稀土气相扩渗BaTiO3基PTC陶瓷的NTCR效应

采用稀土气相扩渗法制备了La改性的BaTiO3基PTC陶瓷,并对其室温电阻率的变化及温-阻效应进行了研究.结果表明,BaTiO3基PTC陶瓷经La气相扩渗后,室温电阻率从2.7×109Ω.m下降到220Ω.m,在25-500℃范围内,电阻率随温度升高单调递减,从220Ω.m降至5.8Ω.m,产生了明显的NTCR效应.结合XRD,SEM,EDAX以及介电性能测试结果分析了La气相扩渗BaTiO3基PTC陶瓷NTCR效应的形成机理,建立了NTCR效应的物理结构模型.     

La_2Ti_6O_(15)-CeTi_(21)O_(38)-PbTiO_3 ceramics formed in gaseous penetration of La-Ce into PbTiO_3 and their electric properties

PbTiO3 ceramics, which are typical ferroelectric materials, are useful in various applied fields. For example, it has a very good candidacy for piezoelectric materials for high temperature and high sensibility. In recent years, the studies on doped PbTiO3 ceramics have received consid-erable attention[1—3]. The modified PbTiO3 ceramics doped with Ca2+, Sm3+, Y3+, Ce4+ etc. have some better properties: their Curies temperature decreases, their tetragonal distortion degree de-grades and th…     

硒酵母中有机硒及硒代氨基酸含量的测定方法

报道了人工培养硒酵母中有机硒及硒代胱氨酸（ＳｅＣｙｓ）和硒代蛋氨酸（ＳｅＭｅｔ）含量的测定方法。采用透析处理法使硒酵母中的无机硒和有机硒得以分离,并采用催化分光光度法测定了硒酵母中有机硒的含量;采用氨基酸自动分析仪测定了硒酵母中ＳｅＣｙｓ和ＳｅＭｅｔ的含量。     

稀土铬酵母的制备及其铬含量研究

研究了稀土元素La、Nd、Sm、Er的添加浓度分别为50μg·g-1、75μg·g-1、100μg·g-1和125μg·g-1时对富铬酵母中铬含量的影响 研究结果表明,稀土元素能够提高富铬酵母中的总铬和有机铬含量,当添加100μg·g-1Nd时,富铬酵母中的总铬含量和有机铬含量最高,分别为784.24μg·g-1和755.85μg·g-1,是未加稀土的富铬酵母的3倍以上     

溶胶凝胶法制备Nd2O3改性钛酸钡陶瓷的研究

The technological condition for the preparation of BaTiO₃ ceramics doped with Nd₂O₃ by Sol-Gel was deter-mined through orthogonal experiment. When n_Ba(Ac)2∶n_Ti(OC4H9)4∶n_Nd2O3∶n_{CH3(CH2)2CH2OH}∶n_H2O=1.00∶1.00∶0.003∶7.30∶37.04, pH=3.5,T=25℃,the light-yellow-transparent-stable solution and thorough transparent gel was generat-ed, the transforming time of solution to gel was 25h. The crystal structure and particle size of BaTiO₃ ceramics doped with Nd₂O₃ were studied by SEM and X-ray respectively, the type of the crystal was tetragonal, the particle size was about 24.7nm. The dielectric constant (ε) and dielectric loss (tanδ) of BaTiO₃ ceramics doped with Nd₂O₃ were determined between 10⁴～10⁶Hz, and the results showed that the dielectric constant was increased obviously, the dielectric loss was decreased clear and the resistivity (ρ_V) was also decreased noticeably.     

L—对苯磺酰乳酸乙酯合成物产率的化学分析法

建立了采用K2CrO4-K2Cr2O7混合指示剂测定L－对甲苯磺酰乳酸、乙酯合成物产率的化学分析方法,K2CrO4-K2Cr2O7的最佳配比为K2CrO4：K2Cr2O7＝6：1（m/m）,体系的最佳酸度为pH 5.8,测得L－乳酸乙酸与甲苯磺酰氯反应制备的L－对甲苯磺酰乳酸乙酯的产率为94.0％。     

三氯锗取代丙酰氢化噻唑-2-硫酮类化合物及其水解产物的合成

某些有机锗化物,例如β-羧乙基锗倍半氧化物及其衍生物能诱发干扰素,对癌症有一定疗效,日本专利报道丙酰胺基锗倍半氧化物及其衍生物也具有抗癌活性^[2,3],白明章等曾合成丙酰芳胺基锗倍半氧化物^[4]。     

稀土改性BaTiO3粉体的制备及其导电性分析

采用溶胶-凝胶法制备了纯BaTiO3粉体,并以La、Pr、Nd、Sm、Gd和Er等稀土元素通过液相掺杂、气相掺杂和液-气共掺3种不同的方式对其进行改性,以提高BaTiO3粉体的导电性.实验结果表明:各种稀土均可降低BaTiO3粉体的电阻率,效果最好的是Sm.不同掺杂方式中液-气共掺的效果最好,通过液相掺杂、气相掺杂和液-气共掺,BaTiO2粉体的电阻率由4.30×109Ω·m分别降至2.38×105,4.34×104和35.4 Ω·m.XRD、SEM、FTIR分析表明.液相掺杂时进入BaTiO3粉体的稀土元素主要集中在晶界处,而气相掺杂后稀土元素主要进入晶格内部,可能取代了Ti4+在晶格中的位置.半径较小的稀土元素更容易迁移而偏离钛氧八面体的中心位置,由此导致稀土掺杂后BaTiO3粉体的电阻率显著降低.     

除草剂中间体R-(+)-2-(4-羟基苯氧基)丙酸酯的不对称合成

报道了一种合成苯氧丙酸类除草剂重要中间体R－（＋）－2－（4－羟基苯氧基）丙酸乙酯（即R－（＋）－HPE）的方法，以L－乳酸为起始原料，先经酯化合成L－乳酸乙酯，再与对甲苯磺酰氯反应制备L－对甲苯磺酰乳酸乙酯，再与对苯二酚综合获得R－（＋）－2－HPE，产品的总收率为72.1%。通过元素分析和红外光谱测定，确定了所合成的R－（＋）－HPE的化学结构和纯度；由旋光度的测定，确定了所合成的R－（＋）－HPE的光学纯度为95.7%。     

面包酵母对微量元素富集作用的研究

微量元素在维持生命的正常代谢过程中起着重要作用[1-12].但无机微量元素不但毒性较大,且以极低水平吸收,有机微量元素吸收迅速且安全,因此,利用工业微生物,尤其以酵母为载体富集微量元素,使微量元素由无机态转为有机态,以提高其生物利用度,已成为国内外研究重点.而且通过一定载体改变其化学状态,还能够确保适度含量,对医学防治具有更重要的意义.本文通过生物富集得到以氨基酸络合物等有机形式存在的微量元素,利于人体吸收利用.