Hydrothermal Synthesis and Structural Characterization of a Novel 3-D Open Framework Zinc Phosphate Microporous Compound(C_5N_2H_(14))·[Zn_3(OH_2)(PO_4)_2(HPO_4)]

One novel organically templated zincophophate(C5N2H14)·[Zn3(OH2)(PO4)2(HPO4)] has been synthesized under hydrothermal conditions and characterized by single-crystal X-ray diffraction together with elemental analysis, infrared spectroscopy, thermogravimetric analysis, and powder X-ray diffraction. The title compound crystallizes in the monoclinic space group P21/n, with a = 9.7904(11), b = 14.0287(14), c = 11.8651(13) , β = 104.690(3), V = 1576.4(3) 3, Z = 4, T = 296(2) K, Mr = 601.31 and Dc = 2.533 g/cm3. The compound consists of a macroanionic [Zn3(OH2)(PO4)2(HPO4)]2- framework and(C5N2H14)2+ cations, and its structure is built up from ZnO3(OH2), ZnO4, HPO4 and PO4 tetrahedral units that result in 4, 8 and 10-ring channels.     

Synthesis and Crystal Structure of a New Pr(Ⅲ)–K(Ⅰ) Heterometallic Oxalate Coordination Polymer

A new 3D heterometallic coordination polymer, namely [K2Pr2(C2O4)4·H2O]n(1), has been successfully synthesized under hydrothermal conditions. X-ray single-crystal diffraction determination reveals that 1 crystallizes in monoclinic system, space group P21/n with a = 12.060(4), b = 8.493(3), c = 15.776(5)(A), β = 93.235(3)°, V = 1613.4(9) 3, Z = 4, Mr = 730.12, Dc = 3.006 Mg/m3, μ = 6.581 mm-1, F(000) = 1368, the final R = 0.0283 and w R = 0.0866 for 2939 observed reflections with I 2σ(I). Complex 1 features an unusual 3D heterometallic coordination framework, in which oxalates exhibit three different coordination behaviours. Moreover, powder X-ray diffraction and thermal properties for 1 have also been investigated.     

材料颗粒度对粉末药型罩特性的影响

为研究粉末材料的颗粒尺寸及其分布对粉末药型罩特性的影响,以W、Cu粉末为药型罩的主体材料,添加少量Bi粉以增加其流动性,在配比一定的条件下,通过改变各组分的颗粒尺寸,制备了3种药型罩。利用扫描电子显微镜,观察了W、Cu粉末的颗粒形貌,发现W粉的颗粒形状为规则的结晶体,而Cu粉颗粒的形状不规则。对3种药型罩进行了微观结构观察、密度测定、维氏硬度测定以及破甲威力实验。结果表明:在粉末材料特性和配比一定的条件下,减小颗粒尺寸可有效提高粉末药型罩的致密性、密度和破甲威力,但对维氏硬度的影响不明显。     

Synthesis,structure, optical,and electric properties of Ce-doped CuInTe_2 compound

Ce-doped Cu In Te2（CICT） semiconducting compounds are successfully synthesized. The phase structures, optical,and electric properties are investigated using powder X-ray diffraction（XRD）, field emission scanning electron microscopy（FESEM）, X-ray photoelectron spectrometer（XPS）, Raman spectrometer, ultraviolet and visible spectrophotometer（UVVis）, and a standard four-probe method. Cu In1-xCex Te2 crystallizes into a tetragonal structure with predominant orientation along the [112] direction. The lattice parameters are a = 6.190（6） A–6.193（0） A and c = 12.406（5） A–12.409（5） A. Ce prefers to occupy the 4b crystal position. According to the analysis of XPS spectra, Ce shows the mixture of valences 4＋and 3＋. Raman spectra reveal that the photon vibrating model in the CICT follows A1 mode in a wavenumber range of123 cm^-1–128 cm^-1. UV-Vis spectra show that the band gap Eg values before and after 0.1 mole Ce doped into Cu In Te2 are 1.28 e V and 1.16 e V, respectively. It might be due to the mixture of valences for Ce. Ce doped into Cu In Te2 still shows the semiconductor characteristics.     

纳米累托石-TiO2光催化剂的制备及表征

以TiCl4和累托石为主要原料，制备出纳米累托石-TiO2粉末，并用X-衍射、透射电镜等对其进行表征．结果表明：纳米累托石-TiO2粉末平均直径为17．5nm当焙烧温度从500℃升至800℃时，累托石-TiO2粉末的比表面积从65．7m^2／g下降至3．3m^2／g，单位质量吸附剂的孔体积从0．1430cm。／u降到0．0213cm^3／g；当焙烧温度从300℃上升至500℃时，孔径变化不大，属中孔范围；当焙烧温度升至800℃时，一些孔道出现坍塌，不利于纳米累托石-TiO2粉末的光催化活性．     

凝胶燃烧法制备超细YBa2Cu3O7-x超导粉末

纳米级细度的YBa2Cu3O7-x超导粉末有可能在第二代超导带材的研制中得到应用．超细YBa2Cu3O7-x超导粉朱已经通过凝胶燃烧法制备成功．使用的起始物质是钇、钡、铜的硝酸盐以及作为燃烧剂的柠檬酸．产物颗粒的尺寸大小及其超导性能依赖于自燃过程的情况，而自燃过程又与凝胶中柠檬酸盐-硝酸盐的YBa2Cu3O7-x超导粉末．在本实验中我们发现最好的燃烧剂一氧化剂摩尔比为0．5．     

纳米Zr-V-O粉末的XRD及TG-DSC研究

利用机械合金化制备纳米Zr-V粉末，对制备过程的材料进行物相分析和热分析试验。初始粉末Zr（150μm）和V（150μm）元素粉末（纯度99．15％）按原子比1：2或1：1进行混合后在氩气气氛中放入SimoloyerCMol—2球磨仓中，按几种不同的试验条件进行球磨。同时在997K和1047K下热处理40min和1h，并对热处理前后的粉末进行了物相和TG-DSC实验分析。     

第一讲中子散射与散裂中子源

中子散射是研究物质微观结构和动态的理想工具之一,广泛地应用于凝聚态物质研究和应用的众多学科领域.散裂中子源能是新一代的加速器基脉冲中子源,能为中子散射提供高通量的脉冲中子.文章简明地介绍了中子散射的特点和它作为物质结构和动态探针的优越性,以及散裂中子源的基本原理、发展状况和多学科的应用优势.我国计划建设的散裂中子源CSNS中,靶站将由多片钨靶、铍/铁反射体和铁/重混凝土生物屏蔽体组成.质子束功率100kW下,脉冲中子通量约为2.4×1016n/cm2/s.第一期将设计建造高通量粉末衍射仪、高分辨粉末衍射仪、小角散射仪、多功能反射仪和直接几何非弹性散射仪等五台典型的中子散射谱仪,以覆盖大部分的中子散射研究领域.     

粉末微波滤波器的制备和特性

利用通电导线的电磁感应和铜粉的趋肤效应,试制了在超导量子计算实验系统中使用的粉末微波滤波器.滤波器的频率响应随频率升高而平缓下降,在1GHz左右衰减至-80dB.我们分析了滤波器的原理,并通过改变参数对滤波器性能的变化进行了详细的研究.     

直接置换法制备包覆型纳米铜-银双金属粉末

 以AgNO₃为主盐，采用直接置换法初步制备了包覆型纳米铜-银双金属粉末，分析了工艺条件对包覆效果的影响，并用透射电子显微镜、X射线能量色散谱仪和X射线衍射仪进行了表征。实验结果表明：纳米铜-银双金属粉末为包覆型结构，平均粒径约70 nm，分散性较好，表面银的原子分数达到74.28%。在洗涤过程中加入一定量的保护剂，有效解决了纳米铜粉的氧化问题。