纳米晶钽在单向拉伸载荷下的分子动力学模拟

利用分子动力学方法模拟了纳米晶钽在单轴拉伸载荷作用下的微观结构演化情况. 结果表明纳米晶钽在塑性变形过程中可以发生从BCC到FCC, HCP结构的应力诱导相变. FCC 结构原子百分比的最大值和试样的抗拉强度成线性关系，据此可推出一个相变发生的临界应 力值. 应变率越大，相变滞后于应力越严重. 当应变达到一定值时，试样会发生晶间断裂现 象，定量分析发现纳米晶钽晶间裂纹初始形成应变不受平均晶粒尺寸的影响，而与应变率和 模拟温度有着密切的关系.     

Dynamic crack growth along a polymer composite-Homalite interface

Dynamic crack growth along the interface of a fiber-reinforced polymer composite-Homalite bimaterial subjected to impact shear loading is investigated experimentally and numerically. In the experiments, the polymer composite-Homalite specimens are impacted with a projectile causing shear dominated interfacial cracks to initiate and subsequently grow along the interface at speeds faster than the shear wave speed of Homalite. Crack growth is observed using dynamic photoelasticity in conjunction with high-speed photography. The calculations are carried out for a plane stress model of the experimental configuration and are based on a cohesive surface formulation that allows crack growth, when it occurs, to emerge as a natural outcome of the deformation history. The effect of impact velocity and loading rate is explored numerically. The experiments and calculations are consistent in identifying discrete crack speed regimes within which crack growth at sustained crack speeds is possible. We present the first conclusive experimental evidence of interfacial crack speeds faster than any characteristic elastic wave speed of the more compliant material. The occurrence of this crack speed was predicted numerically and the calculations were used to design the experiments. In addition, the first experimental observation of a mother-daughter crack mechanism allowing a subsonic crack to evolve into an intersonic crack is documented. The calculations exhibit all the crack growth regimes seen in the experiments and, in addition, predict a regime with a pulse-like traction distribution along the bond line.     

Effects of static electric field on the fracture behavior of piezoelectric ceramics

The paper gives an overview on experimental observations of the failure behavior of electrically insulating and conducting cracks in piezoelectric ceramics. The experiments include the indentation fracture test, the bending test on smooth samples, and the fracture test on pre-notched (or pre-cracked) compact tension samples. For electrically insulating cracks, the experimental results show a complicated fracture behavior under electrical and mechanical loading. Fracture data are much scattered when a static electric field is applied. A statistically based fracture criterion is required. For electrically conducting cracks, the experimental results demonstrate that static electric fields can fracture poled and depoled lead zirconate titanate ceramics and that the concepts of fracture mechanics can be used to measure the electrical fracture toughness. Furthermore, the electrical fracture toughness is much higher than the mechanical fracture toughness. The highly electrical fracture toughness arises from the greater energy dissipation around the conductive crack tip under purely electric loading, which is impossible under mechanical loading in the brittle ceramics. The project supported by an RGC grant from the Research Grant Council of the Hong Kong Special Administrative Region, China     

Local fracture resistance based on microstructural efficiency concept and simulation of injection molding

Local fracture resistance (FR) of short (SGF) and discontinuous long glass fibre (LGF) reinforced polypropylene (PP) was predicted using the ‘microstructural efficiency concept’ together with a simulation program for fibre orientation in injection molding. The ‘microstructural efficiency concept’ describes the relation between microstructural parameters such as the fibre content, the fibre aspect ratio and the processing (injection molding) induced layer structure taking also into account the local fibre orientation. The local fibre orientation in injection molding was predicted with the MOLDFLOW^®-software. The predicted local FR was compared with the measured one, which was determined by using compact tension samples and linear elastic fracture mechanics (LEFM). The comparison showed, that for SGF-PP good consistence between the predicted and measured FR existed, for LGF-PP the discrepancy was higher. Yet for both materials, the ‘microstructural efficiency concept’ together with the results obtained from the simulation of the fibre orientation can be used for FR prediction of an injection molded workpiece.     

Heating during shearing and opening dominated dynamic fracture of polymers

The heat generated from dissipative mechanisms during shearing and opening dominated dynamic fracture of polymethyl methacrylate and polycarbonate was measured with a remote sensing technique that utilizes the detection of infrared radiation. Significant heating was detected for both materials and both modes of fracture. In the shear dominated experiments, the temperature increase at the crack tip in polymethyl methacrylate was 85 K, the approximate increase necessary to reach the glass transition temperature. An adiabatic shear band followed by a dynamically propagating crack were observed during the shear dominated experiments using polycarbonate. The recorded shear band temperature increase was 45 K. This was followed by an additional 100 K temperature increase from the ensuing crack, raising the temperature above glass transition. The maximum temperature increase recorded for the opening mode experiments was 55 K for polymethyl methacrylate and 105 K for polycarbonate. The results of this study show that temperature effects are significant during the dynamic fracture of polymers. The effects are especially important in the shear dominated case where local temperatures approach or exceed the polymer glass transition temperature.     

Integral formulation for a circular cylindrical cavity in infinite solid and a finite length coaxial cylindrical crack compressed axially

A method for solving problems of fracture of an infinite solid with a circular cylindrical cavity and a coaxial cylindrical crack near the surface under an uniform axial compression is proposed using a non-classical criterial approach associated with a mechanism of a local stability loss near the defect. The theory of integral Fourier transforms and series expansions are used to reduce these problems to a system of paired integral equations and then to a system of linear algebraic equations with respect to the contraction parameter.     

自紧身管临界裂纹尺寸的概率断裂力学研究

基于概率断裂力学理论和Mome Caflo模拟方法，本文进行了自紧身管临界裂纹尺寸的可靠性研究。自紧身管内表面的疲劳裂纹考虑为半椭圆形式。裂纹尖端处的应力强度因子由内压和自紧残余应力共同产生。自紧残余应力采用了符合身管材料具有强化和包辛格效应性能推导的公式计算，它产生的应力强度因子通过权函数方法得到。根据断裂准则，可计算出自紧身管的临界裂纹尺寸。实例分析表明，对数正态分布为临界裂纹尺寸的最佳分布，同时给出了在各种置信度和可靠度下自紧身管的临界裂纹尺寸。     

Refinement of the plastic-zone boundary in the vicinity of a crack tip for the quasiviscous and viscous types of fracture

A refined solution of the elastoplastic problem of an insulated mode I crack in a thin plate of reasonably large dimensions is obtained. Estimates of the plastic zone in the vicinity of the crack tip are given for quasiviscous and viscous types of fracture.Translated from Prikladnaya Mekhanika i Tekhnicheskaya Fizika, Vol. 46, No. 1, pp. 126–132, January–February, 2005     

Limiting state of an elastoplastic orthotropic plate with a periodic system of collinear cracks

A modified Dugdale model is used to study the fracture of an orthotropic elastoplastic plate with a periodic system of rectilinear cracks. The material of the plate obeys a general yield criterion. The general form of solution is obtained in terms of Kolosov-Muskhelishvili potentials. The size of the plastic zone is expressed in terms of the external load and geometrical parameters. The equations for the determination of the stresses in the plastic zone and the crack opening displacement are derived. The effect of anisotropy on the formation of the plastic zones at the crack tip is examined __________ Translated from Prikladnaya Mekhanika, Vol. 43, No. 5, pp. 80–88, May 2007.     

转向剂形成人工应力遮挡的实验研究及有限元分析

针对水力压裂过程中采用的人工应力遮挡控制缝高技术,通过室内物理模拟实验,在转向剂浓度一定的条件下考虑携带液与地层压差、渗流量、时间等因素,采用电测法对人工岩芯表面应变进行了测试;利用非线性有限元方法对裂缝尖端应力进行计算,研究了转向剂形成人工应力遮挡的作用效果。结果表明采用转向剂可以建立3~4MPa的人工应力遮档,对采用转向剂的压裂设计和施工参数提出了建议。