累托石/聚丙烯插层纳米复合材料的制备与性能

采用熔融共混法制备了有机改性累托石 (OREC)粘土 均聚聚丙烯 (PP)纳米复合材料 ,以X 射线衍射分析 (XRD)及透射电子显微镜分析 (TEM)观察了复合材料的相貌结构 ,研究了复合材料的力学性能及热性能 .结果表明 ,OREC在添加份数较少时可与均聚聚丙烯熔融插层形成插层型聚丙烯纳米复合材料 ,该复合材料与纯PP相比 ,具有较高的拉伸强度、断裂伸长率及冲击强度 .在有机粘土添加 2 %时 ,复合材料的拉伸强度、断裂伸长率、冲击强度最高 ,与纯PP相比 ,2 %添加量的聚丙烯纳米复合材料拉伸强度提高 6 5 7% ,断裂伸长率提高 2 89 3% ,冲击强度提高 14 1% ,10 %失重率时对应的热分解温度提高 50K .     

INTROMISSION OF WATER-REPELLENT AND HYDROSCOPIC PROPERTIES SIMULTANEOUSLY TO PP BY PLASMA DISCHARGE METHOD

Plasma-induced surface graft copolymerization of acrylic acid on polypropylene non-woven fabric (PP-g-AA) and polypropylene membrane were reported. The extents of grafting were controlled by the plasma and polymerization condition. Hexadecyltrimethyl ammonium bromide was then coupled with the carboxyl group of PP-g-AA to obtain a polyion complex (PIC). At last, CF4 plasma was used to give PICs hydrophobic property. The moisture regain and water-repellency of the processed PICs was investigated. The surfaces were characterized using ATR FT-IR and XPS. The result indicates that the products have very high ability to adsorb moisture, even better than cotton fiber. At the same time, the products show excellent hydrophobic property, which can‘t be wetted by those reagents whose surface tensions were higher than 327mN/m.     

聚丙烯微孔膜基渐变聚合物的制备,结构与性能的研究

以聚丙烯微孔膜为基材，通过扩散控制原位共聚合的方法在人填充了组成沿膜的厚度方向逐渐改变的无规共聚物，Ｘ－光电子能谱（ＸＰＳ）、全反射红外光谱（ＡＴＲ）以及动态粘弹谱的分析结果。说明所制备得到的合膜具有明显的渐变聚合物性质。     

接枝和交联对纳米Si02改性NR／PP共混型热塑弹性体的影响

动态硫化制备纳米二氧化硅（SiO2）改性天然橡胶，聚丙烯共混型热塑性弹性体（NR/PPTPE）．研究了马来酸酐，苯乙烯，过氧化二异丙苯（MAH／St／DCP）多单体“就地”熔融接枝、交联对TPE力学性能、耐溶剂性能和耐热变形性能的影响，并用SEM分析了TPE的断面形貌．结果表明：纳米SiO2和MAH／St／DCP的最佳质量分数分别为0．03和0．0375／0．0188／0．00375时，MAH／St／DCP接枝、交联改性NR／PP／纳米SiO：TPE的力学性能、耐溶剂性能和耐热变形性能最佳．MAH／St／DCP“就地”接枝、交联通过细化交联NR分散相、改善交联NR分散的均匀性和增加两相之间的共交联，使NR与PP两相界面结合强度明显提高，NR／PPTPE的综合性能得到明显的改善．     

分子量对聚丙烯等温结晶的影响

<正> 在高聚物结晶动力学的研究中,分子量对结晶速率的影响是一个有实际意义和理论兴趣的研究课题,由于聚烯烃可以得到分子量变化范围相当宽(MW从10~3到10~6)的试样,因而它是研究结晶速率分子量依赖性较合适的对象,其中研究最多的是聚乙烯和聚丙烯。从前入的研究报道看来,影响聚丙烯结晶速率的因素比聚乙烯要复杂。除了聚丙烯可生成多种晶型结构,会影响其结晶速率以外,用不同聚合方法制备的试样,由于其链结     

β型聚丙烯注塑件的分层结构与力学性能

用X-射线衍射仪研究了不加和加成核剂形成不同晶型的三种聚丙烯注塑件的分层结晶结构,获得各层结晶度和β晶型含量(k_β)随皮芯距离的分布规律,测定了试件弯曲、拉伸和冲击性能。发现,纯等规聚丙烯试件主要含α晶型,皮层的结晶度和k_β低于芯层。加有α成核剂的试件仅含有α晶型,皮层的结晶度也低于芯层。加有β成核剂的试件主要含β晶型,皮层的结晶度和k_β值高于芯层。纯聚丙烯试件和β型为主的试件的分层结构中存在α晶和β晶间的转变。与α型聚丙烯相比,β型聚丙烯有较低的屈服强度,却有较高的抗张强度,显示很高的拉伸韧性和延展性,可明显提高室温以及玻璃化温度以下的低温抗冲击性能。     

TEXTURE AND CRYSTALLINITY EVOLUTION IN ISOTACTIC POLYPROPYLENE INDUCED BY ROLLING AND THEIR INFLUENCE ON MECHANICAL PROPERTIES

The orientation and crystallinity evolution of isotactic polypropylene （iPP） induced by rolling were studied using wide angle X-ray scattering with an area detector. The tensile mechanical properties of rolled isotactic polypropylene sheets were also measured in this work. The texture component method was used to analyze the rolling texture. The rolling texture consists mainly of （010）[001], （130）[001] and [001]//RD fiber components in the sample with a rolling true strain of 1.5. The results reveal that crystallinity drastically decreases during rolling. It is suggested that amorphization is a deformation mechanism which takes place as an alternative to crystallographic intralamellar slip depending on the orientation of the lamellae. Both the orientation and crystallinity affect the tensile mechanical properties of rolled polypropylene. Crystallinity influences the elastic modulus on both directions and yield strength on transverse direction at the first stage of deformation. Orientation is the main reason for the changes of mechanical properties, especially at the latter part of deformation. The changes of both tensile strength and elongation percentage on rolling direction are larger than those on transverse direction, which results from the orientation. At last, the anisotropic mechanical properties occur on the rolling and transverse direction： high tensile strength with low elongation percentage on rolling direction and low tensile strength with high elongation percentage on transverse direction.     

关于超高分子量聚丙烯超拉伸膜的结构性能的研究——Ⅱ.形态结构变化对力学性能的影响

 用X-射线衍射、动态力学测定等手段研究了不同拉伸倍数的超高分子量聚丙烯薄膜的力学性能的变化.以X-射线衍射法并基于串联力学模型的假设得到的各样品的表观晶区模量E_c^app约为34-38GPa.样品模量E_b随拉伸倍数增加而逐渐增大,其变化趋势与非晶区取向因子的变化相类似,说明非晶区取向是左右样品模量的重要因素.室温下,69倍拉伸样品的模量为27GPa,约为表观结晶模量的3/4,且其值在-150-160℃的温度范围内没有急剧变化,说明超拉伸明显改善了材料的力学性能及热稳定性.在各拉伸样品中,考虑伸直链结晶生成的可能性,利用并串联力学模型对伸直链结晶的体积分数做了估算,并对X-射线衍射法所得表观结晶模量进行了修正,认为室温下聚丙烯的真正晶区模量约为47GPa.     

聚丙烯纤维辐射接枝进展

本文对聚丙烯纤维的辐射接枝方法、特征和机理、以及其研究进展和表征进行了扼要综述。