In this paper the values of the crystalline-electric-field
parameters Anm for R2Fe17 and
R2Fe17H3 (R=Tb,Ho,Er) are evaluated by fitting
calculations to the magnetization curves measured on the single
crystal at several temperatures. The fitted Anm for
R2Fe17 are strikingly different from those for the
corresponding R2Fe17H3. The energy gaps between the
lowest four energy levels for Ho ions in Ho2Fe172 can be
reproduced by using the fitted Anm and exchange field
2μBHex, which estimated from the fit of the
temperature dependence of the spontaneous magnetization combined
with inelastic neutron scattering experiment. 相似文献
2.
(Nd1-xYx)3Fe27.31Ti1.69化合物的结构与磁性研究 总被引:2,自引:0,他引:2
制备了(Nd1-xYx)3Fe27.31Ti1.69(0≤x≤0.6)系列化合物,通过X射线衍射和磁性测量等手段研究了它们的结构和磁性.这些化合物均为Nd3(Fe,Ti)29型结构,A2/m空间群.化合物晶胞体积随Y含量增加而单调减少,居里温度Tc随Y含量增加略有降低,说明化合物的居里温度主要由Fe-Fe之间的交换相互作用所决定.温度为5K时,饱和磁化强度Ms随Y含量的增加而单调降低,与一个简单的稀释模型预期结果一致.所得化合物在低温下均发生自旋重取向,自旋重取向温度Tsr随Y含量增加而单调降低,从x=0时的232K减小到x=0.6时的121K.基于磁晶各向异性的研究结果确定了所得化合物的自旋相图. 相似文献
3.
4.
利用X射线和磁性测量研究了Co77Zr(18-x)Mo5Bx合金薄带的结构和磁性.实验发现,在Co-Zr-Mo合金中添加适当含量的B,可以使其矫顽力显著提高,当x=2.0时,制备出具有迄今为止Co-Zr基永磁合金最大矫顽力Hc=7.0 kOe(1 Oe=79.5775 A/m)的快淬薄带.随着B元素添加,Co77Zr18-xMo5Bx合金薄带的晶粒逐渐细化,并根据Henkel plot模型计算得出软磁相fcc-Co与硬磁相Co5Zr相之间的交换耦合作用逐渐增强.合金薄带的矫顽力主要受硬磁相Co5Zr相的晶粒尺寸控制,并随着晶粒尺寸的减小先升高后降低.另一方面,Co77Zr18Mo5合金薄带的矫顽力机理为反磁化核形核模型,添加B元素之后矫顽力机理变为畴壁钉扎模型.通过X射线衍射和热磁分析发现,B元素并没有进入到Co5Zr相的晶格中,而是存在于非晶相中. 相似文献
5.
Magnetic properties and coercivity mechanism of precipitation-hardened Gd-Co based ribbons 下载免费PDF全文
Gd(Co_{0.88-x}Cu_xFe_{0.09}Zr_{0.03})_z ribbons with x=0.075-0.200 and z=6.4-7.7 have been prepared by a melt-spinning technique. A cellular microstructure consisting of 2:17 cells surrounded by the 1:5 cell boundary phase is obtained after precipitation hardening. The dependence of room temperature coercivity on the heat treatment process suggests that the long-time isothermal aging is not helpful for the development of magnetic properties. Positive temperature coefficient of remanence from room temperature to about 673K is typical for all samples, while positive temperature coefficient of coercivity is obtained only in ribbons with low Cu content. The coercivity mechanism of the precipitation-hardened ribbons at different temperatures is also discussed. 相似文献
6.
用快淬方法制备了Pr10Fe74-xCo10+xC4B4 (x=0,2,4,6,8) 条带,研究了成分和工艺对条带磁性能的影响.实验发现,当x=2,带速是20 m·s-1时,条带的磁性能最佳,其剩磁Jr=0.94 T,矫顽力μ0 iHc=0.96 T,最大磁能积 (BH)max=127.32 kJ·m-3.通过Henkel-plot分析,发现x=2,带速为20 m·s-1的样品中的晶间交换作用最强,因而能获得最佳的磁性能. 相似文献
7.
8.
The crystalline-electric-field parameters Anm for RFe11Ti and RFe11TiH (R=Sm, Tb, Ho) are evaluated by fitting calculations to the magnetization curves measured on the single crystals or on magnetically aligned powder samples at 4.2K and higher temperatures. Interstitial hydrogen atom in RFe11Ti has been found to have a significant effect on crystalline-electric-field parameters Anm. By using the parameters of exchange field 2μBHex estimated from inelastic neutron scattering experiments and the fitted Anm, the calculations can reproduce the experimental curves well. 相似文献