水热法合成Ce0.67Zr0.33O0.2固溶体研究

采用两种不同前驱体通过水热法合成了Ce0.67Zr0.33O0.2固溶体,并通过XRD,BET,TPR等手段考察了样品的相结构,比表面及还原特性.结果表明,在180℃,12 h的水热条件下,以共沉淀产物为前驱体所制得的Ce0.67Zr0.33O0.2固溶体比表面积较高,但存在一定程度的相分离;以凝胶产物为前驱体制得的Ce0.67Zr0.33O0.2固溶体结构更完整,具有良好的还原特性及热稳定性.     

CdSe/ZnS-labeled carboxymethyl chitosan as a bioprobe for live cell imaging

A simple and convenient method for the construction of CdSe/ZnS-labeled polysaccharides as bioprobes were developed, which are highly biocompatible and photostable, and have been proven to be suitable for live cell imaging.     

Study on analysis of153Sm-EDTMP stability in vitro and vivo by HPLC

The behavior of¹⁵³Sm-EDTMP in vitro and vivo is analyzed by the size exclusion HPLC. The experimental results show that EDTMP amounts have an obvious effect on the stability in vitro and uptake of¹⁵³Sm-EDTMP in the liver. HPLC analysis of urine sample indicates that¹⁵³Sm-EDTMP es excreted in the original form. The behavior in vivo of¹⁵³Sm-EDTMP containing 4 μg is similar to that of¹⁵³Sm-EDTMP containing 50 μg EDTMP at 1 h post-injection.     

INFLUENCES OF ACID POST-TREATMENT ON THE MORPHOLOGY OF SOAPFREE P（MMA-EA-MAA） PARTICLES PREPARED BY SEEDED EMULSION POLYMERIZATION

Soap-free poly（methyl methacrylate-ethyl acrylate-methacrylic acid） latex particles with narrow size distribution were synthesized by seeded emulsion polymerization, and the porous particles were created by a stepwise alkali/acid treatment method. Effects of acid treatment conditions on the particle morphology were investigated. Results show that one to three pores were formed inside most of particles after post-treatment. At pH 7.0, when the treatment temperature was lower than 70℃, the size of particles and the volume of pores remained almost unchanged, and these two values increased significantly when the temperature was higher than 70℃. Both the particle size and the pore volume decreased with the increase of initial pH value and treatment time in the acid treatment. As the pH was below 4.0 and the treatment time was longer than 180 min, the particles shrunk in size.     

生物柴油及1,3-丙二醇联产工艺产业化进展

生物柴油作为可再生的清洁能源,已在美国、欧盟等多个国家和地区推行使用。在生物柴油的生产过程中,最高可得到约10%的副产物甘油,副产物甘油的去向将成为生物柴油大规模产业化发展所面临的严峻问题。1,3-丙二醇是一种重要的化工原料,作为合成新型聚酯PTT的原料,1,3-丙二醇已引起人们的广泛关注。以生物柴油副产物甘油为原料耦合生产1,3-丙二醇,不仅解决了生物柴油副产物甘油的出路问题,同时降低了1,3-丙二醇的生产成本。本文详细介绍了生物柴油及1,3-丙二醇生产技术及联产工艺的研究进展,并对其应用前景进行了展望。     

金汞齐富集冷原子荧光测汞法的研究

本文介绍了一种用于测定汞的金汞齐富集热解系统。研究了该系统与冷原子荧光测汞仪联用的工作条件和干扰,在最佳条件下的检出下限为4×10~(-13)克汞,分析周期3分钟,相对标准偏差2.5%(1.5×10~(-9)克汞)。     

Eigenschaften von Chalkogen-Chalkogen-Bindungen. XII. Reversible Tellurierung von Tetraisopropyldiphosphan; Stabilisierung von Tellurobis(diisopropylphosphan) als Tetracarbonylchromkomplex

Properties of Chalcogene-Chalcogene Bonds. XII. Reversible Telluration of Tetraisopropyldiphosphane, Stabilisation of Tellurobis(diisopropylphosphane) as Tetracarbonylchromium Complex Tetraisopropyldiphosphane 1 reacts with elemental tellurium by tellurium atom insertion to give tellurobis(diisopropylphosphane) 2. 2 is also available from sodium telluride with chlorodiisopropyl phosphane. ^lH, ^l3C, ^3lP and ^l25Te n.m.r. spectra confirm that in solution 2 is in an equilibrium with the educt 1 and elemental tellurium. Reaction of this equilibrium mixture with tetracarbonyl(norbornadiene)chromium(0) provides tetracarbonyl[tellurobis(diisopropylphosphane)]-chromium(0) 3. 3 was isolated in pure state as stable compound; different from 2,3 does not suffer from loss of tellurium at room temperature.     

氧化铬着色的随角异色颜料的制备与性能研究

采用具有干涉色的云母钛作为基质材料,以氧化铬膜着色,制备了随角异色功能颜料。用XRD、X-RiteMA86Ⅱ5角度分光光度计对产物进行测试分析,研究了不同的基质材料对颜料随角异色效果的影响,分析比较了黑白两种不同背底对颜料的明度和变化效果的影响。结果表明,改变基质材料的干涉色可以制得不同变色效果的随角异色颜料,颜料在黑色背底上的明度值变化范围较大,颜料的变色效果比较明显。     

稀土在鼠肝中的物种分布

采用 ICP-MS、微量蛋白层析分离技术 ,研究了长时间、低剂量混合稀土及短时间、高剂量硝酸镧分别对大鼠及小鼠作用后 ,稀土在鼠肝中的代谢累积及其物种分布 .结果表明 ,鼠肝中各稀土含量随给药剂量的增加而增大 ,其累积速度大小顺序为 La>Ce>Nd>Pr;经柱层析分离未得到与稀土特异结合的鼠肝蛋白 ;稀土可与多种鼠肝蛋白 (包括多种重要的酶 )结合 ,在一定条件下 ,稀土与其结合蛋白可发生解离