烧结温度对Cao.9(NaCe)0.05Bi2Nb2O9无铅压电陶瓷性能的影响

采用传统固相反应法制备了Ca0.9(NaCe)0.05Bi2 Nb2 O9铋层状无铅压电陶瓷.采用XRD、SEM、EDS及相关电学性能测试系统表征了样品的晶体结构、断面形貌、元素组成以及介电、压电、铁电等性能,探究不同烧结温度对于陶瓷性能的影响.结果表明:当烧结温度为1150℃时,样品的晶体结构单一均匀,呈现片层状结构,致密性较好,压电常数高达17 pC/N,介电损耗仅为0.42;,居里温度为908℃,并且具有很好的温度稳定性,说明固相反应法制备的Ca0.9(NaCe)0.05Bi2Nb2O9压电陶瓷最佳烧结温度为1150℃.     

Multiparty Quantum Secret Sharing of Key Using Practical Faint Laser Pulses

Based on a bidirectional quantum key distribution protocol [Phys. Rev. A 70 (2004)012311], we propose a (m-1, m-1)-threshold scheme of m (m≥3)-party quantum secret sharing of key by using practical faint laser pulses. In our scheme, if all the m-1 sharers collaborate, they can obtain the joint secret key from the message sender. Our scheme is more feasible according to the present-day technology.     

存储区域网络中冗余路径的研究

应用马尔科夫可用性模型得出了冗余路径的带故障切换时间的状态转换图，分析了平均无故障时间、平均故障修复时间以及故障切换时间对可用性的影响，冗余路径提高了系统的可用性．应用排队系统建立了冗余路径的I／O处理模型，分析表明采用冗余路径驱动程序的负载均衡算法后，I／O平均响应时间随着吞吐能力的提高而降低．实验数据证实了这一结论．     

函数模拟法求解锥形模超塑挤压的力学场——超塑挤压解析理论之一

本文首次用模拟位移函数的方法,给出锥形模超塑挤压力学场的解析式以及应变、应变速率和应力的约束方程。由于实验选用的是典型超塑性合金ZnAl₅,所以结果有相当的包络性。即使对于非典型超塑性材料,这种方法亦有普遍意义。     

Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

最大度为6的极大外平面图的完备色数

证明了最大度为６的极大外平面图的完备色数为７。     

不可摸数

计算隅500 000以下的不可摸数73 565个。     

煤加氢液化研究—模型化合物的加氢裂解

在快速升温和冷却的共振搅拌反应管中,以四氢萘为溶剂,进行了六种模型化合物的加氢裂解试验。反应条件如下:反应温度300—450℃,氢初压3.0—9.0MPa,表观反应时间5—45 min。试验结果表明,这六种化合物加氢裂解稳定性顺序为:二苯甲烷>二苯醚>二苯乙烷>苯基苄基醚>二苄基硫醚和二苄基二硫醚。裂解为一级反应,根据试验结果计算了苯基苄基醚和二苯乙烷的表观反应速度常数和活化能,前者ΔE 为83.9 kJ/mol,后者ΔE 为150kJ/mol。提高氢初压,使用预硫化的Mo-Ni 催化剂、Y 型和5A 型分子筛或添加易裂解化合物作自由基引发剂对模型化合物的加氢裂解均有利。     

关于不含k-C-圈的n阶r-一致超图的若干结果

主要讨论了不含k-C-圈的n阶r-一致超图,对不同的k,分别得出了它的极大边数的一个下界,并且得出在有些情况下它的下界是最大的.另外,我们得到了Krn含k-C-圈的一个充分必要条件.     

非线性Klein—Gordon方程“蛙跳”格式差分解的收敛性

利用有界延拓法，研究了非线性Ｋｌｅｉｎ－Ｇｏｒｄｏｎ方程初边值问题的“蛙跳”差分解的收敛性与稳定性。避免了校难的先验估计，并放宽了非线 性项的条件。