Influence of Yb-Doped Nanoporous TiO2 Films on Photovoltaic Performance of Dye-Sensitized Solar Cells

Yb-doped TiO2 pastes with different Yb/TiO2 weight ratios are prepared in the sol-gel process to obtain dyesensitized solar cells （DSCs）. The nanocrystalline size of Yb-TiO2 becomes smaller and the lattice parameters change. Lattice distortion is observed and dark current is detected. It is found that a part of Yb existing as insulating oxide Yb2O3 state acts as barrier layers at the electrode-electrolyte interface to suppress charge recombination. A Yb-doped TiO2 electrode applied in DSCs leads to a higher open-circuit voltage and a higher fill factor. How the Yb-doped TiO2 films affect the photovoltaic response of DSCs is discussed.     

阴极还原处理对多孔硅发光性能的影响

对经过阴极还原处理后的多孔硅样片进行了光致发光测试和稳定性测试.实验结果表明这种处理能明显改善多孔硅的发光稳定性,使其表面结构更加稳定.利用原子力显微镜对不同还原时间的多孔硅微结构及形貌进行了比较,在一定范围内随着还原时间的增长多孔硅表面粗糙度增大,PL谱增强.     

Formation of Interfacial Layers in LaAlO3/Silicon during Film Deposition

We have studied the interracial reactions between amorphous LaAlO3 thin films and Si substrates, using high- resolution transmission electron microscopy and x-ray photoelectron spectroscopy. It has been shown that the interracial layer between LaAlO3 film and Si substrate chemical states show that the ratio of La 4d3/2 to Al 2p is SiLaxAlyOz. The depth distributions of La, Si and Al of the interfacial layer remains unchanged with the depth compared to that of the LaAlO3 film. Moreover, the Si content, in the interracial layer gradually decreases with increasing thickness of the interracial layer. These results strongly suggest that the Al element is not deficient in the interracial layer, as previously believed, and the formation of a SiLaxAlyOz interracial layer is mainly due to the diffusion of Si from the substrate during the LaAlO3 film deposition. With the understanding of the interracial layer formation, ones can control the interface characteristics to ensure the desired performances of devices using high-k oxides as gate dielectrics.     

基片光学特性对薄膜光强透过谱的影响

在考虑基片与空气界面反射率以及基片吸收不能忽略的情况下，对常见的基片上薄膜的光强透过率公式进行了修正，导出了该情况下的透过率公式．以非晶硅薄膜为研究对象，采用模拟计算说明基片光学特性对薄膜光强透过谱的影响．     

复合薄膜透湿率对分子筛吸附性能的影响

分子筛经活化后用复合薄膜包装袋封装存放一定时间后使用，由于水汽缓慢渗透和包装袋微量泄漏的存在，可能使分子筛吸湿，从而直接影响其使用效果和有效期，因此试验研究分子筛产品包装贮存前后吸附性能的变化，以验证理论计算结果，并为分子筛应用提供重要的试验依据。     

CHBr薄膜制备的初步研究

碳氢（cH）及其掺杂材料常被用作ICF实验靶丸烧蚀层材料。制备CH薄膜及其掺杂材料的方法有很多，诸如：离子束辅助沉积、离子溅射沉积、低压等离子体化学气相沉积（LPPCVD）等。近年来，详细研究了LPPCVD法制备CH薄膜的制备方法与工艺，形成了比较成熟的技术路线与工艺路线，并为“神光”实验提供了一系列实验靶丸。     

红光激发下掺Ho3+氟化物薄膜的上转换发光

利用激光脉冲沉淀法制备了稀土Ho~(3 )掺杂的氟化物薄膜。观测到处于薄膜中的Ho~(3 )离子在632.8nm红光激发下的上转换发射。这些上转换发射包括:~5S_2→~5I_7,~5F_4→~5I_7和~5S_2→~5I_8。     

热丝加热电流对CH薄膜沉积速率和表面形貌的影响

 热丝辅助裂解法是结合气相沉积制备聚对二甲苯薄膜和热丝化学气相沉积而形成的一种制-CH薄膜的新方法。热丝辅助裂解法的最大特点就是在保持低衬底温度情况下可以获得高沉积速率，而热丝加热电流对薄膜沉积速率和薄膜表面形貌具有重要影响。研究表明，热丝加热电流越大，薄膜沉积速率越高，在加热电流9A时，薄膜沉积速率可达0.002mm/min，同时薄膜表面粗糙度随之增加，薄膜表面也开始出现其它元素污染，因此，一般热丝加热电流选择为7A附近。     

二氧化碳和丙烯直接合成甲基丙烯酸的NiPMo/TiO2催化剂的研究

用溶胶 凝胶法以磷钼酸 (MPA)的镍盐溶液水解钛酸四丁酯制备了NiPMo/TiO2 催化剂 .使用ICP、XRD、TG DTA、IR、TPD MS和微反应技术研究了催化剂的化学组成、热稳定性、化学吸附性质和催化反应性能 .杂多钼酸盐与TiO2 通过O2 -在TiO2 表面发生了键合 .在 6 2 3K下 ,杂多阴离子仍保持原有的Keggin结构 .CO2 在Lewis酸位Ni(Ⅱ )和Lewis碱位Ni-O -Mo的桥氧协同作用下生成CO2 卧式吸附态Ni(Ⅱ )←O - (CO)← (O--Ni) .丙烯有多种吸附态在催化剂上吸附 .在 5 6 3K、1MPa和空速 15 0 0h-1的反应条件下 ,丙烯的摩尔转化率为 3.2 % ,产物MAA选择性为 95 % .     

薄膜偏振分光镜的研究

概述薄膜偏振分光镜的研究现状及其主要特点，重点分析薄膜偏振分光镜的设计原理,并利用等效折射率的方法计算中心波长的反射率．