Epitaxial Bi2Sr2CuOy thin films as p-type transparent conductors

Development of p-type transparent conducting thin films is tireless due to the trade-off issue between optical transparency and conductivity. The rarely concerned low normal state resistance makes Bi-based superconducting cuprates the potential hole-type transparent conductors, which have been realized in Bi₂Sr₂CaCu₂O_y thin films. In this study, epitaxial superconducting Bi₂Sr₂CuO_y and Bi₂Sr_1.8Nd_0.2CuO_y thin films with superior normal state conductivity are proposed as p-type transparent conductors. It is found that the Bi₂Sr_1.8Nd_0.2CuO_y thin film with thickness 15 nm shows an average visible transmittance of 65% and room-temperature sheet resistance of 650 Ω/sq. The results further demonstrate that Bi-based cuprate superconductors can be regarded as potential p-type transparent conductors for future optoelectronic applications.     

Spectroscopic characterization of Yb:Sc₂O₃ transparent ceramics

Yb:Sc2O3 transparent ceramics are fabricated by a conventional ceramic process and sintering in H2 atmosphere. The room-temperature spectroscopic properties are investigated, and the Raman spectrum shows an obvious vibration characteristic band centred at 415 cm 1 . There are three broad absorption bands around 891, 937, and 971 nm, respectively. The strongest emission peak is centred at 1.04 μm with a broad bandwidth (11 nm) and an emission cross-section of 1.8×10 20 cm 2 . The gain coefficient implies a possible laser ability in a range from 990 nm to 1425 nm. The energy-level structure shows that Yb:Sc 2 O 3 ceramics have large Stark splitting at the ground state level due to their strong crystal field. All the results show that Yb:Sc2O3 transparent ceramics are a promising material for short pulse lasers.     

Transparent and flexible field emission display device based on single‐walled carbon nanotubes

A fully transparent and flexible field emission device (FED) has been demonstrated. Single‐walled carbon nanotubes (SWCNTs) coated on arylite substrate were used as electron emitters for the FED and a novel metavanadate phosphor coated on the SWCNTs/arylite film was used as transparent and flexible screen. The SWCNTs/arylite based emitters and the SWCNTs/arylite/metal‐vanadate‐based phosphor showed a transmittance value of 92.6% and 54%, respectively. The assembled device also showed satisfactory transparency and flexibility as well as producing significant current. Metavanadate phosphor is considered to be an excellent candidate due to its superior luminescence properties and easy fabrication onto transparent and flexible conductive substrate at room temperature while retaining reasonable transparency of the substrate. Thus, its transparency and flexibility will open the door to next‐generation FEDs. (© 2012 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Transparent p‐NiO/n‐ZnO diodes used in circuit rectifiers

We report on the fabrication of a transparent photostable cell circuit composed of drive and resistor diodes which are face‐to‐face connected to each other with different device area. The diodes consisted of e‐beam evaporated p‐NiO on sputter‐deposited n‐ZnO for p/n diode formation on indium‐tin‐oxide glass. Our transparent diodes show photostable rectifying behavior, about 10³ on/off current ratio and even dynamic rectification at a maximum frequency of 100 Hz AC input signal in ambient light. The noticeable photo‐responsivity of the circuit was obtained only under ultraviolet (UV) light. We conclude that our transparent diode circuit is promising in enriching the field of transparent device electronics. (© 2012 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

利用直流磁控溅射法在柔性衬底上制备ZnO: Zr新型透明导电薄膜

室温下利用直流磁控溅射法在有ZnO缓冲层的柔性衬底 PET上制备出了可见光透过率高、电阻率低的掺锆氧化锌(ZnO: Zr)透明导电薄膜,研究了厚度对ZnO: Zr薄膜结构及光电性能的影响.结果表明,ZnO: Zr薄膜为六方纤锌矿结构的多晶薄膜.实验获得ZnO: Zr薄膜的最小电阻率为2.4×10-3 Ω·cm,其霍尔迁移率为18.9 cm2·V-1·s-1 ,载流子浓度为2.3×1020 cm-3.实验制备的ZnO: Zr薄膜具有良好的附着性能,其可见光平均透过率超过92;.     

pH值对溶胶-凝胶法制备的掺铝氧化锌薄膜光电性能的影响

采用溶胶-凝胶法在普通载玻片上制备出c轴择优取向的ZnO: Al(ZAO)透明导电薄膜,研究了溶胶pH值对其结构、表面形貌、电学和光学性能的影响.结果表明:随着pH值的降低晶粒尺寸增大;当溶胶pH值从8.4降低到6.8时,薄膜的电阻率先降低而后略有升高,当pH值为7.2时其电阻率达到最小值2.6×10-3 Ω·cm,进一步分析表明,溶胶pH值的变化影响了薄膜晶界散射,而后者又使载流子迁移率发生了变化;薄膜的透光率在可见光部分随着pH值的降低而升高,而禁带宽度则从3.36 eV降到3.32 eV.     

Investigation on the scattering effect of ceramic Nd:YAG

This paper investigates the scattering effect of domestic 0.5 at{\%} ceramic Nd:YAG. An effective method has been utilized to measure the scattering and absorption coefficients. An end-pumped continuous wave (CW) Nd:YAG ceramic laser was also demonstrated. A maximum output power of 6.7~W at 1064~nm was obtained at an 808-nm pump power of 32.9~W. Conversion efficiency and slope efficiency have been achieved. This indicates that scattering has an important effect on the optical performance of ceramic Nd:YAG.     

NiAl-Cr(Mo)-Cr_xS_y自润滑复合材料的摩擦磨损特性

采用滑动磨损试验方法测试了NiAl-Cr(Mo)-CrxSy自润滑复合材料与SiC陶瓷配副在110～960℃的摩擦磨损特性.结果表明:200～400℃,纳米CrxSy晶粒在复合材料摩擦表面形成较完整的润滑膜,产生自润滑性能;700～900℃,复合材料摩擦表面生成了1～3μm厚、完整的玻璃陶瓷润滑膜,产生了自润滑耐磨性能.2种润滑膜材料均可向SiC表面转移,消除了复合材料/SiC的摩擦状态.随着温度的升高,2种润滑膜材料的强度降低,SiC微凸体压入润滑膜,导致润滑膜的剥落加剧,复合材料的摩擦系数与磨损率升高.     

透明管径及管厚的CCD成像在线测量方法

应用光线透过透明管径的折射规律,提出线阵CCD成像在线测量透明管状外径及壁厚的新方法。该方法用计算机进行模拟导出了数理模型。实验证明了这一方法的可行性,为透明管状产品的批量生产、高速、动态、非接触实时在线测量提供了一条新的技术途径。     

伴行循经血管干的透明通道

通过小鼠处死后新鲜皮肤直接铺片的方法 ,发现了伴行循经脉线血管干的一种透明通道 .探讨了这种通道与淋巴管的关系 .这种通道的特性以及它在经络功能中的可能作用值得进一步研究 .