Mesoporous nanotube aggregates obtained from hydrothermally treating TiO2 with NaOH

Nanotube aggregates with high porosity were prepared from hydrothermal treatment of TiO₂ particles in NaOH at 130 °C, followed by HCl rinsing to different pH values. Pore structure of the aggregates, which were mainly mesoporous, was characterized by analyzing the N₂ sorption isotherm with different methods including the t-plot and density function theory. The surface area, pore volume and mean pore size of the aggregates increased with the rinsing acidity to reach a maximum (e.g. 400 m²/g in surface area) at pH 1.6 and then decreased with further increase of the acidity. The crystalline phase and composition of the aggregates were, as well, significantly affected by the acidity of the post-treatment rinsing. Large-surface area aggregates were of loosely-attached nanotubes, composed of both anatase TiO₂ and H₂Ti₂O₅·H₂O, obtained under a mildly acidic rinsing condition, while basic or highly acidic conditions resulted in the formation of closely coagulated dense structures consisting of different crystalline phases.     

AB5型球形合金粉的表面处理研究

由雾化（Gas－atomization）技术制备的AB5型球形合金粉，作为镍氢电池负极材料具有很多优点：粉粒呈球状便于在多孔基片内装填；耐压耐磨性好；抗碱能力强且不易解胶．但它的电化学初活性差，难于活化．有碍电池中的应用．采用适宜的氧化剂（铜盐水溶液）处理，使球粒表面形成一个富铜、富镍亚层，显著地改善了合金粉的电化学活性．经处理的MlNi3.8CO0.5Mn0.3Al0.4球形合金粉，仅3次充放电循环其放电量便可达到240mA·h·g-1；而未经处理的同一合金粉即便经6次充放电循环其放电量也只有103mA·h·g-1．     

后处理对TiO_2纳米薄膜的表面结构和光催化活性的影响

半导体TiO2光催化材料对环境中各种污染物的明显去除效果已引起人们的广泛关注犤1～6犦。在普通钠钙玻璃表面涂制高光催化活性的TiO2纳米薄膜,制成环保建筑材料,不仅可以自洁玻璃表面,而且可以用于净化空气、处理废水等。但由于在热处理过程中玻璃基体内的Na+离子扩散到薄膜表面,形成光生电子和空穴的复合中心,使TiO2纳米薄膜的光催化活性大大降低犤7～10犦。为了减少玻璃中Na+离子对TiO2薄膜光催化活性的有害影响,Paz等犤8犦研究了将钠钙玻璃浸入酸溶液中,使玻璃表面的钠离子被酸中的氢离子置换出来;在玻璃表面形成SiO2凝胶层,以便阻…     

高效液相色谱法所用大孔硅胶填料的制备

对国产ＧＹＱＧ球形硅胶施加高压水热处理并进行扩孔，制备了用于高效液相色谱法的大孔硅胶填料，考察了扩孔压力，扩孔温度和扩孔时间对平均孔径和比表面积的影响。并将产品日本ＳＩＬ－３００３×１０＾－８ｍ硅胶进行了物理性质和孔分布的对比实验，结果表明ＧＹＱＧ硅胶扩孔后平均孔径为２０～３０ｎｍ接近日本ＳＩＬ－３００３×１０＾－８ｍ硅前平平均孔径２５ｎｍ。display structure     

水中铬污染治理的研究进展

综述了水中铬污染治理的研究进展,包括物理法、物理化学法、化学法、电化学法和生物处理法,并分别评述了各种处理方法的优缺点,提出了未来含铬废水治理的发展方向。     

硼酸酯偶联剂的合成与表征

通过分子结构设计，合成了一种氮一硼内配位结构的硼酸酯偶联剂，解决了硼酸酯水解稳定性差的问题，同时分子结构中含有氨基、丁氧基等活性基团。用傅立叶变换红外光谱对硼酸酯进行了结构表征，讨论了原料配比、合成工艺等对硼酸酯收率及反应速率的影响，并通过实验确定了最佳配方及工艺。对硼酸酯的物理性能、溶解性、水解稳定性及对硼酸铝晶须的表面处理效果进行了表征。结果表明：合成的硼酸酯偶联剂由于具有氮-硼内配位作用，表现出优良的水解稳定性，并且硼酸酯偶联剂对硼酸铝晶须具有良好的表面改性效果。     

笼形聚偕胺肟树脂的研究──酸处理树脂吸附H_2PdCl_4

考查了无机酸、羧酸和酚类化合物处理的笼形聚偕胺肟树脂吸附酸性溶液中H_2PdCl_4的能力，其中H_3BO_3/ACAO、HSCH_2CO_2H/ACAO和p－NH_2C_6H_4H/ACAO树脂对H_2PdCl_4的吸附容量分别是2．023、2．368和2．083mmol/g-R或215、252和222mgPd／g－R。优于相同条件下的碱处理树脂（BCAO吸附容量为1．828mmol/g-R）。研究了吸附动力学，讨论了吸附机理。     

INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAPFREE P（MMA-EA-MAA） PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION

Soap-free poly（methyl methacrylate-ethyl acrylate-methacrylic acid） latex particles with narrow size distribution were synthesized by seeded emulsion polymerization, and the porous particles were created by a stepwise alkali/acid treatment method. Effects of acid treatment conditions on the particle morphology were investigated. Results show that one to three pores were formed inside most of particles after post-treatment. At pH 7.0, when the treatment temperature was lower than 70℃, the size of particles and the volume of pores remained almost unchanged, and these two values increased significantly when the temperature was higher than 70℃. Both the particle size and the pore volume decreased with the increase of initial pH value and treatment time in the acid treatment. As the pH was below 4.0 and the treatment time was longer than 180 min, the particles shrunk in size.     

Evaluation of Photocatalytic Activity of Transparent Anatase Nanocrystals-Dispersed Silica Films Prepared by the Sol-Gel Process with Hot Water Treatment

Anatase nanocrystals were precipitated mainly at the surface of the silica-titania gel films with hot water treatment, whereas the addition of poly(ethylene glycol) (PEG) in the films led to the dispersion of anatase nanocrystals in the whole of the films after the treatment. Both films with and without PEG showed high photocatalytic activities for acetaldehyde, NO _x and stearic acid in the gas-solid system, and for methylene blue and potassium iodide in the liquid-solid system. The addition of PEG improved the photocatalytic activities of the resultant films due to the smaller anatase crystallites and the porous film structure. The residual silica under-layer of the superficially anatase-precipitated films is expected to act as a protective one for an organic polymer substrate against the photocatalytic degradation.     

树脂吸附法处理水杨酸甲酯生产废水的研究

采用吸附树脂NDA—99处理水杨酸甲酯生产废水，结果表明该树脂时废水中的5磺基水杨酸及水杨酸均具有良好的吸附—脱附性能．废水经预处理和吸附处理后，CODCr由57000-59000mg／L降至6300mg／L左右，去除率接近89％．用IBV8％NaOH 3BVH2O作脱附剂，在温度为60℃、流量为IBV／h的条件下，脱附率接近100％，树脂可重复使用．高浓度脱附液经酸化、浓缩、冷却结晶，可回收5—磺基水杨酸，回收率为95％左右。纯度为78％。