CeO2-ZrO2-Y2O3对Pt-Rh型三效催化剂性能的影响

采用共沉淀法技术制备了Ce0.35Zr0.55Y0.10固溶体,并对其进行了比表面积、储氧量的测试和XRD的表征.将其用于低贵金属Pt-Rh型三效催化剂的制备,考察了CeO2-ZrO2-Y2O3对三效催化剂性能的影响.结果表明,Ce0.35Zr0.55Y0.10具有与Ce0.50Zr0.50O2相似的立方结构和相近的储氧量,经高温(1000 ℃)后仍能保持较大的比表面积(38.66 m2·g-1).和含Ce0.50Zr0.50O2的三效催化剂相比,含CeO2-ZrO2-Y2O3的三效催化剂经高温老化后,C3H8,CO,NO仍具有较高的转化率和较低的起燃温度.     

具可调光学性质的富勒烯聚合物

聚（Ｃ６０ 甲基丙烯酸甲酯）与聚（Ｃ６０ 苯乙烯）的ＴＨＦ溶液的透射光谱随浓度的增大而不断红移．这种异常的光谱位移可能与富勒烯的纳级（１０－９）簇的形成有关．用简单的办法来“调改”一物质的性质是科学家们长期梦寐以求的，而含Ｃ６０的聚合物正代表了这一群新奇的物质，它们的光学性质可以预期地和可逆地调变，只要简单改变一下浓度．     

Pressurized hot water extraction of berberine, baicalein and glycyrrhizin in medicinal plants

Pressurized hot water extraction (PHWE) using a laboratory made system was applied for the extraction of thermally labile and reasonably polar components such as berberine in coptidis rhizoma, glycyrrhizin in radix glycyrrhizae/liquorice and baicalein in scutellariae radix. PHWE was carried out dynamically at a flow of 1 ml/min, temperature between 95 and 140 °C, an applied pressure of 10-20 bar and extraction time of 40 min. Extraction by PHWE was found to give efficiencies comparable to Soxhlet extraction for baicalein in scutellariae radix and sonication for berberine in coptidis rhizoma, and glycyrrhizin in radix glycyrrhizae. Effects of ethanol added into the water used in PHWE were explored. Pressurized liquid extraction (PLE) with methanol as solvent was used for extraction of baicalein in scutellariae radix. The marker compounds present in the various medicinal plant extracts were determined by gradient elution HPLC.     

Phase transition in single crystal Cs2Nb4O11

We studied temperature dependence of complex capacitance, impedance, and polarized Raman spectra of single crystal Cs2Nb4O11. First, we observed a sharp lambda-shaped peak at 165 degrees C in the complex capacitance, then found drastic changes in the Raman spectra in the same temperature range. Utilizing the pseudosymmetry search of structure space group, we attributed the observed anomalies to a structural change from the room temperature orthorhombic Pnn2 to another orthorhombic Imm2. We also measured room temperature polarized Raman spectra in different symmetries of normal vibrations and assigned high wavenumber Raman bands to the internal vibrations of NbO6 octahedra and NbO4 tetrahedra.     

鹿角短指软珊瑚Sinularia Cervicornis Tix-Dur 中的一个新糖甙-Cervicoside

珊瑚属腔肠动物门 ( Clelenterata) ,海鸡冠目 ( Alcyonacea) ,是一种热带与亚热带海洋中广泛分布Scheme 1　 Structure of cervicoside(1 )的低等海洋生物 .软珊瑚的次生代谢物中含有萜类和甾体类等各类生理活性物质[1～ 5] .我们在对鹿角短指软珊瑚的次生代谢产物研究中 ,分离到一个新三糖甙 ,命名为 Cervicoside( 1 ) ,结构见 Scheme 1 .该化合物具有较强的体外抗癌活性 .1　实验部分1 .1　样品　鹿角短指软珊瑚采自海南岛三亚海域 .样品储藏于中山大学化学与化学工程学院天然有机化学研究室 ,编号为 98- SY- 3.种属由中国科学院南海…     

Fluorinated poly(arylene ether ketone)s bearing pentafluorostyrene moieties prepared by a modified polycondensation

The polycondensation of decafluorobenzophenone with hexafluorobisphenol A was modified by the addition of a molecular sieve dehydrating apparatus to the refluxing reaction system. This modification promoted the polymerization and enabled the reactions to be conducted in milder conditions and completed in a shorter time, thereby depressing side reactions such as branching and crosslinking. The resulting fluorinated poly(arylene ether ketone)s (FPAEK) were free of gel particles and possessed the designed molecular weights. This modified procedure was also suitable for introducing crosslinkable pentafluorostyrene (FSt) moieties into the polymers at the chain ends and/or inside the chain with the vinyl group of FSt being pendant. The resulting FSt containing fluorinated poly(arylene ether ketone)s (FPAEK‐FSt) can then be thermally crosslinked at 100 °C in the presence of 1% benzoyl peroxide (BPO) or at 250 °C without any initiator. The glass‐transition temperatures (T_g's) of FPAEK increased with increasing molecular weight and leveled off at about 147 °C for the polymer with a number‐average molecular weight of 18,600 Da, whereas the values were not apparently affected by the addition of FSt units. However, crosslinking of the FPAEK‐FSt resulted in an approximate 30 °C increase of the T_g. Spin‐coating FPAEK‐FSt onto silicon wafers followed by crosslinking gave films with excellent thermal stability, physical strength, and adhesion to the substrate as well as good reproducibility in terms of film preparation and optical properties. The refractive index and birefringence of the films measured at a wavelength of 1.55 μm were 1.502 and 2.5 × 10^?3, respectively. © 2002 Government of Canada. Exclusive worldwide publication rights in the article have been transferred to Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 4205–4216, 2002     

吉西他滨类似物的设计、合成及体外抗肿瘤活性

吉西他滨是临床一线治疗恶性肿瘤的药物,但其4-位氨基(N4)易与脱氧胞苷脱氨酶(CDA)作用而失活,导致代谢稳定性差,严重影响了临床治疗效果。以吉西他滨为起始原料,经3步反应合成了N4保护的脂溶性吉西他滨衍生物(3a和3b),其结构经1H NMR,13C NMR和HR-MS(ESI)表征。体外活性测试结果显示:化合物3a对多种肿瘤细胞的抗增殖作用均强于临床药物吉西他滨(P<0.05)。酶稳定性实验结果表明:3a几乎不受CDA影响,代谢稳定性显著高于原药吉西他滨。     

K-Pb-Tl-O复合氧化物的合成和电子结构的XPS研究

用熔盐阳极电沉积法合成了导电的复合氧化物K-Pb-Tl-O晶体.这些晶体具有纳米尺寸层状结构.用XPS对其进行了表征,并与相关的化合物进行了比较.实验表明,氧化物中的Pb和Tl都以高价态的单一价态存在,但电子结合能比相应的非导电低价化合物的低.该文用原子外弛豫效应解释了复合氧化物中的Pb和Tl的结合能的反常现象.讨论了它们的价电子结构与导电性的关系.     

Preparations of ginsenoside Rg1 immunogen and125I-labeled antiğen

This work began with the side chain of ginsenoside Rg₁ which was acetylized with Ac₂O-Pyr and oxidized by OsO₄ and NaIO₄ to give ginsenoside Rg₁ aldehyde(2), which was further converted into an unsaturated ester(3) by Wittig-Horner reaction. The unsaturated ester(3) was treated with N₂H₄ and HNO₂ to yield Rg₁ azide(4) which was directly conjugated with BSA to give immunogen: ginsenoside Rg₁-BSA conjugate(5). This azide(4) was conjugated with tyramine to give ginsenoside Rg₁-tyramine conjugate which was labelled with free Na¹²⁵I by CH-T to yield¹²⁵I-labeled antigen: gensenoside Rg₁-¹²⁵I-tyramine(6). The labelling rate was 40%–50% and specific activity was 3.0–4.0 MBq/g.     

Thermal degradation and flame retardancy of flexible polyvinyl chloride containing solid superacid

The objective of the present article was to study the thermal degradation behavior and flame retardancy of flexible polyvinyl chloride (PVC) composites containing TiO₂/SO ^2?₄ solid superacid because of its strong catalytic ability for esterification and dehydration. The TiO₂/SO ^2?₄ solid superacid was synthesized by using precipitation immersion method, and its structure was investigated by X-ray diffraction. As expected, the value of limiting oxygen index for PVC/Sb₂O₃/(TiO₂/SO ^2?₄ ) composite was 32.5% and the char yield of PVC/Sb₂O₃/(TiO₂/SO ^2?₄ ) composite was significantly improved compared to neat PVC in thermogravimetry tests. In addition, the peak heat release rate and smoke production rate of PVC/Sb₂O₃/(TiO₂/SO ^2?₄ ) decreased by 14% and 42%, respectively, compared with neat PVC. Moreover, the results of cone calorimetry tests and electron micrograph of char residue showed that the char yield of TiO₂/SO ^2?₄ was enhanced, resulting in a strong char layer structure with outstanding fire retardance cone. In conclusion, the results of this work showed that the addition of solid superacid promoted the decomposition and dehydration of PVC, which formed a compact and continuous char layer on the surface of the material. Hence, the study provides a new perspective for producing composites with excellent flame retardancy and smoke suppression properties of PVC.