ELECTROSPRAYING/ELECTROSPINNING OF POLY(γ-STEARYL-L-GLUTAMATE): FORMATION OF SURFACES WITH SUPERHYDROPHOBICITY

  Electrospraying/electrospinning of poly(γ-stearyl-L-glutamate) (PSLG) was investigated on a series solutions with different concentrations in chloroform. Field emission scanning electron microscopy (FESEM) and attenuated total reflectance Fourier transform infrared spectroscopy (FT-IR/ATR) were used to characterize the morphology and structure of the electrosprayed/electrospun polypeptide mats. It was found that electrospraying of PSLG with concentrations lower than 16 wt% afforded beads, while microfibers could be electrospun at the concentration of 22 wt%. The hydrophobicity of the electrosprayed/electrospun PSLG mats was investigated with static water contact angle (WCA) and tilt angle measurements. It was demonstrated that the superhydrophobic surfaces of PSLG with WCAs and tilt angles in the ranges of 150°-170° and 16.5°-4.2°, respectively, were obtained through electrospraying/electrospinning process.     

Pt羰基簇合物在NaY内的合成机理

利用IR，EXAFS, ~(13)CO同位素交换反应及与NO作用等手段研究了Pt羰基簇合物[Pt_3(CO)_6]~(2-)_n(n＝3,4)在NaY分子筛超笼内的合成机理．在氧化样品Pt~(2+)/NaY上300－373 K的还愿羰基化过程中，首先Pt~(2+)与CO反应生成PtO(CO)物种(波数σ_(CO)＝2110 cm~(-1))，然后聚集成“Pt_3(CO)_6”(σ_(CO)＝2112，1896和1841 cm~(-1))，最后生成深绿色的Pt羰基簇合物Pt_(12)(CO)_(24)]~(2-)/NaY(σ_(CO)＝2080，1824 cm~(-1))．“Pt_3(CO)_6”的羰基在室温下能迅速地与~(13)CO发生交换，而[Pt_3(CO)_6]~(2-)_n(n＝3,4)的羰基与~(13)CO的同位素交换即使在343 K也进行得很慢，室温下，NO能逐步破坏Pt羰基簇合物的层间和层内Pt－Pt键，得到中间物种“Pt_3(CO)_6”和PtO(CO)，同时在气相产生CO_2和N_2O．而由上述两中间物种出发，300－353 K温度下，在CO气氛中的还原羰基化又能可逆地得到原羰基簇合物．     

Bi-Sr-Ca-Cu-O超导体与氧化物衬底材料的反应性估计

测定了一系列氧化物的电子结合能，显示了铋系超导体与二元氧化物衬底材料的化学反应性可以用固态酸碱反应理论来描述，其反应性大小除了可以用衬底氧化物的酸碱参数估计以外，还可以用衬底氧化物氧离子的内层电子结合能估计．     

由XPS研究CO2在低压甲醇合成中的作用

本文应用XPS,在模拟工业催化剂和实际操作条件下,对低压甲醇合成铜基催化剂的表面形态进行了研究.结果表明,在还原及反应状态下,催化剂表面没有稳定的Cu~(2+)、Cu~+离子存在,仅Cu~0能被检测到;ZnO被还原,形成缺氧结构ZnOx(X≤1),表面出现氧空位.认为高度分散的Cu~0与其紧密接触的部分还原的ZnOx联合组成了甲醇合成的表面活性中心,也即表面上的Cu-Zn-O(“口”为氧空位)构成了最佳合成活性单元.提出反应原料气中适量CO_2的加入有助于金属Cu微晶的分散,认为CO_2的作用主要是使反应气氛中含有一定的氧化势,它与原料气中的CO+H_2一起,对金属Cu微晶起氧化还原作用.CO_2可将Cu~0氧化成Cu~(?+)(甚至Cu~+).但Cu~(?+)会马上被CO+H_2还原成Cu~0.通过这样的氧化还原循环,阻止了Cu微晶的聚集长大,延长了催化剂的使用寿命.     

马来酸酐与1，2－环己烷二羧酸二异丁酯的气液平衡

采用小沸点仪测定了马来酸酐和1,2－环己烷二羧酸二异丁酯二元系统在不同配料组成条件下的温度与压力数据，并通过内插法得到不同压力下的温度与配料组成的数据.进一步采用单纯形法优化NRTL方程参数，推算了平衡气液相组成，发现该二元系统具有最高压力恒沸点，且该恒沸点随压力的变化显著.当压力降低至20 kPa时, 由温度随气相组成的变化趋势知该恒沸点将趋于消失.     

团聚纳米SiO_2在苯乙烯乳液聚合过程中的再分散过程及机理

用二氧化硅 (SiO2 )存在下的乳液聚合法制备了聚苯乙烯 (PSt) 纳米SiO2 复合材料 ,研究了苯乙烯(St)乳液聚合过程中团聚纳米SiO2 的解离与再分散过程及分散的机理 .发现商品纳米SiO2 粒子以团聚体形式存在 ,团聚体大小远超出纳米级范围 .随聚合时间的延长 ,St的转化率逐渐增加 ,而PSt SiO2 复合微胶囊的粒径逐渐减小 ,反应 12 0min后 ,转化率和复合微胶囊粒子的粒径趋于稳定 .透射电镜 (TEM)也显示PSt SiO2 复合微胶囊粒子具有海岛结构 ,而SiO2 粒子的粒径在纳米范围内 ,表明在乳液聚合过程中SiO2 团聚体被逐渐解离 ,并重新分散到纳米尺度 .红外光谱研究发现 ,在乳液聚合过程中 ,除生成PSt均聚物外 ,还在纳米SiO2 表面生成了PSt接枝共聚物 ,改善了无机纳米粒子与聚合物之间的界面相容性 .聚合过程中的反应热和剪切搅拌是团聚体被解离和重新分散的主要原因 ,而生成的聚合物起到隔离作用     

Synthesis and Crystal Structure of a Novel Compound of （C2N2H8O2） H6V10O28

A novel vanadate decamer, involving all vanadium atoms present in +5 oxidation and one formhydroxamic acid dimer cation readical, has been synthesized. The single-crystal X-ray diffraction shows that the orange crystal is formed in the triclinic system, space group Pi, a = 8. 4960 (17), b = 10.447 (2), c = 11.299 (2) A, α= 68. 82 (3)°,β= 87.35 (3)°, γ = 66.97(3)°. V = 855. 3(3) A3, Z = 8, R1 = 0. 0857, wR2=0. 2551. X-ray crystallographic and packing in superlattice studies showed that the crystal structure was constructed by electrostatic attraction of O-H…O hydrogen bonds between formhydroxamic acid dimer cation and decavanadate polyanion. Formhydroxamic acid dimer is got through controlling the condition of the reaction using formhydroxamic acid.     

2，6-二-0-丙基-β-CD键合硅胶固定相的合成与色谱性能考察

合成2，6-二-0-丙基-β-CD键合硅胶固定相(PCDS)；利用傅里叶红外光谱、X射线光电子能谱、莫氏(Molisch)试验颜色反应进行了表征；以邻苯二甲酸二甲酯、甲苯和菲为测试溶质，评价该键合固定相的色谱性能；并考察了该固定相对一些位置异构体和手性药物的色谱分离效果；讨论了可能的分离机理。     

联吡啶铁/H2O2体系在可见光下降解芥子气模拟剂2-CEES

采用联吡啶铁/H2O2体系在可见光照射条件下(λ>450nm)降解芥子气模拟剂2-氯乙基乙基硫醚(2-CEES).考察了不同反应条件下的降解效果,通过EPR分析确定了反应过程中产生的高活性物种,利用GC-MS和NMR等方法分析了反应的产物,跟踪了反应过程中TOC的变化,并根据结果对2-CEES光催化降解的反应机理进行了探讨.     

水热法制备纳米TiO_2及其在水相介质中分散性的研究

以硫酸法钛白粉生产工艺的中间体偏钛酸为原料,采用水热法制备了纳米TiO2粉体。研究了磷酸、硫酸、反应温度及反应时间对TiO2粉体的晶型、粒径及形貌的影响,考察了其在水相介质中的分散性。并借助XRD、SEM、动态激光粒度分析仪和动电位及静态激光粒度分析仪对其进行了表征。