制掺杂AlGaAs/GaAs结构材料和InP/InP外延材料.在生长含磷材料之后,生长条件(真空状态)变差;我们通过采取合理的工艺方法和生长工艺条件的优化,获得了电子迁移率为1.86×105cm2/Vs(77K)调制掺杂AlGaAs/GaAs结构材料和电子迁移率为2.09×105cm2/Vs(77K)δ-Si掺杂AlGaAs/GaAs结构材料.InP/InP材料的电子迁移率为4.57×104 cm2/Vs(77K),该数值是目前国际报道最高迁移率值和最低的电子浓度的InP外延材料.成功地实现了在一个固态源分子束外延设备交替生长高质量的调制掺杂AlGaAs/GaAs结构材料和含磷材料. 相似文献