卤化铅调整Tm3+/Yb3+共掺碲酸盐玻璃上转换发光研究

研究了卤化铅调整Tm³⁺/Yb³⁺共掺碲酸盐玻璃的热稳定性能、Raman 光谱和上转 换发光光谱，分析了Tm³⁺/Yb³⁺共掺氧卤碲酸盐玻璃的上转换发光 机理.结果发 现：混合卤化铅调整Tm³⁺/Yb³⁺共掺碲酸盐玻璃具有好的热稳定性 能、低的声 子能量、强的上转换蓝光.这表明混合卤化铅调整Tm³⁺/Yb³⁺共掺碲 酸盐玻璃是一种上转换蓝光激光器的潜在基质材料. 关键词： 氧卤碲酸盐玻璃 上转换光谱 发光机理 上转换蓝光激光器     

激光二极管抽运(Tm,Ho)∶YLF激光器光谱特性实验分析

Ho∶YLF晶体的5I7和5I8斯塔克能级分裂数较多,形成2047~2070nm宽的增益谱带,对于可调谐2μm激光及宽带激光放大器研究具有重要意义。理论上分析了(Tm,Ho)∶YLF晶体的能级结构,并对晶体掺杂浓度和长度进行了优化。实验研究了激光二极管抽运微片Tm(原子数分数0.06),Ho(原子数分数0.004)∶YLF激光谱线可调谐特性,调谐范围2.0656~2.0671μm。利用(Tm,Ho)∶YLF晶体的宽增益谱特性,将其作为激光二极管抽运激光放大器,成功地将2.048μm(Tm,Ho)∶GdVO4激光功率放大了2.5倍。实验上测量了(Tm,Ho)∶YLF晶体在强抽运条件下480~492nm及530~550nm可见波段的上转换蓝绿光荧光谱。     

Picosecond time-resolved laser emission of coumarin 102: Solvent relaxation

The time-resolved laser emission of coumarin 102 was investigated in various aprotic and protic solvents at picosecond resolution by frequency upconversion technique. The spectral shift of the transient emission spectrum is attributed to solvent reorientation and the results are discussed.     

应用于白光显示的Tm3+/Ho3+/Yb3+共掺碲酸盐玻璃上转换发光特性研究

用高温熔融法制备了Tm³⁺/Ho³⁺/Yb³⁺共掺碲酸盐玻璃(TeO₂-ZnO-La₂O₃)样品,测试了玻璃样品的吸收光谱和上转换发光光谱,分析了上转换发光机理.结果发现:在975 nm波长激光二极管(LD)激励下,制备的碲酸盐玻璃样品可以观察到强烈的红光(662 nm)、绿光(546 nm)和蓝光(480 nm)三基色上转换发光,红光对应于Tm³⁺离子 关键词： 碲酸盐玻璃 上转换发光 白光 3+/Ho³⁺/Yb³⁺共掺')" href="#">Tm³⁺/Ho³⁺/Yb³⁺共掺     

NaLuF4∶Yb3+,Er3+微米晶的制备及上转换发光

采用EDTA辅助法合成了NaLuF4∶Yb3+,Er3+微米晶,用X射线粉末衍射(XRD)对样品的结构进行了表征。XRD分析表明样品NaLuF4为六角相。研究了初始反应溶液的pH值对NaLuF4∶Yb3+,Er3+微米晶的组分、形貌和荧光性质的影响。在980 nm光激发下,观察到了4G11/2→4I15/2、2H9/2→4I15/2、2H11/2→4I15/2、4S3/2→4I15/2和4F9/2→4I15/2发射,荧光强度比I(2H11/2/4S3/2→4I15/2)/I(4F9/2→4I15/2)和I(4G11/2/2H9/2→4I15/2)/I(2H11/2/4S3/2→4I15/2)随着pH值的变化而变化。研究了样品的上转换发光机制。     

Influences of Mg^2＋ ion on dopant occupancy and upconversion luminescence of Ho^3＋ ion in LiNbO3 crystal

The effects of a Mg^2＋ ion on the dopant occupancy and upconversion luminescence of a Ho^3＋ ion in LiNbO3 crystal are reported. The birefringence gradient of the crystal is measured to investigate the optical homogeneity. The X-ray powder diffraction spectrum and the upconversion luminescence are used to investigate defect structure and spectroscopic properties of Mg,Ho：LiNbO3. Under 808-nm excitation, blue, red, and very intense yellow-green bands are observed. Based on the energy levels of Ho^3＋ in LiNbO3, and the pump intensity dependence of the observed emission, an excitation scheme is presented. The upconversion emission spectra reveal an enhancement of upconversion intensity when the Mg^2＋ ions are introduced into Ho：LiNbO3. The main upconversion mechanism is discussed in this work.     

低温下Er3+/Yb3+共掺碲酸盐玻璃的发光特性研究

研究了在8—300K温度范围中, Er³⁺/Yb³⁺共掺碲酸盐玻璃的15μm荧光光谱、上转换光谱与温度的关系. Er³⁺:⁴I_13/2→⁴I_15/2跃迁发射光谱通过高斯拟合和简单的四能级系统估计了Er³⁺离子⁴I_13/2和⁴ 关键词： 碲酸盐玻璃 上转换发光 低温 荧光特性     

水热合成六方相NaYbF4∶Er3+/Tm3+的上转换白光性质

在反应温度为220℃,反应时间为48h的温和条件下,利用水热法合成单掺杂或共掺杂Tm3 、Er3 的六方相NaYbF4体系,利用X射线粉末衍射、紫外-可见-近红外漫反射吸收光谱以及荧光光谱等测试手段,分析体系的物相结构和荧光性能。在980nm红外激光的激发下,NaYbF4∶Er3 体系能发出强的绿光和红光,两者分别对应于Er3 离子的(2H11/2,4S3/2)→4I15/2、4F9/2→4I15/2能级跃迁;NaYbF4∶Tm3 体系能发出对应于Tm3 离子1D2→3F4和1G4→3H6能级跃迁的强蓝光;而NaYbF4∶Er3 /Tm3 体系能同时发出红蓝绿三种颜色的光;各发射的归属与单掺杂相同,但由于Er3 和Tm3 离子之间存在能量交叉弛豫,致使各发光强度发生变化。通过控制Er3 和Tm3 离子的浓度及其比例,可以调整NaYbF4∶Er3 /Tm3 体系的上转换蓝光、绿光和红光强度的比例,结果表明,在980nm红外激光的激发下,NaYbF4∶Er3 /Tm3 (0.4%/0.4%)能发出近似白光的上转换发射。因此,NaYbF4∶Er3 /Tm3 有望成为单一基质的上转换白光材料。